Electromagnetic stirring is one of the widely applied techniques to modify the quality of casting billets.Different from conventional rotate stirring,the helical stirring is more professional in assisting multi-dimens...Electromagnetic stirring is one of the widely applied techniques to modify the quality of casting billets.Different from conventional rotate stirring,the helical stirring is more professional in assisting multi-dimensional flow of molten metal and eliminating solidification defects.In this study,the single-winding helical stirring(SWHS)was introduced,offering advantages such as smaller volume and lower electromagnetic shielding compared to traditional helical stirring methods.Following a comprehensive numerical simulation,the stirring parameters of SWHS were adjusted to yoke inclination angle of 43°and frequency of 12 Hz.The higher electromagnetic force and flow velocity in drawing direction,as well as the lower temperature gradient induced by the SWHS,are positive factors for homogeneous solidification of billet.The experimental results on Al-8%Si alloy and 0.4%C-1.1%Mn steel demonstrate that compared to rotate stirring,the SWHS process can induce better billet quality and is more effective in accelerating the equiaxed expansion and reducing element segregation.The SWHS process can enhance the equiaxed ratio of the billet by 58.3%and reduce segregation degree of carbon element by 10.97%.Consequently,SWHS holds great promise as a potential approach for improving the quality of continuous casting billets.展开更多
Nowadays,having an effective technique in preparing semi-solid slurries for rheocasting process seems to be an essential requirement.In this study,semi-solid slurry of A356 aluminum alloy was prepared by three-phase a...Nowadays,having an effective technique in preparing semi-solid slurries for rheocasting process seems to be an essential requirement.In this study,semi-solid slurry of A356 aluminum alloy was prepared by three-phase annular electromagnetic stirring(A-EMS)technique under different conditions.The effects of stirring current,pouring temperature and stirring time on microstructural evolution,mean particle size,shape factor and solid fraction were investigated.The rheocasting process was carried out by using a drop weight setup and to inject the prepared semi-solid slurry in optimal conditions into the step-die cavity.The filling behavior and mechanical properties of parts were studied.Microstructural evolution showed that the best semi-solid slurry which had fine spherical particles with the average size of~27μm and a shape factor of~0.8 was achieved at the stirring current of 70 A,melt pouring temperature of 670℃,and stirring time of 30 s.Under these conditions,the step-die cavity was completely filled at die preheating temperature of 470℃.The hardness increases by decreasing step thickness as well as die preheating temperature.Moreover,the tensile properties are improved at lower die preheating temperatures.The fracture surface,which consists of a complex topography,indicates a typical ductile fracture.展开更多
A357-SiCp/A357 layered composites were prepared using a semi-solid vacuum stirring suction casting method.The microstructures,mechanical properties,and thermal conductivities of the composites fabricated under differe...A357-SiCp/A357 layered composites were prepared using a semi-solid vacuum stirring suction casting method.The microstructures,mechanical properties,and thermal conductivities of the composites fabricated under different suction casting processes were compared.Additionally,the microstructural evolution characteristics and performance enhancement mechanism of the A357-SiCp/A357 layered composites were discussed.The results demonstrate that suction casting at 610°C with a low solid phase ratio can significantly enhance the material density and reduce the agglomeration of SiCp.The A357-SiC_(p)/A357 interface is clear and straight with good bonding.With an increase in the suction casting temperature,the bending resistance and thermal conductivity of the A357-SiC_(p)/A357 layered composites exhibit a trend of significantly increase at first and then slowly decrease owing to casting defects,interface bonding,and SiCp distribution.Compared with SiCp/A357 composites,the bending strength,deflection,and thermal conductivity of the A357-SiCp/A357 layered composites increase from 257 MPa,1.07 mm,and 155.72 W·(m·K)^(-1) to 298 MPa,2.1 mm,and 169.86 W·(m·K)^(-1),respectively.This study provides a reference for improving the rheological casting of aluminum matrix layered composites.展开更多
Blockage in the storage and transportation of waste resin is a difficult problem in the radioactive waste treatment process of nuclear power plants.In this study,in order to solve the problems of unstable resin transp...Blockage in the storage and transportation of waste resin is a difficult problem in the radioactive waste treatment process of nuclear power plants.In this study,in order to solve the problems of unstable resin transport concentration and easy blockage of conveying equipment and pipelines in nuclear power plants in China,a set of non⁃stirring conveying devices is developed,and theoretical calculations,simulation analysis and experimental verification are carried out.By transporting resin using the no stirring conveying device developed in this paper,it is not only to eliminate the risk of blockage and ensure the safety of transportation,but also to adjust the concentration of conveying resin to change the transport efficiency according to the operating conditions.The effective bearing rate of waste resin storage tank can be improved,so that the comprehensive performance of waste resin storage and transportation in nuclear power plants can be greatly improved.展开更多
The effects of pouring temperature, short electromagnetic stirring with low strength and then soaking treatment on the microstructure of AISi7Mg alloy were investigated. The results show that if AlSi7Mg alloy is poure...The effects of pouring temperature, short electromagnetic stirring with low strength and then soaking treatment on the microstructure of AISi7Mg alloy were investigated. The results show that if AlSi7Mg alloy is poured at 630 or 650℃ and meanwhile stirred by an electromagnetic field at a low power for a short time, the pouring process can be easily controlled and most solidified primary α-Al grains become spherical and only a few of them are rosette-like. Weak electromagnetic stirring makes the temperature field more homogeneous and makes the primary α-Al grains disperse in a larger region, which leads to the spherical microstructures of primary α-Al grains. When the AISi7Mg alloy is soaked or reheated at the semisolid state, the primary α-Al grains ripen further and they become more spherical, which is favorable to the semi-solid forming of AlSi7Mg alloy.展开更多
To investigate the possibility of substituting the mechanical stirring system with electromagnetic stirring (EMS) system for aluminum rheo die-casting, the EMS under the different stirring cooling conditions was carri...To investigate the possibility of substituting the mechanical stirring system with electromagnetic stirring (EMS) system for aluminum rheo die-casting, the EMS under the different stirring cooling conditions was carried out. It was found that in the early period of solidification, the dendrite breakages led to a fine primary phase. When dendrites grew coarsely, the effect of ripening on grain size overwhelmed that of dendrite breakage. It was also found that the high cooling rate favored large nucleation rate, and led to a fine primary phase. But high cooling rate also made the growth rate of the dendrite arm, which prevented the dendrite arm from being sheared off. Therefore there were a suitable stirring time and suitable cooling rate to obtain the best rheo die-casting structure. Qualified semisolid A356 aluminum alloy was successfully manufactured with short time EMS.展开更多
The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were inve...The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were investigated. The results indicated that the semi-solid slurry to satisfy rheocasting can be manufactured by low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power remarkably affected the morphology of primary α-Al and the size of primary α-Al, and there is no obvious effect of stirring time on primary α-Al. Compared with the samples made by low superheat pouring with no stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 were markedly improved by low superheat pouring and weak electromagnetic stirring. On the condition of weak electromagnetic stirring, the pouring temperature with low superheat can be suitably raised to reach the effectiveness obtained from the lower pouring temperature without stirring.展开更多
The semi-solid slurry of hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature and stirring power on the semi-solid slurry making proc...The semi-solid slurry of hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature and stirring power on the semi-solid slurry making process were investigated. The results indicate that the semi-solid slurry to satisfy rheocasting requirement can be made by a combination of low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power significantly affect the morphology and the size of primary α-Al, while there is no obvious effect of the stirring time on primary α-Al. Compared with the samples made by low superheat pouring without stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 Al alloy are markedly improved by a process of applying both low superheat pouring and weak electromagnetic stirring. Under the condition of weak electromagnetic stirring applied, the pouring temperature with low superheat can be equivalently to reach the effectiveness obtained from the even lower pouring temperature without stirring.展开更多
The semi-solid slurry of A356 alloy, which is grain-refined by Al-Ti-B master alloy, is prepared by low superheat pouring and slight electromagnetic stirring. The effects of grain refining on the morphology and the gr...The semi-solid slurry of A356 alloy, which is grain-refined by Al-Ti-B master alloy, is prepared by low superheat pouring and slight electromagnetic stirring. The effects of grain refining on the morphology and the grain size of the primary α phase in the slurry manufactured are researched. The results indicate that the slurry with particle-like and rosette-like primary α phases can be prepared by low superheat pouring and slight electromagnetic stirring from liquid A356 alloy grain-refined, in which the pouring temperature can be suitably raised. Compared with the A356 samples without grain refining, the grain size and particle morphology of primary α phase as well as the distribution of the grain with particle-like or rosette-like along radial in the ingot in A356 are markedly improved by grain refining.展开更多
A new method for producing semisolid slurry, annular electromagnetic stirring (AEMS), to refine and spheroidize grains was exploited. Experimental work was undertaken to investigate the effects of cooling rate, stir...A new method for producing semisolid slurry, annular electromagnetic stirring (AEMS), to refine and spheroidize grains was exploited. Experimental work was undertaken to investigate the effects of cooling rate, stirring power and stirring time on the solidification behavior of A357 alloy using A-EMS. It was found that increasing the cooling rate and stirring power gave rise to substantial grain refinement, which could be attributed to the increase of effective nucleation rate caused by the extremely uniform temperature and composition fields in the bulk liquid during the initial stage of solidification. Results showed that a fully grain refined spherical structure could be obtained using proper processing conditions within 10 s.展开更多
An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring (M-EMS) was performed, in which the influences of stirring parameters with M-EM...An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring (M-EMS) was performed, in which the influences of stirring parameters with M-EMS on the solidification macrostructure of high carbon steel were investigated. The results show that the billet quality is not well controlled under the condition of working current and frequency with EMS, in which the subsurface crack of grade 1.0-2.0 ups to 38.09%, the central pipe of grade 1.0-1.5 reaches to 14.28%, and the central porosity of grade 1.5 is 14.29%. The parameters of current 260 A and frequency 8 Hz as the final optimum scheme has a remarkable effect for improving the macroscopic quality of billet, in which the subsurface crack, central pipe and skin blowhole are all disappeared, and the central porosity and carbon segregation are also well improved.展开更多
Thixocasting requires manufacturing of billets with non-dendritic microstructure.Aluminum alloy A356 billets were produced by rheocasting in a mould placed inside a linear electromagnetic stirrer.Subsequent heat treat...Thixocasting requires manufacturing of billets with non-dendritic microstructure.Aluminum alloy A356 billets were produced by rheocasting in a mould placed inside a linear electromagnetic stirrer.Subsequent heat treatment was used to produce a transition from rosette to globular microstructure.The current and the duration of stirring were explored as control parameters.Simultaneous induction heating of the billet during stirring was quantified using experimentally determined thermal profiles.The effect of processing parameters on the dendrite fragmentation was discussed.Corresponding computational modeling of the process was performed using phase-field modeling of alloy solidification in order to gain insight into the process of morphological changes of a solid during this process.A non-isothermal alloy solidification model was used for simulations.The morphological evolution under such imposed thermal cycles was simulated and compared with experimentally determined one.Suitable scaling using the thermosolutal diffusion distances was used to overcome computational difficulties in quantitative comparison at system scale.The results were interpreted in the light of existing theories of microstructure refinement and globularisation.展开更多
Solidification cracking that occurs during continuous casting of 1Cr13 stainless steel was investigated with and without final elec- tromagnetic stirring (F-EMS). The results show that cracks initiates and propagate...Solidification cracking that occurs during continuous casting of 1Cr13 stainless steel was investigated with and without final elec- tromagnetic stirring (F-EMS). The results show that cracks initiates and propagates along the grain boundaries where the elements of carbon and sulfur are enriched. The final stirrer should be appropriately placed at a location that is 7.5 m away from the meniscus, and the appropri- ate thickness of the liquid core in the stirring zone is 50 ram. As a stirring current of 250 A is imposed, it can promote colurnnar-equiaxed transition, decrease the secondary dendrite arm spacing, and reduce the segregation of both carbon and sulfur. F-EMS can effectively de- crease the amount of cracks in 1Cr13 stainless steel.展开更多
According to the theory of alternating magnetohydrodynamics and magnetic boundary renewal method,mathematical models were proposed for electromagnetic stirring in secondary cooling region( SEMS) of slab caster. The ma...According to the theory of alternating magnetohydrodynamics and magnetic boundary renewal method,mathematical models were proposed for electromagnetic stirring in secondary cooling region( SEMS) of slab caster. The magnetic fields and flow fields of melt were simulated with SEMS. It's shown that the electromagnetic forces with inward and sidelong components produced by travel magnetic field at the wide faces of slab make the melt whirling in horizontal section,and the convection of the melt is strengthened obviously there. In addition,magnetic flux density attenuates from the edge to the center of slab,and the profile of the melt velocity along slab thickness in the center of the horizontal section takes a two-opposite-peak configuration. Ultimately,the stirring intensity and features are determined by the electromagnetic parameters,coil arrangement and stirring types.展开更多
The 6351 wrought aluminum alloy and K2TiF6-CaF2-LiCl components were selected as raw materials to fabricate in situ Al3Ti particulate reinforced aluminum alloy at 720℃via direct melt reaction method with electromagne...The 6351 wrought aluminum alloy and K2TiF6-CaF2-LiCl components were selected as raw materials to fabricate in situ Al3Ti particulate reinforced aluminum alloy at 720℃via direct melt reaction method with electromagnetic stirring(EMS).CaF2 and LiCl acted as fluxes to lower the reaction temperature of the system.It is shown that the electromagnetic stirring and fluxes accelerate the emulsion process of K2TiF6.Optical microscopy,scanning electron microscopy,transmission electron microscopy and energy dispersive spectrum were utilized to analyze the microstructure and components of composites.Compared to composites fabricated without EMS and fluxes,the sizes of endogenetic Al3Ti are refined from 10-15μm to 2-4μm,which are often accompanied with silicon element.The morphology of Al3Ti or Al3TiSi0.22 exhibits triangle,quadrilateral and other clumpy patterns. Because of the Ca elements from CaF2,the sizes of Mg2Si decrease from 8-10μm to 1-2μm due to the formation of Ca2Si.展开更多
The semisolid AlSi7Mg alloy slurry with large capacity was prepared by low superheat pouring and week traveling-wave electromagnetic stirring. The effects of electromagnetic stirring power and frequency on the shape a...The semisolid AlSi7Mg alloy slurry with large capacity was prepared by low superheat pouring and week traveling-wave electromagnetic stirring. The effects of electromagnetic stirring power and frequency on the shape and distribution of primary α-A1 grains in the AlSi7Mg alloy slurry were discussed. The experimental results show that the AlSi7Mg alloy slurry with fine and spherical primary α-A1 grains distributed homogeneously can be obtained. Under the condition of low superheat pouring and week traveling-wave electromagnetic stirring, when the pouring temperature is 630℃, raising the stirring power or frequency appropriately can gain a better shape of primary α-Al grains; but if the stirring power or frequency is increased to a certain value (1.72 kW or10 Hz), the shape of primary α-A1 grains cannot be obviously improved and spherical primary α-Al grains distributed homogeneously can be still obtained.展开更多
The effects of slight electromagnetic stirring on morphology of primary phase in semisolid A356 prepared by low superheat pouring and slight electromagnetic stirring were researched,and some characteristic parameters ...The effects of slight electromagnetic stirring on morphology of primary phase in semisolid A356 prepared by low superheat pouring and slight electromagnetic stirring were researched,and some characteristic parameters characterized the morphology and grain size of the primary phase were calculated.The results indicate that the stirring power has an important effect on the morphology and the grain size.The characteristics of the morphology could be characterized by the fractal dimensions and the shape factors.The fractal dimension and the shape factor change when the morphology changes with processing conditions.Both increase with the increase of the stirring power,but the fractal dimension is still affected by the grain size.The increase of stirring power could obviously improve the grain size,fractal dimension and shape factor of the primary phase.展开更多
A computational model coupling an electromagnetic model with a macroscopic heat and fluid flow model in semi-solid aluminum alloy slurry preparation by annular electromagnetic stirring(A-EMS) was developed.Effects of ...A computational model coupling an electromagnetic model with a macroscopic heat and fluid flow model in semi-solid aluminum alloy slurry preparation by annular electromagnetic stirring(A-EMS) was developed.Effects of A-EMS processing parameters,such as stirring current,stirring frequency and stirring gap width,on macroscopic transport phenomena during the solidification were analyzed by commercial software ANSYS 10.0 with corresponding experimental verification.The results show that the magnetic flux density and the melt velocity increase and the temperature difference decreases as stirring gap width and stirring frequency decrease or the stirring current increases.The slurry with the fine and uniform globular grain structure can be gained by adjusting gap width,electromagnetic frequency and current,such as under the conditions of 10 mm of gap width,10 Hz of electromagnetic frequency and 50 A of current.The calculated results are in reasonably good agreement with the measured ones.展开更多
The influences of the additive CaF2, different molds, mold pre-heating temperature, electromagnetic stirring, and alloying elements on CuCr have been investigated respectively during the preparation of CuCr alloys by ...The influences of the additive CaF2, different molds, mold pre-heating temperature, electromagnetic stirring, and alloying elements on CuCr have been investigated respectively during the preparation of CuCr alloys by thermit-reduction electromagnetic stirring. The results indicate that the reasonable reactant mass ratio of CuO: Cr2O3:Al is 100:140:160; CaF2 can reduce the solidification point of slags to improve the metal separating efficiency from slags; the crystal particles become thinner because of the high cooling velocity in the metal mold; while casting in the graphite mold, the casting properties of CuCr improve with the increase of pre-heating temperature; the compact alloys are prepared at 500℃; electromagnetic stirring can prevent the growth of dendrite crystal into refine crystal particles, as well as homogenize Cu and Cr to improve the CuCr properties; the optimal stirring time is 7 min; when the alloying elements Ni and Co are added to the reactants, elements Cu and Cr can distribute evenly but the crystal particles become thick.展开更多
In this study,the effect of rotating gas bubble stirring treatment on the microstructures of semi-solid AZ91-2Ca alloy was investigated.The semi-solid slurry was produced by injecting fine gas bubbles into the melt th...In this study,the effect of rotating gas bubble stirring treatment on the microstructures of semi-solid AZ91-2Ca alloy was investigated.The semi-solid slurry was produced by injecting fine gas bubbles into the melt through a rotating steel diffuser during solidification,and the samples of semi-solid slurry were taken by the rapid quenching method.The results show that fine and sphericalα-Mg particles can be obtained under rotating gas bubble stirring treatment.The process parameters such as gas flow rate,cooling rate and rotation speed have significant influence on the morphology of primary solid particles.After rotating gas bubble stirring treatment,the higher the particle density,the finer and rounder the primaryα-Mg particles.The formation of numerous solid particles is due to the combination mechanisms of copious nucleation and dendrite fragmentation.展开更多
基金financially supported by the National Key R&D Projects(No.2021YFB3702000)the Regional Company Projects in Ansteel Beijing Research Institute(No.2022BJB07GF&No.2022BJB-13GF)。
文摘Electromagnetic stirring is one of the widely applied techniques to modify the quality of casting billets.Different from conventional rotate stirring,the helical stirring is more professional in assisting multi-dimensional flow of molten metal and eliminating solidification defects.In this study,the single-winding helical stirring(SWHS)was introduced,offering advantages such as smaller volume and lower electromagnetic shielding compared to traditional helical stirring methods.Following a comprehensive numerical simulation,the stirring parameters of SWHS were adjusted to yoke inclination angle of 43°and frequency of 12 Hz.The higher electromagnetic force and flow velocity in drawing direction,as well as the lower temperature gradient induced by the SWHS,are positive factors for homogeneous solidification of billet.The experimental results on Al-8%Si alloy and 0.4%C-1.1%Mn steel demonstrate that compared to rotate stirring,the SWHS process can induce better billet quality and is more effective in accelerating the equiaxed expansion and reducing element segregation.The SWHS process can enhance the equiaxed ratio of the billet by 58.3%and reduce segregation degree of carbon element by 10.97%.Consequently,SWHS holds great promise as a potential approach for improving the quality of continuous casting billets.
基金Central Applied Research Laboratory(CARL)Center of Materials ResearchDepartment of Materials Science and Metallurgy,Shahid Bahonar University of Kerman(SBUK)for support of this work。
文摘Nowadays,having an effective technique in preparing semi-solid slurries for rheocasting process seems to be an essential requirement.In this study,semi-solid slurry of A356 aluminum alloy was prepared by three-phase annular electromagnetic stirring(A-EMS)technique under different conditions.The effects of stirring current,pouring temperature and stirring time on microstructural evolution,mean particle size,shape factor and solid fraction were investigated.The rheocasting process was carried out by using a drop weight setup and to inject the prepared semi-solid slurry in optimal conditions into the step-die cavity.The filling behavior and mechanical properties of parts were studied.Microstructural evolution showed that the best semi-solid slurry which had fine spherical particles with the average size of~27μm and a shape factor of~0.8 was achieved at the stirring current of 70 A,melt pouring temperature of 670℃,and stirring time of 30 s.Under these conditions,the step-die cavity was completely filled at die preheating temperature of 470℃.The hardness increases by decreasing step thickness as well as die preheating temperature.Moreover,the tensile properties are improved at lower die preheating temperatures.The fracture surface,which consists of a complex topography,indicates a typical ductile fracture.
文摘A357-SiCp/A357 layered composites were prepared using a semi-solid vacuum stirring suction casting method.The microstructures,mechanical properties,and thermal conductivities of the composites fabricated under different suction casting processes were compared.Additionally,the microstructural evolution characteristics and performance enhancement mechanism of the A357-SiCp/A357 layered composites were discussed.The results demonstrate that suction casting at 610°C with a low solid phase ratio can significantly enhance the material density and reduce the agglomeration of SiCp.The A357-SiC_(p)/A357 interface is clear and straight with good bonding.With an increase in the suction casting temperature,the bending resistance and thermal conductivity of the A357-SiC_(p)/A357 layered composites exhibit a trend of significantly increase at first and then slowly decrease owing to casting defects,interface bonding,and SiCp distribution.Compared with SiCp/A357 composites,the bending strength,deflection,and thermal conductivity of the A357-SiCp/A357 layered composites increase from 257 MPa,1.07 mm,and 155.72 W·(m·K)^(-1) to 298 MPa,2.1 mm,and 169.86 W·(m·K)^(-1),respectively.This study provides a reference for improving the rheological casting of aluminum matrix layered composites.
基金Sponsored by the Independent Scientific Research Fund of China Nuclear Power Engineering Co.,Ltd(Grant No.KY1744).
文摘Blockage in the storage and transportation of waste resin is a difficult problem in the radioactive waste treatment process of nuclear power plants.In this study,in order to solve the problems of unstable resin transport concentration and easy blockage of conveying equipment and pipelines in nuclear power plants in China,a set of non⁃stirring conveying devices is developed,and theoretical calculations,simulation analysis and experimental verification are carried out.By transporting resin using the no stirring conveying device developed in this paper,it is not only to eliminate the risk of blockage and ensure the safety of transportation,but also to adjust the concentration of conveying resin to change the transport efficiency according to the operating conditions.The effective bearing rate of waste resin storage tank can be improved,so that the comprehensive performance of waste resin storage and transportation in nuclear power plants can be greatly improved.
基金The work was supported by the National Hitech Research Foundation of China under grant No. G2002AA336080 by the National Natural Science Foundation of China under grant No. 50374012.
文摘The effects of pouring temperature, short electromagnetic stirring with low strength and then soaking treatment on the microstructure of AISi7Mg alloy were investigated. The results show that if AlSi7Mg alloy is poured at 630 or 650℃ and meanwhile stirred by an electromagnetic field at a low power for a short time, the pouring process can be easily controlled and most solidified primary α-Al grains become spherical and only a few of them are rosette-like. Weak electromagnetic stirring makes the temperature field more homogeneous and makes the primary α-Al grains disperse in a larger region, which leads to the spherical microstructures of primary α-Al grains. When the AISi7Mg alloy is soaked or reheated at the semisolid state, the primary α-Al grains ripen further and they become more spherical, which is favorable to the semi-solid forming of AlSi7Mg alloy.
文摘To investigate the possibility of substituting the mechanical stirring system with electromagnetic stirring (EMS) system for aluminum rheo die-casting, the EMS under the different stirring cooling conditions was carried out. It was found that in the early period of solidification, the dendrite breakages led to a fine primary phase. When dendrites grew coarsely, the effect of ripening on grain size overwhelmed that of dendrite breakage. It was also found that the high cooling rate favored large nucleation rate, and led to a fine primary phase. But high cooling rate also made the growth rate of the dendrite arm, which prevented the dendrite arm from being sheared off. Therefore there were a suitable stirring time and suitable cooling rate to obtain the best rheo die-casting structure. Qualified semisolid A356 aluminum alloy was successfully manufactured with short time EMS.
基金The project was financially supported by the Hi-tech Research and Development Program of China (No. G2002AA336080) and the National Natural Science Foundation of China (No. 50374012)
文摘The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were investigated. The results indicated that the semi-solid slurry to satisfy rheocasting can be manufactured by low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power remarkably affected the morphology of primary α-Al and the size of primary α-Al, and there is no obvious effect of stirring time on primary α-Al. Compared with the samples made by low superheat pouring with no stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 were markedly improved by low superheat pouring and weak electromagnetic stirring. On the condition of weak electromagnetic stirring, the pouring temperature with low superheat can be suitably raised to reach the effectiveness obtained from the lower pouring temperature without stirring.
基金The paper is supported by the Hi-tech Research and Develop-ment Program of China (Authorized No.: G2002AA336080), andthe National Natural Science Foundation of China (AuthorizedNo.: 50374012).
文摘The semi-solid slurry of hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature and stirring power on the semi-solid slurry making process were investigated. The results indicate that the semi-solid slurry to satisfy rheocasting requirement can be made by a combination of low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power significantly affect the morphology and the size of primary α-Al, while there is no obvious effect of the stirring time on primary α-Al. Compared with the samples made by low superheat pouring without stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 Al alloy are markedly improved by a process of applying both low superheat pouring and weak electromagnetic stirring. Under the condition of weak electromagnetic stirring applied, the pouring temperature with low superheat can be equivalently to reach the effectiveness obtained from the even lower pouring temperature without stirring.
基金financially supported by National High Technical Research and Development Program of China(No.G2002AA336080)National Natural Science Foundation of China(No.50374012)Natural Science Foundation of Jiangxi Province(No.0650047).
文摘The semi-solid slurry of A356 alloy, which is grain-refined by Al-Ti-B master alloy, is prepared by low superheat pouring and slight electromagnetic stirring. The effects of grain refining on the morphology and the grain size of the primary α phase in the slurry manufactured are researched. The results indicate that the slurry with particle-like and rosette-like primary α phases can be prepared by low superheat pouring and slight electromagnetic stirring from liquid A356 alloy grain-refined, in which the pouring temperature can be suitably raised. Compared with the A356 samples without grain refining, the grain size and particle morphology of primary α phase as well as the distribution of the grain with particle-like or rosette-like along radial in the ingot in A356 are markedly improved by grain refining.
基金supported by National High Technical Research and Development Program of China (No.2009AA03Z534)National Basic Research Program of China (No.2006CB605203)
文摘A new method for producing semisolid slurry, annular electromagnetic stirring (AEMS), to refine and spheroidize grains was exploited. Experimental work was undertaken to investigate the effects of cooling rate, stirring power and stirring time on the solidification behavior of A357 alloy using A-EMS. It was found that increasing the cooling rate and stirring power gave rise to substantial grain refinement, which could be attributed to the increase of effective nucleation rate caused by the extremely uniform temperature and composition fields in the bulk liquid during the initial stage of solidification. Results showed that a fully grain refined spherical structure could be obtained using proper processing conditions within 10 s.
基金supported by the Program for New Century Excellent Talents in University from the Ministry of Education of China (No.NCET-04-0285)
文摘An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring (M-EMS) was performed, in which the influences of stirring parameters with M-EMS on the solidification macrostructure of high carbon steel were investigated. The results show that the billet quality is not well controlled under the condition of working current and frequency with EMS, in which the subsurface crack of grade 1.0-2.0 ups to 38.09%, the central pipe of grade 1.0-1.5 reaches to 14.28%, and the central porosity of grade 1.5 is 14.29%. The parameters of current 260 A and frequency 8 Hz as the final optimum scheme has a remarkable effect for improving the macroscopic quality of billet, in which the subsurface crack, central pipe and skin blowhole are all disappeared, and the central porosity and carbon segregation are also well improved.
文摘Thixocasting requires manufacturing of billets with non-dendritic microstructure.Aluminum alloy A356 billets were produced by rheocasting in a mould placed inside a linear electromagnetic stirrer.Subsequent heat treatment was used to produce a transition from rosette to globular microstructure.The current and the duration of stirring were explored as control parameters.Simultaneous induction heating of the billet during stirring was quantified using experimentally determined thermal profiles.The effect of processing parameters on the dendrite fragmentation was discussed.Corresponding computational modeling of the process was performed using phase-field modeling of alloy solidification in order to gain insight into the process of morphological changes of a solid during this process.A non-isothermal alloy solidification model was used for simulations.The morphological evolution under such imposed thermal cycles was simulated and compared with experimentally determined one.Suitable scaling using the thermosolutal diffusion distances was used to overcome computational difficulties in quantitative comparison at system scale.The results were interpreted in the light of existing theories of microstructure refinement and globularisation.
基金financially supported by the National Natural Science Foundation of China (No. 50834009)the Key Project of the Ministry of Education of China (No. 311014)the 111 Project of China (No. B07015)
文摘Solidification cracking that occurs during continuous casting of 1Cr13 stainless steel was investigated with and without final elec- tromagnetic stirring (F-EMS). The results show that cracks initiates and propagates along the grain boundaries where the elements of carbon and sulfur are enriched. The final stirrer should be appropriately placed at a location that is 7.5 m away from the meniscus, and the appropri- ate thickness of the liquid core in the stirring zone is 50 ram. As a stirring current of 250 A is imposed, it can promote colurnnar-equiaxed transition, decrease the secondary dendrite arm spacing, and reduce the segregation of both carbon and sulfur. F-EMS can effectively de- crease the amount of cracks in 1Cr13 stainless steel.
基金Item Sponsored by National Key Fundamental Research Development Project of China(G1998061510)National High Technology Research and Development Project of China(2001AA337040)
文摘According to the theory of alternating magnetohydrodynamics and magnetic boundary renewal method,mathematical models were proposed for electromagnetic stirring in secondary cooling region( SEMS) of slab caster. The magnetic fields and flow fields of melt were simulated with SEMS. It's shown that the electromagnetic forces with inward and sidelong components produced by travel magnetic field at the wide faces of slab make the melt whirling in horizontal section,and the convection of the melt is strengthened obviously there. In addition,magnetic flux density attenuates from the edge to the center of slab,and the profile of the melt velocity along slab thickness in the center of the horizontal section takes a two-opposite-peak configuration. Ultimately,the stirring intensity and features are determined by the electromagnetic parameters,coil arrangement and stirring types.
基金Project(2007AA03Z548)supported by the National High-Tech Research and Development Program of ChinaProject(207038)supported by the Key Program of Ministry of Education of China+3 种基金Project(06-D-021)supported by the Talents Peak in Six Key Fields of Jiangsu Province in ChinaProject(07JDG084)supported by the Technical Enablement Foundation for the Super Special Talents of Jiangsu UniversityProject(20071108)supported by the Technical Enablement Foundation of Ministry of Education for the Returned ScholarsProject(20060299006)supported by the PhD Programs Foundation of Ministry of Education of China
文摘The 6351 wrought aluminum alloy and K2TiF6-CaF2-LiCl components were selected as raw materials to fabricate in situ Al3Ti particulate reinforced aluminum alloy at 720℃via direct melt reaction method with electromagnetic stirring(EMS).CaF2 and LiCl acted as fluxes to lower the reaction temperature of the system.It is shown that the electromagnetic stirring and fluxes accelerate the emulsion process of K2TiF6.Optical microscopy,scanning electron microscopy,transmission electron microscopy and energy dispersive spectrum were utilized to analyze the microstructure and components of composites.Compared to composites fabricated without EMS and fluxes,the sizes of endogenetic Al3Ti are refined from 10-15μm to 2-4μm,which are often accompanied with silicon element.The morphology of Al3Ti or Al3TiSi0.22 exhibits triangle,quadrilateral and other clumpy patterns. Because of the Ca elements from CaF2,the sizes of Mg2Si decrease from 8-10μm to 1-2μm due to the formation of Ca2Si.
基金supported by the National High-Tech Research and Development Program of China (No.2006AA03Z115)the National Basic Research Priorities Program of China (No.2006CB605203)the National Natural Science Foundation of China (No.50374012)
文摘The semisolid AlSi7Mg alloy slurry with large capacity was prepared by low superheat pouring and week traveling-wave electromagnetic stirring. The effects of electromagnetic stirring power and frequency on the shape and distribution of primary α-A1 grains in the AlSi7Mg alloy slurry were discussed. The experimental results show that the AlSi7Mg alloy slurry with fine and spherical primary α-A1 grains distributed homogeneously can be obtained. Under the condition of low superheat pouring and week traveling-wave electromagnetic stirring, when the pouring temperature is 630℃, raising the stirring power or frequency appropriately can gain a better shape of primary α-Al grains; but if the stirring power or frequency is increased to a certain value (1.72 kW or10 Hz), the shape of primary α-A1 grains cannot be obviously improved and spherical primary α-Al grains distributed homogeneously can be still obtained.
基金Project (50774007) supported by the National Natural Science Foundation of ChinaProject (0650047) supported by the National Natural Science Foundation of Jiangxi ProvinceProject(GJJ09229) supported by Science and Technology Program of the Education Department of Jiangxi Province
文摘The effects of slight electromagnetic stirring on morphology of primary phase in semisolid A356 prepared by low superheat pouring and slight electromagnetic stirring were researched,and some characteristic parameters characterized the morphology and grain size of the primary phase were calculated.The results indicate that the stirring power has an important effect on the morphology and the grain size.The characteristics of the morphology could be characterized by the fractal dimensions and the shape factors.The fractal dimension and the shape factor change when the morphology changes with processing conditions.Both increase with the increase of the stirring power,but the fractal dimension is still affected by the grain size.The increase of stirring power could obviously improve the grain size,fractal dimension and shape factor of the primary phase.
基金Project(2006CB605203) supported by National Basic Research Program of ChinaProject(2009AA03Z534) supported by the National Hi-tech Research and Development Program of China
文摘A computational model coupling an electromagnetic model with a macroscopic heat and fluid flow model in semi-solid aluminum alloy slurry preparation by annular electromagnetic stirring(A-EMS) was developed.Effects of A-EMS processing parameters,such as stirring current,stirring frequency and stirring gap width,on macroscopic transport phenomena during the solidification were analyzed by commercial software ANSYS 10.0 with corresponding experimental verification.The results show that the magnetic flux density and the melt velocity increase and the temperature difference decreases as stirring gap width and stirring frequency decrease or the stirring current increases.The slurry with the fine and uniform globular grain structure can be gained by adjusting gap width,electromagnetic frequency and current,such as under the conditions of 10 mm of gap width,10 Hz of electromagnetic frequency and 50 A of current.The calculated results are in reasonably good agreement with the measured ones.
基金This work was financially supported by the National Natural Science Foundation of China (No.50374026, 50644016)
文摘The influences of the additive CaF2, different molds, mold pre-heating temperature, electromagnetic stirring, and alloying elements on CuCr have been investigated respectively during the preparation of CuCr alloys by thermit-reduction electromagnetic stirring. The results indicate that the reasonable reactant mass ratio of CuO: Cr2O3:Al is 100:140:160; CaF2 can reduce the solidification point of slags to improve the metal separating efficiency from slags; the crystal particles become thinner because of the high cooling velocity in the metal mold; while casting in the graphite mold, the casting properties of CuCr improve with the increase of pre-heating temperature; the compact alloys are prepared at 500℃; electromagnetic stirring can prevent the growth of dendrite crystal into refine crystal particles, as well as homogenize Cu and Cr to improve the CuCr properties; the optimal stirring time is 7 min; when the alloying elements Ni and Co are added to the reactants, elements Cu and Cr can distribute evenly but the crystal particles become thick.
基金This project is sponsored by National Natural Science Foundation of China(No.51275295)Funded Projects of SAST-SJTU Joint Research Centre of Advanced Aerospace Technology(No.USCAST2012-15)Research Fund for the Doctoral Program of Higher Education of China(No.20120073120011).
文摘In this study,the effect of rotating gas bubble stirring treatment on the microstructures of semi-solid AZ91-2Ca alloy was investigated.The semi-solid slurry was produced by injecting fine gas bubbles into the melt through a rotating steel diffuser during solidification,and the samples of semi-solid slurry were taken by the rapid quenching method.The results show that fine and sphericalα-Mg particles can be obtained under rotating gas bubble stirring treatment.The process parameters such as gas flow rate,cooling rate and rotation speed have significant influence on the morphology of primary solid particles.After rotating gas bubble stirring treatment,the higher the particle density,the finer and rounder the primaryα-Mg particles.The formation of numerous solid particles is due to the combination mechanisms of copious nucleation and dendrite fragmentation.