The new Cu-Co based （Cu/Co/Zn/Zr） catalysts for higher-alcohol synthesis were prepared using coprecipitation method, plasma enhanced method and reverse coprecipitation method under ultrasound irradiation. The cataly...The new Cu-Co based （Cu/Co/Zn/Zr） catalysts for higher-alcohol synthesis were prepared using coprecipitation method, plasma enhanced method and reverse coprecipitation method under ultrasound irradiation. The catalysts were investigated by the means of BET, SEM, XRD, H2-TPR and XPS. Catalytic properties of the catalysts prepared by various methods were examined using CO hydrogenation reaction. It was found that plasma enhanced method and reverse coprecipitation method under ultrasound irradiation were both effective in enhancing the catalytic properties of Cu/Co/Zn/Zr mixed oxides. The small particle size, high dispersion of active components, the improvement of specific surface area and surface contents of active phases could account for the excellent performance of the experimental Cu/Co/Zn/Zr catalysts.展开更多
Nanocrystalline powders of ZrO_2–8mol%SmO1.5（8Sm SZ）, ZrO_2–8mol%GdO1.5（8Gd SZ）, and ZrO_2–8mol%YO1.5（8YSZ） were prepared by a simple reverse-coprecipitation technique. Differential thermal analysis/thermogra...Nanocrystalline powders of ZrO_2–8mol%SmO1.5（8Sm SZ）, ZrO_2–8mol%GdO1.5（8Gd SZ）, and ZrO_2–8mol%YO1.5（8YSZ） were prepared by a simple reverse-coprecipitation technique. Differential thermal analysis/thermogravimetry（DTA/TG）, Fourier transform infrared spectroscopy（FTIR）, X-ray diffraction（XRD）, Raman spectroscopy, and high-resolution transmission electron microscopy（HRTEM） were used to study the phase transformation and crystal growth behavior. The DTA results showed that the ZrO_2 freeze-dried precipitates crystallized at 529, 465, and 467°C in the case of 8Sm SZ, 8Gd SZ, and 8YSZ, respectively. The XRD and Raman results confirmed the presence of tetragonal ZrO_2 when the dried precipitates were calcined in the temperature range from 600 to 1000°C for 2 h. The crystallite size increased with increasing calcination temperature. The activation energies were calculated as 12.39, 12.45, and 16.59 k J/mol for 8Sm SZ, 8Gd SZ, and 8YSZ respectively.展开更多
基金supported by the National Natural Science Foundation of China(205903603)the New Century Excellent Talent Project of China(NCET-05-0783)
文摘The new Cu-Co based （Cu/Co/Zn/Zr） catalysts for higher-alcohol synthesis were prepared using coprecipitation method, plasma enhanced method and reverse coprecipitation method under ultrasound irradiation. The catalysts were investigated by the means of BET, SEM, XRD, H2-TPR and XPS. Catalytic properties of the catalysts prepared by various methods were examined using CO hydrogenation reaction. It was found that plasma enhanced method and reverse coprecipitation method under ultrasound irradiation were both effective in enhancing the catalytic properties of Cu/Co/Zn/Zr mixed oxides. The small particle size, high dispersion of active components, the improvement of specific surface area and surface contents of active phases could account for the excellent performance of the experimental Cu/Co/Zn/Zr catalysts.
文摘Nanocrystalline powders of ZrO_2–8mol%SmO1.5（8Sm SZ）, ZrO_2–8mol%GdO1.5（8Gd SZ）, and ZrO_2–8mol%YO1.5（8YSZ） were prepared by a simple reverse-coprecipitation technique. Differential thermal analysis/thermogravimetry（DTA/TG）, Fourier transform infrared spectroscopy（FTIR）, X-ray diffraction（XRD）, Raman spectroscopy, and high-resolution transmission electron microscopy（HRTEM） were used to study the phase transformation and crystal growth behavior. The DTA results showed that the ZrO_2 freeze-dried precipitates crystallized at 529, 465, and 467°C in the case of 8Sm SZ, 8Gd SZ, and 8YSZ, respectively. The XRD and Raman results confirmed the presence of tetragonal ZrO_2 when the dried precipitates were calcined in the temperature range from 600 to 1000°C for 2 h. The crystallite size increased with increasing calcination temperature. The activation energies were calculated as 12.39, 12.45, and 16.59 k J/mol for 8Sm SZ, 8Gd SZ, and 8YSZ respectively.