TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure ti...TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.展开更多
Studies on texture and microstructure evolution in hot extruded Al 6061 aluminium alloy reinforced with uncoated and nickel coated SiC p were carried out by electron backscattered diffraction technique.Textures of bot...Studies on texture and microstructure evolution in hot extruded Al 6061 aluminium alloy reinforced with uncoated and nickel coated SiC p were carried out by electron backscattered diffraction technique.Textures of both the alloy and its composite with nickel coated SiC p do exhibit strong β fiber with its axis parallel to the direction of extrusion.In addition to the dominant cube texture(001) 100,fully recrystallized grains with partially equiaxed structure have been observed in the alloy reinforced with uncoated SiC p.The recrystallization texture of this composite can be attributed to the particle stimulated nucleation(PSN) due to the presence of SiC p with size less than 5 μm.Under these conditions,the low value of Zener-Hollomon,Z(~1012s-1) confirms that PSN is one of the dominant mechanisms for recrystallization and is governed by formation of deformation zone rather than stored energy.展开更多
Corrosion inhibition characteristics of bio polymer dextran was studied for the corrosion control of 6061 Al-15%_((v)) SiC_((P)) composite and its base alloy in 1 mol·L^(-1) HCl. Standard electrochemical techniqu...Corrosion inhibition characteristics of bio polymer dextran was studied for the corrosion control of 6061 Al-15%_((v)) SiC_((P)) composite and its base alloy in 1 mol·L^(-1) HCl. Standard electrochemical techniques such as potentiodynamic polarization(PDP) measurements and electrochemical impedance spectroscopy(EIS) method were adopted for corrosion rate measurement. Surface morphology was studied by scanning electron microscopy(SEM) and elemental mapping was done by energy dispersive X-ray(EDX) analysis. Suitable mechanism was proposed for corrosion and inhibition process. Results indicated that dextran acts as an excellent anticorrosive agent for the corrosion control of 6061 Al-15%_((v)) SiC_((P)) composite, with maximum inhibition efficiency of 91% for the concentration of 0.4 g·L^(-1) at 303 K. Dextran acted as a mixed type of inhibitor, and got physically adsorbed both on composite and base alloy by obeying Langmuir adsorption isotherm. Dextran is proved to be a green inhibitor with environmental and economic benefits.展开更多
The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning elect...The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning electron microscope. X ray diffraction analysis revealed that the coatings are amorphous structure. The results of X ray photoelectron spectroscopy indicated that the mixed REM conversion coatings consist predominantly of Ce and O, the contents of other rare earth elements (such as La, Pr) are relatively low, the coatings are about 2~4 μm thickness with excellent adhesion and wearability. The results of mass loss test showed that the mixed REM conversion coatings produce corrosion resistant surface of 2024 alloy and Al6061/SiC p. [展开更多
The creep properties of as-cast Mg-9Al-1Si alloy and Mg-9Al-1Si-1SiC composite were compared.The results show that Mg-9A1-lSi-lSiC composite performs a better creep resistance than that of Mg-9Al-1Si alloy at constant...The creep properties of as-cast Mg-9Al-1Si alloy and Mg-9Al-1Si-1SiC composite were compared.The results show that Mg-9A1-lSi-lSiC composite performs a better creep resistance than that of Mg-9Al-1Si alloy at constant temperature and stress(473 K,70MPa).Besides,the creep behavior of Mg-9Al-1 Si-1SiC composite at various temperature from 448 K to 498 K and under stresses of 70-90 MPa were systematically investigated.The Mg-9Al-1 Si-1SiC composite exhibited a stress exponent from 5.5 to 6.9 and the creep activation energy fell within the range of 86-111 kJ/mol.The results showed that the creep mechanism of Mg-9Al-1Si-1SiC composite was mainly attributed to the effects of secondary phase strengthening mechanism and dislocation climb mechanism.展开更多
The effects of interface shape on stress wave distribution and attenuation were investiga- ted using finite element method ( FEM ). The simulation results indicate that when the stress wave propagates from SiC ceram...The effects of interface shape on stress wave distribution and attenuation were investiga- ted using finite element method ( FEM ). The simulation results indicate that when the stress wave propagates from SiC ceramic to A1 alloy, the tensile stress decreases and the attenuation coefficient of the stress wave increases with increasing central angle of the concave interface between SiC and A1. But for the convex interface, the tensile stress increases and attenuation coefficient decreases with increasing central angle. As the stress wave propagates from A1 alloy to SiC ceramic, the atten- uation coefficient of stress wave decreases with increasing the central angle of the concave interface. For the convex interface, the attenuation coefficient increases with increasing central angle.展开更多
基金supports from the National Natural Science Foundation of China(Nos.52075472,52004242)the National Key Research and Development Program of China(No.2018YFA0707300)the Natural Science Foundation of Hebei Province,China(No.E2020203001)。
文摘TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.
基金granting financial assistance to carry out this work which is a part of research project No.SR/S3/ME/019/2004-SERC
文摘Studies on texture and microstructure evolution in hot extruded Al 6061 aluminium alloy reinforced with uncoated and nickel coated SiC p were carried out by electron backscattered diffraction technique.Textures of both the alloy and its composite with nickel coated SiC p do exhibit strong β fiber with its axis parallel to the direction of extrusion.In addition to the dominant cube texture(001) 100,fully recrystallized grains with partially equiaxed structure have been observed in the alloy reinforced with uncoated SiC p.The recrystallization texture of this composite can be attributed to the particle stimulated nucleation(PSN) due to the presence of SiC p with size less than 5 μm.Under these conditions,the low value of Zener-Hollomon,Z(~1012s-1) confirms that PSN is one of the dominant mechanisms for recrystallization and is governed by formation of deformation zone rather than stored energy.
文摘Corrosion inhibition characteristics of bio polymer dextran was studied for the corrosion control of 6061 Al-15%_((v)) SiC_((P)) composite and its base alloy in 1 mol·L^(-1) HCl. Standard electrochemical techniques such as potentiodynamic polarization(PDP) measurements and electrochemical impedance spectroscopy(EIS) method were adopted for corrosion rate measurement. Surface morphology was studied by scanning electron microscopy(SEM) and elemental mapping was done by energy dispersive X-ray(EDX) analysis. Suitable mechanism was proposed for corrosion and inhibition process. Results indicated that dextran acts as an excellent anticorrosive agent for the corrosion control of 6061 Al-15%_((v)) SiC_((P)) composite, with maximum inhibition efficiency of 91% for the concentration of 0.4 g·L^(-1) at 303 K. Dextran acted as a mixed type of inhibitor, and got physically adsorbed both on composite and base alloy by obeying Langmuir adsorption isotherm. Dextran is proved to be a green inhibitor with environmental and economic benefits.
文摘The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning electron microscope. X ray diffraction analysis revealed that the coatings are amorphous structure. The results of X ray photoelectron spectroscopy indicated that the mixed REM conversion coatings consist predominantly of Ce and O, the contents of other rare earth elements (such as La, Pr) are relatively low, the coatings are about 2~4 μm thickness with excellent adhesion and wearability. The results of mass loss test showed that the mixed REM conversion coatings produce corrosion resistant surface of 2024 alloy and Al6061/SiC p. [
基金Shanxi provice scientific facilities and instruments shared service platform of magnesium-based matierals electric impulse aided forming(201805D141005)National Natural Science Foundation of China(51404166,51704209,U1810208)+3 种基金Science and Technology Major Project of Shanxi province(20191102008,20191102007,20181101008)Natural Science Foundation of Shanxi Province(201701D121045)Shanxi Province Science Foundation for Youths(2016021063)The Projects of International Cooperation in Shanxi(201803D421086).
文摘The creep properties of as-cast Mg-9Al-1Si alloy and Mg-9Al-1Si-1SiC composite were compared.The results show that Mg-9A1-lSi-lSiC composite performs a better creep resistance than that of Mg-9Al-1Si alloy at constant temperature and stress(473 K,70MPa).Besides,the creep behavior of Mg-9Al-1 Si-1SiC composite at various temperature from 448 K to 498 K and under stresses of 70-90 MPa were systematically investigated.The Mg-9Al-1 Si-1SiC composite exhibited a stress exponent from 5.5 to 6.9 and the creep activation energy fell within the range of 86-111 kJ/mol.The results showed that the creep mechanism of Mg-9Al-1Si-1SiC composite was mainly attributed to the effects of secondary phase strengthening mechanism and dislocation climb mechanism.
基金Supported by the National Basic Research Program of China("973" Program)(613135)
文摘The effects of interface shape on stress wave distribution and attenuation were investiga- ted using finite element method ( FEM ). The simulation results indicate that when the stress wave propagates from SiC ceramic to A1 alloy, the tensile stress decreases and the attenuation coefficient of the stress wave increases with increasing central angle of the concave interface between SiC and A1. But for the convex interface, the tensile stress increases and attenuation coefficient decreases with increasing central angle. As the stress wave propagates from A1 alloy to SiC ceramic, the atten- uation coefficient of stress wave decreases with increasing the central angle of the concave interface. For the convex interface, the attenuation coefficient increases with increasing central angle.
基金National Natural Science Foundation of China(51665012)Jiangxi Province Science Foundation for Outstanding Scholarship(20171BCB23061,2018ACB21020)Primary Research&Development Plan of Jiangxi Province(2019BBEL50019)。