The effect of the microstructure of plates fabricated both in the traditional process, involving casting, hot rolling and cold rolling （HR）, and in the novel twin roll casting ＋ cold rolling （TRC） process on the ...The effect of the microstructure of plates fabricated both in the traditional process, involving casting, hot rolling and cold rolling （HR）, and in the novel twin roll casting ＋ cold rolling （TRC） process on the surface quality of presensitized （PS） plates was analyzed by optical microscopy （OM）, scanning electron microscopy （SEM）, and energy-dispersive X-ray spectroscopy （EDXS）. The formation of pores on the surface of the electrolyzed HR plate could be attributed to the presence of approximately 1-μm-sized large Al-Fe precipitates in the HR plate compared to the smaller precipitates in the TRC plate. Moreover, residual graphite lubricants used during the TRC process were entrapped on the surface of the TRC plate during the subsequent rolling process. The entrapped pollutants tended to further deteriorate the formation of pores on the surface of the TRC plate, and no residual carbon was detected on the surface of the HR plate. Furthermore, the surface quality of the TRC plate can be improved by surface cleaning before the cold rolling process, which could dramatically lower the residual graphite on the surface.展开更多
采用极化曲线测定、扫描电镜和金相显微镜技术,对比国外优质1050 PS版板基,研究了热处理工艺对板基电蚀性能的影响。结果表明,具有大量细及均匀分布的第二相颗粒和均匀晶粒组织的板基电解腐蚀性能好。经过600℃×3 m in的高温快速...采用极化曲线测定、扫描电镜和金相显微镜技术,对比国外优质1050 PS版板基,研究了热处理工艺对板基电蚀性能的影响。结果表明,具有大量细及均匀分布的第二相颗粒和均匀晶粒组织的板基电解腐蚀性能好。经过600℃×3 m in的高温快速退火处理后的板基微观组织得到细化,均匀性提高,细小弥散的第二相颗粒大量析出,板基电解活化性能增强,腐蚀均匀、稳定,电解腐蚀性能显著提高。展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51074117)the International Scientific and Technological Cooperation Projects of China (No. 2013DFG12750)+1 种基金the Beijing Natural Science Foundation (No. 3142007)the Great Wall Scholar Program (No. CIT&TCD20140301)
文摘The effect of the microstructure of plates fabricated both in the traditional process, involving casting, hot rolling and cold rolling （HR）, and in the novel twin roll casting ＋ cold rolling （TRC） process on the surface quality of presensitized （PS） plates was analyzed by optical microscopy （OM）, scanning electron microscopy （SEM）, and energy-dispersive X-ray spectroscopy （EDXS）. The formation of pores on the surface of the electrolyzed HR plate could be attributed to the presence of approximately 1-μm-sized large Al-Fe precipitates in the HR plate compared to the smaller precipitates in the TRC plate. Moreover, residual graphite lubricants used during the TRC process were entrapped on the surface of the TRC plate during the subsequent rolling process. The entrapped pollutants tended to further deteriorate the formation of pores on the surface of the TRC plate, and no residual carbon was detected on the surface of the HR plate. Furthermore, the surface quality of the TRC plate can be improved by surface cleaning before the cold rolling process, which could dramatically lower the residual graphite on the surface.
文摘采用极化曲线测定、扫描电镜和金相显微镜技术,对比国外优质1050 PS版板基,研究了热处理工艺对板基电蚀性能的影响。结果表明,具有大量细及均匀分布的第二相颗粒和均匀晶粒组织的板基电解腐蚀性能好。经过600℃×3 m in的高温快速退火处理后的板基微观组织得到细化,均匀性提高,细小弥散的第二相颗粒大量析出,板基电解活化性能增强,腐蚀均匀、稳定,电解腐蚀性能显著提高。