In this paper, the NU308 bearing rings were subjected to strengthen grinding treatment (SGT) at ambient temperature. And the running reliabilities of specimens that subjected to SGT and conventional treatment (CT) wer...In this paper, the NU308 bearing rings were subjected to strengthen grinding treatment (SGT) at ambient temperature. And the running reliabilities of specimens that subjected to SGT and conventional treatment (CT) were respectively investigated by testing dynamic properties including the running temperature, vibrations, and surface burning. Moreover, the residual stress, microtopography, and microstructures on the cross-section were respectively tested with residual stress analyzer and field-emission scanning electron microscopy. The results showed that the running reliabilities of the specimen after SGT had been significantly improved with the reduction of running temperature, vibration, and surface burning. Further study showed that the specimen’s surface was filled with disordered micropores after SGT compared to the regular strip texture on the CT specimen’s surface, and the maximum residual compressive stress induced by SGT was about −900 MPa. Moreover, the thickness of the residual compressive stress layer was over 180 µm, while the thickness of severe plastic deformation layer was about 50 µm.展开更多
文摘In this paper, the NU308 bearing rings were subjected to strengthen grinding treatment (SGT) at ambient temperature. And the running reliabilities of specimens that subjected to SGT and conventional treatment (CT) were respectively investigated by testing dynamic properties including the running temperature, vibrations, and surface burning. Moreover, the residual stress, microtopography, and microstructures on the cross-section were respectively tested with residual stress analyzer and field-emission scanning electron microscopy. The results showed that the running reliabilities of the specimen after SGT had been significantly improved with the reduction of running temperature, vibration, and surface burning. Further study showed that the specimen’s surface was filled with disordered micropores after SGT compared to the regular strip texture on the CT specimen’s surface, and the maximum residual compressive stress induced by SGT was about −900 MPa. Moreover, the thickness of the residual compressive stress layer was over 180 µm, while the thickness of severe plastic deformation layer was about 50 µm.