The distributions of the axial stress and shear stress in Al2O3-TiC/Q235 diffusion bonded joints were studied using finite element method （FEM）. The effect of interlayer thickness on the axial stress and shear stres...The distributions of the axial stress and shear stress in Al2O3-TiC/Q235 diffusion bonded joints were studied using finite element method （FEM）. The effect of interlayer thickness on the axial stress and shear stress was also investigated. The results indicate that the gradients of the axial stress and shear stress are great near the joint edge. The maximal shear stress produces at the interface of the Al2O3-TIC and Ti interlayer. With the increase of Cu interlayer thickness, the magnitudes of the axial stress and shear stress first decrease and then increase. The distribution of the axial stress changes greatly with a little change in the shear stress. The shear fracture initiates at the interface of the Al2O3-TiC/ Ti interlayer with high shear stress and then propagates to the Al2O3-TIC side, which is consistent with the stress FEM calculating results.展开更多
The ablation tests on coated and uncoated Q235 B steel sheets were conducted under 30/80 μs impulse current simulating the lightning first return stroke current, aimed at further understanding the ablation characteri...The ablation tests on coated and uncoated Q235 B steel sheets were conducted under 30/80 μs impulse current simulating the lightning first return stroke current, aimed at further understanding the ablation characteristics of steel and investigating the impact of anti-corrosion coating on these characteristics. Ablation characteristics were investigated through the macroscopic morphology and x-ray diffraction patterns on the surface of damaged zones, the microstructure and micro Vickers hardness on the cross-section of damaged zones, and the maximum rear-face temperature of sample sheets. It can be concluded that the ablation areas of uncoated sheet consist of the melted layer and the heat-affect layer. These ablation areas include not only the area ablated directly by the arc root, of which the depth is deeper, but also the area forming due to the splashing of molten steel, of which the depth is shallower and decreases when the area’s distance from the arc attachment point increases. For coated sheet, coating materials have decomposed and evaporated forming an ablation pit on the sheet surface, in which the steel surface is exposed, and zinc filler of coating primer has infused into the exposed surface. The ablation diameter of uncoated sheet relates to the amplitude of the 30/80 μs impulse current in quadratic function, while for coated sheet, the relation is linear. In general, under the 30/80 μs impulse current, the coating can decrease the energy injected from the arc to the steel sheet and reduce the melting and splashing of steel. As a result, the ablation severity of uncoated sheet is severer than that of coated sheet.展开更多
In this research,2205/Q235 B clad plates were prepared by a vacuum hot rolling composite process.The effects of adding Fe,Ni,and Nb interlayers on the bonding interface structures and the shear strengths of the clad s...In this research,2205/Q235 B clad plates were prepared by a vacuum hot rolling composite process.The effects of adding Fe,Ni,and Nb interlayers on the bonding interface structures and the shear strengths of the clad steel plates were studied.The results showed that 2205 duplex stainless steel and the three interlayers produced a large amount of plastic deformation and low-angle boundaries,and the main structures were the recrystallized and deformed grains.There were many recrystallized grains in the microstructure of the Q235 B low-carbon steel due to the low deformation in the rolling process.The Fe interlayer had better wettability with the two kinds of steel,but the lower strength led to the reduction of shear strength by about14 MPa compared with the original clad steel plate.The C element in the Q235 B low-carbon steel easily diffused into the Fe interlayer,and the clad steel plate attained a poor corrosion resistance because a large decarburization area was formed.The Nb interlayer reacted with the Mo element in the 2205 duplex stainless steel to form an Nb-Mo binary alloy,which generated long-banded ferrite.The decarburization area was also produced because the Nb reacted with the C element in the Q235 B to form hard and brittle NbCx.As a result,the shear strength was significantly reduced by about 282 MPa,and the corrosion resistance of the bonding surface was deteriorated.The Ni interlayer did not react with the alloy elements in both sides,and therefore effectively prevented element diffusion and improved the corrosion resistance of the bonding surface.Due to the low strength of the Ni interlayer and the increased number of bonding surfaces of the clad steel plates,the shear strength was reduced to some extent(about 40 MPa),but it still met the engineering application standards.展开更多
2205/Q235B clad steel plates were fabricated using a thermal simulator.The metallographic microscope,scanning electron microscope,energy-dispersive spectrometer,shear test,electrochemical corrosion test and acid immer...2205/Q235B clad steel plates were fabricated using a thermal simulator.The metallographic microscope,scanning electron microscope,energy-dispersive spectrometer,shear test,electrochemical corrosion test and acid immersion test were used to study the influence of the pass reduction ratio on the microstructure and properties of 2205/Q235B clad steel plate.The results show that the clad steel plates had a good bonding surface when the pass reduction ratios were between 16.3%and 36.0%.There existed the mutual diffusion effect of elements near the bonding surface,which caused the long austenite strip on the side of 2205 stainless steel and the decarburization layer on the side of Q235B low-carbon steel.The transformation ofδferrite toγaustenite and the generation of the decarburization layer were promoted because of the lower pass reduction ratio.The corrosio n resista nee of 2205 duplex-phases stainless steel worse ned by the decrease in 8 ferrite con tent.The increase in the decarburization layer thickness made the shear strength of the clad steel plates reduce from 453 to 390 MPa.The potential of the decarburization layer was lower than that of 2205 stainless steel and Q235B low-carb on steel,which was easily corroded in the corrosive medium.展开更多
The joining of Mg alloy to steel was realized by metal inert-gas arc welding, and the weld thermal cycle characteristics and Mg-steel joints were investigated. The results show that the temperature distribution in the...The joining of Mg alloy to steel was realized by metal inert-gas arc welding, and the weld thermal cycle characteristics and Mg-steel joints were investigated. The results show that the temperature distribution in the joints is uneven. Mg alloy welds present a fine equiaxed grain structure. There exists a transition layer consisting mainly of AlFe, AlFe3 and Mg（Fe, Al）2O4 phases at Mg/steel interface, and it is the weakest link in Mg？steel joints. The welding heat input and weld Al content have the significant effect on the joint strength. The joint strength increases with increasing the heat input from 1680 J/cm to 2093 J/cm, due to promoting Mg/steel interface reaction. When weld Al content is increased to 6.20%, the joint strength reaches 192 MPa, 80% of Mg alloy base metal strength. It is favorable to select the suitable welding heat input and weld Al content for improving joint strength.展开更多
基金supported by the National Key Research and Development Program of China(No.2018YFA0707300)the National Natural Science Foundation of China(Nos.51901151,51905372,52275362,52171122)China Postdoctoral Science Foundation(Nos.2020M680918,2021T140503)。
基金supported by National Natural Science Foundation of China (Grant No. 50874069)Development Project of Science and Technology of Shandong Province (2007GG10004016)+1 种基金Shandong Province Natural Science Foundation (Y2007F54)Excellent Mid-Youth Foundation of Shandong Province (2006BS04004)
文摘The distributions of the axial stress and shear stress in Al2O3-TiC/Q235 diffusion bonded joints were studied using finite element method （FEM）. The effect of interlayer thickness on the axial stress and shear stress was also investigated. The results indicate that the gradients of the axial stress and shear stress are great near the joint edge. The maximal shear stress produces at the interface of the Al2O3-TIC and Ti interlayer. With the increase of Cu interlayer thickness, the magnitudes of the axial stress and shear stress first decrease and then increase. The distribution of the axial stress changes greatly with a little change in the shear stress. The shear fracture initiates at the interface of the Al2O3-TiC/ Ti interlayer with high shear stress and then propagates to the Al2O3-TIC side, which is consistent with the stress FEM calculating results.
基金supported by National Natural Science Foundation of China (No. 51577117)
文摘The ablation tests on coated and uncoated Q235 B steel sheets were conducted under 30/80 μs impulse current simulating the lightning first return stroke current, aimed at further understanding the ablation characteristics of steel and investigating the impact of anti-corrosion coating on these characteristics. Ablation characteristics were investigated through the macroscopic morphology and x-ray diffraction patterns on the surface of damaged zones, the microstructure and micro Vickers hardness on the cross-section of damaged zones, and the maximum rear-face temperature of sample sheets. It can be concluded that the ablation areas of uncoated sheet consist of the melted layer and the heat-affect layer. These ablation areas include not only the area ablated directly by the arc root, of which the depth is deeper, but also the area forming due to the splashing of molten steel, of which the depth is shallower and decreases when the area’s distance from the arc attachment point increases. For coated sheet, coating materials have decomposed and evaporated forming an ablation pit on the sheet surface, in which the steel surface is exposed, and zinc filler of coating primer has infused into the exposed surface. The ablation diameter of uncoated sheet relates to the amplitude of the 30/80 μs impulse current in quadratic function, while for coated sheet, the relation is linear. In general, under the 30/80 μs impulse current, the coating can decrease the energy injected from the arc to the steel sheet and reduce the melting and splashing of steel. As a result, the ablation severity of uncoated sheet is severer than that of coated sheet.
基金financially supported by the Shandong Taishan Industry Leading Talents Project(SF1503302301)
文摘In this research,2205/Q235 B clad plates were prepared by a vacuum hot rolling composite process.The effects of adding Fe,Ni,and Nb interlayers on the bonding interface structures and the shear strengths of the clad steel plates were studied.The results showed that 2205 duplex stainless steel and the three interlayers produced a large amount of plastic deformation and low-angle boundaries,and the main structures were the recrystallized and deformed grains.There were many recrystallized grains in the microstructure of the Q235 B low-carbon steel due to the low deformation in the rolling process.The Fe interlayer had better wettability with the two kinds of steel,but the lower strength led to the reduction of shear strength by about14 MPa compared with the original clad steel plate.The C element in the Q235 B low-carbon steel easily diffused into the Fe interlayer,and the clad steel plate attained a poor corrosion resistance because a large decarburization area was formed.The Nb interlayer reacted with the Mo element in the 2205 duplex stainless steel to form an Nb-Mo binary alloy,which generated long-banded ferrite.The decarburization area was also produced because the Nb reacted with the C element in the Q235 B to form hard and brittle NbCx.As a result,the shear strength was significantly reduced by about 282 MPa,and the corrosion resistance of the bonding surface was deteriorated.The Ni interlayer did not react with the alloy elements in both sides,and therefore effectively prevented element diffusion and improved the corrosion resistance of the bonding surface.Due to the low strength of the Ni interlayer and the increased number of bonding surfaces of the clad steel plates,the shear strength was reduced to some extent(about 40 MPa),but it still met the engineering application standards.
基金the support by Shandong Taishan Industry Leading Talents Project(SF1503302301)the help of Shandong Iron&Steel Group Co.,Ltd.,in the experiment of raw materials and thermal simulation.
文摘2205/Q235B clad steel plates were fabricated using a thermal simulator.The metallographic microscope,scanning electron microscope,energy-dispersive spectrometer,shear test,electrochemical corrosion test and acid immersion test were used to study the influence of the pass reduction ratio on the microstructure and properties of 2205/Q235B clad steel plate.The results show that the clad steel plates had a good bonding surface when the pass reduction ratios were between 16.3%and 36.0%.There existed the mutual diffusion effect of elements near the bonding surface,which caused the long austenite strip on the side of 2205 stainless steel and the decarburization layer on the side of Q235B low-carbon steel.The transformation ofδferrite toγaustenite and the generation of the decarburization layer were promoted because of the lower pass reduction ratio.The corrosio n resista nee of 2205 duplex-phases stainless steel worse ned by the decrease in 8 ferrite con tent.The increase in the decarburization layer thickness made the shear strength of the clad steel plates reduce from 453 to 390 MPa.The potential of the decarburization layer was lower than that of 2205 stainless steel and Q235B low-carb on steel,which was easily corroded in the corrosive medium.
文摘The joining of Mg alloy to steel was realized by metal inert-gas arc welding, and the weld thermal cycle characteristics and Mg-steel joints were investigated. The results show that the temperature distribution in the joints is uneven. Mg alloy welds present a fine equiaxed grain structure. There exists a transition layer consisting mainly of AlFe, AlFe3 and Mg（Fe, Al）2O4 phases at Mg/steel interface, and it is the weakest link in Mg？steel joints. The welding heat input and weld Al content have the significant effect on the joint strength. The joint strength increases with increasing the heat input from 1680 J/cm to 2093 J/cm, due to promoting Mg/steel interface reaction. When weld Al content is increased to 6.20%, the joint strength reaches 192 MPa, 80% of Mg alloy base metal strength. It is favorable to select the suitable welding heat input and weld Al content for improving joint strength.