Structure,magnetic properties and ductile of melt-spun Fe_(83-x)Si_(4)B_(13-y)C_(y)Cu_(x)(x=0-1.7;y=0-8)alloys were investigated.The addition of 1.7 at.%Cu in a Fe_(83)Si_(4)B_(13) amorphous alloy generates abundantα...Structure,magnetic properties and ductile of melt-spun Fe_(83-x)Si_(4)B_(13-y)C_(y)Cu_(x)(x=0-1.7;y=0-8)alloys were investigated.The addition of 1.7 at.%Cu in a Fe_(83)Si_(4)B_(13) amorphous alloy generates abundantα-Fe crystals by providing nucleation sites,and further C doping promotes the growth of the crystals by suitable turning amorphous-forming ability,hence they increase saturation magnetic flux density(B_(s))and slightly worse magnetic softness of the as-spun alloys.The as-spun Fe_(81.3)Si_(4)B_(7)C_(6)Cu_(1.7) alloy possesses a combined structure of a fully amorphous layer in wheel side surface and predominating nanocrystalline structure with gradually enlargedα-Fe crystal,whose average size and volume fraction are determined as about 12 nm and 32%,respectively,therefore superior soft magnetic properties and ductile with a high B_(s)of 1.74 T,coercivity(H_(c))of 32.7 A/m,effective permeability(μ_(e),at 1 kHz)of 3200 and high relatively strain at fracture(ε_(f))of 3.61%can be achieved directly in this alloy by only using melt-spinning.The annealing at 578 K releases internal stress,promotes the growth of theα-Fe crystals and remains the amorphous layer of the Fe_(81.3)Si_(4)B_(7)C_(6)Cu_(1.7) alloy,then improves the soft magnetic properties and maintains the superior ductile with increasing the B_(s)andμ_(e)to 1.80 T and 14,100,respectively,lowering the H_(c)to9.4 A/m and slightly reducing theε_(f)to 2.39%.The combination of superior soft magnetic properties and ductile and simplified synthesis process entitles the Fe-Si-B-C-Cu nanocrystalline alloys great potentials in high performance electromagnetic applications.展开更多
基金financially supported by the National Key Research and Development Program of China(No.2016YFB0300500)the Youth Innovation Promotion Association CAS(No.2021294)+1 种基金the National Natural Science Foundation of China(No.51571047)Ningbo Major Special Projects of the Plan"Science and Technology Innovation 2025"(No.2018B10084)。
文摘Structure,magnetic properties and ductile of melt-spun Fe_(83-x)Si_(4)B_(13-y)C_(y)Cu_(x)(x=0-1.7;y=0-8)alloys were investigated.The addition of 1.7 at.%Cu in a Fe_(83)Si_(4)B_(13) amorphous alloy generates abundantα-Fe crystals by providing nucleation sites,and further C doping promotes the growth of the crystals by suitable turning amorphous-forming ability,hence they increase saturation magnetic flux density(B_(s))and slightly worse magnetic softness of the as-spun alloys.The as-spun Fe_(81.3)Si_(4)B_(7)C_(6)Cu_(1.7) alloy possesses a combined structure of a fully amorphous layer in wheel side surface and predominating nanocrystalline structure with gradually enlargedα-Fe crystal,whose average size and volume fraction are determined as about 12 nm and 32%,respectively,therefore superior soft magnetic properties and ductile with a high B_(s)of 1.74 T,coercivity(H_(c))of 32.7 A/m,effective permeability(μ_(e),at 1 kHz)of 3200 and high relatively strain at fracture(ε_(f))of 3.61%can be achieved directly in this alloy by only using melt-spinning.The annealing at 578 K releases internal stress,promotes the growth of theα-Fe crystals and remains the amorphous layer of the Fe_(81.3)Si_(4)B_(7)C_(6)Cu_(1.7) alloy,then improves the soft magnetic properties and maintains the superior ductile with increasing the B_(s)andμ_(e)to 1.80 T and 14,100,respectively,lowering the H_(c)to9.4 A/m and slightly reducing theε_(f)to 2.39%.The combination of superior soft magnetic properties and ductile and simplified synthesis process entitles the Fe-Si-B-C-Cu nanocrystalline alloys great potentials in high performance electromagnetic applications.