An in-situ study of static recrystallization in Mg using high temperature EBSD

It has been a common method to improve the mechanical properties of metals by manipulating their microstructures via static recrystallization,i.e.,through heat treatment.Therefore,the knowledge of recrystallization and grain growth is critical to the success of the technique.In the present work,by using in-situ high temperature EBSD,the mechanisms that control recrystallization and grain growth of an extruded pure Mg were studied.The experimental results revealed that the grains of priority for dynamic recrystallization exhibit fading competitiveness under static recrystallization.It is also found that grain boundary movement or grain growth is likely to show an inverse energy gradient effect,i.e.,low energy grains tend to swallow or grow into high energy grains,and grain boundaries of close to 30°exhibit superior growth advantage to others.Another finding is that{10-12}tensile twin boundaries are sites of hardly observed for recrystallization,and are finally swallowed by adjacent recrystallized grains.The above findings may give comprehensive insights of static recrystallization and grain growth of Mg,and may guide the design of advanced materials processing in microstructural engineering.

The Early Mesozoic NE-SW Extensional Model and Exhumation Processes at the Southeastern Margin of the Central Asian Orogenic Belt:Insights from the Strain and Kinematic Vorticity Analysis of the Sonid Zuoqi Ductile Detachment Zone

The Sonid Zuoqi ductile detachment zone is located at the southeastern margin of the Central Asian orogenic belt(CAOB),striking EW and dipping to the S.The major rock type of the Sonid Zuoqi ductile detachment zone is mylonite derived from granite.The sequence of mylonite features is:(1)S and C foliations of mylonite,and(2)extensional crenulation cleavage(ecc)or C′and the kinematic vorticity(Wk)value changed from 0.70 to 0.95 and from 0.37 to 0.69,respectively;the strain type of the mylonites within the Sonid Zuoqi ductile detachment zone is compressional to planar strain.The strong deformation mylonite and Halatu plutons yielded a zircon U-Pb age of 244 Ma and a zircon(U-Th)/He age of 214 Ma,respectively.Based on the strain and kinematic vorticity analysis,together with the zircon U-Pb and zircon(U-Th)/He ages and the regional tectonic background,the study area experienced three stage evolution:tangential simpleshear(244 Ma),simple-shear-dominated general shear represented by upper crustal extension(224 Ma)and pure-shear-dominated general shear represented by the Halatu pluton doming(214 Ma),which constrained the early Mesozoic NE-SW crustal extension at the southeastern margin of the CAOB.This NE-SW extension probably originated from the postorogenic extensional collapse of the CAOB,subsequent exhumation being controlled by the far afield effects of the closure of the Mongol-Okhotsk belt.

Effects of cold rolling path on recrystallization behavior and mechanical properties of pure copper during annealing

The recrystallization behavior,grain boundary characteristic distribution,and mechanical properties of pure Cu sheets that were subjected to different cold rolling paths,and then annealed at 400°C for 10,30,60,and 420 min,were investigated.Different rolling paths changed the grain boundary orientations of cold-rolled copper,causing recrystallized grains to nucleate and grow in an oriented manner.However,the evolution of the texture indicated that cold-rolled copper with different rolling paths did not show an obvious preferred orientation after annealing.The RD-60 specimen exhibited the smallest grain size(6.6μm).The results indicated that the grain size and low-ΣCSL grain boundaries worked together to provide RD-60 samples with appropriate mechanical properties and high plasticity.The yield strength,ultimate tensile strength,and elongation of RD-60 sample were 81 MPa,230 MPa,and 49%,respectively.These results could provide guidance for tuning the microstructures and properties of pure Cu foils,as well as designing fabrication routes for pure Cu foils through processes such as rolling and drawing.

Stable operation of highly loaded pure Si-Fe anode under ambient pressure via carboxy silane-directed robust solid electrolyte interphase

Incorporation of higher content Si anode material beyond 5 wt% to Li-ion batteries(LIBs)is challenging,owing to large volume change,swelling,and solid electrolyte interphase(SEI)instability issues.Herein,a strategy of diacetoxydimethylsilane(DAMS)additive-directed SEI stabilization is proposed for a stable operation of Si-0.33FeSi_(2)(named as Si-Fe)anode without graphite,which provides siloxane inorganics and organics enrichment that compensate insufficient passivation of fluoroethylene carbonate(FEC)additive and reduce a dependence on FEC.Unprecedented stable cycling performance of highly loaded(3.5 mA h cm^(-2))pure Si-Fe anode is achieved with 2 wt%DAMS combined with 9 wt%FEC additives under ambient pressure,yielding high capacity 1270 mA h g^(-1)at 0.5 C and significantly improved capacity retention of 81% after 100 cycles,whereas short circuit and rapid capacity fade occur with FEC only additive.DAMS-directed robust SEI layer dramatically suppresses swelling and particles crossover through separator,and therefore prevents short circuit,demonstrating a possible operation of pure Si or Sidominant anodes in the next-generation high-energy-density and safe LIBs.

A low-frequency pure metal metamaterial absorber with continuously tunable stiffness

To address the incompatibility between high environmental adaptability and deep subwavelength characteristics in conventional local resonance metamaterials,and overcome the deficiencies in the stability of existing active control techniques for band gaps,this paper proposes a design method of pure metal vibration damping metamaterial with continuously tunable stiffness for wideband elastic wave absorption.We design a dual-helix narrow-slit pure metal metamaterial unit,which possesses the triple advantage of high spatial compactness,low stiffness characteristics,and high structural stability,enabling the opening of elastic flexural band gaps in the low-frequency range.Similar to the principle of a sliding rheostat,the introduction of continuously sliding plug-ins into the helical slits enables the continuous variation of the stiffness of the metamaterial unit,achieving a continuously tunable band gap effect.This successfully extends the effective band gap by more than ten times.The experimental results indicate that this metamaterial unit can be used as an additional vibration absorber to absorb the low-frequency vibration energy effectively.Furthermore,it advances the metamaterial absorbers from a purely passive narrowband design to a wideband tunable one.The pure metal double-helix metamaterials retain the subwavelength properties of metamaterials and are suitable for deployment in harsh environments.Simultaneously,by adjusting its stiffness,it substantially broadens the effective band gap range,presenting promising potential applications in various mechanical equipment operating under adverse conditions.

Strongly Coupled Ag/Sn-SnO_(2)Nanosheets Toward CO_(2)Electroreduction to Pure HCOOH Solutions at Ampere‑Level Current

Electrocatalytic reduction of CO_(2) converts intermittent renewable electricity into value-added liquid products with an enticing prospect,but its practical application is hampered due to the lack of high-performance electrocatalysts.Herein,we elaborately design and develop strongly coupled nanosheets composed of Ag nanoparticles and Sn-SnO_(2) grains,designated as Ag/Sn-SnO_(2) nanosheets(NSs),which possess optimized electronic structure,high electrical conductivity,and more accessible sites.As a result,such a catalyst exhibits unprecedented catalytic performance toward CO_(2)-to-formate conversion with near-unity faradaic efficiency(≥90%),ultrahigh partial current density(2,000 mA cm^(−2)),and superior long-term stability(200 mA cm^(−2),200 h),surpassing the reported catalysts of CO_(2) electroreduction to formate.Additionally,in situ attenuated total reflection-infrared spectra combined with theoretical calculations revealed that electron-enriched Sn sites on Ag/Sn-SnO_(2)NSs not only promote the formation of*OCHO and alleviate the energy barriers of*OCHO to*HCOOH,but also impede the desorption of H*.Notably,the Ag/Sn-SnO_(2)NSs as the cathode in a membrane electrode assembly with porous solid electrolyte layer reactor can continuously produce~0.12 M pure HCOOH solution at 100 mA cm^(−2)over 200 h.This work may inspire further development of advanced electrocatalysts and innovative device systems for promoting practical application of producing liquid fuels from CO_(2).

“Component flow”conditions and its effects on enhancing production of continental medium-to-high maturity shale oil

Based on the production curves,changes in hydrocarbon composition and quantities over time,and production systems from key trial production wells in lacustrine shale oil areas in China,fine fraction cutting experiments and molecular dynamics numerical simulations were conducted to investigate the effects of changes in shale oil composition on macroscopic fluidity.The concept of“component flow”for shale oil was proposed,and the formation mechanism and conditions of component flow were discussed.The research reveals findings in four aspects.First,a miscible state of light,medium and heavy hydrocarbons form within micropores/nanopores of underground shale according to similarity and intermiscibility principles,which make components with poor fluidity suspended as molecular aggregates in light and medium hydrocarbon solvents,such as heavy hydrocarbons,thereby decreasing shale oil viscosity and enhancing fluidity and outflows.Second,small-molecule aromatic hydrocarbons act as carriers for component flow,and the higher the content of gaseous and light hydrocarbons,the more conducive it is to inhibit the formation of larger aggregates of heavy components such as resin and asphalt,thus increasing their plastic deformation ability and bringing about better component flow efficiency.Third,higher formation temperatures reduce the viscosity of heavy hydrocarbon components,such as wax,thereby improving their fluidity.Fourth,preservation conditions,formation energy,and production system play important roles in controlling the content of light hydrocarbon components,outflow rate,and forming stable“component flow”,which are crucial factors for the optimal compatibility and maximum flow rate of multi-component hydrocarbons in shale oil.The component flow of underground shale oil is significant for improving single-well production and the cumulative ultimate recovery of shale oil.

Clinical characteristics and analysis of vestibular-evoked myogenic potentials in patients with sudden sensorineural hearing loss in different ages

BACKGROUND Numerous studies have found that patients experiencing sudden sensorineural hearing loss(SSHL),with or without accompanying vertigo,often show impaired vestibular function.However,there is a dearth of studies analyzing vestibularevoked myogenic potentials(VEMPs)in SSHL patients across various age groups.AIM To investigate vestibular condition in SSHL patients across various age demographics.METHODS Clinical data of 84 SSHL patients were investigated retrospectively.Audiometry,cervical vestibular evoked myogenic potentials(c-VEMPs),and ocular vestibular evoked myogenic potentials(o-VEMPs)were conducted on these patients.Parameters assessed included the latencies of P1 and N1 waves,as well as the amplitudes of P1–N1 waves.Moreover,the study evaluated the influence of factors such as sex,affected side,configuration of hearing loss,and presence of accompanying vertigo.RESULTS Among the 84 SSHL patients,no significant differences were observed among the three groups in terms of gender,affected side,and the presence or absence of vertigo.Group II(aged 41–60 years)had the highest number of SSHL cases.The rates of absent o-VEMPs in the affected ears were 20.83%,31.58%,and 22.72%for the three age groups,respectively,with no statistically significant difference among them.The rates of absent c-VEMPs in the affected ears were 8.3%,34.21%,and 18.18%for the three age groups,respectively,with significant differences.In the unaffected ears,there were differences observed in the extraction rates of o-VEMPs in the unaffected ears among the age groups.In the three age groups,no significant differences were noted in the three age groups in the latencies of P1 and N1 waves or in the amplitude of N1–P1 waves for c-VEMPs and o-VEMPs,either on the affected side or on the unaffected side,across the three age groups.CONCLUSION The extraction rate of VEMPs is more valuable than parameters.Regardless of the presence of vertigo,vestibular organs are involved in SSHL.Notably,SSHL patients aged 41–60 appear more susceptible to damage to the inferior vestibular nerve and saccule.

Design and Analysis of Power and Transmission System of Downhole Pure Electric Command Vehicle

Electric vehicles use electric motors, which turn electrical energy into mechanical energy. As electric motors are conventionally used in all the industry, it is an established development site. It’s a mature technology with ideal power and torque curves for vehicular operation. Conventional vehicles use oil and gas as fuel or energy storage. Although they also have an excellent economic impact, the continuous use of oil and gas threatened the world’s reservation of total oil and gas. Also, they emit carbon dioxide and some toxic ingredients through the vehicle’s tailpipe, which causes the greenhouse effect and seriously impacts the environment. So, as an alternative, electric car refers to a green technology of decarbonization with zero emission of greenhouse gases through the tailpipe. So, they can remove the problem of greenhouse gas emissions and solve the world’s remaining non-renewable energy storage problem. Pure electric vehicles (PEV) can be applied in all spheres, but their special implementation can only be seen in downhole operations. They are used for low noise and less pollution in the downhole process. In this study, the basic structure of the pure electric command vehicle is studied, the main components of the command vehicle power system, namely the selection of the drive motor and the power battery, are analyzed, and the main parameters of the drive motor and the power battery are designed and calculated. The checking calculation results show that the power and transmission system developed in this paper meets the design requirements, and the design scheme is feasible and reasonable.

PCTC货舱通风关键技术

为降低汽车运输船(Pure Car Truck Carrier,PCTC)的噪声,减小其电力消耗,对风机房和风道的主要组成部分、独立风机房和结构风机房的不同的特点进行分析,并对货舱内部流场、通风阻力、噪声控制等3方面的关键技术进行研究。结果表明:货舱内部流场主要取决于通风总体方案;控制风道通风阻力是设计的关键,对风机房选型和控制噪声有很大影响;计算流体力学(Computational Fluid Dynamics,CFD)分析可有效提高设计的准确性。研究成果可为PCTC货舱通风设计提供一定参考。

铁酸钴纳米微粒的共沉淀法制备和磁性质(英文)

The cobalt ferrite nanoparticles were prepared by coprecipitation in the presence of poly (N-vinylpyrrolidone) (PVP) and characterized by XRD, TEM, EDX and magnetometry. XRD results suggest the formation of pure cobalt ferrite. The mean particle sizes of CoFe2O4 samples annealed at 400 ℃ and 600 ℃ were ca. 6 and 25 nm, respectively as obtained by transmission electron microscopy (TEM). The magnetic measurements indicated that nano-particles obtained at 400 ℃ were superparamagnetic while that prepared at 600 ℃ were ferrimagnetic.

Microstructure and texture of commercially pure titanium in cold deep drawing

The development of microstructure and texture during cold deep drawing of commercially pure titanium（CP-Ti） was investigated.Three parts,stretching region,drawing region and flange region,were sequentially formed in the deep drawing process of the hemispheric surface part,with reference to deformation modes and strain regimes.Results show that the plastic strain is accommodated by dislocation slip and deformation twinning in the whole deep drawing process.The texture of the CP-Ti sheet and its drawn part consists of rolling texture component and recrystallization texture component.The intensity and type of the initial texture varied during the drawing process are related to the production of deformation twinning and dislocation slip.Twinning weakens the initial texture by randomizing the orientations of crystals,especially for the recrystallization texture.The recrystallization texture in the drawing region disappears due to the significant forming of twinning.Furthermore,over drawing would result in the predominance of dislocation slip and the texture is strengthened.

Effect of electrical current on tribological property of Cu matrix composite reinforced by carbon nanotubes

Cu matrix composite reinforced with 10%（volume fraction） carbon nanotubes（CNTs/Cu） and pure Cu bulk were prepared by powder metallurgy techniques under the same consolidation processing condition.The effect of electrical current on tribological property of the materials was investigated by using a pin-on-disk friction and wear tester.The results show that the friction coefficient and wear rate of CNTs/Cu composite as well as those of pure Cu bulk increase with increasing the electrical current without exception,and the effect of electrical current is more obvious on tribological property of pure Cu bulk than on that of CNTs/Cu composite;the dominant wear mechanisms are arc erosion wear and plastic flow deformation,respectively;CNTs can improve tribological property of Cu matrix composites with electrical current.

Preparation and characterization of ZrO_2/TiO_2 composite photocatalytic film by micro-arc oxidation

ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.

Grain refinement of pure aluminum by direct current pulsed magnetic field and inoculation

The combined effects of direct current pulsed magnetic field （DC-PMF） and inoculation on pure aluminum were investigated, the grain refinement behavior of DC-PMF and inoculation was discussed. The experimental results indicate that the solidification micro structure of pure aluminum can be greatly refined under DC-PMF. Refinement of pure aluminum is attributed to electromagnetic undercooling and forced convection caused by DC-PMF. With single DC-PMF, the grain size in the equiaxed zone is uneven. However, under DC-PMF, by adding 0.05% （mass fraction） Al5Ti-B, the grain size of the sample is smaller, and the size distribution is more uniform than that of single DC-PMF. Furthermore, under the combination of DC-PMF and inoculation, with the increase of output current, the grain size is further reduced. When the output current increases to 100 A, the average grain size can decrease to 113 μn.

A gradient nano/micro-structured surface layer on copper induced by severe plasticity roller burnishing

In order to investigate a gradient nano/micro-structured surface layer on pure copper produced by severe plasticity roller burnishing （SPRB） and grain refinement mechanism, the microstructure characteristics and material properties of sample at various depths from the topmost surface were investigated by SEM, TEM, XRD, OM etc. The experimental results show that the gradient nano/micro-structure was introduced into the surface layer of over 100μm in thickness. The remarkable increase in hardness near the topmost surface was mainly attributed to the reduced grain size. The equiaxed nano-sized grains were in random orientation and the most of their boundaries were low-angle grain boundaries （LAGBs）. The coarse grains are refined into the few micro-sized grains by dislocation activities;deformation twinning was found to be the primary form for the formation of submicron grains;the formation of nanostructure was dominated by dislocation activities accompanied with rotation of grains in local region.

Deformation and fracture behavior of commercially pure titanium with gradient nano-to-micron-grained surface layer

Titanium with gradient nano-to-micron scale grains from surface to matrix was fabricated by surface mechanical grinding treatment(SMGT) at room temperature.The SMGT-treated titanium shows higher strength than that of as-received one,but moderate ductility between those of ultra-fine grained(UFG) and coarse-grained titanium.Tensile stress-strain curves of SMGT-treated titanium show double strain hardening regimes.The strain hardening rate(dσ/dε) decreases with increasing strain in tensile deformation.The high strain hardening rate at initial yielding is attributed to nano-to-micron-grained surface layer.The low strain hardening rate at large plastic strain regime primarily results from coarse-grained matrix.The SMGT-treated titanium shows a ductile fracture mode with a large number of dimples.The small size of dimples in the treated surface layer is due to the combination of the high strength and strain hardening exponent.The difference between dimple size in nano-to-micron-grained surface layer and coarse-grained matrix is discussed in terms of plastic zone size at the tip of crack in the SMGT-treated titanium.

Pure Sperm梯度离心法和上游法处理精液效果的比较

目的 比较PureSperm(硅烷化硅胶悬浮液)梯度密度离心法和Earel’s液上游法处理精液在体外受精-胚胎移植(IVF -ET)中的应用情况。方法 4 5例丈夫精液密度(2 0～4 0 )×10 6/ml,a级精子比例<15 %或精液量少于1ml者用PureSperm处理,其余用Earel’s液上游法处理。结果 处理后两种方法均可以显著性提高精子的总活力、a级精子率。梯离组和上游组畸形精子率分别为:6 8 8% ,75 1% ,与处理前81 2 %比显著降低,但两种方法之间的降低程度无差别(P >0 0 5 )。梯离法在总活动精子回收率及a级精子的获得方面优于上游法(P <0 0 5 )。PureSperm组与上游组的受精率分别为6 8% ,70 1% (P均>0 0 5 ) ,无统计学差异,胚胎发育潜能:卵裂率、优胚率、着床率、临床妊娠率、流产率也均无统计学差异。结论 相对于稍差者的精液来说,用PureSperm梯度密度离心处理效果更佳;PureSperm对胚胎的毒性作用极小,不影响IVF -ET的结局,在IVF -ET技术中可以安全使用。

Nutrient characteristics in rhizosphere of pure and mixed plantations of Manchur ian walnut and Dahurian larch

A comparison study was made for the characteristics of pH value, orga nic matter content, nutrient element N, P and K contents in rhizosphere soils of pure and mixed plantations of Manchurian walnut and Dahurian larch and in bulk soils. The results show that the pH values of rhizosphere soil for all the plant ations except the pure walnut stand, which was slightly higher, were lower than those of bulk soils, while the organic matter contents in the rhizosphere soil f or all the plantations except the mixed plantation, which was slightly lower, we re higher than that in bulk soil. There exists a relative nitrogen accumulation in the rhizosphere and the extent to which the nitrogen accumulates is closely r elated to tree species and mixed pattern. As far as the total P and K contents a re considered, there exists a deficient tendency in rhizosphere in comparison wi th bulk soil. The element N, P and K are all mobilized in the rhizosphere of the pure or mixed plantation, characterized by the higher contents of the available N, P and K in the rhizosphere. The available N content in the rhizosphere of th e larch in mixed plantation was obviously higher than that of its pure plantatio n, whereas the available P and K contents in the rhizosphere of walnut in the mi xed plantation, on the other hand, were significantly higher than those of its p ure plantation.

非金属夹杂物对纯镍N6焊接接头组织性能的影响

以纯镍N6为主要研究对象,借助光学显微镜(OM)、扫描电镜(SEM)、能谱分析仪(EDS)、X射线衍射仪(XRD)及电解萃取装置等手段分析了非金属夹杂物对纯镍N6焊接接头结构及性能的影响。结果表明:纯镍N6试样断裂与非金属夹杂物尺寸、形貌、数量等因素有直接的关系;非正常断裂试样的断口表现为沿晶断裂,断口上夹杂物主要由Al、Si、Ca、Mg、O、Fe等元素组成;对试样的金相组织与夹杂物进行分析发现非正常断裂试样中夹杂物数量及尺寸均大于正常试样,杂物数量大于50个/mm2且夹杂物尺寸大于10μm的试样均发生断裂;夹杂物主要为氧化铝类(Al2O3、SiO2)、硅酸盐类、氮化物类(AlN、TiN、Ti(C,N))及复相夹杂物;原位拉伸试验表明,断裂的主要原因是在金属基体中存在的夹杂物诱发裂纹源,在应力的作用下裂纹扩展导致断裂。综合分析表明,纯镍N6焊接接头在生产中的断裂是由脆性夹杂物的存在而引起的。