The using of the iron to extract reduced iron with T Fe ≥ 69.5% Al 2O 3+SiO 2<0.3% was studied. Preparation of reduced iron powder in this experimental research can produce ultra pure magnetite concentrate...The using of the iron to extract reduced iron with T Fe ≥ 69.5% Al 2O 3+SiO 2<0.3% was studied. Preparation of reduced iron powder in this experimental research can produce ultra pure magnetite concentrate. The quality of the final product reaches the product standard of SC 100.26 and NC 100.24.展开更多
A facile and practical route was introduced to prepare LiFePO4/C cathode material with nano-sized primary particles and excellent electrochemical performance. LiH2PO4 was synthesized by using H3PO4 and LiOH as raw mat...A facile and practical route was introduced to prepare LiFePO4/C cathode material with nano-sized primary particles and excellent electrochemical performance. LiH2PO4 was synthesized by using H3PO4 and LiOH as raw materials. Then, as-prepared LiH2PO4, reduced iron powder andα-D-glucose were ball-milled, dried and sin-tered to prepare LiFePO4/C. X-ray diffractometry was used to characterize LiH2PO4, ball-milled product and LiFePO4/C. Differential scanning calorimeter-thermo gravimetric analysis was applied to investigate possible reac-tions in sintering and find suitable temperature for LiFePO4 formation. Scanning electron microscopy was em-ployed for the morphology of LiFePO4/C. As-prepared LiH2PO4 is characterized to be in P21cn（33） space group, which reacts with reduced iron powder to form Li3PO4, Fe3（PO4）2 and H2 in ball-milling and sintering. The appro-priate temperature for LiFePO4/C synthesis is 541.3-976.7 ℃. LiFePO4/C prepared at 700 ℃ presents nano-sized primary particles forming aggregates. Charge-discharge examination indicates that as-prepared LiFePO4/C displays appreciable discharge capacities of 145 and 131 mA·h·g^-1 at 0.1 and 1 C respectively and excellent discharge ca-pacity retention.展开更多
文摘The using of the iron to extract reduced iron with T Fe ≥ 69.5% Al 2O 3+SiO 2<0.3% was studied. Preparation of reduced iron powder in this experimental research can produce ultra pure magnetite concentrate. The quality of the final product reaches the product standard of SC 100.26 and NC 100.24.
基金Supported partially by the Natural Science Foundation of Yunnan Province(2010ZC051)Analysis and Testing Foundation(2009-041)Starting Research Fund(14118245) from Kunming University of Science and Technology
文摘A facile and practical route was introduced to prepare LiFePO4/C cathode material with nano-sized primary particles and excellent electrochemical performance. LiH2PO4 was synthesized by using H3PO4 and LiOH as raw materials. Then, as-prepared LiH2PO4, reduced iron powder andα-D-glucose were ball-milled, dried and sin-tered to prepare LiFePO4/C. X-ray diffractometry was used to characterize LiH2PO4, ball-milled product and LiFePO4/C. Differential scanning calorimeter-thermo gravimetric analysis was applied to investigate possible reac-tions in sintering and find suitable temperature for LiFePO4 formation. Scanning electron microscopy was em-ployed for the morphology of LiFePO4/C. As-prepared LiH2PO4 is characterized to be in P21cn（33） space group, which reacts with reduced iron powder to form Li3PO4, Fe3（PO4）2 and H2 in ball-milling and sintering. The appro-priate temperature for LiFePO4/C synthesis is 541.3-976.7 ℃. LiFePO4/C prepared at 700 ℃ presents nano-sized primary particles forming aggregates. Charge-discharge examination indicates that as-prepared LiFePO4/C displays appreciable discharge capacities of 145 and 131 mA·h·g^-1 at 0.1 and 1 C respectively and excellent discharge ca-pacity retention.