A method was developed to make a quantitative analysis of the microstructure of asphalt modified with styrene-butadiene-styrene block(SBS) copolymer. Moreover, both mixed and branched SBS were employed in the prepar...A method was developed to make a quantitative analysis of the microstructure of asphalt modified with styrene-butadiene-styrene block(SBS) copolymer. Moreover, both mixed and branched SBS were employed in the preparation of modified asphalt. By sampling specimens from the top, middle, and bottom, a number of microscope slides were made and 400 times micro images were gained. Binarized with the software of MATLAB, the images then went to the process of distribution test, when four typical distributions were employed to investigate the distribution of modifi er spread in asphalt. The distribution characteristic and its parameter were both found. The results show that asphalt phase clearly obeys Poisson distribution, and its parameter, λ, is bond up with the condition SBS performs in. Based on this parameter, indexes can be set up to evaluate the structure of the mixture and its performance as well. Compared with that modifi ed with mixed SBS, the asphalt modifi ed with branched SBS has better performance but worse stability, for it is easier to segregate.展开更多
Both macro and micro-methods were introduced to study the physical and chemical properties of thermal oxidative aging of SBS (styrene-butadiene-styrene) modified asphalt. The physical properties of SBS modified asph...Both macro and micro-methods were introduced to study the physical and chemical properties of thermal oxidative aging of SBS (styrene-butadiene-styrene) modified asphalt. The physical properties of SBS modified asphalt before and after aging were analyzed by normal tests. The structure and quality variation of SBS modified asphalt during the aging process was analyzed by FTIR (Fourier transform infrared spectrum). FTIR result shows that the degeneration of SBS modified asphalt is mainly caused by oxidative reaction and rupture of C=C double bond. The molecular weight variations of asphalt function groups and SBS polymer were studied by GPC (Gel Permeation Chromatography). GPC result shows that small molecules transform into larger one in asphalt and SBS polymer molecule degrade during the aging process. SBS polymer may lose its modifying function after long time aging.展开更多
The aging mechanism of SBS modified asphalt during its aging process was studied.The characterizations of base asphalt,SBS polymer and its modified asphalt were determined in different aging time by Fourier transform ...The aging mechanism of SBS modified asphalt during its aging process was studied.The characterizations of base asphalt,SBS polymer and its modified asphalt were determined in different aging time by Fourier transform infrared spectrum(FTIR).FTIR shows that oxidative dehydrogenation reaction occurs in asphalt,and unsaturated carbon bond is generated under short-term thermal aging condition.Additionally,SBS polymer was aged significantly under that condition,the speed of which was faster than that of base asphalt.The aging laws of both asphalt and SBS polymer during the aging process of SBS modified asphalt were similar to their aging laws respectively.Due to the protective effect between asphalt and SBS polymer,the aging degrees of asphalt and SBS polymer were lower than those aged independently.展开更多
Owing to the environmental protection potential and the desirable high performance capabilities,asphalt rubber(AR)and styrene-butadiene-styrene(SBS)modified asphalt have been widely used.However,the poor construction ...Owing to the environmental protection potential and the desirable high performance capabilities,asphalt rubber(AR)and styrene-butadiene-styrene(SBS)modified asphalt have been widely used.However,the poor construction workability and segregation issues of AR,along with the exorbitant cost of SBS modified asphalt,are of the serious problems that plague their application scope.Moreover,SBS/crumb rubber(CR)modified asphalt is gradually becoming widespread and it therefore becomes incumbent to find appropriate ways to mitigate the issues that may limit its use.As a consequence,it becomes crucial to analyze the interaction between CR and SBS modifiers in the composite mixture,as well as evaluate the influence of modifier dosage on the performance of the modified asphalt.This study presents a comprehensive review of the effects of SBS modifier,CR modifier and composite SBS/CR on the performance of modified asphalts.Macro analysis and micro analysis,including analysis on the conventional physical properties,are carried out.It can uncover the interaction between modifier and asphalt,which reveals how the modifiers influence the properties of modified asphalts.This study will serve as a source of invaluable information to researchers,engineers,and designers,informing them the development,potential and challenges of the CR,SBS and SBS/CR modified asphalts,the optimum contents to attain the best performance along with the mechanism involved.展开更多
基金Funded by the National Natural Science Foundation of China(51178348)
文摘A method was developed to make a quantitative analysis of the microstructure of asphalt modified with styrene-butadiene-styrene block(SBS) copolymer. Moreover, both mixed and branched SBS were employed in the preparation of modified asphalt. By sampling specimens from the top, middle, and bottom, a number of microscope slides were made and 400 times micro images were gained. Binarized with the software of MATLAB, the images then went to the process of distribution test, when four typical distributions were employed to investigate the distribution of modifi er spread in asphalt. The distribution characteristic and its parameter were both found. The results show that asphalt phase clearly obeys Poisson distribution, and its parameter, λ, is bond up with the condition SBS performs in. Based on this parameter, indexes can be set up to evaluate the structure of the mixture and its performance as well. Compared with that modifi ed with mixed SBS, the asphalt modifi ed with branched SBS has better performance but worse stability, for it is easier to segregate.
基金Funded by the National Natural Science Foundation of China(Nos.50878054,51108081)
文摘Both macro and micro-methods were introduced to study the physical and chemical properties of thermal oxidative aging of SBS (styrene-butadiene-styrene) modified asphalt. The physical properties of SBS modified asphalt before and after aging were analyzed by normal tests. The structure and quality variation of SBS modified asphalt during the aging process was analyzed by FTIR (Fourier transform infrared spectrum). FTIR result shows that the degeneration of SBS modified asphalt is mainly caused by oxidative reaction and rupture of C=C double bond. The molecular weight variations of asphalt function groups and SBS polymer were studied by GPC (Gel Permeation Chromatography). GPC result shows that small molecules transform into larger one in asphalt and SBS polymer molecule degrade during the aging process. SBS polymer may lose its modifying function after long time aging.
基金Funded by the National Natural Science Foundation of China(No.50878054)
文摘The aging mechanism of SBS modified asphalt during its aging process was studied.The characterizations of base asphalt,SBS polymer and its modified asphalt were determined in different aging time by Fourier transform infrared spectrum(FTIR).FTIR shows that oxidative dehydrogenation reaction occurs in asphalt,and unsaturated carbon bond is generated under short-term thermal aging condition.Additionally,SBS polymer was aged significantly under that condition,the speed of which was faster than that of base asphalt.The aging laws of both asphalt and SBS polymer during the aging process of SBS modified asphalt were similar to their aging laws respectively.Due to the protective effect between asphalt and SBS polymer,the aging degrees of asphalt and SBS polymer were lower than those aged independently.
基金funded by Key Research and Development Project of Shaanxi Province(2022SF-328)the Science and Technology Project of Henan Department of Transportation(2020J-2-3)+1 种基金Science and Technology Project of Shaanxi Department of Transportation(No.19-10K,No.19-28K)Rising Tech Star Project of Shaanxi Department of Science and Technology(No.2019KJXX-035)。
文摘Owing to the environmental protection potential and the desirable high performance capabilities,asphalt rubber(AR)and styrene-butadiene-styrene(SBS)modified asphalt have been widely used.However,the poor construction workability and segregation issues of AR,along with the exorbitant cost of SBS modified asphalt,are of the serious problems that plague their application scope.Moreover,SBS/crumb rubber(CR)modified asphalt is gradually becoming widespread and it therefore becomes incumbent to find appropriate ways to mitigate the issues that may limit its use.As a consequence,it becomes crucial to analyze the interaction between CR and SBS modifiers in the composite mixture,as well as evaluate the influence of modifier dosage on the performance of the modified asphalt.This study presents a comprehensive review of the effects of SBS modifier,CR modifier and composite SBS/CR on the performance of modified asphalts.Macro analysis and micro analysis,including analysis on the conventional physical properties,are carried out.It can uncover the interaction between modifier and asphalt,which reveals how the modifiers influence the properties of modified asphalts.This study will serve as a source of invaluable information to researchers,engineers,and designers,informing them the development,potential and challenges of the CR,SBS and SBS/CR modified asphalts,the optimum contents to attain the best performance along with the mechanism involved.