Despite the success of guided wave ultrasonic inspection for internal defect detection in steel pipes,its application on polyethylene(PE)pipe remains relatively unexplored.The growth of internal cracks in PE pipe seve...Despite the success of guided wave ultrasonic inspection for internal defect detection in steel pipes,its application on polyethylene(PE)pipe remains relatively unexplored.The growth of internal cracks in PE pipe severely affects its pressure-holding capacity,hence the early detection of internal cracks is crucial for effective pipeline maintenance strategies.This study extends the scope of guided wave-based ultrasonic testing to detect the growth of internal cracks in a natural gas distribution PE pipe.Laboratory experiments and a finite element model were planned to study the wave-crack interaction at different stages of axially oriented internal crack growth with a piezoceramic transducer-based setup arranged in a pitch-catch configuration.Mode dispersion analysis supplemented with preliminary experiments was performed to isolate the optimal inspection frequency,leading to the selection of the T(0,1)mode at 50-kHz for the investigation.A transmission index based on the energy of the T(0,1)mode was developed to trace the extent of simulated crack growth.The findings revealed an inverse linear correlation between the transmission index and the crack depth for crack growth beyond 20%crack depth.展开更多
CsPbX_(3)-based(X=I,Br,Cl)inorganic perovskite solar cells(PSCs)prepared by low-temperature process have attracted much attention because of their low cost and excellent thermal stability.However,the high trap state d...CsPbX_(3)-based(X=I,Br,Cl)inorganic perovskite solar cells(PSCs)prepared by low-temperature process have attracted much attention because of their low cost and excellent thermal stability.However,the high trap state density and serious charge recombination between low-temperature processed TiO_(2)film and inorganic perovskite layer interface seriously restrict the performance of all-inorganic PSCs.Here a thin polyethylene oxide(PEO)layer is employed to modify TiO_(2)film to passivate traps and promote carrier collection.The impacts of PEO layer on microstructure and photoelectric characteristics of TiO_(2)film and related devices are systematically studied.Characterization results suggest that PEO modification can reduce the surface roughness of TiO_(2)film,decrease its average surface potential,and passivate trap states.At optimal conditions,the champion efficiency of CsPbI_(2)Br PSCs with PEO-modified TiO_(2)(PEO-PSCs)has been improved to 11.24%from 9.03%of reference PSCs.Moreover,the hysteresis behavior and charge recombination have been suppressed in PEO-PSCs.展开更多
Several works have been based on the study of thermal variations in biomass to derive more valuable products such as fuels capable of replacing oil in the event of a crisis or activated carbon used as an adsorbent mat...Several works have been based on the study of thermal variations in biomass to derive more valuable products such as fuels capable of replacing oil in the event of a crisis or activated carbon used as an adsorbent material, widely used in industry for the elimination of unwanted materials, both in liquid and gaseous environments. A study of thermal parameters such as: heating speed, retention time, drying temperature, carbonization temperature, particle size, was carried out with the aim of determining the characteristic factors of the carbonization of Polyethylene terephthalate (PET), sawdust (SC) and sawdust/polyethylene terephthalate (CPS) mixture. The results of the immediate analysis revealed a very low level of ash in PET (0.013%) compared to the level of ash in sawdust (2.9%), as well as a high level of fixed carbon (82.960%), which suggests the presence of mineral oxides and a significant carbon matrix unlike PET, which indicates a very significant organic matrix (essentially made up of organic matter) with the absence of mineral oxides. The study of thermal parameters showed the water loss from Sawdust (SC) and the Sawdust/Polyethylene terephthalate (CPS) mixture, an increase with temperature, unlike that of PET whose variation is essentially zero. Without heat treatment, sawdust alone contains approximately 7% water. The optimal drying temperature for this study is 110˚C for a stay of 24 hours. It appears that the largest mass losses for the PET samples are between 87.19% and 96.05%, followed by that of the mixture, between 47.33% and 64.37%. And the lowest are observed, those of sawdust (from 24.02% to 62.6%). However, here we can say that the influence of the mass is not great, given the slight difference between the losses by temperature. The results of the study of the influence of grain size showed that the differences are insignificant, even if we vary the diameter of the grains from simple to triple. To better minimize physical constraints such as the intragranular diffusibility of the volatile matter and the homogeneity of the temperature in the grains, 75 μm particles are found to be optimal for our study. It can be noted when studying the heating rate that the mass loss at the end of the reaction is approximately the same depending on each precursor material. However, it has been demonstrated that the heating rate strongly influences the nature of the reaction products both for volatile materials and for the solid residue as well as on the kinetic parameters of the chemical reaction. Furthermore, the variation in apparent density shows a decrease as a function of the increase in the residence time of the materials in the reactor. As the carbonization time increases, the apparent density decreases. We note, for the lignocellulosic material, that the apparent density stabilizes after 60 minutes.展开更多
Currently,accelerated aging tests are widely used to study the aging process of polyethylene pipelines.However,this approach can only simulate one or several main influencing factors in the natural environment,which a...Currently,accelerated aging tests are widely used to study the aging process of polyethylene pipelines.However,this approach can only simulate one or several main influencing factors in the natural environment,which are often quite different from the actual environment of the buried pipelines.In this study,five types of PE80 buried pipelines in service for 9e18 years were taken as the research object,while new PE80 pipelines were taken as the reference group.The aging process and mechanism of polyethylene buried pipelines were studied through mechanical and chemical property tests and microstructural analysis.The results showed that the pipeline exhibited cross-linking as the main aging mechanism after being in service for 0e18 years.The aging degree and law of the inner and outer surface of the pipeline were compared,and the observed mechanism of both surfaces was explained.After 18 years in service,the elongation at the break of the pipe decreased by 16.2%,and the toughness of the matrix in the main collapse area of the tensile sample was the fundamental reason responsible for changes in the mechanical properties.Finally,after 18 years in service,the oxidation induction time of the pipeline was 25.7 min,which was 28.5% higher than the national standard value.There were no potential safety hazards during continuous long-term service.The results of this paper provide reference data and theoretical guidance for the aging process study of buried polyethylene pipelines.展开更多
基金the financial support provided by USDOT Pipeline and Hazardous Materials Safety Administration (PHMSA)through the Competitive Academic Agreement Program (CAAP)。
文摘Despite the success of guided wave ultrasonic inspection for internal defect detection in steel pipes,its application on polyethylene(PE)pipe remains relatively unexplored.The growth of internal cracks in PE pipe severely affects its pressure-holding capacity,hence the early detection of internal cracks is crucial for effective pipeline maintenance strategies.This study extends the scope of guided wave-based ultrasonic testing to detect the growth of internal cracks in a natural gas distribution PE pipe.Laboratory experiments and a finite element model were planned to study the wave-crack interaction at different stages of axially oriented internal crack growth with a piezoceramic transducer-based setup arranged in a pitch-catch configuration.Mode dispersion analysis supplemented with preliminary experiments was performed to isolate the optimal inspection frequency,leading to the selection of the T(0,1)mode at 50-kHz for the investigation.A transmission index based on the energy of the T(0,1)mode was developed to trace the extent of simulated crack growth.The findings revealed an inverse linear correlation between the transmission index and the crack depth for crack growth beyond 20%crack depth.
基金financially supported by the Guangzhou Basic and Applied Basic Research Foundation,China(No.303523)。
文摘CsPbX_(3)-based(X=I,Br,Cl)inorganic perovskite solar cells(PSCs)prepared by low-temperature process have attracted much attention because of their low cost and excellent thermal stability.However,the high trap state density and serious charge recombination between low-temperature processed TiO_(2)film and inorganic perovskite layer interface seriously restrict the performance of all-inorganic PSCs.Here a thin polyethylene oxide(PEO)layer is employed to modify TiO_(2)film to passivate traps and promote carrier collection.The impacts of PEO layer on microstructure and photoelectric characteristics of TiO_(2)film and related devices are systematically studied.Characterization results suggest that PEO modification can reduce the surface roughness of TiO_(2)film,decrease its average surface potential,and passivate trap states.At optimal conditions,the champion efficiency of CsPbI_(2)Br PSCs with PEO-modified TiO_(2)(PEO-PSCs)has been improved to 11.24%from 9.03%of reference PSCs.Moreover,the hysteresis behavior and charge recombination have been suppressed in PEO-PSCs.
文摘Several works have been based on the study of thermal variations in biomass to derive more valuable products such as fuels capable of replacing oil in the event of a crisis or activated carbon used as an adsorbent material, widely used in industry for the elimination of unwanted materials, both in liquid and gaseous environments. A study of thermal parameters such as: heating speed, retention time, drying temperature, carbonization temperature, particle size, was carried out with the aim of determining the characteristic factors of the carbonization of Polyethylene terephthalate (PET), sawdust (SC) and sawdust/polyethylene terephthalate (CPS) mixture. The results of the immediate analysis revealed a very low level of ash in PET (0.013%) compared to the level of ash in sawdust (2.9%), as well as a high level of fixed carbon (82.960%), which suggests the presence of mineral oxides and a significant carbon matrix unlike PET, which indicates a very significant organic matrix (essentially made up of organic matter) with the absence of mineral oxides. The study of thermal parameters showed the water loss from Sawdust (SC) and the Sawdust/Polyethylene terephthalate (CPS) mixture, an increase with temperature, unlike that of PET whose variation is essentially zero. Without heat treatment, sawdust alone contains approximately 7% water. The optimal drying temperature for this study is 110˚C for a stay of 24 hours. It appears that the largest mass losses for the PET samples are between 87.19% and 96.05%, followed by that of the mixture, between 47.33% and 64.37%. And the lowest are observed, those of sawdust (from 24.02% to 62.6%). However, here we can say that the influence of the mass is not great, given the slight difference between the losses by temperature. The results of the study of the influence of grain size showed that the differences are insignificant, even if we vary the diameter of the grains from simple to triple. To better minimize physical constraints such as the intragranular diffusibility of the volatile matter and the homogeneity of the temperature in the grains, 75 μm particles are found to be optimal for our study. It can be noted when studying the heating rate that the mass loss at the end of the reaction is approximately the same depending on each precursor material. However, it has been demonstrated that the heating rate strongly influences the nature of the reaction products both for volatile materials and for the solid residue as well as on the kinetic parameters of the chemical reaction. Furthermore, the variation in apparent density shows a decrease as a function of the increase in the residence time of the materials in the reactor. As the carbonization time increases, the apparent density decreases. We note, for the lignocellulosic material, that the apparent density stabilizes after 60 minutes.
基金Special technical support program of the State Administration of Market Supervision(2021YJ021)Science and technology program of the State Administration of Market Supervision(2021MK118,2021MK119).
文摘Currently,accelerated aging tests are widely used to study the aging process of polyethylene pipelines.However,this approach can only simulate one or several main influencing factors in the natural environment,which are often quite different from the actual environment of the buried pipelines.In this study,five types of PE80 buried pipelines in service for 9e18 years were taken as the research object,while new PE80 pipelines were taken as the reference group.The aging process and mechanism of polyethylene buried pipelines were studied through mechanical and chemical property tests and microstructural analysis.The results showed that the pipeline exhibited cross-linking as the main aging mechanism after being in service for 0e18 years.The aging degree and law of the inner and outer surface of the pipeline were compared,and the observed mechanism of both surfaces was explained.After 18 years in service,the elongation at the break of the pipe decreased by 16.2%,and the toughness of the matrix in the main collapse area of the tensile sample was the fundamental reason responsible for changes in the mechanical properties.Finally,after 18 years in service,the oxidation induction time of the pipeline was 25.7 min,which was 28.5% higher than the national standard value.There were no potential safety hazards during continuous long-term service.The results of this paper provide reference data and theoretical guidance for the aging process study of buried polyethylene pipelines.