Preparation of polymer microspheres from naturally occurring resource is a challenge.Here,a rosin-based polyol(RAG)was used to prepare polyurethane resin(RPU)firstly,and then act as both self-assembled precursor and e...Preparation of polymer microspheres from naturally occurring resource is a challenge.Here,a rosin-based polyol(RAG)was used to prepare polyurethane resin(RPU)firstly,and then act as both self-assembled precursor and emulsifier,rosin based polyurethane microspheres(RPUMs)were prepared.In the process of self-emulsification,the RPU formed vesicles by self-assembly.The outer shell of the vesicle consisted of hydrophilic segments,while the inner shell contained the hydrophobic phase.After cross-linking the RPU and removal of the solvent in the core,the porous-hollow microspheres with pH-sensitive were obtained.The microspheres were characterized by optical microscope(OM),scanning electron microscopy(SEM)and transmission electron microscope(TEM).The effect of type and amount of the hydrophilic chain extender,and solvent on the morphology,particle size and distribution,and buffer volume of the microspheres were determined.The best conditions for synthetic RPUMs were as follows:n_(NCO)/n_(OH)=1,n_(RAG):n_(1-(2-hydroxyethyl)piperazine)=4:6,with azodiisobutyronitrile level of 1.0 wt.%,based on reactive monomers,mixing speed of both emulsification and polymerization at 400 r·min-1,the RPUMs synthesized had porous-hollow structure with a buffer volume of 1.6 mL.展开更多
基金The authors greatly acknowledge the financial support from the National Natural Science Foundation of China(No.51863007).
文摘Preparation of polymer microspheres from naturally occurring resource is a challenge.Here,a rosin-based polyol(RAG)was used to prepare polyurethane resin(RPU)firstly,and then act as both self-assembled precursor and emulsifier,rosin based polyurethane microspheres(RPUMs)were prepared.In the process of self-emulsification,the RPU formed vesicles by self-assembly.The outer shell of the vesicle consisted of hydrophilic segments,while the inner shell contained the hydrophobic phase.After cross-linking the RPU and removal of the solvent in the core,the porous-hollow microspheres with pH-sensitive were obtained.The microspheres were characterized by optical microscope(OM),scanning electron microscopy(SEM)and transmission electron microscope(TEM).The effect of type and amount of the hydrophilic chain extender,and solvent on the morphology,particle size and distribution,and buffer volume of the microspheres were determined.The best conditions for synthetic RPUMs were as follows:n_(NCO)/n_(OH)=1,n_(RAG):n_(1-(2-hydroxyethyl)piperazine)=4:6,with azodiisobutyronitrile level of 1.0 wt.%,based on reactive monomers,mixing speed of both emulsification and polymerization at 400 r·min-1,the RPUMs synthesized had porous-hollow structure with a buffer volume of 1.6 mL.