Using Cu-BTC prepared by hydrothermal method as precursor, carbon-based catalysts were obtained as model materials for low-temperature DeNO_x. These catalysts were characterized by X-ray diffractometry（XRD）, Raman s...Using Cu-BTC prepared by hydrothermal method as precursor, carbon-based catalysts were obtained as model materials for low-temperature DeNO_x. These catalysts were characterized by X-ray diffractometry（XRD）, Raman spectroscopy, scanning electron microscopy（SEM） and energy dispersive X-ray spectrometry（EDS）. The results showed that all carbon-based catalysts held the octahedron shape of Cu-BTC in most parts, and they mainly consisted of face-centered cubic copper. CuO_x/C exhibited excellent catalytic activity, and such catalytic activity was further improved with the introduction of Ag. The catalyst with a Cu to Ag mole ratio of 6：1 and an activated temperature of 600 °C showed the best catalytic performance, and its catalytic denitration rate reached 100% at a temperature as low as 235 °C. During the catalytic reaction process, Cu~＋ mainly played a catalytic role.展开更多
基金This work was supported by the National Basic Research Monties Programme of China (No. 2003CB515302) Shanghai Science and Technology Developing Foundation (No. 00JC14021).
基金Project(738010004)supported by the Project of Low Concentration Sulfur Dioxide Flue Gas Treatment,ChinaProject(2017GK4010)supported by the Scientific and Technological Breakthrough and Major Achievements Transformation of Strategic Emerging Industries of Hunan Province in 2017,China
文摘Using Cu-BTC prepared by hydrothermal method as precursor, carbon-based catalysts were obtained as model materials for low-temperature DeNO_x. These catalysts were characterized by X-ray diffractometry（XRD）, Raman spectroscopy, scanning electron microscopy（SEM） and energy dispersive X-ray spectrometry（EDS）. The results showed that all carbon-based catalysts held the octahedron shape of Cu-BTC in most parts, and they mainly consisted of face-centered cubic copper. CuO_x/C exhibited excellent catalytic activity, and such catalytic activity was further improved with the introduction of Ag. The catalyst with a Cu to Ag mole ratio of 6：1 and an activated temperature of 600 °C showed the best catalytic performance, and its catalytic denitration rate reached 100% at a temperature as low as 235 °C. During the catalytic reaction process, Cu~＋ mainly played a catalytic role.