The process of the epoxy-bonded Sm_2TM_(17) magnets includes:(1)after melting,the ingots are treated by solid soluiion,and then aged and pulverized;(2)the obtained alloy powder is mixed with epoxy resin bind- er;(3)th...The process of the epoxy-bonded Sm_2TM_(17) magnets includes:(1)after melting,the ingots are treated by solid soluiion,and then aged and pulverized;(2)the obtained alloy powder is mixed with epoxy resin bind- er;(3)the mixture is pressed in a magnetic field;(4)the compacts are cured.When the SmCo_(4.9)Fe_(2.7)Cu_(0.54)Zr_(0.13) alloy is heat treated and pressed with optimum pressing parameters,the high quality bonded magnets with B_r=8250 G,_iH_c=13000 Oe,and(BH)_(max)=16MGOe can be obtained.The stability of the magnets is studied also.The irreversible loss of O.C.(open circuit)remanence B_r in the temperature range between 25 and 150℃,is less than 4%.The average temperature coefficient at temperatures between 25 and 70℃ is-0.03%/℃.The magnets obtained have heat resistance up to 130℃ even in long-term service, and have good corrosion resistance in acid,alkali and salt solutions.展开更多
文摘The process of the epoxy-bonded Sm_2TM_(17) magnets includes:(1)after melting,the ingots are treated by solid soluiion,and then aged and pulverized;(2)the obtained alloy powder is mixed with epoxy resin bind- er;(3)the mixture is pressed in a magnetic field;(4)the compacts are cured.When the SmCo_(4.9)Fe_(2.7)Cu_(0.54)Zr_(0.13) alloy is heat treated and pressed with optimum pressing parameters,the high quality bonded magnets with B_r=8250 G,_iH_c=13000 Oe,and(BH)_(max)=16MGOe can be obtained.The stability of the magnets is studied also.The irreversible loss of O.C.(open circuit)remanence B_r in the temperature range between 25 and 150℃,is less than 4%.The average temperature coefficient at temperatures between 25 and 70℃ is-0.03%/℃.The magnets obtained have heat resistance up to 130℃ even in long-term service, and have good corrosion resistance in acid,alkali and salt solutions.