The bimetallic catalyst Ru-Pt/ γ -Al 2O 3 was prepared by impregnating H 2PtCl 6 and RuCl 3 aqueous solution in the presence of PVP(40 000). Its catalytic performance in selective hydrogenation of \{ p -chloronitrobe...The bimetallic catalyst Ru-Pt/ γ -Al 2O 3 was prepared by impregnating H 2PtCl 6 and RuCl 3 aqueous solution in the presence of PVP(40 000). Its catalytic performance in selective hydrogenation of \{ p -chloronitrobenzene\}( p -CNB) was studied. The results indicate that the activity of Ru-Pt/ γ -Al 2O 3[\{ n (ruthenium)\}∶ n (platinum)=4∶1] is much higher than that of Ru/ γ -Al 2O 3,while the amount of dehalogenation product(aniline) and other by-products are much fewer than that by using Pt/ γ -Al 2O 3 as the catalyst. There is synergistic effect of ruthenium and platinum in bimetallic catalyst for selective hydrogenation of p -CNB. Under the reaction conditions t =50 ℃, p H 2 = 1.0 MPa, reaction time 60 min,\{ n (substrate)∶\} n (total amount of metal content)=1000∶1,the conversion of p -CNB and the selectivity to p -chloroaniline( p -CNA) by using Ru-Pt/ γ -Al 2O 3 as the catalyst are 48.2% and 85.9%,respectively. The effect of other metal cations(introduced to the reaction system with the corresponding metal chloride solution) on the reaction was investigated. It was found that catalytic performance of Ru-Pt/ γ -Al 2O 3 could be greatly improved by modfication of some metal cations. When Co 2+ and Ni 2+ were used as modifiers for the catalyst Ru-Pt/ γ -Al 2O 3 under above mentioned reaction conditions,the conversions of p -CNB increase to 74.5% and 87.8%,as well as the selectivities of p -CAN increase to 98.9% and 99.4%,respectively. Fe 3+ and Sn 4+ were the best modifiers for Ru-Pt/ γ -Al 2O 3 under the same reaction conditions. The conversions of p -CNB and the selectivities of p -CAN can reach 100% and >99.0%,respectively. However,the catalysts can be poisoned by Zn 2+ and Sn 2+ .展开更多
（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with...（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.展开更多
Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were...Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.展开更多
BN coated A1203 fibre-reinforced NiAl-alloy composites were fabricated by hot pressing at 1 200-1 400 ℃, and the interracial microstructure and chemical stability of BN coated Al2O3 fibre-reinforced NiAl-alloy compos...BN coated A1203 fibre-reinforced NiAl-alloy composites were fabricated by hot pressing at 1 200-1 400 ℃, and the interracial microstructure and chemical stability of BN coated Al2O3 fibre-reinforced NiAl-alloy composites were investigated by scanning electron microscopy （SEM） and analytical transmission electron microscopy （TEM）. It was found that the complicated chemical reactions and diffusion processes happened in the interface area between BN-layer and Ni25.8A19.6Ta8.3 during the hot pressing at 1 200-1 400 ℃. A continuous AlN-layer was formed at the interface due to the reaction between NiAl and BN. At the same time, Cr diffused extensively into the BN-layer and reacted with boron to form Cr boride precipitates （CrsB3）. In addition, a few particles of Ta-rich phase were also precipitated in NiAl matrix near the interface.展开更多
文摘The bimetallic catalyst Ru-Pt/ γ -Al 2O 3 was prepared by impregnating H 2PtCl 6 and RuCl 3 aqueous solution in the presence of PVP(40 000). Its catalytic performance in selective hydrogenation of \{ p -chloronitrobenzene\}( p -CNB) was studied. The results indicate that the activity of Ru-Pt/ γ -Al 2O 3[\{ n (ruthenium)\}∶ n (platinum)=4∶1] is much higher than that of Ru/ γ -Al 2O 3,while the amount of dehalogenation product(aniline) and other by-products are much fewer than that by using Pt/ γ -Al 2O 3 as the catalyst. There is synergistic effect of ruthenium and platinum in bimetallic catalyst for selective hydrogenation of p -CNB. Under the reaction conditions t =50 ℃, p H 2 = 1.0 MPa, reaction time 60 min,\{ n (substrate)∶\} n (total amount of metal content)=1000∶1,the conversion of p -CNB and the selectivity to p -chloroaniline( p -CNA) by using Ru-Pt/ γ -Al 2O 3 as the catalyst are 48.2% and 85.9%,respectively. The effect of other metal cations(introduced to the reaction system with the corresponding metal chloride solution) on the reaction was investigated. It was found that catalytic performance of Ru-Pt/ γ -Al 2O 3 could be greatly improved by modfication of some metal cations. When Co 2+ and Ni 2+ were used as modifiers for the catalyst Ru-Pt/ γ -Al 2O 3 under above mentioned reaction conditions,the conversions of p -CNB increase to 74.5% and 87.8%,as well as the selectivities of p -CAN increase to 98.9% and 99.4%,respectively. Fe 3+ and Sn 4+ were the best modifiers for Ru-Pt/ γ -Al 2O 3 under the same reaction conditions. The conversions of p -CNB and the selectivities of p -CAN can reach 100% and >99.0%,respectively. However,the catalysts can be poisoned by Zn 2+ and Sn 2+ .
基金Project(51272141)supported by the National Natural Science Foundation of ChinaProject(ts20110828)supported by the Taishan Scholars Project of Shandong Province,ChinaProject(2015AA034404)supported by the Ministry of Science and Technology of China
文摘（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.
基金Project(2012MS0801)supported by the Natural Science Foundation of Inner Mongolia,China
文摘Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.
基金Project (10972190) supported by the National Natural Science Foundation of China Projects (09A089, 08C207) supported by the Scientific Research Fund of Hunan Provincial Education Department,ChinaProject (2010FJ3132) supported by the Planned Science and Technology Project of Hunan Province,China
文摘BN coated A1203 fibre-reinforced NiAl-alloy composites were fabricated by hot pressing at 1 200-1 400 ℃, and the interracial microstructure and chemical stability of BN coated Al2O3 fibre-reinforced NiAl-alloy composites were investigated by scanning electron microscopy （SEM） and analytical transmission electron microscopy （TEM）. It was found that the complicated chemical reactions and diffusion processes happened in the interface area between BN-layer and Ni25.8A19.6Ta8.3 during the hot pressing at 1 200-1 400 ℃. A continuous AlN-layer was formed at the interface due to the reaction between NiAl and BN. At the same time, Cr diffused extensively into the BN-layer and reacted with boron to form Cr boride precipitates （CrsB3）. In addition, a few particles of Ta-rich phase were also precipitated in NiAl matrix near the interface.