CdS microcrystallite doped SiO 2 glass films on titanium metal substrates were prepared by sol gel process. The effects of solution composition and viscosity, heat treatment parameters and substrate pretreatment m...CdS microcrystallite doped SiO 2 glass films on titanium metal substrates were prepared by sol gel process. The effects of solution composition and viscosity, heat treatment parameters and substrate pretreatment method on the film qualities were studied. The transformation process of gel to CdS doped SiO 2 glass film, the structure of these films, the substrate/film interface bonding state and crystalline phase were analyzed by DTA, IRRS, SEM, EDS and XRD. The IRRS results show that Si O Ti linkages are formed between titanium substrate and thin film during heat treatment process. The preferential heat treatment of titanium surface in oxidizing atmosphere will be beneficial to increase the interface bonding strength. The thin films bonded with the substrates chemically and contained very fine CdS crystals with 20～40 nm in size.展开更多
A stable colloidal boehmite sol was made with the aluminium iso propoxide made in China and used to prepare the supported γ alumina membrane using sol gel method. The γ alumina thin layer was characterized by SE...A stable colloidal boehmite sol was made with the aluminium iso propoxide made in China and used to prepare the supported γ alumina membrane using sol gel method. The γ alumina thin layer was characterized by SEM, N 2 sorption method and permeation measurement. The γ alumina membrane was prepared with uniform surface, thickness of 3 μm and average diameter of about 5 nm. The permeabilities of the single gases of H 2, N 2, Ar and their separation factors were measured. The experimental data explained a behavior of Knudsen diffusion for the gas transport through the thin membrane.展开更多
This paper concentrates on the development of glasses with self-cleaning surfaces exhibiting high water contact angles. In this study, we prepared super-hydrophobic nano-ceramic coated glass based on titania & sil...This paper concentrates on the development of glasses with self-cleaning surfaces exhibiting high water contact angles. In this study, we prepared super-hydrophobic nano-ceramic coated glass based on titania & silica using simple sol-gel & dip coating methods and studied the best composition of the coatings by altering ratios of titanium tetraisopropoxide (TTIP)/tetraethyl orthosilicate (TEOS) with different homogenizing agents. We characterized the coatings by surface roughness measurement, percentage of optical transmission, static contact angle, near-infrared (NIR) transmission, and diffuse reflectance. The fabrication of coatings on glass substrates played an important role in increasing the water contact angle of about 95° and visible & NIR transmission of about 90%. We compared our modified glass substrate with commercial low emissivity (Low E) glass using X-ray diffraction (XRD) analysis, which showed pure amorphous surface claiming excellent wettability and thus the prepared glass substrate could have a variety of applications in different fields.展开更多
文摘CdS microcrystallite doped SiO 2 glass films on titanium metal substrates were prepared by sol gel process. The effects of solution composition and viscosity, heat treatment parameters and substrate pretreatment method on the film qualities were studied. The transformation process of gel to CdS doped SiO 2 glass film, the structure of these films, the substrate/film interface bonding state and crystalline phase were analyzed by DTA, IRRS, SEM, EDS and XRD. The IRRS results show that Si O Ti linkages are formed between titanium substrate and thin film during heat treatment process. The preferential heat treatment of titanium surface in oxidizing atmosphere will be beneficial to increase the interface bonding strength. The thin films bonded with the substrates chemically and contained very fine CdS crystals with 20～40 nm in size.
文摘A stable colloidal boehmite sol was made with the aluminium iso propoxide made in China and used to prepare the supported γ alumina membrane using sol gel method. The γ alumina thin layer was characterized by SEM, N 2 sorption method and permeation measurement. The γ alumina membrane was prepared with uniform surface, thickness of 3 μm and average diameter of about 5 nm. The permeabilities of the single gases of H 2, N 2, Ar and their separation factors were measured. The experimental data explained a behavior of Knudsen diffusion for the gas transport through the thin membrane.
文摘This paper concentrates on the development of glasses with self-cleaning surfaces exhibiting high water contact angles. In this study, we prepared super-hydrophobic nano-ceramic coated glass based on titania & silica using simple sol-gel & dip coating methods and studied the best composition of the coatings by altering ratios of titanium tetraisopropoxide (TTIP)/tetraethyl orthosilicate (TEOS) with different homogenizing agents. We characterized the coatings by surface roughness measurement, percentage of optical transmission, static contact angle, near-infrared (NIR) transmission, and diffuse reflectance. The fabrication of coatings on glass substrates played an important role in increasing the water contact angle of about 95° and visible & NIR transmission of about 90%. We compared our modified glass substrate with commercial low emissivity (Low E) glass using X-ray diffraction (XRD) analysis, which showed pure amorphous surface claiming excellent wettability and thus the prepared glass substrate could have a variety of applications in different fields.