In engineering practice, tubular X-joints have been widely used in offshore structures. The fatigue failure of tubular X-joints in offshore engineering is mainly caused by axial tensile stress. In this study, the stre...In engineering practice, tubular X-joints have been widely used in offshore structures. The fatigue failure of tubular X-joints in offshore engineering is mainly caused by axial tensile stress. In this study, the stress concentration factor distribution along the weld toe in the hot spot stress region for tubular X-joints subject to axial loads have been analyzed by use of finite element method. Through numerical analysis, it has been found that the peak stress concentration factor is located at the saddle position. Thereafter, 80 models have been analyzed, and the effect of the geometric parameters of a tubular X-joint on the stress concentration factor has been investigated. Based on the experimental values of the numerical stress concentration factor, a parametric equation to calculate the stress concentration factor of tubular X-joints has been proposed. The accuracy of this equation has been verified against the requirement of the Fatigue Guidance Review Panel, and the proposed equation is found capable of producing reasonably accurate stress concentration factor values for tubular X-joints subject to axial loads.展开更多
对承受疲劳载荷的海洋平台K型管节点首先进行了静力测试,确定了沿着焊缝的热应力区的应力分布及热应力区最大应力点的位置,从而判断裂纹产生的位置;然后通过专用测试设备提供循环疲劳载荷,用ACPD(Alternating Current Potential Drop,...对承受疲劳载荷的海洋平台K型管节点首先进行了静力测试,确定了沿着焊缝的热应力区的应力分布及热应力区最大应力点的位置,从而判断裂纹产生的位置;然后通过专用测试设备提供循环疲劳载荷,用ACPD(Alternating Current Potential Drop,即交流电流势能落差法)技术检测裂纹的产生和增长过程,得到裂纹最深点,用S-N曲线估算其疲劳寿命。对已有裂纹的K型管节点,用应力强度因子估计其剩余寿命。同时用测试的结果验证了S-N的准确性和可靠性。展开更多
基金The research work was financially supported by the National Natural Scientice Foundation of China(Grant No.10142001)by the Shandong Provincial Natural Scientice Foundation(Grant No.Y2006F46)
文摘In engineering practice, tubular X-joints have been widely used in offshore structures. The fatigue failure of tubular X-joints in offshore engineering is mainly caused by axial tensile stress. In this study, the stress concentration factor distribution along the weld toe in the hot spot stress region for tubular X-joints subject to axial loads have been analyzed by use of finite element method. Through numerical analysis, it has been found that the peak stress concentration factor is located at the saddle position. Thereafter, 80 models have been analyzed, and the effect of the geometric parameters of a tubular X-joint on the stress concentration factor has been investigated. Based on the experimental values of the numerical stress concentration factor, a parametric equation to calculate the stress concentration factor of tubular X-joints has been proposed. The accuracy of this equation has been verified against the requirement of the Fatigue Guidance Review Panel, and the proposed equation is found capable of producing reasonably accurate stress concentration factor values for tubular X-joints subject to axial loads.
文摘对承受疲劳载荷的海洋平台K型管节点首先进行了静力测试,确定了沿着焊缝的热应力区的应力分布及热应力区最大应力点的位置,从而判断裂纹产生的位置;然后通过专用测试设备提供循环疲劳载荷,用ACPD(Alternating Current Potential Drop,即交流电流势能落差法)技术检测裂纹的产生和增长过程,得到裂纹最深点,用S-N曲线估算其疲劳寿命。对已有裂纹的K型管节点,用应力强度因子估计其剩余寿命。同时用测试的结果验证了S-N的准确性和可靠性。