A novel Mg-Al LDH film was in-situ prepared hydrothermally in an alkaline aqueous solution on an Al-alloyed AZ31 substrate.The structural,chemical and functional characteristics of the film were explored by means of s...A novel Mg-Al LDH film was in-situ prepared hydrothermally in an alkaline aqueous solution on an Al-alloyed AZ31 substrate.The structural,chemical and functional characteristics of the film were explored by means of scanning electron microscope(SEM),X-ray diffraction(XRD),energy dispersive spectrometer(EDS),polarization curve,AC impedance and salt immersion tests,respectively.The anti-corrosion results indicated that the Mg-Al LDH film on the Al-alloyed AZ31 surface could effectively protect the AZ31 from corrosion attack even after 90 days of immersion in 3.5 wt.%NaCl solution.The protection performance is surprisingly better than most of the reported coatings on Mg alloys.More interestingly,when the Mg-Al LDH film was scratched,the exposed Al-alloyed surface might gradually release metal ions and re-generate dense LDH nano-sheets in the corrosive environment to inhibit the further corrosion there,exhibiting a self-repairing behavior.The combination of the benign long-term protection and desirable self-repairing performance in this new process of surface-alloying and LDH-formation may significantly extend the practical application of magnesium alloys.展开更多
It is recently suggested that air-formed film plays an important role in controlling corrosion resistance of Mg-Li alloys. However, the structure of the air-formed film and its effect on corrosion resistance of Mg-Li ...It is recently suggested that air-formed film plays an important role in controlling corrosion resistance of Mg-Li alloys. However, the structure of the air-formed film and its effect on corrosion resistance of Mg-Li alloys has not been fully understood. Firstly, the air-formed films formed on α and β phases in a dual-phase LZ91 Mg-Li alloy after exposure to laboratory air for up to 48 h have been examined by SEM under the assistance of ultramicrotomy. Then, the effect of the air-formed film on surface potential and, consequently, corrosion/oxidation behavior of the alloy has been investigated. Finally, in order to exclude the influence from α phase, the structure of the air-formed film on β phase and its effect on corrosion/oxidation behavior of Mg-Li alloys have been studied based on a single-phase LA141 Mg-Li alloy. The results show that the air-formed film is thin and negligible on α phase but thick on β phase after prolonged exposure to laboratory air. The thick air-formed film on β phase has a multilayer structure with an inner layer consisting of Mg O/Mg(OH)_(2) and outer layer consisting of Li_(2)CO_(3), which greatly elevates the surface potential of β phase in air. Both LZ91 and LA141 Mg-Li alloys firstly undergo uniform corrosion and then filiform corrosion when immersed in Na Cl solution and the pre-existed air-formed film on β-Li phase can retard the occurrence of filiform corrosion in the alloys.展开更多
Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in th...Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in the fields of biomedical electronics. Magnesium and its alloys are strong candidates for biodegradable and implantable conducting materials because of their high conductivity and biocompatibility, in addition to their well-understood dissolution behavior. One critical drawback of Mg and its alloys is their considerably high dissolution rates originating from their low anodic potential, which disturbs the compatibility to biomedical applications. Herein, we introduce a single-phase thin film of a Mg-Zn binary alloy formed by sputtering, which enhances the corrosion resistance of the device electrode, and verify its applicability in biodegradable electronics. The formation of a homogeneous solid solution of single-phase Mg-3Zn was confirmed through X-ray diffraction and transmission electron microscopy. In addition, the dissolution behavior and chemistry was also investigated in various biological fluids by considering the effect of different ion species. Micro-tensile tests showed that the Mg-3Zn alloy electrode exhibited an enhanced yield strain and elongation in relation to a pure Mg electrode. Cell viability test revealed the high biocompatibility rate of the Mg-3Zn binary alloy thin film. Finally, the fabrication of a wireless heater demonstrated the integrability of biodegradable electrodes and highlighted the ability to prolong the lifecycle of thermotherapy-relevant electronics by enhancing the dissolution resistance of the Mg alloy.展开更多
This study employs advanced electrochemical and surface characterization techniques to investigate the impact of electrochemical hydrogen charging on the corrosion behavior and surface film of the Ti-6Al-4V alloy.The ...This study employs advanced electrochemical and surface characterization techniques to investigate the impact of electrochemical hydrogen charging on the corrosion behavior and surface film of the Ti-6Al-4V alloy.The findings revealed the formation ofγ-TiH andδ-TiH_(2) hydrides in the alloy after hydrogen charging.Prolonging hydrogen charging resulted in more significant degradation of the alloy microstructure,leading to deteriorated protectiveness of the surface film.This trend was further confirmed by the electrochemical measurements,which showed that the corrosion resistance of the alloy progressively worsened as the hydrogen charging time was increased.Consequently,this work provides valuable insights into the mechanisms underlying the corrosion of Ti-6Al-4V alloy under hydrogen charging conditions.展开更多
Golden yellow cerium conversion film was obtained on magnesium alloys surface by immersion method and the preparation parameters were established. The influence of different process parameters on the surface morpholog...Golden yellow cerium conversion film was obtained on magnesium alloys surface by immersion method and the preparation parameters were established. The influence of different process parameters on the surface morphology and performance of the conversion film were analyzed by means of SEM and electrochemical method. Formation dynamics about cerium conversion film on magnesium alloy in solution containing cerium salt and the anti-corrosion behavior of the conversion film in 3.5% NaCl solution were studied by electrochemical method respectively. The results shows that the conversion film is more compact at room temperature when concentration of cerium sulfate is 10 g·L-1 in the solution; the open circuit potential of the magnesium sample moves up to positive direction about 100 mV, the surface of conversion film becomes even and lustrous, and the adhesion intensity of conversion film increases when adding aluminum nitrate into the solution containing cerium salt. The pH value of the solution and immersion time of the sample in the solution also affect the surface morphology and anti-corrosion property of the conversion film. After covered by rare earths conversion film, the anti-corrosion property of magnesium alloy is obviously improved. Rare earth conversion film has self-repairing capability in corrosion medium.展开更多
The effect of cerium on ignition temperature of AZ91D magnesium alloy was studie d. By the addition of cerium of 1%, the ignition temperature is raised by 180 ℃ , s o the magnesium alloy added with cerium can be melt...The effect of cerium on ignition temperature of AZ91D magnesium alloy was studie d. By the addition of cerium of 1%, the ignition temperature is raised by 180 ℃ , s o the magnesium alloy added with cerium can be melted in air. The burning temper ature increases with the increasing of cerium. The structure and chemical compos itions of the surface oxide film were investigated by XRD and Auger electron spe ctrometry(AES). The results of XRD indicate that the oxide film of the surface o f ignition-inhibition magnesium alloy can change from loose structure of simple magnesia to compact composite structure consisting of magnesia, cerium oxide, M g17 A112 and aluminum oxide, which has excellent ignition-inhibition effect. AE S depth profile analysis shows that the oxide film can be divided into three lay ers. The outside layer is mainly made up of magnesia, the middle layer, which co nsists of cerium oxide, magnesia, and aluminum oxide, is compound and compact. T hermodynamic analysis indicates that the structure of the surface oxide film is accordant to the change of free energy and high vapor pressure of magnesium.展开更多
The electrochemical behavior of Yb3+ and electrodeposition of Mg-Yb alloy film at solid magnesium cathode in the molten LiCl-KCl-YbCl3(2 wt.%) system at 773 K was investigated.Transient electrochemical techniques,such...The electrochemical behavior of Yb3+ and electrodeposition of Mg-Yb alloy film at solid magnesium cathode in the molten LiCl-KCl-YbCl3(2 wt.%) system at 773 K was investigated.Transient electrochemical techniques,such as cyclic voltammetry,chronopotentiometry and chronoamperometry were used in order to explore the deposition mechanism of Yb.The reduction process of Yb3+ is stepwise reactions which are single-electron and double-electron reversible charge transfer reactions.The speed control step was a diffu...展开更多
Nano cerium oxide films were applied on AA7020-T6 aluminum alloy and the effects of acetic acid concentration on the microstructure and electrochemical properties of the coated samples were investigated by using scann...Nano cerium oxide films were applied on AA7020-T6 aluminum alloy and the effects of acetic acid concentration on the microstructure and electrochemical properties of the coated samples were investigated by using scanning electron microscopy (SEM), X-ray diffraction (XRD), and potentiodynamic polarization methods. It has been found that by increasing the acetic acid/CeCl3·7H2O molar ratio, high uniform and crack-free films with well-developed grains were obtained and grain sizes of the films decreased. Elimination of cracks and decreasing grain size of the nano cerium oxide films caused corrosion resistance to increase.展开更多
Anodic oxide films of the titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate electrolyte without hydrofluoric acid or fluoride were fabricated. The morphology, components, and microstructure of the films were characte...Anodic oxide films of the titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate electrolyte without hydrofluoric acid or fluoride were fabricated. The morphology, components, and microstructure of the films were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and Raman spectroscopy. The results showed that the films were thick, uniform, and nontransparent. Such films exhibited sedimentary morphology, with a thickness of about 3 μm, and the pore diameters of the deposits ranged from several hundred nanometers to 1.5 μm. The films were mainly titanium dioxide. Some coke-like deposits, which may contain or be changed by OH, NH, C-C, C-O, and C=O groups, were doped in the films. The films were mainly amorphous with a small amount of anatase and rutile phase.展开更多
Micro-arc oxidation(MAO)is one of the promising methods to improve the corrosion resistance of magnesium alloys.However,there are plenty of micro-pores in the traditional MAO films,deteriorating their protection prope...Micro-arc oxidation(MAO)is one of the promising methods to improve the corrosion resistance of magnesium alloys.However,there are plenty of micro-pores in the traditional MAO films,deteriorating their protection property.A novel self-sealing pore MAO film was developed in this paper.The morphologies and chemical composition of the film were detected by scanning electron microscopy(SEM)and energy dispersive X-ray spectroscopy(EDX).The corrosion behavior was investigated by electrochemical and salt spray tests.The possible film formation and corrosion mechanisms were proposed.The self-sealing pore film presents a blue appearance.Most of the micro-pores in the surface of the film are sealed during the film formation process.The chemical composition of the film mainly contains Mg,O,Ti,F and P.The self-sealing pore film exhibits better corrosion resistance compared with the traditional silicate film.Especially,the self-sealing pore film keeps intact after salt spray test for 2000 h,which can be attributed to its high compactness.展开更多
To study the mechanism of formation and inhibition of Ce conversion films on Al 2024-T3 alloy, scanning microreference electrode technique (SMRE) is used to probe the potential map on Al 2024-T3 in CeCl 3 solution, t...To study the mechanism of formation and inhibition of Ce conversion films on Al 2024-T3 alloy, scanning microreference electrode technique (SMRE) is used to probe the potential map on Al 2024-T3 in CeCl 3 solution, the localized corrosion of Al alloy decreases with immersion time and disappears finally, which results from the competition of Cl - aggression and Ce 3+ inhibition on alloy surface. The results of X-ray photoelectron spectroscopy (XPS) indicate that the Ce conversion films consist of Al 2O 3, CeO 2 and Ce 2O 3(Ce(OH) 3), and CeO 2/Ce 2O 3 ratio decreases with the immersion time. When a critical pH for Ce(OH) 3 formation was reached, Ce(OH) 3 will precipitate on the micro cathodic area on alloy surface. Consequently, H 2O 2, the product of the catholic reaction will oxidize a part of Ce(OH) 3 to CeO 2, which appears a better corrosion resistance for Al alloys.展开更多
After removing tin coating of tinplates offered by some steel works, we discovered massive, highly disperse gray points outspreading along rolling direction on the surface of the alloy layer. Morphology of the alloy l...After removing tin coating of tinplates offered by some steel works, we discovered massive, highly disperse gray points outspreading along rolling direction on the surface of the alloy layer. Morphology of the alloy layer was observed by scanning electron microscope (SEM), and many cavities of the alloy layer were found out in the gray point. After analyzing the composition of the alloy layer, we found that content of Fe in the gray points was more than that in the normal alloy layer. Moreover, corrosion resistance of the alloy layer declines with increase of amount of gray points. In addition, the hot-humidity testing was carried out for some plates whose surface has many gray points. After 14 days, there were many rust points occurring in the edge of gray points and in the small gray points. The morphology of rust points was observed by atomic force microscope (AFM). The reason why rust points generated in the edge of gray points and in the small gray points was discussed.展开更多
In this paper, diamond-like carbon (DLC) films were deposited on Ti alloy by electro-deposition. DLC films were brown andcomposed of the compact grains whose diameter was about 400 nm. Examined by XPS, the main compos...In this paper, diamond-like carbon (DLC) films were deposited on Ti alloy by electro-deposition. DLC films were brown andcomposed of the compact grains whose diameter was about 400 nm. Examined by XPS, the main composition of the filmswas carbon. In the Raman spectrum, there were a broad peak at 1350 cm^(-1) and a broad peak at 1600 cm^(-1), which indicatedthat the films were DLC films.展开更多
Gd-Co alloy films were synthesized by potentiostatic electrolysis on Cu substrates in urea-acetamide-NaBr-KBr melt at 353 K. The electroreduction of Co^2+ and Gd^3+ was investigated by cyclic voltammetry. The reduct...Gd-Co alloy films were synthesized by potentiostatic electrolysis on Cu substrates in urea-acetamide-NaBr-KBr melt at 353 K. The electroreduction of Co^2+ and Gd^3+ was investigated by cyclic voltammetry. The reduction of Co^2+ is an irreversible process. Gd^3+ cannot be reduced alone, but it can be inductively co-deposited with Co^2+. Both the Gd content and microstructure of the prepared Gd-Co alloy films can be controlled by the deposited potential. The content of Gd was analyzed using an inductively coupled plasma emission spectrometer (ICPES), and the microstructure was observed by scanning electron micrograph (SEM). The films were crystallized by heat-treatment at 823 K for 30 s in Ar atmosphere, and then were investigated by XRD. The hysteresis loops of the Gd-Co alloy films were measured by a vibrating sample magnetometer (VSM). The experimental results reveal that the deposited Gd-Co alloy films are amorphous, while the annealing causes the samples to change from amorphous to polycrystalline, thus enhancing their magnetocrystalline anisotropy and coercivity. Moreover, the magnetic properties of the Gd-Co alloy films depend strongly on the Gd content.展开更多
A Fe-Ni soft magnetic film was prepared in sulphate solution by electroplating. The influences of the molar ratio of n[Fe2+]/n[Ni2+], current density, bath temperature, pH and L-ascorbic acid concentration on magnetic...A Fe-Ni soft magnetic film was prepared in sulphate solution by electroplating. The influences of the molar ratio of n[Fe2+]/n[Ni2+], current density, bath temperature, pH and L-ascorbic acid concentration on magnetic properties of Fe-Ni alloy film were investigated. The results show that the saturated flux density(BS) of the film increases initially and decreases after it reaches the specific value with the increase of n[Fe2+]/n[Ni2+] molar ratio, current density, bath temperature and pH. However, the relationship between L-ascorbic acid concentration and BS keeps linear. It is observed that the coercive force(Hc) is enhanced with the increase of n[Fe2+]/n[Ni2+] molar ratio, current density and pH. By comparison, when the bath temperature increases, Hc always decreases. With the increase of L-ascorbic acid concentration, the coercive force increases initially and then decreases.展开更多
The oxidation kinetics,surface morphology and phase structure of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres at 900 ℃ for 20 h were investigated.The anti-coking performance and resistance to...The oxidation kinetics,surface morphology and phase structure of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres at 900 ℃ for 20 h were investigated.The anti-coking performance and resistance to carburization of the two oxide films were compared using 25Cr20Ni alloy tubes with an inner diameter of 10 mm and a length of 850 mm in a bench scale naphtha steam pyrolysis unit.The oxidation kinetics followed a parabolic law in an air-H2O atmosphere and a logarithm law in a H2-H2O atmosphere in the steady-state stage.The oxide film grown in the air-H2O atmosphere had cracks where the elements Fe and Ni were enriched and the un-cracked area was covered with octahedral-shaped MnCr2O4 spinels and Cr1.3Fe0.7O3 oxide clusters,while the oxide film grown in the H2-H2O atmosphere was intact and completely covered with dense standing blade MnCr2O4 spinels.In the pyrolysis tests,the anti-coking performance and resistance to carburization of the oxide film grown in the H2-H2O atmosphere were far better than that in the air-H2O atmosphere.The mass of coke formed in the oxide film grown in the H2-H2O atmosphere was less than 10% of that in the air-H2O atmosphere.The Cr1.3Fe0.7O3 oxide clusters converted into Cr23C6 carbides and the cracks were filled with carbon in the oxide film grown in the air-H2O atmosphere after repeated coking and decoking tests,while the dense standing blade MnCr2O4 spinels remained unchanged in the oxide film grown in the H2-H2O atmosphere.The ethylene,propylene and butadiene yields in the pyrolysis tests were almost the same for the two oxide films.展开更多
The reduction of Ni(Ⅱ) is an irreversible reaction and La(Ⅲ) cannot be reduced to La directly but be co-deposited inductively in the present of Ni(Ⅱ) in the Acetamide-Urea-NaBr molten salt electrolyte at 353 K. The...The reduction of Ni(Ⅱ) is an irreversible reaction and La(Ⅲ) cannot be reduced to La directly but be co-deposited inductively in the present of Ni(Ⅱ) in the Acetamide-Urea-NaBr molten salt electrolyte at 353 K. The uncrystallized alloy film of La-Ni is obtained by potentiostatic electrolysis, and the amount of La grows with increasing cathodic overpotential, molar ratios of La(Ⅲ) to Ni(Ⅱ) and the electrolysis time. The maximum amount of La in alloy film reaches to 78.81% (mass fraction) in present study.展开更多
Dense, adhesive and uniform Sm-Co alloy films were prepared by potentiostatic electrolysis on copper substrates in urea-acetamide-NaBr-KBr melt at 353 K, which were observed by SEM. The electroreduction of Co2+ and Sm...Dense, adhesive and uniform Sm-Co alloy films were prepared by potentiostatic electrolysis on copper substrates in urea-acetamide-NaBr-KBr melt at 353 K, which were observed by SEM. The electroreduction of Co2+ and Sm3+ was investigated by cyclic voltammetry. The reduction of Co2+ is an irreversible process. Sm3+ can not be reduced alone, but Sm-Co can be co-deposited by induced deposition. The films could be crystallized by heat-treatment at different temperature from 723 to 923 K under Ar atmosphere. The annealed time was chosen as 30 s. The phases of deposited and annealed films were investigated by XRD. The content of Sm was analyzed by Inductive Coupled Plasma Emission Spectrometer (ICPES). The hysteresis loops of the Sm-Co alloy films have been measured by Vibrating Sample Magnetometer (VSM). The experimental results reveal that, the heat-treatment has important influence on coercive field Hc and remanent squareness S of Sm-Co alloy films; the deposited Sm-Co alloy films are amorphous, while the annealed those become polycrystalline; in addition, the magnetocrystalline anisotropy and preferring orientation of films depend strongly on the contents of crystal phases.展开更多
The chemical stripping method of titanium alloy oxide films was studied. An environment friendly solution hydrogen peroxide and sodium hydroxide without hydrofluoric acid or fluoride were used to strip the oxide films...The chemical stripping method of titanium alloy oxide films was studied. An environment friendly solution hydrogen peroxide and sodium hydroxide without hydrofluoric acid or fluoride were used to strip the oxide films. The morphologies of the surface and cross-section of the oxide films before and after the films stripping were characterized by using scanning electron microscopy (SEM). The microstructure and chemical compositions of the oxide films before and after the films stripping were investigated by using Raman spectroscopy (Raman) and X-ray photoelectron spectroscopy (XPS). It was shown that the thickness of the oxide film was in the range of 5-6 μm. The oxide films were stripped for 2 to 8 min in the solution. Moreover, the effect of the stripping time on the efficiency of the film stripping was investigated, and the optimum stripping time was between 6-8 min. When the stripping solution completely dissolved the whole film, the α/β microstructure of the titanium alloy Ti-10V-2Fe-3Al was partly revealed. The stripping mechanism was discussed in terms of the dissolution of film delamination. The hydrogen peroxide had a significant effect on the dissolution of the titanium alloy anodic oxide film. The feasibility of the dissolution reaction also was evaluated.展开更多
The cyclic voltammetry and chronoamperometry were used to investigate the electrochemical behaviors of Er(Ⅲ) and Ni(Ⅱ) in LiClO 4 DMSO(dimethylsufoxide) system on Pt and Cu electrodes. Experimental results indica...The cyclic voltammetry and chronoamperometry were used to investigate the electrochemical behaviors of Er(Ⅲ) and Ni(Ⅱ) in LiClO 4 DMSO(dimethylsufoxide) system on Pt and Cu electrodes. Experimental results indicated that the reduction of Er(Ⅲ) to Er and Ni(Ⅱ) to Ni were irreversible in one step on Pt and Cu electrodes. The diffusion coefficient and electron transfer coefficient of Er(Ⅲ) in 0.01 mol·L -1 ErCl 3 -0.1 mol·L -1 LiClO 4 DMSO system at 303K were 1.47×10 -10 m 2·s -1 and 0.108 respectively, and the diffusion coefficient and electron transfer coefficient of Ni(Ⅱ) in 0.01 mol·L -1 NiCl 2-0.1 mol·L -1 LiClO 4 DMSO system at 303K were 3.38×10 -10 m 2·s -1 and 0.160 respectively. The homogeneous, strong adhesive Er Ni alloy films with metallic lu- stre was prepared by potentiostatic electrolysis on Cu electrode in ErCl 3 NiCl 2 LiClO 4 DMSO system at -1.90~ -2.55 V (vs SCE).展开更多
基金The research is supported by the National Science Foundation of China(key project grant No.51731008 and general project grant No.51671163).
文摘A novel Mg-Al LDH film was in-situ prepared hydrothermally in an alkaline aqueous solution on an Al-alloyed AZ31 substrate.The structural,chemical and functional characteristics of the film were explored by means of scanning electron microscope(SEM),X-ray diffraction(XRD),energy dispersive spectrometer(EDS),polarization curve,AC impedance and salt immersion tests,respectively.The anti-corrosion results indicated that the Mg-Al LDH film on the Al-alloyed AZ31 surface could effectively protect the AZ31 from corrosion attack even after 90 days of immersion in 3.5 wt.%NaCl solution.The protection performance is surprisingly better than most of the reported coatings on Mg alloys.More interestingly,when the Mg-Al LDH film was scratched,the exposed Al-alloyed surface might gradually release metal ions and re-generate dense LDH nano-sheets in the corrosive environment to inhibit the further corrosion there,exhibiting a self-repairing behavior.The combination of the benign long-term protection and desirable self-repairing performance in this new process of surface-alloying and LDH-formation may significantly extend the practical application of magnesium alloys.
基金gratefully acknowledge Chongqing Talent Plan: Leading Talents in Innovation and Entrepreneurship (CQYC201903051)University Innovation Research Group of Chongqing (CXQT20023)Natural Science Foundation of Chongqing (cstc2021ycjh-bgzxm0184)。
文摘It is recently suggested that air-formed film plays an important role in controlling corrosion resistance of Mg-Li alloys. However, the structure of the air-formed film and its effect on corrosion resistance of Mg-Li alloys has not been fully understood. Firstly, the air-formed films formed on α and β phases in a dual-phase LZ91 Mg-Li alloy after exposure to laboratory air for up to 48 h have been examined by SEM under the assistance of ultramicrotomy. Then, the effect of the air-formed film on surface potential and, consequently, corrosion/oxidation behavior of the alloy has been investigated. Finally, in order to exclude the influence from α phase, the structure of the air-formed film on β phase and its effect on corrosion/oxidation behavior of Mg-Li alloys have been studied based on a single-phase LA141 Mg-Li alloy. The results show that the air-formed film is thin and negligible on α phase but thick on β phase after prolonged exposure to laboratory air. The thick air-formed film on β phase has a multilayer structure with an inner layer consisting of Mg O/Mg(OH)_(2) and outer layer consisting of Li_(2)CO_(3), which greatly elevates the surface potential of β phase in air. Both LZ91 and LA141 Mg-Li alloys firstly undergo uniform corrosion and then filiform corrosion when immersed in Na Cl solution and the pre-existed air-formed film on β-Li phase can retard the occurrence of filiform corrosion in the alloys.
基金supported by the Renewable Energy Technology Development (Develop technology to enhance reliability and durability for parts of hydrogen storage tank system) (2022303004020B) grant funded by the Korea Energy Technology Evaluation Planning (KETEP)the Ministry of Science and ICT (Development Project for Emerging Research Instruments Technology),(Project Number: (2022)ERIC)06_1Commercialization Promotion Agency for R&D Outcomes (COMPA)。
文摘Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in the fields of biomedical electronics. Magnesium and its alloys are strong candidates for biodegradable and implantable conducting materials because of their high conductivity and biocompatibility, in addition to their well-understood dissolution behavior. One critical drawback of Mg and its alloys is their considerably high dissolution rates originating from their low anodic potential, which disturbs the compatibility to biomedical applications. Herein, we introduce a single-phase thin film of a Mg-Zn binary alloy formed by sputtering, which enhances the corrosion resistance of the device electrode, and verify its applicability in biodegradable electronics. The formation of a homogeneous solid solution of single-phase Mg-3Zn was confirmed through X-ray diffraction and transmission electron microscopy. In addition, the dissolution behavior and chemistry was also investigated in various biological fluids by considering the effect of different ion species. Micro-tensile tests showed that the Mg-3Zn alloy electrode exhibited an enhanced yield strain and elongation in relation to a pure Mg electrode. Cell viability test revealed the high biocompatibility rate of the Mg-3Zn binary alloy thin film. Finally, the fabrication of a wireless heater demonstrated the integrability of biodegradable electrodes and highlighted the ability to prolong the lifecycle of thermotherapy-relevant electronics by enhancing the dissolution resistance of the Mg alloy.
基金Supported by National Natural Science Foundation of China(Grant Nos.52001142,52005228,51801218,51911530211,51905110)Young Scientists Sponsorship Program by CAST(Grant No.2022QNRC001).
文摘This study employs advanced electrochemical and surface characterization techniques to investigate the impact of electrochemical hydrogen charging on the corrosion behavior and surface film of the Ti-6Al-4V alloy.The findings revealed the formation ofγ-TiH andδ-TiH_(2) hydrides in the alloy after hydrogen charging.Prolonging hydrogen charging resulted in more significant degradation of the alloy microstructure,leading to deteriorated protectiveness of the surface film.This trend was further confirmed by the electrochemical measurements,which showed that the corrosion resistance of the alloy progressively worsened as the hydrogen charging time was increased.Consequently,this work provides valuable insights into the mechanisms underlying the corrosion of Ti-6Al-4V alloy under hydrogen charging conditions.
基金Project supported by the Science and Technology Foundation of Sci. & Tec. Office of Qinhuangdao City (200507)
文摘Golden yellow cerium conversion film was obtained on magnesium alloys surface by immersion method and the preparation parameters were established. The influence of different process parameters on the surface morphology and performance of the conversion film were analyzed by means of SEM and electrochemical method. Formation dynamics about cerium conversion film on magnesium alloy in solution containing cerium salt and the anti-corrosion behavior of the conversion film in 3.5% NaCl solution were studied by electrochemical method respectively. The results shows that the conversion film is more compact at room temperature when concentration of cerium sulfate is 10 g·L-1 in the solution; the open circuit potential of the magnesium sample moves up to positive direction about 100 mV, the surface of conversion film becomes even and lustrous, and the adhesion intensity of conversion film increases when adding aluminum nitrate into the solution containing cerium salt. The pH value of the solution and immersion time of the sample in the solution also affect the surface morphology and anti-corrosion property of the conversion film. After covered by rare earths conversion film, the anti-corrosion property of magnesium alloy is obviously improved. Rare earth conversion film has self-repairing capability in corrosion medium.
文摘The effect of cerium on ignition temperature of AZ91D magnesium alloy was studie d. By the addition of cerium of 1%, the ignition temperature is raised by 180 ℃ , s o the magnesium alloy added with cerium can be melted in air. The burning temper ature increases with the increasing of cerium. The structure and chemical compos itions of the surface oxide film were investigated by XRD and Auger electron spe ctrometry(AES). The results of XRD indicate that the oxide film of the surface o f ignition-inhibition magnesium alloy can change from loose structure of simple magnesia to compact composite structure consisting of magnesia, cerium oxide, M g17 A112 and aluminum oxide, which has excellent ignition-inhibition effect. AE S depth profile analysis shows that the oxide film can be divided into three lay ers. The outside layer is mainly made up of magnesia, the middle layer, which co nsists of cerium oxide, magnesia, and aluminum oxide, is compound and compact. T hermodynamic analysis indicates that the structure of the surface oxide film is accordant to the change of free energy and high vapor pressure of magnesium.
基金supported by 863 Project of Ministry of Science and Technology of China (2006AA03Z510)the National Natural Science Foundation of China (50871033)+1 种基金the Scientific Technology Project of Heilongjiang Province (GC06A212)the fund from Harbin Municipal Science & Technology Bureau (2006PFXXG006)
文摘The electrochemical behavior of Yb3+ and electrodeposition of Mg-Yb alloy film at solid magnesium cathode in the molten LiCl-KCl-YbCl3(2 wt.%) system at 773 K was investigated.Transient electrochemical techniques,such as cyclic voltammetry,chronopotentiometry and chronoamperometry were used in order to explore the deposition mechanism of Yb.The reduction process of Yb3+ is stepwise reactions which are single-electron and double-electron reversible charge transfer reactions.The speed control step was a diffu...
文摘Nano cerium oxide films were applied on AA7020-T6 aluminum alloy and the effects of acetic acid concentration on the microstructure and electrochemical properties of the coated samples were investigated by using scanning electron microscopy (SEM), X-ray diffraction (XRD), and potentiodynamic polarization methods. It has been found that by increasing the acetic acid/CeCl3·7H2O molar ratio, high uniform and crack-free films with well-developed grains were obtained and grain sizes of the films decreased. Elimination of cracks and decreasing grain size of the nano cerium oxide films caused corrosion resistance to increase.
文摘Anodic oxide films of the titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate electrolyte without hydrofluoric acid or fluoride were fabricated. The morphology, components, and microstructure of the films were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and Raman spectroscopy. The results showed that the films were thick, uniform, and nontransparent. Such films exhibited sedimentary morphology, with a thickness of about 3 μm, and the pore diameters of the deposits ranged from several hundred nanometers to 1.5 μm. The films were mainly titanium dioxide. Some coke-like deposits, which may contain or be changed by OH, NH, C-C, C-O, and C=O groups, were doped in the films. The films were mainly amorphous with a small amount of anatase and rutile phase.
基金financial support by the National Natural Science Foundation of China(No.51171198)National Key Basic Research Program of China(No.2013CB632205)the International Science&Technology Cooperation Program of China(2011DFA50904).
文摘Micro-arc oxidation(MAO)is one of the promising methods to improve the corrosion resistance of magnesium alloys.However,there are plenty of micro-pores in the traditional MAO films,deteriorating their protection property.A novel self-sealing pore MAO film was developed in this paper.The morphologies and chemical composition of the film were detected by scanning electron microscopy(SEM)and energy dispersive X-ray spectroscopy(EDX).The corrosion behavior was investigated by electrochemical and salt spray tests.The possible film formation and corrosion mechanisms were proposed.The self-sealing pore film presents a blue appearance.Most of the micro-pores in the surface of the film are sealed during the film formation process.The chemical composition of the film mainly contains Mg,O,Ti,F and P.The self-sealing pore film exhibits better corrosion resistance compared with the traditional silicate film.Especially,the self-sealing pore film keeps intact after salt spray test for 2000 h,which can be attributed to its high compactness.
文摘To study the mechanism of formation and inhibition of Ce conversion films on Al 2024-T3 alloy, scanning microreference electrode technique (SMRE) is used to probe the potential map on Al 2024-T3 in CeCl 3 solution, the localized corrosion of Al alloy decreases with immersion time and disappears finally, which results from the competition of Cl - aggression and Ce 3+ inhibition on alloy surface. The results of X-ray photoelectron spectroscopy (XPS) indicate that the Ce conversion films consist of Al 2O 3, CeO 2 and Ce 2O 3(Ce(OH) 3), and CeO 2/Ce 2O 3 ratio decreases with the immersion time. When a critical pH for Ce(OH) 3 formation was reached, Ce(OH) 3 will precipitate on the micro cathodic area on alloy surface. Consequently, H 2O 2, the product of the catholic reaction will oxidize a part of Ce(OH) 3 to CeO 2, which appears a better corrosion resistance for Al alloys.
文摘After removing tin coating of tinplates offered by some steel works, we discovered massive, highly disperse gray points outspreading along rolling direction on the surface of the alloy layer. Morphology of the alloy layer was observed by scanning electron microscope (SEM), and many cavities of the alloy layer were found out in the gray point. After analyzing the composition of the alloy layer, we found that content of Fe in the gray points was more than that in the normal alloy layer. Moreover, corrosion resistance of the alloy layer declines with increase of amount of gray points. In addition, the hot-humidity testing was carried out for some plates whose surface has many gray points. After 14 days, there were many rust points occurring in the edge of gray points and in the small gray points. The morphology of rust points was observed by atomic force microscope (AFM). The reason why rust points generated in the edge of gray points and in the small gray points was discussed.
基金Our work is supported by the Natural Science Fund of Jiangsu Province(BK20001414).
文摘In this paper, diamond-like carbon (DLC) films were deposited on Ti alloy by electro-deposition. DLC films were brown andcomposed of the compact grains whose diameter was about 400 nm. Examined by XPS, the main composition of the filmswas carbon. In the Raman spectrum, there were a broad peak at 1350 cm^(-1) and a broad peak at 1600 cm^(-1), which indicatedthat the films were DLC films.
基金financially supported by the Science Foundation of the Educational Department of Fujian Prov-ince (No. 2008F5021)the Natural Science Foundation of Fujian Province (No. A0510013)the National Natural Science Foundation of China (No. 60676055)
文摘Gd-Co alloy films were synthesized by potentiostatic electrolysis on Cu substrates in urea-acetamide-NaBr-KBr melt at 353 K. The electroreduction of Co^2+ and Gd^3+ was investigated by cyclic voltammetry. The reduction of Co^2+ is an irreversible process. Gd^3+ cannot be reduced alone, but it can be inductively co-deposited with Co^2+. Both the Gd content and microstructure of the prepared Gd-Co alloy films can be controlled by the deposited potential. The content of Gd was analyzed using an inductively coupled plasma emission spectrometer (ICPES), and the microstructure was observed by scanning electron micrograph (SEM). The films were crystallized by heat-treatment at 823 K for 30 s in Ar atmosphere, and then were investigated by XRD. The hysteresis loops of the Gd-Co alloy films were measured by a vibrating sample magnetometer (VSM). The experimental results reveal that the deposited Gd-Co alloy films are amorphous, while the annealing causes the samples to change from amorphous to polycrystalline, thus enhancing their magnetocrystalline anisotropy and coercivity. Moreover, the magnetic properties of the Gd-Co alloy films depend strongly on the Gd content.
基金This work was financially supported by the National High-Tech Research and Development Program (No.2003AA302510) and the Beijing Municipal Science and Technology Program (No.D0405003040121).
文摘A Fe-Ni soft magnetic film was prepared in sulphate solution by electroplating. The influences of the molar ratio of n[Fe2+]/n[Ni2+], current density, bath temperature, pH and L-ascorbic acid concentration on magnetic properties of Fe-Ni alloy film were investigated. The results show that the saturated flux density(BS) of the film increases initially and decreases after it reaches the specific value with the increase of n[Fe2+]/n[Ni2+] molar ratio, current density, bath temperature and pH. However, the relationship between L-ascorbic acid concentration and BS keeps linear. It is observed that the coercive force(Hc) is enhanced with the increase of n[Fe2+]/n[Ni2+] molar ratio, current density and pH. By comparison, when the bath temperature increases, Hc always decreases. With the increase of L-ascorbic acid concentration, the coercive force increases initially and then decreases.
基金financially supported by the scientific research project of China Petroleum and Chemical Corporation(No.409075)
文摘The oxidation kinetics,surface morphology and phase structure of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres at 900 ℃ for 20 h were investigated.The anti-coking performance and resistance to carburization of the two oxide films were compared using 25Cr20Ni alloy tubes with an inner diameter of 10 mm and a length of 850 mm in a bench scale naphtha steam pyrolysis unit.The oxidation kinetics followed a parabolic law in an air-H2O atmosphere and a logarithm law in a H2-H2O atmosphere in the steady-state stage.The oxide film grown in the air-H2O atmosphere had cracks where the elements Fe and Ni were enriched and the un-cracked area was covered with octahedral-shaped MnCr2O4 spinels and Cr1.3Fe0.7O3 oxide clusters,while the oxide film grown in the H2-H2O atmosphere was intact and completely covered with dense standing blade MnCr2O4 spinels.In the pyrolysis tests,the anti-coking performance and resistance to carburization of the oxide film grown in the H2-H2O atmosphere were far better than that in the air-H2O atmosphere.The mass of coke formed in the oxide film grown in the H2-H2O atmosphere was less than 10% of that in the air-H2O atmosphere.The Cr1.3Fe0.7O3 oxide clusters converted into Cr23C6 carbides and the cracks were filled with carbon in the oxide film grown in the air-H2O atmosphere after repeated coking and decoking tests,while the dense standing blade MnCr2O4 spinels remained unchanged in the oxide film grown in the H2-H2O atmosphere.The ethylene,propylene and butadiene yields in the pyrolysis tests were almost the same for the two oxide films.
文摘The reduction of Ni(Ⅱ) is an irreversible reaction and La(Ⅲ) cannot be reduced to La directly but be co-deposited inductively in the present of Ni(Ⅱ) in the Acetamide-Urea-NaBr molten salt electrolyte at 353 K. The uncrystallized alloy film of La-Ni is obtained by potentiostatic electrolysis, and the amount of La grows with increasing cathodic overpotential, molar ratios of La(Ⅲ) to Ni(Ⅱ) and the electrolysis time. The maximum amount of La in alloy film reaches to 78.81% (mass fraction) in present study.
基金the National Key Project for Basic Research of China (20005CB623605)NSF of Fujian Province(A0510013)
文摘Dense, adhesive and uniform Sm-Co alloy films were prepared by potentiostatic electrolysis on copper substrates in urea-acetamide-NaBr-KBr melt at 353 K, which were observed by SEM. The electroreduction of Co2+ and Sm3+ was investigated by cyclic voltammetry. The reduction of Co2+ is an irreversible process. Sm3+ can not be reduced alone, but Sm-Co can be co-deposited by induced deposition. The films could be crystallized by heat-treatment at different temperature from 723 to 923 K under Ar atmosphere. The annealed time was chosen as 30 s. The phases of deposited and annealed films were investigated by XRD. The content of Sm was analyzed by Inductive Coupled Plasma Emission Spectrometer (ICPES). The hysteresis loops of the Sm-Co alloy films have been measured by Vibrating Sample Magnetometer (VSM). The experimental results reveal that, the heat-treatment has important influence on coercive field Hc and remanent squareness S of Sm-Co alloy films; the deposited Sm-Co alloy films are amorphous, while the annealed those become polycrystalline; in addition, the magnetocrystalline anisotropy and preferring orientation of films depend strongly on the contents of crystal phases.
基金Funded by the National Natural Science Foundation of China(No. 51171011)
文摘The chemical stripping method of titanium alloy oxide films was studied. An environment friendly solution hydrogen peroxide and sodium hydroxide without hydrofluoric acid or fluoride were used to strip the oxide films. The morphologies of the surface and cross-section of the oxide films before and after the films stripping were characterized by using scanning electron microscopy (SEM). The microstructure and chemical compositions of the oxide films before and after the films stripping were investigated by using Raman spectroscopy (Raman) and X-ray photoelectron spectroscopy (XPS). It was shown that the thickness of the oxide film was in the range of 5-6 μm. The oxide films were stripped for 2 to 8 min in the solution. Moreover, the effect of the stripping time on the efficiency of the film stripping was investigated, and the optimum stripping time was between 6-8 min. When the stripping solution completely dissolved the whole film, the α/β microstructure of the titanium alloy Ti-10V-2Fe-3Al was partly revealed. The stripping mechanism was discussed in terms of the dissolution of film delamination. The hydrogen peroxide had a significant effect on the dissolution of the titanium alloy anodic oxide film. The feasibility of the dissolution reaction also was evaluated.
文摘The cyclic voltammetry and chronoamperometry were used to investigate the electrochemical behaviors of Er(Ⅲ) and Ni(Ⅱ) in LiClO 4 DMSO(dimethylsufoxide) system on Pt and Cu electrodes. Experimental results indicated that the reduction of Er(Ⅲ) to Er and Ni(Ⅱ) to Ni were irreversible in one step on Pt and Cu electrodes. The diffusion coefficient and electron transfer coefficient of Er(Ⅲ) in 0.01 mol·L -1 ErCl 3 -0.1 mol·L -1 LiClO 4 DMSO system at 303K were 1.47×10 -10 m 2·s -1 and 0.108 respectively, and the diffusion coefficient and electron transfer coefficient of Ni(Ⅱ) in 0.01 mol·L -1 NiCl 2-0.1 mol·L -1 LiClO 4 DMSO system at 303K were 3.38×10 -10 m 2·s -1 and 0.160 respectively. The homogeneous, strong adhesive Er Ni alloy films with metallic lu- stre was prepared by potentiostatic electrolysis on Cu electrode in ErCl 3 NiCl 2 LiClO 4 DMSO system at -1.90~ -2.55 V (vs SCE).