The reactive diluent prepared by siloxane modified Trimethylene oxide can improve the performance of the UV curing system.Therefore,1,7-bis[(3-ethyl-3-methoxyoxacylobutane)propyl]octadecylosiloxane(BEMOPOMTS)was synth...The reactive diluent prepared by siloxane modified Trimethylene oxide can improve the performance of the UV curing system.Therefore,1,7-bis[(3-ethyl-3-methoxyoxacylobutane)propyl]octadecylosiloxane(BEMOPOMTS)was synthesized from diethyl carbonate,trimethylopropanes,allyl bromide,and 1,1,3,3,5,5,7,7-octadecylosiloxane as the main raw materials.BEMOPOMTS can be used as reactive diluents in the field of cationic UV curing.It has good thermal stability,and the addition of BEMOPOMTS significantly improves the tensile strength and elongation at break of epoxy resin.Compared with the pure epoxy resin,adding 20%BEMOPOMTS increased the elastic modulus by 25%to 677 MPa.展开更多
A Aeries of hydroxylic hyperbranched polymers were derived from 2,2-bis(methylol) propionic acid and tris(methylol) propane reacted with acrylic acid to various extents. The obtained acrylated hyperbranched polymers a...A Aeries of hydroxylic hyperbranched polymers were derived from 2,2-bis(methylol) propionic acid and tris(methylol) propane reacted with acrylic acid to various extents. The obtained acrylated hyperbranched polymers alone or with a monofunctional diluent, isobornylene acrylate(IBOA) were further cured by UV radiation. The cured films based on the modified polymers alone all demonstrated poor mechanical properties due to their high network densities and low moving ability of polymer chains. For the composite systems, the cured films demonstrated improved mechanical properties due to the low network densities and high chain moving ability. With more IBOA included in the systems, acrylate groups can react to a higher extent during the curing process.展开更多
To meet the processing requirements of resin transfer moulding(RTM)technology,reactive diluent containing m-phenylene moiety was synthesized to physically mixed with phenylethynyl terminated cooligoimides with well-de...To meet the processing requirements of resin transfer moulding(RTM)technology,reactive diluent containing m-phenylene moiety was synthesized to physically mixed with phenylethynyl terminated cooligoimides with well-designed molecular weights of 1500-2500 g/mol derived from 4,4’-(hexafluoroisopropylidene)diphthalic anhydride(6 FDA),3,4’-oxydianiline(3,4’-ODA)and m-phenylenediamine(m-PDA).This blend shows low minimum melting viscosity(<1 Pa·s)and enlarged processing temperature window(260–361℃).FPI-R-1 stays below 1 Pa·s for2 h at 270℃.The relationship between the molecular weight of the blend and its melting stability was first explored.Blending oligoimides with lower molecular weights exhibit better melting stability.Upon curing at 380℃for 2 h,the thermosetting polyimide resin demonstrates superior heat resistance(T_(g)=420-426℃).展开更多
基金Funded by the National Natural Science Foundation of China(No.21865017)。
文摘The reactive diluent prepared by siloxane modified Trimethylene oxide can improve the performance of the UV curing system.Therefore,1,7-bis[(3-ethyl-3-methoxyoxacylobutane)propyl]octadecylosiloxane(BEMOPOMTS)was synthesized from diethyl carbonate,trimethylopropanes,allyl bromide,and 1,1,3,3,5,5,7,7-octadecylosiloxane as the main raw materials.BEMOPOMTS can be used as reactive diluents in the field of cationic UV curing.It has good thermal stability,and the addition of BEMOPOMTS significantly improves the tensile strength and elongation at break of epoxy resin.Compared with the pure epoxy resin,adding 20%BEMOPOMTS increased the elastic modulus by 25%to 677 MPa.
基金Supported by the National Natural Science Foundation of China(No.2 0 2 0 4 0 0 5 ,5 0 2 330 30 ) and Basic Research Fund ofTsinghua University(No.JC2 0 0 2 0 30 )
文摘A Aeries of hydroxylic hyperbranched polymers were derived from 2,2-bis(methylol) propionic acid and tris(methylol) propane reacted with acrylic acid to various extents. The obtained acrylated hyperbranched polymers alone or with a monofunctional diluent, isobornylene acrylate(IBOA) were further cured by UV radiation. The cured films based on the modified polymers alone all demonstrated poor mechanical properties due to their high network densities and low moving ability of polymer chains. For the composite systems, the cured films demonstrated improved mechanical properties due to the low network densities and high chain moving ability. With more IBOA included in the systems, acrylate groups can react to a higher extent during the curing process.
基金financially supported by the National Natural Science Foundation of China(No.51803222)Science and Technology Service Network Initiative,Chinese Academy of Sciences。
文摘To meet the processing requirements of resin transfer moulding(RTM)technology,reactive diluent containing m-phenylene moiety was synthesized to physically mixed with phenylethynyl terminated cooligoimides with well-designed molecular weights of 1500-2500 g/mol derived from 4,4’-(hexafluoroisopropylidene)diphthalic anhydride(6 FDA),3,4’-oxydianiline(3,4’-ODA)and m-phenylenediamine(m-PDA).This blend shows low minimum melting viscosity(<1 Pa·s)and enlarged processing temperature window(260–361℃).FPI-R-1 stays below 1 Pa·s for2 h at 270℃.The relationship between the molecular weight of the blend and its melting stability was first explored.Blending oligoimides with lower molecular weights exhibit better melting stability.Upon curing at 380℃for 2 h,the thermosetting polyimide resin demonstrates superior heat resistance(T_(g)=420-426℃).