Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found ...Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found to have finer Si particles （～5μm） compared to the squeeze-cast specimen （10-25μm）.The tensile strength and elongation of the spray-cast specimen are also higher than those of the squeeze cast one.It was considered that the increased mechanical properties of the spray-cast specimen were mainly due to finer size of the Si particles distributed in Al matrix.展开更多
Tensile testing results of spray cast Ni3Al-based superalloy indicated that the yield strength and tensile strength increase with the increasing of temperature and reached maximum at around 760℃, then decrease with t...Tensile testing results of spray cast Ni3Al-based superalloy indicated that the yield strength and tensile strength increase with the increasing of temperature and reached maximum at around 760℃, then decrease with the increasing of temperature. After high temperature isostatic pressing (HIP), yield strength decreased and ductility and tensile strength increased. Stereographic projection showed that no matter at room temperature, medium temperature or high temperature, cracks extend along (111).展开更多
文摘Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were in- vestigated and then these results were compared with those by squeeze cast.The spray-cast specimen was found to have finer Si particles （～5μm） compared to the squeeze-cast specimen （10-25μm）.The tensile strength and elongation of the spray-cast specimen are also higher than those of the squeeze cast one.It was considered that the increased mechanical properties of the spray-cast specimen were mainly due to finer size of the Si particles distributed in Al matrix.
文摘Tensile testing results of spray cast Ni3Al-based superalloy indicated that the yield strength and tensile strength increase with the increasing of temperature and reached maximum at around 760℃, then decrease with the increasing of temperature. After high temperature isostatic pressing (HIP), yield strength decreased and ductility and tensile strength increased. Stereographic projection showed that no matter at room temperature, medium temperature or high temperature, cracks extend along (111).