Finite element method(FEM) was used to simulate the forming process of shotpeening the wing skin panel. Experiment of shotpeeing the wing skin panel was carried out. The results show that equivalent deformation in sho...Finite element method(FEM) was used to simulate the forming process of shotpeening the wing skin panel. Experiment of shotpeeing the wing skin panel was carried out. The results show that equivalent deformation in shotpeening process can be obtained using the elongation and bending result caused by thermal stress that is induced by applying temperature load on the surface of the part. Deformation of the part in the shotpeeing process can be analyzed using this method. The parameters and their relationships are identified.展开更多
We focused on the optimization of corn-stalk skin flake-wood shaving composite technology. We studied the effects of material-mixture ratio, glue content, hot- pressing temperature, and hot-pressing time on the appear...We focused on the optimization of corn-stalk skin flake-wood shaving composite technology. We studied the effects of material-mixture ratio, glue content, hot- pressing temperature, and hot-pressing time on the appear- ance, physical, and mechanical properties of the composite by the orthogonal experiment method. Our findings yielded highly significant results in all three cases： the effects of the material-mixture ratio on 2 h of thickness swelling （2hTS） and the modulus of rupture （MOR）; the effects of glue con- tent on 2hTS, internal bond strength, and modulus of elas- ticity （MOE）; and the effects of hot-pressing temperature on MOR and MOE. Product optimization is achieved when the ratio of corn stalk skin flake to wood shaving is 3：7, the glue content is 12 %, the hot-pressing temperature is 150 ℃, and the hot-pressing time is 4.5 min.展开更多
文摘Finite element method(FEM) was used to simulate the forming process of shotpeening the wing skin panel. Experiment of shotpeeing the wing skin panel was carried out. The results show that equivalent deformation in shotpeening process can be obtained using the elongation and bending result caused by thermal stress that is induced by applying temperature load on the surface of the part. Deformation of the part in the shotpeeing process can be analyzed using this method. The parameters and their relationships are identified.
文摘We focused on the optimization of corn-stalk skin flake-wood shaving composite technology. We studied the effects of material-mixture ratio, glue content, hot- pressing temperature, and hot-pressing time on the appear- ance, physical, and mechanical properties of the composite by the orthogonal experiment method. Our findings yielded highly significant results in all three cases： the effects of the material-mixture ratio on 2 h of thickness swelling （2hTS） and the modulus of rupture （MOR）; the effects of glue con- tent on 2hTS, internal bond strength, and modulus of elas- ticity （MOE）; and the effects of hot-pressing temperature on MOR and MOE. Product optimization is achieved when the ratio of corn stalk skin flake to wood shaving is 3：7, the glue content is 12 %, the hot-pressing temperature is 150 ℃, and the hot-pressing time is 4.5 min.