Ti1Al2O3 Functionally Gradient Material (FGM) was prepared by an explosive compaction/SHS process. Ten sheets of the compounding powder were laminated and pressed to get a green body of FGM. It was then compacted expl...Ti1Al2O3 Functionally Gradient Material (FGM) was prepared by an explosive compaction/SHS process. Ten sheets of the compounding powder were laminated and pressed to get a green body of FGM. It was then compacted explosively By burying the explosive compaction body into a stoichiometric Al/TiO2 mixture and igniting the combustion of the stoichiometric Al/TiO2 mixture, the SHS reaction of the explosive compaction body was initiated by the heat released from the combustion of the stoichiometric Al/TiO2 mixture. In this way, Ti/Al2O3 FGM was synthesized. The adiabatic temperatures of each gradient layer were calculated when the preheating temperatures were 298 K and 1173 K, respectively The microstructure, composition and properties of Ti/Al2O3 FGM and the reaction mechanism of each gradient layer were studied. It was found that Ti/Al2O3 FGM prepared by the explosive compaction/SHS process had a high density and a high microhardness. Its structure, composition and properties showed apparent gradient distribution. The structure of the standard stoichiometric ratio gradient layer of FGM was a network structure. Its reaction mode could be described as follows: Al powder melted first, then the molten Al penetrated into the TiO2 zone and reacted with TiO2, and big pores were left in the original positions of Al powder. The reaction of gradient layers with the addition of Al3O3 as diluents was similar to that of the standard stoichiometric ratio gradient layer, so were their structure and composition. However, the reaction of gradient layers with the addition of Ti as diluents was more complex and the composition deviated slightly from the designed one展开更多
SHS method with reductive process was used to synthesize TiB2 ceramic powder from B2O3-TiO2-Mg system. X-ray diffraction, SEM and Image analysis were used to analyse microstructure of TiB2 powder and compare with micr...SHS method with reductive process was used to synthesize TiB2 ceramic powder from B2O3-TiO2-Mg system. X-ray diffraction, SEM and Image analysis were used to analyse microstructure of TiB2 powder and compare with microstructure of TiB, fabricated by SHS elements syn-thesis from Ti+B system. The results show that TiB? powder fabricated by SHS reductive synthesis is finer (about 1. 5?m) ,uni former and free-agglomerate.展开更多
TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM...TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.展开更多
文摘Ti1Al2O3 Functionally Gradient Material (FGM) was prepared by an explosive compaction/SHS process. Ten sheets of the compounding powder were laminated and pressed to get a green body of FGM. It was then compacted explosively By burying the explosive compaction body into a stoichiometric Al/TiO2 mixture and igniting the combustion of the stoichiometric Al/TiO2 mixture, the SHS reaction of the explosive compaction body was initiated by the heat released from the combustion of the stoichiometric Al/TiO2 mixture. In this way, Ti/Al2O3 FGM was synthesized. The adiabatic temperatures of each gradient layer were calculated when the preheating temperatures were 298 K and 1173 K, respectively The microstructure, composition and properties of Ti/Al2O3 FGM and the reaction mechanism of each gradient layer were studied. It was found that Ti/Al2O3 FGM prepared by the explosive compaction/SHS process had a high density and a high microhardness. Its structure, composition and properties showed apparent gradient distribution. The structure of the standard stoichiometric ratio gradient layer of FGM was a network structure. Its reaction mode could be described as follows: Al powder melted first, then the molten Al penetrated into the TiO2 zone and reacted with TiO2, and big pores were left in the original positions of Al powder. The reaction of gradient layers with the addition of Al3O3 as diluents was similar to that of the standard stoichiometric ratio gradient layer, so were their structure and composition. However, the reaction of gradient layers with the addition of Ti as diluents was more complex and the composition deviated slightly from the designed one
文摘SHS method with reductive process was used to synthesize TiB2 ceramic powder from B2O3-TiO2-Mg system. X-ray diffraction, SEM and Image analysis were used to analyse microstructure of TiB2 powder and compare with microstructure of TiB, fabricated by SHS elements syn-thesis from Ti+B system. The results show that TiB? powder fabricated by SHS reductive synthesis is finer (about 1. 5?m) ,uni former and free-agglomerate.
文摘TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.