P-polarization high reflectors are deposited by e-beam from hafnia and silica. 1-on-1 and N-on-1 tests at 1064-nm wavelength with P-polarization at 45° incidence are carried out on these samples. Microscope and s...P-polarization high reflectors are deposited by e-beam from hafnia and silica. 1-on-1 and N-on-1 tests at 1064-nm wavelength with P-polarization at 45° incidence are carried out on these samples. Microscope and scanning electron microscope are applied to investigate the damage morphologies in both 1-on-1 and N-on^l tests. It is found that the laser damage threshold is higher in N-on-1 tests and nodular defect is the main inducement that leads to the damage because nodular ejection with plasma scalding is the typical damage morphology. Similar damage morphology observed in the two tests indicates that the higher laser damage threshold in N-on-1 test is attributed to the mechanical stabilization process of nodular defects, owing to the gradually increased laser fluence radiation. Based on the typical morphology study, some process optimizations are given.展开更多
The purpose of this research is to study the dynamic responses of gravity quay walls with block type consisting of“three blocks”experimentally.For this purpose,1g shaking table tests were conducted under different c...The purpose of this research is to study the dynamic responses of gravity quay walls with block type consisting of“three blocks”experimentally.For this purpose,1g shaking table tests were conducted under different cyclic loadings for two different saturated granular backfill materials(Soil 1 and Soil 2).In this study,D_(n50) of Soil 1 and Soil 2 are selected as 2.2 cm and 1.0 cm,respectively.During the experiments,accelerations,soil pressures and displacements were measured for each block.Test results pointed out that Soil 2 caused more damage on structures.The measurements for displacement and tilting of each block were discussed in view of“acceptable level of damage in performance-based design”given in PIANC(2001).The result of the study showed that the definitions of damaged levels given in PIANC(2001)were reliable for using in performance-based methods for seismic design of block type quay walls.展开更多
The conventional forming limit diagram （FLD） is described as a plot of major strain versus minor strain. However, FLD is dependent on forming history and strain path. In the present study, a forming limit stress-bas...The conventional forming limit diagram （FLD） is described as a plot of major strain versus minor strain. However, FLD is dependent on forming history and strain path. In the present study, a forming limit stress-based diagram （FLSD） has been adopted to predict the fracture limit of aluminum alloy （AA） 5052-O1 sheet. Nakazima test is simulated by plastic constitutive formula derived from the modified Gurson-Tvergaard-Needleman （GTN） model. An in situ tensile test with scanning electron microscope （SEM） is proposed to determine the parameters in GTN model. The damage evolution is observed and recorded, and the parameters of GTN model are identified through counting void fraction at three damage stages of AA5052-O 1. According to the experimental results, the original void volume fraction, the volume fraction of potential nucleated voids, the critical void volume fraction, the void volume fraction at the final failure of material are assigned as 0.002 918, 0.024 9, 0.030 103, 0.048 54, respectively. The stress and strain are obtained at the last loading step before crack. FLSD and FLD of AA5052-O 1 are plotted. Compared with the experimental Nakazima test and uniaxial tensile test, the predicted results show a good agreement. The parameters determined by in situ tensile test can be applied to the research of the forming limit for ductile metals.展开更多
基金supported by the National"863"Program of China under Grant No.2006AA804908
文摘P-polarization high reflectors are deposited by e-beam from hafnia and silica. 1-on-1 and N-on-1 tests at 1064-nm wavelength with P-polarization at 45° incidence are carried out on these samples. Microscope and scanning electron microscope are applied to investigate the damage morphologies in both 1-on-1 and N-on^l tests. It is found that the laser damage threshold is higher in N-on-1 tests and nodular defect is the main inducement that leads to the damage because nodular ejection with plasma scalding is the typical damage morphology. Similar damage morphology observed in the two tests indicates that the higher laser damage threshold in N-on-1 test is attributed to the mechanical stabilization process of nodular defects, owing to the gradually increased laser fluence radiation. Based on the typical morphology study, some process optimizations are given.
基金The study was financially supported by the Scientific and Technological Research Council of Turkey(TUBITAK)(Grant No.111Y006).
文摘The purpose of this research is to study the dynamic responses of gravity quay walls with block type consisting of“three blocks”experimentally.For this purpose,1g shaking table tests were conducted under different cyclic loadings for two different saturated granular backfill materials(Soil 1 and Soil 2).In this study,D_(n50) of Soil 1 and Soil 2 are selected as 2.2 cm and 1.0 cm,respectively.During the experiments,accelerations,soil pressures and displacements were measured for each block.Test results pointed out that Soil 2 caused more damage on structures.The measurements for displacement and tilting of each block were discussed in view of“acceptable level of damage in performance-based design”given in PIANC(2001).The result of the study showed that the definitions of damaged levels given in PIANC(2001)were reliable for using in performance-based methods for seismic design of block type quay walls.
基金Aeronautical Science Foundation of China （03H53048）
文摘The conventional forming limit diagram （FLD） is described as a plot of major strain versus minor strain. However, FLD is dependent on forming history and strain path. In the present study, a forming limit stress-based diagram （FLSD） has been adopted to predict the fracture limit of aluminum alloy （AA） 5052-O1 sheet. Nakazima test is simulated by plastic constitutive formula derived from the modified Gurson-Tvergaard-Needleman （GTN） model. An in situ tensile test with scanning electron microscope （SEM） is proposed to determine the parameters in GTN model. The damage evolution is observed and recorded, and the parameters of GTN model are identified through counting void fraction at three damage stages of AA5052-O 1. According to the experimental results, the original void volume fraction, the volume fraction of potential nucleated voids, the critical void volume fraction, the void volume fraction at the final failure of material are assigned as 0.002 918, 0.024 9, 0.030 103, 0.048 54, respectively. The stress and strain are obtained at the last loading step before crack. FLSD and FLD of AA5052-O 1 are plotted. Compared with the experimental Nakazima test and uniaxial tensile test, the predicted results show a good agreement. The parameters determined by in situ tensile test can be applied to the research of the forming limit for ductile metals.