Pulsed microwaves are widely used inradar,navigation, and communication. The average power density is low at narrow pulse widths or large pulse intervals,but pulsed microwaves at certain peak densities exert numerous ...Pulsed microwaves are widely used inradar,navigation, and communication. The average power density is low at narrow pulse widths or large pulse intervals,but pulsed microwaves at certain peak densities exert numerous biological effects, including展开更多
The effect of sintering temperature on microstructure, electrical properties, and pulse aging behavior of （V2O5-Mn3O4-Er2O3）-doped zinc oxide varistor ceramics was systematically studied. When the sintering temperat...The effect of sintering temperature on microstructure, electrical properties, and pulse aging behavior of （V2O5-Mn3O4-Er2O3）-doped zinc oxide varistor ceramics was systematically studied. When the sintering temperature increased, the average grain size increased from 6.1 to 8.7μm and the sintered density decreased from 5.52 to 5.43 g/cm3. The breakdown field decreased from 3856 to 922 V/cm with an increase in the sintering temperature up to 900 °C, whereas a further increase to 2352 V/cm at 925 °C. The nonlinear coefficient increased pronouncedly from 4.6 to 30.0 with an increase in the sintering temperature. The varistor ceramics sintered at 850 °C exhibited the best clamping characteristics, with the clamp voltage ratio of the range of 2.22-2.88 for pulse current of 1-25 A. The varistor ceramics sintered at 925 °C exhibited the strongest stability, with %ΔE1 mA/cm2=-8.8% after applying the multi-pulse current of 25 A.展开更多
基金supported by the Foundation of Astronaut Research and Training Center of China [No.SMFA14B06 and No.14ZS017]
文摘Pulsed microwaves are widely used inradar,navigation, and communication. The average power density is low at narrow pulse widths or large pulse intervals,but pulsed microwaves at certain peak densities exert numerous biological effects, including
文摘The effect of sintering temperature on microstructure, electrical properties, and pulse aging behavior of （V2O5-Mn3O4-Er2O3）-doped zinc oxide varistor ceramics was systematically studied. When the sintering temperature increased, the average grain size increased from 6.1 to 8.7μm and the sintered density decreased from 5.52 to 5.43 g/cm3. The breakdown field decreased from 3856 to 922 V/cm with an increase in the sintering temperature up to 900 °C, whereas a further increase to 2352 V/cm at 925 °C. The nonlinear coefficient increased pronouncedly from 4.6 to 30.0 with an increase in the sintering temperature. The varistor ceramics sintered at 850 °C exhibited the best clamping characteristics, with the clamp voltage ratio of the range of 2.22-2.88 for pulse current of 1-25 A. The varistor ceramics sintered at 925 °C exhibited the strongest stability, with %ΔE1 mA/cm2=-8.8% after applying the multi-pulse current of 25 A.