通过水热改性氢氧化锆制备了SO42-/ZrO2固体酸催化剂。以冰乙酸和正丁醇的酯化反应为探针反应,确定了固体超强酸的最佳制备条件。分别考察了浸渍硫酸浓度、硫酸浸渍时间和焙烧温度等对催化活性的影响。并以水热改性和未经水热改性氢氧...通过水热改性氢氧化锆制备了SO42-/ZrO2固体酸催化剂。以冰乙酸和正丁醇的酯化反应为探针反应,确定了固体超强酸的最佳制备条件。分别考察了浸渍硫酸浓度、硫酸浸渍时间和焙烧温度等对催化活性的影响。并以水热改性和未经水热改性氢氧化锆制备SO42-/ZrO2固体超强酸做了对比实验,采用XRD、BET对催化剂进行了表征。实验结果表明:水热改性氢氧化锆制备SO42-/ZrO2固体酸催化剂的最佳条件是:浸渍硫酸浓度为0.5mol/L,浸渍时间是120 m in,焙烧温度500℃。乙酸正丁酯较佳的合成工艺条件是:反应温度105~110℃,反应时间2 h,n(正丁醇)∶n(冰乙酸)=2∶1,催化剂用量占反应投料总质量的0.27%,冰乙酸的酯化率达99.1%。催化剂重复使用4次后催化活性降低5%。展开更多
The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1...The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1% of catalyst with the molar ration of xylol to styrene being 7.5:1,at temperature of 140℃ for 3 h;The yield of diphenylethylane under such conditions was about 97.5%.展开更多
文摘通过水热改性氢氧化锆制备了SO42-/ZrO2固体酸催化剂。以冰乙酸和正丁醇的酯化反应为探针反应,确定了固体超强酸的最佳制备条件。分别考察了浸渍硫酸浓度、硫酸浸渍时间和焙烧温度等对催化活性的影响。并以水热改性和未经水热改性氢氧化锆制备SO42-/ZrO2固体超强酸做了对比实验,采用XRD、BET对催化剂进行了表征。实验结果表明:水热改性氢氧化锆制备SO42-/ZrO2固体酸催化剂的最佳条件是:浸渍硫酸浓度为0.5mol/L,浸渍时间是120 m in,焙烧温度500℃。乙酸正丁酯较佳的合成工艺条件是:反应温度105~110℃,反应时间2 h,n(正丁醇)∶n(冰乙酸)=2∶1,催化剂用量占反应投料总质量的0.27%,冰乙酸的酯化率达99.1%。催化剂重复使用4次后催化活性降低5%。
文摘The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1% of catalyst with the molar ration of xylol to styrene being 7.5:1,at temperature of 140℃ for 3 h;The yield of diphenylethylane under such conditions was about 97.5%.