Existing studies have focused on the behavior of the retaining wall equipped with expanded polystyrene(EPS)geofoam inclusions under semi-infinite surcharge loading rather than limited surcharge loading.In this paper,t...Existing studies have focused on the behavior of the retaining wall equipped with expanded polystyrene(EPS)geofoam inclusions under semi-infinite surcharge loading rather than limited surcharge loading.In this paper,the failure mode and the earth pressure acting on the rigid retaining wall with EPS geofoam inclusions and granular backfills(henceforth referred to as EPS-wall),under limited surcharge loading are investigated through two-and three-dimensional model tests.The testing results show that different from the sliding of almost all the backfill in the EPS-wall under semi-infinite surcharge loading,only an approximately triangular backfill slides in the wall under limited surcharge loading.The distribution of the lateral earth pressure on the EPS-wall under limited surcharge loading is non-linear,and the distribution changes from the increase of the wall depth to the decrease with the increase of the limited surcharge loading.An approach based on the force equilibrium of a differential element is developed to predict the lateral earth pressure behind the EPS-wall subjected to limited surcharge loading,and its performance was fully validated by the three-dimensional model tests.展开更多
The catalytic conversion of polystyrene (PS) was studied in the presence of the materials type HZSM-5, CeO<sub>2</sub>, 10% CeO<sub>2</sub>/HZSM-5 and 20% CeO<sub>2</sub>/HZSM-5, wh...The catalytic conversion of polystyrene (PS) was studied in the presence of the materials type HZSM-5, CeO<sub>2</sub>, 10% CeO<sub>2</sub>/HZSM-5 and 20% CeO<sub>2</sub>/HZSM-5, which were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and nitrogen adsorption at 77K. The catalytic tests were performed via thermogravimetric analysis (TG) at heating rates of 5, 10 and 20˚C min<sup>−1</sup> in a temperature range from 30˚C to 900˚C. For the tests, a ratio of 30% by mass of each catalytic material mixed with PS was used and the activation energy of the degradation process was determined by the Vyazovkin method. The obtained results showed that the addition of the catalyst to the PS in general reduced its degradation temperature. The 10% CeO<sub>2</sub>/HZSM-5 catalyst showed greater efficiency, as it resulted in lower activation energy for PS degradation. Thus, the combination of CeO<sub>2</sub> with HZSM-5 resulted in materials with potential for application in the catalytic degradation of polystyrene and the results indicate that the production of a composite material can be a good strategy to generate an increase in catalytic activity and a decrease in energy process activation.展开更多
Managing agricultural waste and expanded polystyrene (EPS) poses significant environmental and economic challenges. This study aims to create composites from millet husks, rice husks, and recycled EPS, using a manufac...Managing agricultural waste and expanded polystyrene (EPS) poses significant environmental and economic challenges. This study aims to create composites from millet husks, rice husks, and recycled EPS, using a manufacturing method that involves dissolving the polystyrene in a solvent followed by cold pressing. Various particle sizes and two binder dosages were investigated to assess their influence on the physico-mechanical properties of the composites. The mechanical properties obtained range from 2.54 to 4.47 MPa for the Modulus of Rupture (MOR) and from 686 to 1400 MPa for the Modulus of Elasticity in Bending (MOE). The results indicate that these composites have potential for applications in the construction sector, particularly for wood structures and interior decoration. Moreover, surface treatments could enhance their durability and mechanical properties. This research contributes to the valorization of agricultural and plastic waste as eco-friendly and economical construction materials.展开更多
Electrospinning is a simple technique used to fabricate polymeric nano-fibrous membranes.These nano-fibers have found a wide range of valuable applications in the biomedical field.However,it has not been utilized with...Electrospinning is a simple technique used to fabricate polymeric nano-fibrous membranes.These nano-fibers have found a wide range of valuable applications in the biomedical field.However,it has not been utilized with solid high explosives yet.Herein,the electrospinning technique has been used to fabricate polystyrene(PS)/1,3,5-trinitro-1,3,5-triazinane(RDX)composite nanofibers.The governed electrospinning parameters,voltage,distance from the collector,flow rate,mandrel rotating speed,time,and solution concentration,that greatly affect the morphology of the obtained nanofibers were optimized.The fabricated PS/RDX nano-fibers were characterized using scanning electron microscopy(SEM),X-ray diffractometer(XRD),and Fourier Transform Infrared(FTIR)spectroscopy.The impact and friction sensitivities of PS/RDX were also measured.The thermal behavior of the prepared composite and the pure materials were studied by the thermal gravimetric analysis technique(TGA).SEM results proved the fabrication of PS/RDX fibers in the nano-size via electrospinning.FTIR spectroscopy confirmed the existence of the characteristic functional groups of both PS and RDX in the composite nano-fibers.XRD sharp peaks showed the conversion of amorphous PS into crystalline shape via electrospinning and also confirmed the formation of PS/RDX composite.The PS fibers absorbed the heat and increased the onset decomposition of the pure RDX from 181.5 to 200.7℃in the case of PS/RDX fibers.Interestingly,PS/RDX nano-fibers showed the relatively low impact and friction sensitivities of 100 J and 360 N respectively.These results could introduce PS/RDX nanofibrous composite in the field of explosives detection with high levels of safety.展开更多
基金funding support from National Natural Science Foundation of China(Grant No.52179109)Jiangsu Provincial Natural Science Foundation(Grant No.BK20230967)Open Research Fund of State Key Laboratory of Mechanical Behavior and System Safety of Traffic Engineering Structures,Shijiazhuang Tiedao University(Grant No.KF2022-02).
文摘Existing studies have focused on the behavior of the retaining wall equipped with expanded polystyrene(EPS)geofoam inclusions under semi-infinite surcharge loading rather than limited surcharge loading.In this paper,the failure mode and the earth pressure acting on the rigid retaining wall with EPS geofoam inclusions and granular backfills(henceforth referred to as EPS-wall),under limited surcharge loading are investigated through two-and three-dimensional model tests.The testing results show that different from the sliding of almost all the backfill in the EPS-wall under semi-infinite surcharge loading,only an approximately triangular backfill slides in the wall under limited surcharge loading.The distribution of the lateral earth pressure on the EPS-wall under limited surcharge loading is non-linear,and the distribution changes from the increase of the wall depth to the decrease with the increase of the limited surcharge loading.An approach based on the force equilibrium of a differential element is developed to predict the lateral earth pressure behind the EPS-wall subjected to limited surcharge loading,and its performance was fully validated by the three-dimensional model tests.
文摘The catalytic conversion of polystyrene (PS) was studied in the presence of the materials type HZSM-5, CeO<sub>2</sub>, 10% CeO<sub>2</sub>/HZSM-5 and 20% CeO<sub>2</sub>/HZSM-5, which were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and nitrogen adsorption at 77K. The catalytic tests were performed via thermogravimetric analysis (TG) at heating rates of 5, 10 and 20˚C min<sup>−1</sup> in a temperature range from 30˚C to 900˚C. For the tests, a ratio of 30% by mass of each catalytic material mixed with PS was used and the activation energy of the degradation process was determined by the Vyazovkin method. The obtained results showed that the addition of the catalyst to the PS in general reduced its degradation temperature. The 10% CeO<sub>2</sub>/HZSM-5 catalyst showed greater efficiency, as it resulted in lower activation energy for PS degradation. Thus, the combination of CeO<sub>2</sub> with HZSM-5 resulted in materials with potential for application in the catalytic degradation of polystyrene and the results indicate that the production of a composite material can be a good strategy to generate an increase in catalytic activity and a decrease in energy process activation.
文摘Managing agricultural waste and expanded polystyrene (EPS) poses significant environmental and economic challenges. This study aims to create composites from millet husks, rice husks, and recycled EPS, using a manufacturing method that involves dissolving the polystyrene in a solvent followed by cold pressing. Various particle sizes and two binder dosages were investigated to assess their influence on the physico-mechanical properties of the composites. The mechanical properties obtained range from 2.54 to 4.47 MPa for the Modulus of Rupture (MOR) and from 686 to 1400 MPa for the Modulus of Elasticity in Bending (MOE). The results indicate that these composites have potential for applications in the construction sector, particularly for wood structures and interior decoration. Moreover, surface treatments could enhance their durability and mechanical properties. This research contributes to the valorization of agricultural and plastic waste as eco-friendly and economical construction materials.
文摘Electrospinning is a simple technique used to fabricate polymeric nano-fibrous membranes.These nano-fibers have found a wide range of valuable applications in the biomedical field.However,it has not been utilized with solid high explosives yet.Herein,the electrospinning technique has been used to fabricate polystyrene(PS)/1,3,5-trinitro-1,3,5-triazinane(RDX)composite nanofibers.The governed electrospinning parameters,voltage,distance from the collector,flow rate,mandrel rotating speed,time,and solution concentration,that greatly affect the morphology of the obtained nanofibers were optimized.The fabricated PS/RDX nano-fibers were characterized using scanning electron microscopy(SEM),X-ray diffractometer(XRD),and Fourier Transform Infrared(FTIR)spectroscopy.The impact and friction sensitivities of PS/RDX were also measured.The thermal behavior of the prepared composite and the pure materials were studied by the thermal gravimetric analysis technique(TGA).SEM results proved the fabrication of PS/RDX fibers in the nano-size via electrospinning.FTIR spectroscopy confirmed the existence of the characteristic functional groups of both PS and RDX in the composite nano-fibers.XRD sharp peaks showed the conversion of amorphous PS into crystalline shape via electrospinning and also confirmed the formation of PS/RDX composite.The PS fibers absorbed the heat and increased the onset decomposition of the pure RDX from 181.5 to 200.7℃in the case of PS/RDX fibers.Interestingly,PS/RDX nano-fibers showed the relatively low impact and friction sensitivities of 100 J and 360 N respectively.These results could introduce PS/RDX nanofibrous composite in the field of explosives detection with high levels of safety.