Cu^2＋-doped nanostructured TiO2-coated SiO2 （TiO2/SiO2） particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized by the sol-gel ...Cu^2＋-doped nanostructured TiO2-coated SiO2 （TiO2/SiO2） particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized by the sol-gel method using TiOSO4 as a precursor. The experimental results showed that TiO2 nanopowders on the surface of SiO2 particles were well distributed and compact. The amount of TiO2 increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550℃. The 2-layer coated TiO2 particles on the surface showed a higher degradation rate compared with all the different-layer samples. The photocatalytic activity of Cu^2＋-doped TiO2/SiO2 was higher than that ofundoped TiO2/SiO2. The optimum dopant content was about 0.10wt%.展开更多
The study of nanocrystalline SnO2 (n-SnO2) and SiO2-doped SnO2 (n-Si-SnO2) samples pre-pared by the sol-gel process showed that SiO2 doping can effectively restrained the growth of nanocrystalline SnO2 grains, thus im...The study of nanocrystalline SnO2 (n-SnO2) and SiO2-doped SnO2 (n-Si-SnO2) samples pre-pared by the sol-gel process showed that SiO2 doping can effectively restrained the growth of nanocrystalline SnO2 grains, thus improving thermal stability of the materials.展开更多
ZnO/SiO\-2 and ZnO\|SiO\-2 catalysts were prepared by the impregnation and sol\|gel method, respectively. The characterization of the catalysts by XPS and FTIR indicated that much "free" zinc oxide and unrea...ZnO/SiO\-2 and ZnO\|SiO\-2 catalysts were prepared by the impregnation and sol\|gel method, respectively. The characterization of the catalysts by XPS and FTIR indicated that much "free" zinc oxide and unreacted Si\_OH existed on the surface of ZnO/SiO\-2 sample. As for ZnO\|SiO\-2 sol\|gel catalyst, the corresponding phenomena were not observed. The prepared samples were also used as the catalysts for decomposition of 2\|butanol. A high selectivity for dehydrogenation was observed over the supported catalyst. However, a high selectivity for dehydration was shown over the ZnO\|SiO\-2 sol\|gel catalyst. The opposite selectivity for dehydration or dehydrogenation observed over the two kinds of catalysts may be just because of the different surface structures of the catalysts.展开更多
Supported loaded semiconductors （MoO3,ZnO）-TiO2/SiO2 were pre pared by an isovolumetric impregnation method from TiO2/SiO2 pre pared by chemical modification reaction. The chemisorption property and photon a bsorpti...Supported loaded semiconductors （MoO3,ZnO）-TiO2/SiO2 were pre pared by an isovolumetric impregnation method from TiO2/SiO2 pre pared by chemical modification reaction. The chemisorption property and photon a bsorption ability of MoO3-TiO2/SiO2 and ZnO-TiO2/SiO 2 were investigated by BET, UV-Vis DRS, IR and TPD-MS techniques. The gas -phase photocatalytic reaction of CH4 with H2O was performed at 150 ℃ in a fixed-bed annular reactor. The results show that the conversion of met hane and the selectivity of methanol reach to 5.1% and 87.3% respectively over MoO3-TiO2/SiO2, and MoO3-TiO2/SiO2 ex hibits higher photocatalytic acivity than ZnO-TiO2/SiO2.展开更多
基金the Department of Education of Hebei Province, China (No.2005362)
文摘Cu^2＋-doped nanostructured TiO2-coated SiO2 （TiO2/SiO2） particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized by the sol-gel method using TiOSO4 as a precursor. The experimental results showed that TiO2 nanopowders on the surface of SiO2 particles were well distributed and compact. The amount of TiO2 increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550℃. The 2-layer coated TiO2 particles on the surface showed a higher degradation rate compared with all the different-layer samples. The photocatalytic activity of Cu^2＋-doped TiO2/SiO2 was higher than that ofundoped TiO2/SiO2. The optimum dopant content was about 0.10wt%.
文摘The study of nanocrystalline SnO2 (n-SnO2) and SiO2-doped SnO2 (n-Si-SnO2) samples pre-pared by the sol-gel process showed that SiO2 doping can effectively restrained the growth of nanocrystalline SnO2 grains, thus improving thermal stability of the materials.
文摘ZnO/SiO\-2 and ZnO\|SiO\-2 catalysts were prepared by the impregnation and sol\|gel method, respectively. The characterization of the catalysts by XPS and FTIR indicated that much "free" zinc oxide and unreacted Si\_OH existed on the surface of ZnO/SiO\-2 sample. As for ZnO\|SiO\-2 sol\|gel catalyst, the corresponding phenomena were not observed. The prepared samples were also used as the catalysts for decomposition of 2\|butanol. A high selectivity for dehydrogenation was observed over the supported catalyst. However, a high selectivity for dehydration was shown over the ZnO\|SiO\-2 sol\|gel catalyst. The opposite selectivity for dehydration or dehydrogenation observed over the two kinds of catalysts may be just because of the different surface structures of the catalysts.
文摘Supported loaded semiconductors （MoO3,ZnO）-TiO2/SiO2 were pre pared by an isovolumetric impregnation method from TiO2/SiO2 pre pared by chemical modification reaction. The chemisorption property and photon a bsorption ability of MoO3-TiO2/SiO2 and ZnO-TiO2/SiO 2 were investigated by BET, UV-Vis DRS, IR and TPD-MS techniques. The gas -phase photocatalytic reaction of CH4 with H2O was performed at 150 ℃ in a fixed-bed annular reactor. The results show that the conversion of met hane and the selectivity of methanol reach to 5.1% and 87.3% respectively over MoO3-TiO2/SiO2, and MoO3-TiO2/SiO2 ex hibits higher photocatalytic acivity than ZnO-TiO2/SiO2.