In the present study, the market needs for the (HAZ) toughness are analyzed, and the mechanism of the development of steel plates with excellent heat affected zone decrease in the HAZ toughness during high-heat inpu...In the present study, the market needs for the (HAZ) toughness are analyzed, and the mechanism of the development of steel plates with excellent heat affected zone decrease in the HAZ toughness during high-heat input welding is discussed.The important countermeasure for improving the HAZ toughness is to employ the technology of oxide metallurgy ,namely,to make use of fine inclusion particles for improving the microstructure of HAZ. The progress and theories of oxide metallurgy technologies developed in the Nippon Steel Corporation ( NSC), the JFE Steel Corporation and the Kobe Steel Group are illustrated. Steel plates developed by these three companies with excellent HAZ toughness are introduced.展开更多
The paper describes field test results of 7.62×51 mm M61 AP(armour piercing) ammunition fired into mild steel targets at an outdoor range.The targets varied from 10 mm to 32 mm in thickness.The tests recorded pen...The paper describes field test results of 7.62×51 mm M61 AP(armour piercing) ammunition fired into mild steel targets at an outdoor range.The targets varied from 10 mm to 32 mm in thickness.The tests recorded penetration depth,probability of perforation(i.e.,complete penetration),muzzle and impact velocities,bullet mass,and plate yield strength and hardness.The measured penetration depth exhibited a variability of approximately±12%.The paper then compared ballistic test results with predictive models of steel penetration depth and thickness to prevent perforation.Statistical parameters were derived for muzzle and impact velocity,bullet mass,plate thickness,plate hardness,and model error.A Monte-Carlo probabilistic analysis was then developed to estimate the probability of plate perforation of 7.62 mm M61 AP ammunition for a range of impact velocities,and for mild steels,and High Hardness Armour(HHA) plates.This perforation fragility analysis considered the random variability of impact velocity,bullet mass,plate thickness,plate hardness,and model error.Such a probabilistic analysis allows for reliability-based design,where,for example,the plate thickness with 95% reliability(i.e.only 1 in 20 shots will penetrate the wall) can be estimated knowing the probabilistic distribution of perforation.Hence,it was found that the plate thickness to ensure a low 5% probability of perforation needs to be 11-15% thicker than required to have a 50/50 chance of perforation for mild steel plates.Plates would need to be 20-30% thicker if probability of perforation is reduced to zero.展开更多
As one of the important categories of hot-rolled products, hot-rolled steel plates for automobile applications generally undergo uniform corrosion or localized corrosion according to different environments of manufact...As one of the important categories of hot-rolled products, hot-rolled steel plates for automobile applications generally undergo uniform corrosion or localized corrosion according to different environments of manufacturing, transportation and/or storage of the plates. General corrosion often takes place on the surface of a plate in the exterior part of a package, and only reduces the thickness of the plate and slightly increases the roughness of the surface; however, localized corrosion on the surface of a plate inside the package is likely to result in the formation of pit-like defects on the substrate of the plate, which cannot be removed thoroughly by normal acid pickling or sand blasting, and affects the application of the plate. This research report analyzes the phenomena and characteristics of the rusting behavior of hot- rolled steel plates for automobile applications, and the influencing factors are summaried. The corresponding preventative measures are proposed.展开更多
Presented in this study is the result of steel plates developed at laboratory by using the technique of chemistry design based on microstructure evolution.It has been shown that the produced 50mm thickness steel plate...Presented in this study is the result of steel plates developed at laboratory by using the technique of chemistry design based on microstructure evolution.It has been shown that the produced 50mm thickness steel plates with yield and tensile strength being 420 MPa and 530 MPa respectively exhibit excellent large heat input weldability:the Charpy impact tests in the whole range of heat affected zone(HAZ) including the fusion line at the welded joint with large heat input of 100 -300 kJ/cm showed uniform impact toughness of above 140 J at -40℃.Welding simulations were also performed for heat inputs of 200-600 kJ/cm,which showed far better toughness at -20℃.Analysis on the results of the simulations and the practical welding tests were done and the microstructure evolution mechanisms were proposed.Finally suggestions were given to improve the simulation processes as well as chemistry modification.展开更多
The Moso bamboo,a renewable green building material used in various new green buildings,have received exten-sive attention with the promotion of the concept of green buildings.To explore the mechanical properties of M...The Moso bamboo,a renewable green building material used in various new green buildings,have received exten-sive attention with the promotion of the concept of green buildings.To explore the mechanical properties of Moso bamboo connections with external clamp steel plates,the 16 specimens were designed by changing the bolt diameters and the end distances of the bolt holes.Their static tension tests were conducted to investigate bearing capacities and failure modes of different connection configurations.Based on test results,three failure modes of these connections were obtained,including the shear failure of bolt shank,bearing failure of bolt hole and punch-ing shear failure of the Moso bamboo.The influence of bolt diameters and end distances of bolt holes on bearing capacities of the connections was quantitatively analyzed.Based on a simplified mechanical model,the analytical models were deduced for the bolt shear failure and the bearing failure of bolt holes.The results showed that the predictive values are in substantial agreement with the experimental results.Finally,the design and manufacturing suggestions are recommended for this Moso bamboo connections.展开更多
The composition and production technology of the type of hot-rolled steel plate used in two-sided enameling were briefly described. The microstructure and mechanical properties before and after enameling were contrast...The composition and production technology of the type of hot-rolled steel plate used in two-sided enameling were briefly described. The microstructure and mechanical properties before and after enameling were contrastively investigated,and the precipitates in the samples were analyzed using transmission electron microscope and energy dispersive spectrometer. The results show the ferrite grain size of the steel plate after high-temperature enamel firing to be fine,with a large number of TiC and Ti;C;S;precipitates dispersed throughout the ferrite matrix. After two rounds of enamel firing at a temperature range of 800-890 ℃,its yield strength can still reach342 MPa. The results of a hydrogen permeation test show that the hydrogen storage properties of the steel plate are much better than those of ordinary structural carbon steel. A better bubble structure in the enamel layer can be obtained by this steel plate,with no fish-scale defects on the enameled steel-plate surface.展开更多
The 2205 duplex stainless + DH36 clad steel plate was welded by gas metal arc welding(GMAW), and the welding performance of the clad steel plate was investigated. The results show that the adaptability of the weldi...The 2205 duplex stainless + DH36 clad steel plate was welded by gas metal arc welding(GMAW), and the welding performance of the clad steel plate was investigated. The results show that the adaptability of the welding procedure for the base metal of carbon steel, the transition layer, and the cladding material is excellent. The test results indicate that the phase proportion and component dilution of the GMAW-welded joints of clad steel plate can be effectively controlled to yield joints with good mechanical properties and corrosion resistance.展开更多
In this study,the interface characteristics of a direct hot rolling titanium-clad steel plate were analyzed, and the mechanism of interface cracking was explored. The detrimental effect from the formation of TiFe ,TiC...In this study,the interface characteristics of a direct hot rolling titanium-clad steel plate were analyzed, and the mechanism of interface cracking was explored. The detrimental effect from the formation of TiFe ,TiC,and a Si-enriched layer on the bonding strength was clarified, and an industrial-scaled titanium-clad steel plate with shear strength over 200 MPa was produced with a carefully set schedule accordingly. It was found that hot rolling titanium-clad steel plates had a flat interface without obvious cracks. In the rolling process,both Ti and Fe atoms interdiflhsed,but Fe difthsed much faster than Ti. The Fe-diffused area consisted of three regions. After a high temperature heat treatment, the diffusion depth of Fe and Ti elements increased significantly and evident Si segregation and TiFe layers were identified. Thermal cracking initiated in the Si segregation layer and then propagated along the TiFe layer and Fe-diffused layer on the titanium side.展开更多
Considering the specialities of the steel plate production, the TMCP study has been carried out with Gleeble 2000 tester to explore the possibility of fine grained ferrite in the low carbon steel plates with the chemi...Considering the specialities of the steel plate production, the TMCP study has been carried out with Gleeble 2000 tester to explore the possibility of fine grained ferrite in the low carbon steel plates with the chemical composition of C 0.13--0.18, Si 0.12-0.18, Mn 0.50-0. 65, P 0. 010-0. 025, and S 0. 005-0. 028. The plates with thickness of 8. 7 mm in which the ferrite grain size is smaller than 8μm have been produced by special de- formation process in the laboratory. Furthermore, the trial production of special plain carbon steel plates of 16-25 mm in thickness and 2 000- 2 800 mm in width with fine grained ferrite has been successfully carried out in the Shougang Steel Plate Rolling Plant. The ferrite grain size is 5.5-7μm in the surface layers and 9.5-15μm in the central layer respectively. The yield strength is 320- 360 MPa, tensile strength is 440-520 MPa and the elongation is 25%- 34 %. It is very important for the rolling plants to improve the low carbon steel plates' mechanical properties. The results show that the ferrite grains in the surface layer can be refined effectively by the appropriate rolling process, and the strength can be also increased.展开更多
Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure...Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure will diminish through certain annealing process,while the cracks formed from fly-line microstructure will remain.Therefore,fly-line microstructure can be considered as a plastic deformation microstructure and crack source s meanwhile its formation is considered as a special plastic deformation mechanism of metal under explosive load.展开更多
Segmental tunnel lining strengthened with steel plates is widely used worldwide to provide a permanent strengthening method.Most existing studies assume an ideal steel-concrete interface,ignoring discontinuous deforma...Segmental tunnel lining strengthened with steel plates is widely used worldwide to provide a permanent strengthening method.Most existing studies assume an ideal steel-concrete interface,ignoring discontinuous deformation characteristics,making it difficult to accurately analyze the strengthened structure’s failure mechanism.In this study,interfacial fracture mechanics of composite material was applied to the segmental tunnel lining strengthened with steel plates,and a numerical three-dimensional solid nonlinear model of the lining structure was established,combining the extended finite element method with a cohesive-zone model to account for the discontinuous deformation characteristics of the interface.The results accurately describe the crack propagation process,and are verified by full-scale testing.Next,dynamic simulations based on the calibrated model were conducted to analyze the sliding failure and cracking of the steel-concrete interface.Lastly,detailed location of the interface bonding failure are further verified by model test.The results show that,the cracking failure and bond failure of the interface are the decisive factors determining the instability and failure of the strengthened structure.The proposed numerical analysis is a major step forward in revealing the interface failure mechanism of strengthened composite material structures.展开更多
As the protective component,steel plate had attracted extensive attention because of frequently threats of explosive loads.In this paper,the evolution of microstructure and the mechanism of damage in the quasi-crackin...As the protective component,steel plate had attracted extensive attention because of frequently threats of explosive loads.In this paper,the evolution of microstructure and the mechanism of damage in the quasi-cracking area of steel plate subjected to explosive load were discussed and the relationships between micro defects and dynamic mechanical response were revealed.After the explosion experiment,five observation points were selected equidistant from the quasi-cracking area of the section of the steel plate along the thickness direction,and the characteristics of micro defects at the observation points were analyzed by optical microscope(OM),scanning electron microscope(SEM) and electron backscattered diffraction(EBSD).The observation result shows that many slip bands(SBs) appeared,and the grain orientation changed obviously in the steel plate,the two were the main damage types of micro defects.In addition,cracks,peeling pits,grooves and other lager micro defects were appeared in the lower area of the plate.The stress parameters of the observation points were obtained through an effective numerical model.The mechanism of damage generation and crack propagation in the quasicracking area were clarified by comparing the specific impulse of each observation point with the corresponding micro defects.The result shows that the generation and expansion of micro defects are related to the stress area(i.e.the upper compression area,the neutral plane area,and the lower tension area).The micro defects gather and expand at the grain boundary,and will become macroscopic damage under the continuous action of tensile stress.Besides,the micro defects at the midpoint of the section of the steel plate in the direction away from the explosion center(i.e.the horizontal direction) were also studied.It was found that the specific impulse at these positions were much smaller than that in the thickness direction,the micro defects were only SBs and a few micro cracks,and the those decreased with the increase of the distance from the explosion center.展开更多
The application of ultra-high performance concrete(UHPC)as a covering layer for steel bridge decks has gained widespread popularity.By employing a connection without a shear connector between the steel plate and UHPC,...The application of ultra-high performance concrete(UHPC)as a covering layer for steel bridge decks has gained widespread popularity.By employing a connection without a shear connector between the steel plate and UHPC,namely,the sandblasted interface and the epoxy adhesive with sprinkled basalt aggregate interface,the installation cannot only be simplified but also the stress concentration resulting from the welded shear connectors can be eliminated.This study develops constitutive models for these two interfaces without shear connectors,based on the interfacial pull-off and push-out tests.For validation,three-point bending tests on the steel-UHPC composite plates are conducted.The results indicated that the proposed bilinear traction-separation model for the sandblasted interface and the trapezoidal traction-separation model for the epoxy adhesive with sprinkled basalt aggregate interface can generally calibrate the interfacial behavior.However,the utilization of the experimentally determined pure shear strength underestimates the load-carrying capacity of the composite plates in the case of three-point bending tests.By recalling the Mohr-Coulomb criterion,this underestimation is attributed to the enhancement of the interface shear strength by the presence of normal stress.展开更多
It was found that the steel plate in the composite plate in the WJ-8 fastener used in high speed rail is rusty. The objective of this study is to test the zinc coating of the steel plate. A literature review was condu...It was found that the steel plate in the composite plate in the WJ-8 fastener used in high speed rail is rusty. The objective of this study is to test the zinc coating of the steel plate. A literature review was conducted to identify the zinc coating techniques, and the companies that can provide different coating service was identified. A salt fog chamber was built that was in compliance with the ANSI B117 code, and the steel plates that were coated by the identified companies were tested using the salt fog chamber. The results indicated that the coating technique that had the best performance in preventing corrosion was the Greenkote plates with passivation. The galvanized option had the roughest coating layer, and it was the most reactive in the salt water solution. This makes it non-ideal for the dynamic rail environment because the increased friction of the plate could damage the supports, especially during extreme temperatures that would cause the rail to expand or contract. Greenkote with Phosphate and ArmorGalv also provided increased corrosion prevention with a smooth, strong finish, but it had more rust on the surface area than the Greenkote with ELU passivation. The ArmorGalv sample had more rust on the surface area than the Greenkote samples. This may not be a weakness in the ArmorGalv process;rather, it likely was the result of this particular sample not having the added protection of a colored coating.展开更多
Moso bamboos have attracted excessive attention as a renewable green building material to the concept of sustainable development.In this paper,the 20 bolted Moso bamboo connection specimens with embedded steel plates ...Moso bamboos have attracted excessive attention as a renewable green building material to the concept of sustainable development.In this paper,the 20 bolted Moso bamboo connection specimens with embedded steel plates and grouting materials were designed according to connection configurations with different bolt diameters and end distance of bolt holes,and their bearing capacities and failure modes were analyzed by static tension tests.According to the test results of all connectors,the failure modes of the specimens are divided into four categories,and the effects of bolt diameter and bolt hole end distance on the connection bearing capacity and failure mode are analyzed.The test results show that the deformation and failure process can be divided into four stages.The main influence factor of connector bearing capacity is bolt diameter.Connectors can be divided into four failure modes,and brittle failure can be avoided by adopting certain structural measures.Filling with grouting material can improve the bearing capacity of joints.Due to the large variability of bamboo,further experiments are needed.展开更多
Arc ion plating (AIP) is applied to form Ti/(Ti,Cr)N/CrN multilayer coating on the surface of 316L stainless steel (SS316L) as bipolar plates for proton exchange membrane fuel cells (PEMFCs). The characterizations of ...Arc ion plating (AIP) is applied to form Ti/(Ti,Cr)N/CrN multilayer coating on the surface of 316L stainless steel (SS316L) as bipolar plates for proton exchange membrane fuel cells (PEMFCs). The characterizations of the coating are analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Interfacial contact resistance (ICR) between the coated sample and carbon paper is 4.9 m Omega cm(2) under 150 N/cm(2), which is much lower than that of the SS316L substrate. Potentiodynamic and potentiostatic tests are performed in the simulated PEMFC working conditions to investigate the corrosion behaviors of the coated sample. Superior anticorrosion performance is observed for the coated sample, whose corrosion current density is 0.12 mu A/cm(2). Surface morphology results after corrosion tests indicate that the substrate is well protected by the multilayer coating. Performances of the single cell with the multilayer coated SS316L bipolar plate are improved significantly compared with that of the cell with the uncoated SS316L bipolar plate, presenting a great potential for PEMFC application. (C) 2016 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.展开更多
Proton exchange membrane fuel cell(PEMFC)powered automobiles have been recognized to be the ultimate solution to replace traditional fuel automobiles because of their advantages of PEMFCs such as no pollution,low temp...Proton exchange membrane fuel cell(PEMFC)powered automobiles have been recognized to be the ultimate solution to replace traditional fuel automobiles because of their advantages of PEMFCs such as no pollution,low temperature start-up,high energy density,and low noise.As one of the core components,the bipolar plates(BPs)play an important role in the PEMFC stack.Traditional graphite BPs and composite BPs have been criticized for their shortcomings such as low strength,high brittleness,and high processing cost.In contrast,stainless steel BPs(SSBPs)have recently attracted much attention of domestic and foreign researchers because of their excellent comprehensive performance,low cost,and diverse options for automobile applications.However,the SSBPs are prone to corrosion and passivation in the PEMFC working environment,which lead to reduced output power or premature failure.This review is aimed to summarize the corrosion and passivation mechanisms,characterizations and evaluation,and the surface modification technologies in the current SSBPs research.The non-coating and coating technical routes of SSBPs are demonstrated,such as substrate component regulation,thermal nitriding,electroplating,ion plating,chemical vapor deposition,and physical vapor deposition,etc.Alternative coating materials for SSBPs are metal coatings,metal nitride coatings,conductive polymer coatings,and polymer/carbon coatings,etc.Both the surface modification technologies can solve the corrosion resistance problem of stainless steel without affecting the contact resistance,however still facing restraints such as long-time stability,feasibility of low-cost,and mass production process.This paper is believed to enrich the knowledge of high-performance and long-life BPs applied for PEMFC automobiles.展开更多
Some of the major manufacturing processes and corresponding mechanical properties of titanium clad steel plates were analyzed, and the consequences of research, manufacturing, and application of titanium clad steel pl...Some of the major manufacturing processes and corresponding mechanical properties of titanium clad steel plates were analyzed, and the consequences of research, manufacturing, and application of titanium clad steel plates in both markets of China and overseas were also summarized. As an economical and environmentally friendly technology, the roll bonding process is expected to become the next-generation mainstream process for the manufacturing of titanium clad steel plate. Some of the crucial and most important technical problems of this particular process, including vacuum sealing technology, surface treatment process technology, application of a transition layer, and rolling process, were discussed along with the advantageous mechanical properties and life-cycle economy of these plates processed by this technology. Finally, the market needs, application trends, and requirements of titanium clad steel plate were also considered from industries of petrochemical, shipbuilding, marine, and electric power.展开更多
Ni–Cr enrichment on stainless steel SS316 L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thi...Ni–Cr enrichment on stainless steel SS316 L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thin continuous Ag-doped carbon film on a porous carbon-coated SS316 L substrate. The corrosion resistance of this film in 0.5 mol·L^(-1) H_2SO_4 solution containing 5 ppm F- at 80°C was investigated using polarization tests. The results showed that the surface treatment of the SS316 L strongly affected the adhesion of the carbon coating to the stainless steel. Compared to the bare SS316 L, the Ag-doped carbon-coated SS316 L bipolar plate was remarkably more stable in both the anode and cathode environments of proton exchange membrane fuel cell(PEMFC) and the interface contact resistance between the specimen and Toray 060 carbon paper was reduced from 333.0 m?·cm^2 to 21.6 m?·cm^2 at a compaction pressure of 1.2 MPa.展开更多
Two dissimilar steel plates,structural steel and mild steel,were joined by explosion welding to form a composite.The composite was then heat-treated by quenching at 840℃ for 30 min followed by tempering at 200℃ for ...Two dissimilar steel plates,structural steel and mild steel,were joined by explosion welding to form a composite.The composite was then heat-treated by quenching at 840℃ for 30 min followed by tempering at 200℃ for 3 h.The microstructure was investigated under an optical microscope and a scanning electron microscope.The mechanical properties were measured using Vickers microhardness and Charpy impact tests.The results show a deformed interface with typical wave features at the welding zone,but no defects were observed.Moreover,the ferrite in the parent plate in the weld zone was elongated due to the strong plastic deformation from the explosion.After heat treatment,the hardness of the flyer plate(structural steel)was over HV0.2800,while that of the parent plate(mild steel)was HV0.2200.The increase in hardness was due to the presence of martensite.Moreover,the average impact energy was increased from 18.5 to 44.0 J following heat treatment;this is because of the formation of recrystallized grains at the weld interface,which is due to the dynamic recovery and local recrystallization,and the strong elemental diffusion that occurred between the two plates.展开更多
文摘In the present study, the market needs for the (HAZ) toughness are analyzed, and the mechanism of the development of steel plates with excellent heat affected zone decrease in the HAZ toughness during high-heat input welding is discussed.The important countermeasure for improving the HAZ toughness is to employ the technology of oxide metallurgy ,namely,to make use of fine inclusion particles for improving the microstructure of HAZ. The progress and theories of oxide metallurgy technologies developed in the Nippon Steel Corporation ( NSC), the JFE Steel Corporation and the Kobe Steel Group are illustrated. Steel plates developed by these three companies with excellent HAZ toughness are introduced.
基金The authors appreciate the laboratory assistance of Goran Simundic and Michael Goodwin for assistance with measurement of the field test results The assistance of final year honours student Richard Szlicht is gratefully acknowledged.
文摘The paper describes field test results of 7.62×51 mm M61 AP(armour piercing) ammunition fired into mild steel targets at an outdoor range.The targets varied from 10 mm to 32 mm in thickness.The tests recorded penetration depth,probability of perforation(i.e.,complete penetration),muzzle and impact velocities,bullet mass,and plate yield strength and hardness.The measured penetration depth exhibited a variability of approximately±12%.The paper then compared ballistic test results with predictive models of steel penetration depth and thickness to prevent perforation.Statistical parameters were derived for muzzle and impact velocity,bullet mass,plate thickness,plate hardness,and model error.A Monte-Carlo probabilistic analysis was then developed to estimate the probability of plate perforation of 7.62 mm M61 AP ammunition for a range of impact velocities,and for mild steels,and High Hardness Armour(HHA) plates.This perforation fragility analysis considered the random variability of impact velocity,bullet mass,plate thickness,plate hardness,and model error.Such a probabilistic analysis allows for reliability-based design,where,for example,the plate thickness with 95% reliability(i.e.only 1 in 20 shots will penetrate the wall) can be estimated knowing the probabilistic distribution of perforation.Hence,it was found that the plate thickness to ensure a low 5% probability of perforation needs to be 11-15% thicker than required to have a 50/50 chance of perforation for mild steel plates.Plates would need to be 20-30% thicker if probability of perforation is reduced to zero.
文摘As one of the important categories of hot-rolled products, hot-rolled steel plates for automobile applications generally undergo uniform corrosion or localized corrosion according to different environments of manufacturing, transportation and/or storage of the plates. General corrosion often takes place on the surface of a plate in the exterior part of a package, and only reduces the thickness of the plate and slightly increases the roughness of the surface; however, localized corrosion on the surface of a plate inside the package is likely to result in the formation of pit-like defects on the substrate of the plate, which cannot be removed thoroughly by normal acid pickling or sand blasting, and affects the application of the plate. This research report analyzes the phenomena and characteristics of the rusting behavior of hot- rolled steel plates for automobile applications, and the influencing factors are summaried. The corresponding preventative measures are proposed.
文摘Presented in this study is the result of steel plates developed at laboratory by using the technique of chemistry design based on microstructure evolution.It has been shown that the produced 50mm thickness steel plates with yield and tensile strength being 420 MPa and 530 MPa respectively exhibit excellent large heat input weldability:the Charpy impact tests in the whole range of heat affected zone(HAZ) including the fusion line at the welded joint with large heat input of 100 -300 kJ/cm showed uniform impact toughness of above 140 J at -40℃.Welding simulations were also performed for heat inputs of 200-600 kJ/cm,which showed far better toughness at -20℃.Analysis on the results of the simulations and the practical welding tests were done and the microstructure evolution mechanisms were proposed.Finally suggestions were given to improve the simulation processes as well as chemistry modification.
基金The authors would like to appreciate the support from the Graduate Research and Innovation Foundation of Chongqing in China(Grant No.CYS20026)the National Key Research and Development Program of China(Grant No.2017YFC0703504).
文摘The Moso bamboo,a renewable green building material used in various new green buildings,have received exten-sive attention with the promotion of the concept of green buildings.To explore the mechanical properties of Moso bamboo connections with external clamp steel plates,the 16 specimens were designed by changing the bolt diameters and the end distances of the bolt holes.Their static tension tests were conducted to investigate bearing capacities and failure modes of different connection configurations.Based on test results,three failure modes of these connections were obtained,including the shear failure of bolt shank,bearing failure of bolt hole and punch-ing shear failure of the Moso bamboo.The influence of bolt diameters and end distances of bolt holes on bearing capacities of the connections was quantitatively analyzed.Based on a simplified mechanical model,the analytical models were deduced for the bolt shear failure and the bearing failure of bolt holes.The results showed that the predictive values are in substantial agreement with the experimental results.Finally,the design and manufacturing suggestions are recommended for this Moso bamboo connections.
文摘The composition and production technology of the type of hot-rolled steel plate used in two-sided enameling were briefly described. The microstructure and mechanical properties before and after enameling were contrastively investigated,and the precipitates in the samples were analyzed using transmission electron microscope and energy dispersive spectrometer. The results show the ferrite grain size of the steel plate after high-temperature enamel firing to be fine,with a large number of TiC and Ti;C;S;precipitates dispersed throughout the ferrite matrix. After two rounds of enamel firing at a temperature range of 800-890 ℃,its yield strength can still reach342 MPa. The results of a hydrogen permeation test show that the hydrogen storage properties of the steel plate are much better than those of ordinary structural carbon steel. A better bubble structure in the enamel layer can be obtained by this steel plate,with no fish-scale defects on the enameled steel-plate surface.
文摘The 2205 duplex stainless + DH36 clad steel plate was welded by gas metal arc welding(GMAW), and the welding performance of the clad steel plate was investigated. The results show that the adaptability of the welding procedure for the base metal of carbon steel, the transition layer, and the cladding material is excellent. The test results indicate that the phase proportion and component dilution of the GMAW-welded joints of clad steel plate can be effectively controlled to yield joints with good mechanical properties and corrosion resistance.
文摘In this study,the interface characteristics of a direct hot rolling titanium-clad steel plate were analyzed, and the mechanism of interface cracking was explored. The detrimental effect from the formation of TiFe ,TiC,and a Si-enriched layer on the bonding strength was clarified, and an industrial-scaled titanium-clad steel plate with shear strength over 200 MPa was produced with a carefully set schedule accordingly. It was found that hot rolling titanium-clad steel plates had a flat interface without obvious cracks. In the rolling process,both Ti and Fe atoms interdiflhsed,but Fe difthsed much faster than Ti. The Fe-diffused area consisted of three regions. After a high temperature heat treatment, the diffusion depth of Fe and Ti elements increased significantly and evident Si segregation and TiFe layers were identified. Thermal cracking initiated in the Si segregation layer and then propagated along the TiFe layer and Fe-diffused layer on the titanium side.
文摘Considering the specialities of the steel plate production, the TMCP study has been carried out with Gleeble 2000 tester to explore the possibility of fine grained ferrite in the low carbon steel plates with the chemical composition of C 0.13--0.18, Si 0.12-0.18, Mn 0.50-0. 65, P 0. 010-0. 025, and S 0. 005-0. 028. The plates with thickness of 8. 7 mm in which the ferrite grain size is smaller than 8μm have been produced by special de- formation process in the laboratory. Furthermore, the trial production of special plain carbon steel plates of 16-25 mm in thickness and 2 000- 2 800 mm in width with fine grained ferrite has been successfully carried out in the Shougang Steel Plate Rolling Plant. The ferrite grain size is 5.5-7μm in the surface layers and 9.5-15μm in the central layer respectively. The yield strength is 320- 360 MPa, tensile strength is 440-520 MPa and the elongation is 25%- 34 %. It is very important for the rolling plants to improve the low carbon steel plates' mechanical properties. The results show that the ferrite grains in the surface layer can be refined effectively by the appropriate rolling process, and the strength can be also increased.
文摘Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure will diminish through certain annealing process,while the cracks formed from fly-line microstructure will remain.Therefore,fly-line microstructure can be considered as a plastic deformation microstructure and crack source s meanwhile its formation is considered as a special plastic deformation mechanism of metal under explosive load.
基金the financial support provided by the National Key Basic Research Program of China(No.2015CB057801)the Projects of the Construction Department of Zhejiang Province(Nos.2022K073 and 2022K169).
文摘Segmental tunnel lining strengthened with steel plates is widely used worldwide to provide a permanent strengthening method.Most existing studies assume an ideal steel-concrete interface,ignoring discontinuous deformation characteristics,making it difficult to accurately analyze the strengthened structure’s failure mechanism.In this study,interfacial fracture mechanics of composite material was applied to the segmental tunnel lining strengthened with steel plates,and a numerical three-dimensional solid nonlinear model of the lining structure was established,combining the extended finite element method with a cohesive-zone model to account for the discontinuous deformation characteristics of the interface.The results accurately describe the crack propagation process,and are verified by full-scale testing.Next,dynamic simulations based on the calibrated model were conducted to analyze the sliding failure and cracking of the steel-concrete interface.Lastly,detailed location of the interface bonding failure are further verified by model test.The results show that,the cracking failure and bond failure of the interface are the decisive factors determining the instability and failure of the strengthened structure.The proposed numerical analysis is a major step forward in revealing the interface failure mechanism of strengthened composite material structures.
基金supported by the Science and Technology Project of Fire Rescue Bureau of Ministry of Emergency Management (Grant No.2022XFZD05)S&T Program of Hebei(Grant No.22375419D)National Natural Science Foundation of China (Grant No.11802160)。
文摘As the protective component,steel plate had attracted extensive attention because of frequently threats of explosive loads.In this paper,the evolution of microstructure and the mechanism of damage in the quasi-cracking area of steel plate subjected to explosive load were discussed and the relationships between micro defects and dynamic mechanical response were revealed.After the explosion experiment,five observation points were selected equidistant from the quasi-cracking area of the section of the steel plate along the thickness direction,and the characteristics of micro defects at the observation points were analyzed by optical microscope(OM),scanning electron microscope(SEM) and electron backscattered diffraction(EBSD).The observation result shows that many slip bands(SBs) appeared,and the grain orientation changed obviously in the steel plate,the two were the main damage types of micro defects.In addition,cracks,peeling pits,grooves and other lager micro defects were appeared in the lower area of the plate.The stress parameters of the observation points were obtained through an effective numerical model.The mechanism of damage generation and crack propagation in the quasicracking area were clarified by comparing the specific impulse of each observation point with the corresponding micro defects.The result shows that the generation and expansion of micro defects are related to the stress area(i.e.the upper compression area,the neutral plane area,and the lower tension area).The micro defects gather and expand at the grain boundary,and will become macroscopic damage under the continuous action of tensile stress.Besides,the micro defects at the midpoint of the section of the steel plate in the direction away from the explosion center(i.e.the horizontal direction) were also studied.It was found that the specific impulse at these positions were much smaller than that in the thickness direction,the micro defects were only SBs and a few micro cracks,and the those decreased with the increase of the distance from the explosion center.
基金supported by the National Natural Science Foundation of China(Grant Nos.52108168&52208398).
文摘The application of ultra-high performance concrete(UHPC)as a covering layer for steel bridge decks has gained widespread popularity.By employing a connection without a shear connector between the steel plate and UHPC,namely,the sandblasted interface and the epoxy adhesive with sprinkled basalt aggregate interface,the installation cannot only be simplified but also the stress concentration resulting from the welded shear connectors can be eliminated.This study develops constitutive models for these two interfaces without shear connectors,based on the interfacial pull-off and push-out tests.For validation,three-point bending tests on the steel-UHPC composite plates are conducted.The results indicated that the proposed bilinear traction-separation model for the sandblasted interface and the trapezoidal traction-separation model for the epoxy adhesive with sprinkled basalt aggregate interface can generally calibrate the interfacial behavior.However,the utilization of the experimentally determined pure shear strength underestimates the load-carrying capacity of the composite plates in the case of three-point bending tests.By recalling the Mohr-Coulomb criterion,this underestimation is attributed to the enhancement of the interface shear strength by the presence of normal stress.
文摘It was found that the steel plate in the composite plate in the WJ-8 fastener used in high speed rail is rusty. The objective of this study is to test the zinc coating of the steel plate. A literature review was conducted to identify the zinc coating techniques, and the companies that can provide different coating service was identified. A salt fog chamber was built that was in compliance with the ANSI B117 code, and the steel plates that were coated by the identified companies were tested using the salt fog chamber. The results indicated that the coating technique that had the best performance in preventing corrosion was the Greenkote plates with passivation. The galvanized option had the roughest coating layer, and it was the most reactive in the salt water solution. This makes it non-ideal for the dynamic rail environment because the increased friction of the plate could damage the supports, especially during extreme temperatures that would cause the rail to expand or contract. Greenkote with Phosphate and ArmorGalv also provided increased corrosion prevention with a smooth, strong finish, but it had more rust on the surface area than the Greenkote with ELU passivation. The ArmorGalv sample had more rust on the surface area than the Greenkote samples. This may not be a weakness in the ArmorGalv process;rather, it likely was the result of this particular sample not having the added protection of a colored coating.
基金support from 111 Project(Grant No.B18062)the Graduate Research and Innovation Foundation of Chongqing in China(Grant No.CYS20026)the National Key Research and Development Program of China(Grant No.2017YFC0703504).
文摘Moso bamboos have attracted excessive attention as a renewable green building material to the concept of sustainable development.In this paper,the 20 bolted Moso bamboo connection specimens with embedded steel plates and grouting materials were designed according to connection configurations with different bolt diameters and end distance of bolt holes,and their bearing capacities and failure modes were analyzed by static tension tests.According to the test results of all connectors,the failure modes of the specimens are divided into four categories,and the effects of bolt diameter and bolt hole end distance on the connection bearing capacity and failure mode are analyzed.The test results show that the deformation and failure process can be divided into four stages.The main influence factor of connector bearing capacity is bolt diameter.Connectors can be divided into four failure modes,and brittle failure can be avoided by adopting certain structural measures.Filling with grouting material can improve the bearing capacity of joints.Due to the large variability of bamboo,further experiments are needed.
基金financially supported by the National Basic Research Program of China (973 Program) (no. 2012CB215500)the National Key Technology Research and Development Program of China (no. 2015BAG06B00)+1 种基金Major Program of the National Natural Science Foundation of China (no. 61433013)National Natural Science Foundation of China (no. 21206012)
文摘Arc ion plating (AIP) is applied to form Ti/(Ti,Cr)N/CrN multilayer coating on the surface of 316L stainless steel (SS316L) as bipolar plates for proton exchange membrane fuel cells (PEMFCs). The characterizations of the coating are analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Interfacial contact resistance (ICR) between the coated sample and carbon paper is 4.9 m Omega cm(2) under 150 N/cm(2), which is much lower than that of the SS316L substrate. Potentiodynamic and potentiostatic tests are performed in the simulated PEMFC working conditions to investigate the corrosion behaviors of the coated sample. Superior anticorrosion performance is observed for the coated sample, whose corrosion current density is 0.12 mu A/cm(2). Surface morphology results after corrosion tests indicate that the substrate is well protected by the multilayer coating. Performances of the single cell with the multilayer coated SS316L bipolar plate are improved significantly compared with that of the cell with the uncoated SS316L bipolar plate, presenting a great potential for PEMFC application. (C) 2016 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.
基金supported by the National Natural Science Foundation of China(No.51704017)the National Key Research and Development plan of China(No.2018YFB1502403)the Communication Program for Young Scientist in USTB(No.QNXM20210010)。
文摘Proton exchange membrane fuel cell(PEMFC)powered automobiles have been recognized to be the ultimate solution to replace traditional fuel automobiles because of their advantages of PEMFCs such as no pollution,low temperature start-up,high energy density,and low noise.As one of the core components,the bipolar plates(BPs)play an important role in the PEMFC stack.Traditional graphite BPs and composite BPs have been criticized for their shortcomings such as low strength,high brittleness,and high processing cost.In contrast,stainless steel BPs(SSBPs)have recently attracted much attention of domestic and foreign researchers because of their excellent comprehensive performance,low cost,and diverse options for automobile applications.However,the SSBPs are prone to corrosion and passivation in the PEMFC working environment,which lead to reduced output power or premature failure.This review is aimed to summarize the corrosion and passivation mechanisms,characterizations and evaluation,and the surface modification technologies in the current SSBPs research.The non-coating and coating technical routes of SSBPs are demonstrated,such as substrate component regulation,thermal nitriding,electroplating,ion plating,chemical vapor deposition,and physical vapor deposition,etc.Alternative coating materials for SSBPs are metal coatings,metal nitride coatings,conductive polymer coatings,and polymer/carbon coatings,etc.Both the surface modification technologies can solve the corrosion resistance problem of stainless steel without affecting the contact resistance,however still facing restraints such as long-time stability,feasibility of low-cost,and mass production process.This paper is believed to enrich the knowledge of high-performance and long-life BPs applied for PEMFC automobiles.
文摘Some of the major manufacturing processes and corresponding mechanical properties of titanium clad steel plates were analyzed, and the consequences of research, manufacturing, and application of titanium clad steel plates in both markets of China and overseas were also summarized. As an economical and environmentally friendly technology, the roll bonding process is expected to become the next-generation mainstream process for the manufacturing of titanium clad steel plate. Some of the crucial and most important technical problems of this particular process, including vacuum sealing technology, surface treatment process technology, application of a transition layer, and rolling process, were discussed along with the advantageous mechanical properties and life-cycle economy of these plates processed by this technology. Finally, the market needs, application trends, and requirements of titanium clad steel plate were also considered from industries of petrochemical, shipbuilding, marine, and electric power.
基金financially supported by the National Natural Science Foundation of China(No.21106012)the Educational Department Foundation of Liaoning Province of China(NO.L2014180)
文摘Ni–Cr enrichment on stainless steel SS316 L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thin continuous Ag-doped carbon film on a porous carbon-coated SS316 L substrate. The corrosion resistance of this film in 0.5 mol·L^(-1) H_2SO_4 solution containing 5 ppm F- at 80°C was investigated using polarization tests. The results showed that the surface treatment of the SS316 L strongly affected the adhesion of the carbon coating to the stainless steel. Compared to the bare SS316 L, the Ag-doped carbon-coated SS316 L bipolar plate was remarkably more stable in both the anode and cathode environments of proton exchange membrane fuel cell(PEMFC) and the interface contact resistance between the specimen and Toray 060 carbon paper was reduced from 333.0 m?·cm^2 to 21.6 m?·cm^2 at a compaction pressure of 1.2 MPa.
基金financially supported by the State Key Laboratory of Solidification Processing of Northwestern Polytechnical University(2019-QZ-01)。
文摘Two dissimilar steel plates,structural steel and mild steel,were joined by explosion welding to form a composite.The composite was then heat-treated by quenching at 840℃ for 30 min followed by tempering at 200℃ for 3 h.The microstructure was investigated under an optical microscope and a scanning electron microscope.The mechanical properties were measured using Vickers microhardness and Charpy impact tests.The results show a deformed interface with typical wave features at the welding zone,but no defects were observed.Moreover,the ferrite in the parent plate in the weld zone was elongated due to the strong plastic deformation from the explosion.After heat treatment,the hardness of the flyer plate(structural steel)was over HV0.2800,while that of the parent plate(mild steel)was HV0.2200.The increase in hardness was due to the presence of martensite.Moreover,the average impact energy was increased from 18.5 to 44.0 J following heat treatment;this is because of the formation of recrystallized grains at the weld interface,which is due to the dynamic recovery and local recrystallization,and the strong elemental diffusion that occurred between the two plates.