Water swelling rubber (WSR) was prepared by reaction blending SBR and sodium polyacrylate (PAANa). The existing states of water in the WSR was studied by means of DSC and TG. It was found that water exists in three st...Water swelling rubber (WSR) was prepared by reaction blending SBR and sodium polyacrylate (PAANa). The existing states of water in the WSR was studied by means of DSC and TG. It was found that water exists in three states: nonfreezing water, bound freezable water and free water. The relationships between water states and structure of PAANa were investigated. The results showed that the amount of non-freezing water was related to total water content, and the ratio of non-freezing water versus -COONa groups on PAANa (mol/mol) was about 4. However, total water content slightly affected the content of bound freezable water and remarkably affected the amount of free waer.展开更多
基金Project supported by the National Natural Science Foundation of China.
文摘Water swelling rubber (WSR) was prepared by reaction blending SBR and sodium polyacrylate (PAANa). The existing states of water in the WSR was studied by means of DSC and TG. It was found that water exists in three states: nonfreezing water, bound freezable water and free water. The relationships between water states and structure of PAANa were investigated. The results showed that the amount of non-freezing water was related to total water content, and the ratio of non-freezing water versus -COONa groups on PAANa (mol/mol) was about 4. However, total water content slightly affected the content of bound freezable water and remarkably affected the amount of free waer.