Mechanical properties and microstructural evolution of rheocast A356 semi-solid slurry prepared by annular electromagnetic stirring

Nowadays,having an effective technique in preparing semi-solid slurries for rheocasting process seems to be an essential requirement.In this study,semi-solid slurry of A356 aluminum alloy was prepared by three-phase annular electromagnetic stirring(A-EMS)technique under different conditions.The effects of stirring current,pouring temperature and stirring time on microstructural evolution,mean particle size,shape factor and solid fraction were investigated.The rheocasting process was carried out by using a drop weight setup and to inject the prepared semi-solid slurry in optimal conditions into the step-die cavity.The filling behavior and mechanical properties of parts were studied.Microstructural evolution showed that the best semi-solid slurry which had fine spherical particles with the average size of~27μm and a shape factor of~0.8 was achieved at the stirring current of 70 A,melt pouring temperature of 670℃,and stirring time of 30 s.Under these conditions,the step-die cavity was completely filled at die preheating temperature of 470℃.The hardness increases by decreasing step thickness as well as die preheating temperature.Moreover,the tensile properties are improved at lower die preheating temperatures.The fracture surface,which consists of a complex topography,indicates a typical ductile fracture.

Degassing effect of ultrasonic vibration in molten melt and semi-solid slurry of Al-Si alloys

In the process of semi-solid slurry preparation with direct ultrasonic vibration (UV) by dipping the horn into the melt, one of the questions is whether the gas content in the melt would be increased or not by the cavitation effect of ultrasonic vibration. By application of quantitative gas content measurement technique, this paper investigated the effect of the ultrasonic vibration on the gas content of both the melt and the semi-solid slurry of Al-Si alloys, and the variations of the gas contents in two kinds of aluminum alloys, i.e., A356 alloy and Al-20Si-2Cu-1Ni-0.6RE alloy (Al-20Si for short). The results show that ultrasonic vibration has an obvious degassing effect on the molten melt, especially on the semi-solid slurry of Al-Si alloy which is below the liquidus temperature by less than 20 ℃. The ultrasonic degassing efficiency of the A356 alloy decreases with the reduction of the initial gas content in the melt, and it is nearly unchanged for the Al-20Si alloy. The gas content of both alloys decreases when the ultrasonic vibration time is increased. The best vibration time for Al-20Si alloy at the liquid temperature of 710 ℃ and semi-solid temperature of 680 ℃ is 60 s and 90 s, respectively; and the degassing efficiency is 48% and 35%, respectively. The mechanism of ultrasonic degassing effect is discussed.

Effects of solution treatment and aging process on microstructure refining of semi-solid slurry of wrought aluminum alloy 7A09

A new method was exploited using solution treatment and aging process as a pretreatment in preparing semi-solid slurry with fine microstructure before isothermal treatment of wrought aluminum alloy 7A09.Parameters of pretreatment were optimized by orthogonal experiment design and proper precursor was prepared.The evolution of microstructure of semi-solid slurry during isothermal treatment was analyzed and the mechanism of microstructure refining was discussed.The result of orthogonal experiment design shows that the optimum parameters are 462 ℃for solution temperature,40min for solution time,132 ℃for aging temperature and 14 h for aging time.Microstructure of isothermal treatment is fine,homogenous,with globular solid grains and a solid fraction between 50%and 70%,which is qualified for later semi-solid forming process.Mechanism of microstructure evolution includes the agglomeration ofα-phase and Ostwald ripening.Precipitations prepared by solution and aging treatment prevent the grains from coarsening and promote the grain ripening to globular shape.

Performance of Semi-solid Slurry Produced by Twin-screw Stirring Mixer and Rheo-diecasting Process of AZ91D Alloy

The microstructure of semi-solid slurry of AZ91D alloy, which was produced by twin-screw stirring mixer under the different parameters, was investigated.Rheoforming by cold chamber die casting process was performed thereafter. The results indicate that with decreasing of the barrel temperature of the mixer and the pouring temperature of molten Mg alloy, the solid fraction of semi-solid slurry increases and the size of non-dendritic grains becomes smaller. While the shear rate increases, the solid fraction of semi-solid slurry decreases. The tensile strength and elongation of metal rheoformed by die casting are higher by about 37% and 44% respectively than those produced by conventional liquid die casting.

COMPUTER SIMULATION OF CONTINUOUS ELECTROMAGNETIC STIRRING FOR MAKING RHEOLOGIC SEMI-SOLID SLURRY OF ZL112Y ALUMINUM ALLOY

To realize the technology of fabricating the rheologic semi-solid slurry of ZL112Y aluminum alloy via continues electromagnetic stirring process, ANSYS software was used to simulate electromagnetic force field and fluid velocity field in the alloy melt in a crucible tube in three coils. In the first section of the paper, eletromagnetic force field and fluid velocity field caused by single coil were simulated. The result of this simulation gives an average velocity of 3.2 cm/s and it is called critical velocity because a fluid velocity over it will cause a fine and spherical structure of solid primary a in a semi-solid melt. And, from this result, a reasonable temperature of semi-solid of the alloy and an electrical current intensity were established. The electrical current intensity of the result of this simulation corresponded to the current intensity used in a practice experiment, in which the primary α was obviously refined and sphericized. Based on this simulation of single coil electromagnetic stirring, in the second section of the paper, eletromagnetic force field and fluid velocity field caused by three coils were simulated. The result of the simulation shows that, 1） there is a semi-solid zone of 32 mm from bottom of the crucible tube to the upper; 2） the electrical current intensities of three coils of 400 A, 600 A, and 400 A, which were set to top range, middle range and bottom range of the tube, respectively, were the optimum parameters of electromagnetic current intensity under the condition of this investigation; and 3） under effect of these electromagnetic current intensity, the fluid velocities of the melt in the tube were 6.3 cm/s in top range, 3.75 cm/s in middle range, and 3.9 cm/s in bottom range of it, respectively.

Effects of annular electromagnetic stirring processing parameters on semi-solid slurry production

A computational model coupling an electromagnetic model with a macroscopic heat and fluid flow model in semi-solid aluminum alloy slurry preparation by annular electromagnetic stirring(A-EMS) was developed.Effects of A-EMS processing parameters,such as stirring current,stirring frequency and stirring gap width,on macroscopic transport phenomena during the solidification were analyzed by commercial software ANSYS 10.0 with corresponding experimental verification.The results show that the magnetic flux density and the melt velocity increase and the temperature difference decreases as stirring gap width and stirring frequency decrease or the stirring current increases.The slurry with the fine and uniform globular grain structure can be gained by adjusting gap width,electromagnetic frequency and current,such as under the conditions of 10 mm of gap width,10 Hz of electromagnetic frequency and 50 A of current.The calculated results are in reasonably good agreement with the measured ones.

Effects of primary phase morphology on mechanical properties of Al-Si-Mg-Fe alloy in semi-solid slurry casting process

The gas induced semi-solid(GISS) process was developed to create semi-solid slurry with fine and uniform globular structure.The combination of local rapid heat extraction and vigorous agitation by the injection of fine inert gas bubbles through a graphite diffuser in molten metal held at a temperature above its liquidus temperature changes the morphology of primary α(Al) from coarse dendritic to rosette-like and finally to fine globular.The GISS process produced semi-solid slurry at low solid fractions and then formed the slurry by a squeeze casting process to produce casting parts.The effects of primary phase morphology on the mechanical properties of Al-Si-Mg-Fe alloy were investigated.The results show that the ultimate tensile strength and elongation are affected by the shape factor and particle size of the primary α(Al).

Preparation of semi-solid slurry at power frequency by annulus electromagnetic stirring method

The effect of stirring frequency on the semi-solid A357 aluminum alloy microstructure was investigated by annulus electromagnetic stirring(AEMS) method. The microstructures obtained by AEMS method and ordinary electromagnetic stirring(EMS)method were compared and analyzed. The results show that the primary α(Al) particles become more spherical and fine, and disperse uniformly in a liquid matrix with increasing stirring frequency, and higher stirring frequency is advantageous to obtain the fine spherical semi-solid microstructure by AEMS. Compared with the microstructures obtained at stirring frequency of 50 Hz in EMS, the fine spherical and uniformly distributed semi-solid microstructures can be still obtained at stirring frequency of 50 Hz in AEMS, so stirring frequency of 50 Hz is recommended in AEMS to save investment cost on frequency-conversion facilities.

Research on semi-solid slurry of a hypoeutectic Al-Si alloy prepared by low superheat pouring and weak electromagnetic stirring

The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were investigated. The results indicated that the semi-solid slurry to satisfy rheocasting can be manufactured by low superheat pouring and weak electromagnetic stirring. The pouring temperature （or superheat） and the stirring power remarkably affected the morphology of primary α-Al and the size of primary α-Al, and there is no obvious effect of stirring time on primary α-Al. Compared with the samples made by low superheat pouring with no stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 were markedly improved by low superheat pouring and weak electromagnetic stirring. On the condition of weak electromagnetic stirring, the pouring temperature with low superheat can be suitably raised to reach the effectiveness obtained from the lower pouring temperature without stirring.

Manufacture technique of semi-solid slurry of hypoeutectic Al-Si alloy by low superheat pouring and weak electromagnetic stirring

The semi-solid slurry of hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature and stirring power on the semi-solid slurry making process were investigated. The results indicate that the semi-solid slurry to satisfy rheocasting requirement can be made by a combination of low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power significantly affect the morphology and the size of primary α-Al, while there is no obvious effect of the stirring time on primary α-Al. Compared with the samples made by low superheat pouring without stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 Al alloy are markedly improved by a process of applying both low superheat pouring and weak electromagnetic stirring. Under the condition of weak electromagnetic stirring applied, the pouring temperature with low superheat can be equivalently to reach the effectiveness obtained from the even lower pouring temperature without stirring.

Semi-solid slurry preparation and rolling of 1Cr18Ni9Ti stainless steel

The preparation and rolling of the semi-solid slurry 1Cr18Ni9Ti stainlesssteel were researched. The experimental results show that when stirred for 2-3 min under the giventest condition, the semi-solid slurry with about 50 percent-60 percent (volume fraction) solid andthe spherical primary austenitic grains in the size of 100-200 mu m can be obtained, and it is easyto be discharged from the bottom little hole of the stirring chamber. The semi-solid slurry of1Cr18Ni9Ti stainless steel can be rolled into the given plate successfully. However, the solid phaseand liquid phase are easily separated in the rolling process, so that the solid primary austeniticgrains are concentrated in the center and the liquid phase is near the edge of the rolled plate. Thestrengths of the plate rolled in the semi-solid state are higher than that of the traditionallyrepeated hot-rolled plate of 1Cr18Ni9Ti stainless steel.

Semi-solid slurry of AZ91 magnesium alloy prepared by electromagnetic stirring near liquidus temperature

An electromagnetic stirring process near liquidus temperature was designed and demonstrated experimentally to produce semi-solid slurry of AZ91 magnesium alloy,in order to avoid not only contamination from mechanical stirring but also the inflammation of Mg alloy melt at elevated temperature. AZ91 alloy feedstock was isothermally heat treated at 600-610 for 20 min,and then stirred by electromagnetic field. Globular primary particle characteristic was observed optically in the castings. Mechanical properties were also studied.

Effect of pouring temperature on semi-solid slurry of A356 Al alloy prepared by weak electromagnetic stirring

The semi-solid slurry of A356 Al alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature on the slurry manufactured by weak electromagnetic stirring were researched. The results indicate that it is feasible to manufacture the slurry with particle-like primary phases by low superheat pouring and weak electromagnetic stirring, and there is an important effect of the pouring temperature (superheat temperature) on the morphology and the size of primaryα-Al in A356 Al alloy. By the action of suitable weak electromagnetic stirring, increasing pouring temperature to put low superheat pouring in practice is capable of obtaining semi-solid slurry of A356 Al alloy with particle-like primary phase. Compared with the samples made only by low superheat pouring without stirring, raising pouring temperature by 15-35 ℃ above the liquidus temperature under condition of weak electromagnetic stirring can ensure the same grain size and morphology of the primary phase.

Effect of pouring temperature on semi-solid slurry of ZL101 alloy prepared by slightly electromagnetic stirring

The semi-solid slurry of ZL101 alloy is prepared by a combination technology of low superheat pouring and slightly electromagnetic stirring.The effects of pouring temperature on the slurry prepared by the technology are investigated.The results indicate that it is feasible to prepare the slurry with globular primary phases by low superheat pouring and slightly electromagnetic stirring,and that the pouring temperature has an important effect on the morphology and the size of primaryα-Al in ZL101 alloy.By applying suitable slightly electromagnetic stirring combining with relatively increased pouring temperature,i.e.,in a practical way to apply low superheat pouring technology,is capable of obtaining appropriate semi-solid slurry of ZL101 alloy with globular shape of primary phase.Compared with the samples made by low superheat pouring only without stirring,the samples prepared by applying both slightly electromagnetic stirring and low superheat pouring can enable to achieve the same grain size and morphology of the primary phase with that of pouring at 15-35℃higher.

Microstructure evolution of Al-Si semi-solid slurry by gas bubble stirring method

A novel technique of introducing gas bubble stirring during solidification was studied to prepare Al-Si semi-solid slurry. The microstructure evolution of the slurry during slow cooling process after stirring was investigated. The effects of the solidification rate on the microstructure of the semi-solid slurry were investigated under three different solidification conditions. The results show that fine non-dendritic slurry can be obtained using the gas bubble stirring method. Ripening and coarsening of primary Al grains are observed during the slow cooling process, and at last coarsened eutectic Si appears. Primary Al grains with different sizes and eutectic Si are obtained, corresponding to three different solidification rates.

Taper barrel rheomoulding process for semi-solid slurry preparation and microstructure evolution of A356 aluminum alloy

The self-developed taper barrel rheomoulding (TBR) machine for light alloy semi-solid slurry preparation was introduced.The semi-solid slurry was obtained from the intense shearing turbulence of the alloy melt in the cause of solidification, which was further caused by the relative rotation of the internal and external taper barrel whose surface contained wale and groove.The heat transmission model of TBR process, the flow rules and the shearing model of the alloy melt were deduced.Taking A365 as experimental material, the microstructure evolution rules under different slurry preparation processes were analyzed.The results show that decreasing the pouring temperature of A365 alloy melt properly or increasing the shearing rate helps to obtain ideal semi-solid microstructure with the primary particle size of about 70 μm and the shape factor of above 0.8.

Research on casing deformation prevention technology based on cementing slurry system optimization

The casing deformation prevention technology based on the optimization of cement slurry is proposed to reduce the casing deformation of shale oil and gas wells during hydraulic fracturing. In this paper, the fracture mechanism of hollow particles in cement sheath was firstly analyzed by discrete element method, and the effect of hollow particles in cement on casing deformation was investigated by laboratory experiment method. Finally, field test was carried out to verify the improvement effect of the casing deformation based on cement slurry modification. The results show that the formation displacement can be absorbed effectively by hollow particles inside the cement transferring the excessive deformation away from casing. The particles in the uncemented state provide deformation space during formation slipping. The casing with diameter of 139.7 mm could be passed through by bridge plug with the diameter of 99 mm when the mass ratio of particle/cement reaches 1:4. According to the field test feedback, the method based on optimization of cement slurry can effectively reduce the risk of casing deformation, and the recommended range of hollow microbeads content in the cement slurry is between 15% and 25%.

To improve robustness of mechanical properties of semi-solid cast A356 alloy using taguchi design method

Mechanical properties of semi-solid casting are dependent on multiple processing parameters,and improper processing parameters will not only reduce mean data but also increase variations.The present study investigated the impact of parameters in slurry preparation and heat treatment on the yield strength and ductility of T6 heat-treated A356 Al-Si alloy using rapid slurry forming(RSF)semi-solid casting.The focus was primarily on the robustness of mechanical properties based on Taguchi design method.By analyzing signal-to-noise ratio and minimum value calculated from-3S,the optimum slurry preparation parameters and heat treatment parameters were determined to be no quench,enthalpy exchange material(EEM)temperature of 140℃,EEM-to-melt ratio of 6mass%,stirring time of 18 s,solution heat treated at 520℃ for 2 h,and ageing heat treated at 190℃ for 6 h.In a small batch validation,the-3S yield strength and-3S elongation reach 256.1 MPa and 5.03% respectively,showing a satisfactory robustness.The hardness and microstructure of heat-treated samples with the best and worst properties were characterized to gain insight into the underlying mechanisms affecting the mean value and variations of mechanical properties.

Preparation and Electrochemical Performance Study of Catalytic Cracking Oil Slurry-based Porous Carbon Materials

Catalytic cracking oil slurry is a by-product of catalytic cracking projects,and the efficient conversion and sustainable utilization of this material are issues of continuous concern in the petroleum refining industry.In this study,oxygen-enriched activated carbon is prepared using a one-step KOH activation method with catalytic cracking oil slurry as the raw material.The as-prepared oil slurry-based activated carbon exhibits a high specific surface area of 2102 m^(2)/g,welldefined micropores with an average diameter of 2 nm,and a rich oxygen doping content of 32.97%.The electrochemical performance of the nitrogen-doped porous carbon is tested in a three-electrode system using a 6 mol/L KOH solution as the electrolyte.It achieves a specific capacitance of up to 230 F/g at a current density of 1 A/g.Moreover,the capacitance retention rate exceeds 89%after 10000 charge and discharge cycles,demonstrating excellent cycle stability.This method not only improves the utilization efficiency of industrial fuel waste but also reduces the production cost of supercapacitor electrode materials,thereby providing a simple and effective strategy for the resource utilization of catalytic cracking oil slurries.

Enhanced recovery of high-purity Fe powder from iron-rich electrolytic manganese residue by slurry electrolysis

Iron-rich electrolytic manganese residue(IREMR)is an industrial waste produced during the processing of electrolytic metal manganese,and it contains certain amounts of Fe and Mn resources and other heavy metals.In this study,the slurry electrolysis technique was used to recover high-purity Fe powder from IREMR.The effects of IREMR and H2SO4 mass ratio,current density,reaction temper-ature,and electrolytic time on the leaching and current efficiencies of Fe were studied.According to the results,high-purity Fe powder can be recovered from the cathode plate,and the slurry electrolyte can be recycled.The leaching efficiency,current efficiency,and purity of Fe reached 92.58%,80.65%,and 98.72wt%,respectively,at a 1:2.5 mass ratio of H2SO4 and IREMR,reaction temperature of 60℃,electric current density of 30 mA/cm^(2),and reaction time of 8 h.In addition,vibrating sample magnetometer(VSM)analysis showed that the coercivity of electrolytic iron powder was 54.5 A/m,which reached the advanced magnetic grade of electrical pure-iron powder(DT4A coercivity standard).The slurry electrolytic method provides fundamental support for the industrial application of Fe resource recovery in IRMER.