Refinement of primary Si grains of A390 alloy slurry through serpentine channel pouring process

In this paper, the serpentine channel pouring process for preparing a semi-solid A390 alloy slurry and refining the primary Si grains of the A390 alloy, was used. The effects of the pouring temperature, the cooling water flow and the number of the curves on the size of the primary Si grains in the semi-solid A390 alloy slurry were investigated. The results show that the pouring temperature, the cooling water flow and the number of the curves have a major effect on the size and the distribution of primary Si grains. Under the experimental condition of the four-curve copper channel whose cooling water flow was 500 L·h-1 and the pouring temperature was 690 oC, the primary Si grains of the semi-solid A390 alloy slurry were refined to the greatest extent and the lath-like grains were changed into granular ones. Additionally, the equivalent grain diameter and the average shape factor of the primary Si grains of the satisfactory semi-solid A390 alloy slurry are 18.6 μm and 0.8, respectively. Further, the refinement mechanism of the primary Si grains through the serpentine channel pouring process was analyzed and discussed. In summary, the primary Si nuclei could be easily precipitated due to the chilling effect of the channel inner wall, thus the primary Si grains were greatly refined. Meanwhile, the subsequent alloy melt fluid also promoted the separation of primary Si grains from the inner wall, further refining the primary Si grains.

Refinement of primary Si grains in Al–20%Si alloy slurry through serpentine channel pouring process

In this study, a serpentine channel pouring process was used to prepare the semi-solid A1-20%Si alloy slurry and refine primary Si grains in the alloy. The effects of the pouring temperature, number of curves in the serpentine channel, and material of the serpentine channel on the size of primary Si grains in the semi-solid A1-20%Si alloy slurry were investigated. The results showed that the pouting temperature, number of the curves, and material of the channel strongly affected the size and distribution of the primary Si grains. The pouring tempera- ture exerted the strongest effect, followed by the number of the curves and then the material of the channel. Under experimental conditions of a four-curve copper channel and a pouring temperature of 701℃, primary Si grains in the semi-solid A1-20%Si alloy slurry were refined to the greatest extent, and the lath-like grains were changed into granular grains. Moreover, the equivalent grain diameter and the average shape coefficient of primary Si grains in the satisfactory semi-solid A1-20%Si alloy slurry were 24.4 μm and 0.89, respectively. Finally, the re- finement mechanism and distribution rule of primary Si grains in the slurry prepared through the serpentine channel pouring process were analyzed and discussed.