To meet the demand of the domestic pressure vessel industry for roll-bonded clad steel plates, Baosteel has developed an S30403 ＋ Q345R roll-bonded clad steel plate. Comprehensive inspections of the composition, micr...To meet the demand of the domestic pressure vessel industry for roll-bonded clad steel plates, Baosteel has developed an S30403 ＋ Q345R roll-bonded clad steel plate. Comprehensive inspections of the composition, microstructure, and properties are made to systematically evaluate the steel plate in the normalized and normalized ＋ stress relieved states. The results show the cladding interface of the S30403 ＋ Q345R roll-bonded clad steel plate has high shear strength, the base metal has good properties, and the mechanical properties of the steel plate head and tail are uniform. The performance is fully consistent with the technical requirements of the roll-bonded clad steel plate for pressure vessels.展开更多
Repassivation behaviour of the passive film formed on lean duplex stainless steel UNS S32101 and austenitic stainless steel UNS S30403 in a CO2-saturated oilfield environment has been studied. The native passive film ...Repassivation behaviour of the passive film formed on lean duplex stainless steel UNS S32101 and austenitic stainless steel UNS S30403 in a CO2-saturated oilfield environment has been studied. The native passive film on the alloys was thinned/removed by stepping the potential of the alloy to ﹣850 mV/Ag/AgCl for 30 minutes. Potentiostatic measurements were then taken at potentials of ﹣200, ﹣100, 0, 100 and 200 mV versus Ag/AgCl. Results show that the passive film repassivates at potentials of ﹣200 and ﹣100 mV and 0 mV for both alloys at 50°C. The current density however continues to rise for potentials of 100 and 200 mV. This shows that both alloys are susceptible to pitting at potentials above 100 mV at the test temperature of 50°C.展开更多
文摘To meet the demand of the domestic pressure vessel industry for roll-bonded clad steel plates, Baosteel has developed an S30403 ＋ Q345R roll-bonded clad steel plate. Comprehensive inspections of the composition, microstructure, and properties are made to systematically evaluate the steel plate in the normalized and normalized ＋ stress relieved states. The results show the cladding interface of the S30403 ＋ Q345R roll-bonded clad steel plate has high shear strength, the base metal has good properties, and the mechanical properties of the steel plate head and tail are uniform. The performance is fully consistent with the technical requirements of the roll-bonded clad steel plate for pressure vessels.
文摘Repassivation behaviour of the passive film formed on lean duplex stainless steel UNS S32101 and austenitic stainless steel UNS S30403 in a CO2-saturated oilfield environment has been studied. The native passive film on the alloys was thinned/removed by stepping the potential of the alloy to ﹣850 mV/Ag/AgCl for 30 minutes. Potentiostatic measurements were then taken at potentials of ﹣200, ﹣100, 0, 100 and 200 mV versus Ag/AgCl. Results show that the passive film repassivates at potentials of ﹣200 and ﹣100 mV and 0 mV for both alloys at 50°C. The current density however continues to rise for potentials of 100 and 200 mV. This shows that both alloys are susceptible to pitting at potentials above 100 mV at the test temperature of 50°C.