NH_3 selective catalytic reduction of NO: A large surface TiO_2 support and its promotion of V_2O_5 dispersion on the prepared catalyst

A titania support with a large surface area was developed, which has a BET surface area of 380.5 m^2/g, four times that of a traditional titania support. The support was ultrasonically impregnated with 5 wt% vanadia. A special heat treatment was used in the calcination to maintain the large surface area and high dispersion of vanadium species. This catalyst was compared to a common V2O5-TiO2 catalyst with the same vanadia loading prepared by a traditional method. The new catalyst has a surface area of 117.7 m^2/g, which was 38% higher than the traditional V2O5-TiO2 catalyst. The selective catalytic reduction（SCR） performance demonstrated that the new catalyst had a wider temperature window and better N2 selectivity compared to the traditional one. The NO conversion was 80% from 200 to 450 °C. The temperature window was 100 °C wider than the traditional catalyst. Raman spectra indicated that the vanadium species formed more V-O-V linkages on the catalyst prepared by the traditional method. The amount of V-O-Ti and V=O was larger for the new catalyst. Temperature programmed desorption of NH3, temperature programmed reduction by H2 and X-ray photoelectron spectroscopy results showed that its redox ability and total acidity were enhanced. The results are helpful for developing a more efficient SCR catalyst for the removal of NOx in flue gases.

Improving the denitration performance and K-poisoning resistance of the V_2O_5-WO_3/TiO_2 catalyst by Ce^(4+) and Zr^(4+) co-doping

A series of V2O5‐WO3/TiO2‐ZrO2,V2O5‐WO3/TiO2‐CeO2,and V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalysts were synthesized to improve the selective catalytic reduction(SCR)performance and the K‐poisoning resistance of a V2O5‐WO3/TiO2 catalyst.The physicochemical properties were investigated by using XRD,BET,NH3‐TPD,H2‐TPR,and XPS,and the catalytic performance and K‐poisoning resistance were evaluated via a NH3‐SCR model reaction.Ce^4+and Zr^4+co‐doping were found to enhance the conversion of NOx,and exhibit the best K‐poisoning resistance owing to the largest BET‐specific surface area,pore volume,and total acid site concentration,as well as the minimal effects on the surface acidity and redox ability from K poisoning.The V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalyst also presents outstanding H2O+SO2 tolerance.Finally,the in situ DRIFTS reveals that the NH3‐SCR reaction over the V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalyst follows an L‐H mechanism,and that K poisoning does not change the reaction mechanism.

Effect of TiO_2 surface properties on the SCR activity of NOx emission abatement catalyst

NOx emission abatement catalysts V 2O 5 supported on various TiO 2 including anatase, rutile and mixture of both were investigated with various physico\|chemical measurements such as BET, NH\-3\|TPD, NARP, XRD and so on, and the effect of TiO\-2 surface properties on the SCR(selective catalytic reduction) activity of V\-2O\-5/TiO\-2 catalysts was studied. It was found that the TiO\-2 surface properties had strong affect on the SCR activity of V\-2O\-5/TiO\-2 catalysts. The stronger acidic property resulted in the higher exposure of active sites as well as the higher SCR activity.

钒钛基SCR催化剂中毒及再生研究进展

在烟气脱硝系统中,选择性催化还原催化剂的中毒和再生是广泛关注的问题。文章介绍了钒钛基催化剂的碱金属中毒、碱土金属中毒、砷中毒和二氧化硫中毒,探讨其成因,并对中毒机理进行了分析,同时研究了避免催化剂中毒的措施以及中毒催化剂的再生技术。对碱金属中毒和碱土金属中毒催化剂的水洗再生和硫酸酸洗再生方法进行了实验评价。文章对溶胶凝胶法制备的以陶瓷颗粒为骨架的纳米负载型催化剂V2O5-WO3/TiO2(C)进行研究。实验结果表明,硫酸酸洗再生对碱金属和碱土金属中毒催化剂具有较好的再生效果。在380～410℃温度范围内可使中毒催化剂的NO去除率恢复至90%以上。水洗再生对碱金属中毒催化剂无明显效果,而在380～410℃温度范围内可使碱土金属中毒催化剂的NO去除率达到80%以上。对V2O5-WO3/TiO2(C)抗SO2性能研究表明,以锐钛TiO2为载体的V2O5-WO3/TiO2(C)催化剂具有较好的抗SO2效果。

不同制备工艺钒系SCR催化剂理化及催化性能研究

本文研究了制备工艺对TiO_2-WO_3-V_2O_5-载体型催化剂理化特性及其在NH_3-SCR反应中催化性能的影响。通过XRD、TG/DTA等分析方法考察了煅烧温度等对催化剂中各组分晶体结构的影响,确定了制备负载型催化剂的最佳煅烧温度为500℃。不同制备工艺催化剂理化性能的对比表明,多步浸渍法不仅提高了锐钛矿型TiO_2向金红石型TiO_2的转变温度,而且使更多的钒氧化物处于较低的价态,有利于提高还原反应的催化性能;催化活性评价试验也表明使用多步浸渍法制备的SCR催化剂具有较高的催化活性和更宽的高活性反应温度窗口。最后考察了反应空速对多步浸渍法所制备催化剂NO_x转化效率的影响,结果表明:随空速的增加,NO_x转化效率逐渐降低。

氧化物替代对钒钛SCR催化剂性能影响研究

采用浸渍法制备了La_2O_3、Ce_2O_3和Co_2O_3等金属氧化物部分替代V_2O_5的氧化物-MoO_3-TiO_2型催化剂,并进行了理化性能和催化活性表征。结果表明:替代型催化剂的比表面积与钒型催化剂差别不大。在NH_3-SCR反应中,镧型和铈型催化剂不仪低温活性较高而且NO_x净化率在500℃时才开始衰减,具有最宽的活性温度窗口;钴型催化剂虽然低温活性最好,但其NO_x净化率在400℃即开始衰减,导致其活性温度窗口较窄,但还是比钒型催化剂宽。此外,反应温度是影响HC和CO排放变化的主要因素,而催化剂种类对其影响较小。1×10~5 h^(-1)以下时,不同空速对NO_x净化率影响较小;而空速达到3×10~5 h^(-1)时,NO_x净化率显著下降。