The polyporous carbon supported tungsten carbide（polyporous C@WC_（1-x）） composite was prepared using hexagonal silica MCM-41 as the hard template by raw material solution impregnation,mechanical milling and simult...The polyporous carbon supported tungsten carbide（polyporous C@WC_（1-x）） composite was prepared using hexagonal silica MCM-41 as the hard template by raw material solution impregnation,mechanical milling and simultaneous reduction and carbonization by temperature programming in mixture gas（CH4/H2）.The structure and morphology of polyporous C@WC（1-x） composite were studied via X-ray diffraction,transmission electron microscopy and so on.The electrocatalytic property was tested for the electroreduction of p-nitrophenol（PNP） in neutral media.Results revealed that the composite is consisted of polyporous carbon and nanocrystalline WC（1-x）,possessing good electrocatalytic activity in the reaction of PNP reduction.展开更多
基金supported by the National Natural Science Foundation of China(No.20973156)
文摘The polyporous carbon supported tungsten carbide（polyporous C@WC_（1-x）） composite was prepared using hexagonal silica MCM-41 as the hard template by raw material solution impregnation,mechanical milling and simultaneous reduction and carbonization by temperature programming in mixture gas（CH4/H2）.The structure and morphology of polyporous C@WC（1-x） composite were studied via X-ray diffraction,transmission electron microscopy and so on.The electrocatalytic property was tested for the electroreduction of p-nitrophenol（PNP） in neutral media.Results revealed that the composite is consisted of polyporous carbon and nanocrystalline WC（1-x）,possessing good electrocatalytic activity in the reaction of PNP reduction.