SAW高速焊接焊丝和焊剂国产化替代的开发研究

卧式埋弧焊机高速焊接使用的焊丝和焊剂进行国产化替代,并在此基础上使用气保焊焊丝代替埋弧焊焊丝进行焊接,获得了成功。通过实践、理化试验相关金相证明,该焊接新工艺是可靠的。探索出的一条适合该卧式高速焊接的焊接工艺即ER50-6+SJ101的焊接新工艺,与旧工艺相比,新工艺应用广泛、取材广,应用价值和经济性更好。新工艺已经成熟,焊接质量稳定,焊接速度满足生产要求,焊接成本也大幅度下降,经济效益可观。

Influence of welding-flux moisture on welding quality

A high hydrogen content in weld produces hydrogen embrittlement, welding cold cracks, and even blowholes,which seriously affect joint performance and welding quality. Submerged-arc-welding flux has a great influence on the hydrogen content of the final weld. To simulate different flux storage circumstances and pre- welding treatments,the effects of different welding-flux states on the welding quality and hydrogen content in weld were compared, using moisture content determination test and hydrogen content in deposited metal determination test. The test results reveal that to ensure the quality of welding, it is necessary to strictly control the storage of welding flux and procedures followed when using it.

高韧性埋弧焊烧结焊剂

采用均匀设计对埋弧自动焊烧结焊剂工艺性能进行了试验研究,研制出一种工艺性能较好、低温冲击韧性较高的烧结焊剂,并找出了主要组分对焊剂工艺性能的影响规律。结果表明均匀设计用于焊剂配方设计是一种有效的方法,可在焊剂新品种开发中推广应用。

线锯切割中锯丝的高梯度磁场数值和理论分析

线锯切割常用锯丝——镀铜钢丝,作为一种聚磁材料,在匀强磁场中会被磁化产生高梯度磁场,对其附近的磁性磨粒产生磁力作用,使磨粒吸附在锯丝上,故在游离磨料线锯切割中添加辅助磁场,增加了切割区域内磨粒的数量,更有利于切割。为进一步研究锯丝产生的高梯度磁场,通过对辅助磁场与锯丝组成的磁系统进行数学建模,采用有限元的方法对整个系统进行数值模拟,发现辅助磁场的改变与产生的高梯度磁场的磁感应强度存在关系,即高梯度磁场的磁感应强度会随着永磁体之间距离的减小、永磁体宽度和高度的增大而变大。并通过理论计算与仿真结果的对比验证了仿真的正确性。

耐候钢埋弧焊用焊剂/焊丝的研制

通过焊接熔敷金属的周期浸润腐蚀和力学性能等试验 ,表明研制的埋弧焊焊丝 /焊剂适用于高耐候结构钢及高强度焊接结构耐候钢。

螺旋焊管板头对接FCB法单面焊双面成形工艺研究

为了实现螺旋焊管生产用钢带对接焊缝的单面焊双面成形,对埋弧焊FCB法单面焊双面成形工艺进行了试验研究。首先在试验室完成了壁厚16 mm、20 mm和22.5 mm焊接试板的FCB法单面焊双面成形工艺试验,优化了FCB工艺的焊接参数。在此基础上,完成了螺旋焊管生产线板头对接双丝焊改造,在线进行了18 mm、22 mm两种壁厚板头对接单面焊双面成形试验,基本实现了螺旋焊管卷板头尾对接工序的单面焊双面成形工艺的应用。试验及生产线应用表明,FCB法单面焊双面成型焊接接头各区域基本性能满足技术指标要求,该项工艺可以推广应用于输水管线、结构管等承压能力和钢级较低的螺旋管的板头对接缝焊接,可以提高焊接生产效率,降低生产成本。