The green long-after-glow luminescence from Tb3＋-doped Sr2SiO4 phosphors, which are synthesized by the high temperature solid state reaction in a reductive atmosphere, is observed in this paper. The results show that...The green long-after-glow luminescence from Tb3＋-doped Sr2SiO4 phosphors, which are synthesized by the high temperature solid state reaction in a reductive atmosphere, is observed in this paper. The results show that under ultraviolet excitation, the obtained phosphors produce an intense green-lighting-emission from the Tb3＋, and the green-lighting long- after-glow luminescence related to Tb3＋ can last half an hour after the irradiation source has been removed. Moreover, the effects of co-doping Li＋, Dy3＋, Er3＋, Gd3＋, and Yb3＋ with Tb3＋ on the decay properties and thermoluminescence properties are investigated to confirm the long-after-glow mechanism.展开更多
Li2SiO3 was synthesized by combination of sol-gel method and calcination at high temperature using Li2CO3, HNO3, Si（OC2H5）4 and C2H5OH as starting materials. The effects of calcination temperature and refluxing syst...Li2SiO3 was synthesized by combination of sol-gel method and calcination at high temperature using Li2CO3, HNO3, Si（OC2H5）4 and C2H5OH as starting materials. The effects of calcination temperature and refluxing system on the composition and properties of lithium silicate were investigated. The samples were characterized by TGA/DTA, XRD, SEM and particle size analysis. Li2FeSiO4 was prepared by the solid-state reaction between Li2SiO3 and FeC2O4·2H2O. The XRD patterns show that the use of refluxing system in the sol-gel preparation can decrease the Li2Si2O5 and Li4SiO4 impurities in the Li2SiO3 sample. The calcination temperature plays an important role in the properties of the Li2SiO3 samples. The sample calcined at 700 °C has high purity of 97% Li2SiO3 and good morphology as precursor of Li2FeSiO4. It consists of primary particles with size of 1-3 μm, and the primary particle clusters form agglomerates with loose and porous appearance.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.51272097,61265004,and 61265007)
文摘The green long-after-glow luminescence from Tb3＋-doped Sr2SiO4 phosphors, which are synthesized by the high temperature solid state reaction in a reductive atmosphere, is observed in this paper. The results show that under ultraviolet excitation, the obtained phosphors produce an intense green-lighting-emission from the Tb3＋, and the green-lighting long- after-glow luminescence related to Tb3＋ can last half an hour after the irradiation source has been removed. Moreover, the effects of co-doping Li＋, Dy3＋, Er3＋, Gd3＋, and Yb3＋ with Tb3＋ on the decay properties and thermoluminescence properties are investigated to confirm the long-after-glow mechanism.
基金Foundation item: Project (2007CB613607) support by the National Basic Research Program of ChinaProject (2010QZZD0101) supported by the Basic Research Foundation for the Chinese Central Universities
文摘Li2SiO3 was synthesized by combination of sol-gel method and calcination at high temperature using Li2CO3, HNO3, Si（OC2H5）4 and C2H5OH as starting materials. The effects of calcination temperature and refluxing system on the composition and properties of lithium silicate were investigated. The samples were characterized by TGA/DTA, XRD, SEM and particle size analysis. Li2FeSiO4 was prepared by the solid-state reaction between Li2SiO3 and FeC2O4·2H2O. The XRD patterns show that the use of refluxing system in the sol-gel preparation can decrease the Li2Si2O5 and Li4SiO4 impurities in the Li2SiO3 sample. The calcination temperature plays an important role in the properties of the Li2SiO3 samples. The sample calcined at 700 °C has high purity of 97% Li2SiO3 and good morphology as precursor of Li2FeSiO4. It consists of primary particles with size of 1-3 μm, and the primary particle clusters form agglomerates with loose and porous appearance.