Influence of the Partial Substitution of Bitumen by a Mixture of Sulphur and Tyre and Plastic Bottle Powders on the Behaviour of Bituminous Concrete

This article deals with the influence of the partial substitution of bitumen by a mixture of sulphur and tyre and plastic bottle powders on the characterization of asphalt concrete. The approach adopted was to subject a control asphalt concrete to level 2 formulation tests as well as those modified at 10%, 20%, 30% and 40% by substituting bitumen with a mixture of tyre powder, plastic bottle powder and sulphur at 40%, 28% and 32% respectively. The results of the PCG, Duriez and rutting tests carried out on the control and modified bituminous concretes (manufactured using the wet process) revealed three (03) major findings, in particular with regard to workability, resistance to simple compression and rutting. The experimental results show an increasing trend in the essential parameters. At 40% substitution, there was a 22.73% increase in compactness, reflecting a significant improvement in the material’s workability. With regard to simple compressive strength, the increase is 34.02% at 40% substitution, highlighting the limitation of crack formation and propagation under heavy precipitation. With regard to rutting, the 16% drop in susceptibility at 40% substitution reflects a significant improvement in the behaviour of the material under dynamic mechanical stresses in heavy precipitation. The improvement in these behaviours results from the insertion of the plastic bottle powder into the interstices of the granular skeleton, thus reducing its cellular structure, and also from the interactions between the sulphur with the tyre powder and the sulphur with the plastic bottle powder, i.e. cross-linking or vulcanisation.

Lignite oxidative desulphurization Notice 1.Process condition selection

The process of lignite desulphurization via its treatment by an oxidant(air or air–steam mixture)has been studied.The research objective was useful determination of steam application in oxidative lignite desulphurization.It has been proved that the water steam should be included in the oxidant composition to increase the hydrogen sulphide and combustible constituent content in the gases obtained during the processes under research.The impact of factors which affect the reactions between solid(in our case–lignite)and gaseous reagent(oxidant,i.e.air and or air–steam mixture)upon the research process has been investigated,if these reactions occur in the kinetic area.Such factors are linear rate of oxidant movement and coal grain size.The values of oxidant movement linear rate and coal grain size,which the reaction transfer from pyrite sulphur and organic content of lignite from diffusion into kinetic area occurs by,have been determined.Under these‘‘transfer’’conditions,the values of coefficients of oxidant mass transfer(β,m/s)as well as Sherwood criteria and boiling layer differences have been calculated.

Study of oxidative desulphurization process of coal with different metamorphism degrees

The oxidative desulphurization process of coal with different metamorphism degrees treated by an air-steam mixture has been studied.It has been shown that the pyrite present in black coal and anthracite is oxidized with the sulphur dioxide formation,and the process chemical mechanism does not depend on the quality of organic matter.The medium-metamorphized coal,capable of turning into a plastic state and cake in the range of investigated temperatures(350～450 ℃),is desulphurized with the greatest difficulty.The chemical mechanism dealing with the transformations of pyritic sulphur present in brown coal differs from similar processes taking place in black coal and anthracite,because FeS2 is converted with hydrogen sulphide formation at desulphurization.

Experimental Research on Refining Slag Systems Containing BaO for Ultra-Low Sulphur Steel

The experimental research on refining slag systems for ultra-low sulphur steel was carried out in a 10 kg induction furnace.It was proved that sulphur element in molten steel can be removed to less than 5×10^(-6) by adding CaO-Al_2O_3-SiO_2-MgO-CaF_2 slag on the surface of molten steel and feeding CaO-BaO-CaF2 wire into molten steel.And L_s,which is the coefficient of sulphur between slag and molten steel,that is ω(s)/ω[s],increases by increasing I(I = ωBaO/ωCaO).When I=5/3,L_s can be up to its maximum of 633.The CaSi is effective for deep desulphurization,especially when it is added to the slag of wire feeding.

Influence of Sulphur Fertilizer on Sulphur Cycling and Its Implications on Sulphur Fertilizer Requirement of Grazed Pasture in Warm Seasonal Rangeland of Nei Monggol Steppe of China

Sulphur (S) cycling and implications on S fertilizer requirement in sheep-grazed pastures receiving three levels of S fertilizer at rates of 0, 30 and 60 kg S/hm 2 in 1995 and 1996 were studied using a mass-balance approach which accounted both for S inputs to and outputs from the soil-plant-animal system. Results indicated that S fertilizer increased by 50% of herbage S uptake and 15% or more of S bio-cycling rate in grazing system. The total S recovery of 30 and 60 kg S/hm 2 treatments from 1995 to 1996 was 74.0% and 37.6% respectively. Mineralization of organic S may be an important source of S for pasture when other S sources are low, accounted for 70% of the total S inputs without S fertilizer. The grazing sheep has an important ecological function, the feature of S cycling in grazed pastures was that 90% of herbage S ingested by grazing sheep was returned to soils as excreta. The amount of S released by sheep excreta accounted about 30% of the total released S through S bio-recycling. Loss from soil S leaching beyond the major plant rooting zone was the main S output from grazing system. However, urinary and fecal S losses, including transfer and leaching losses, also affected S budgets of grazing system. It is therefore important to investigate the recycling rate of both urinary and fecal S under field conditions. Based on the mass-balance principle, at least 10 kg S/hm 2 per year may be necessary for sustainable development of grazing system.

Study on Dyeing Performance of Cationic Water-soluble Sulphur Black on Silk

A novel polyquaternaryammonium cationic sulphur black dye was synthesized and its dyeing behavior on silk was studied. The dye exhibited excellent dyeing fixation of up to 98.2 %, as well as excellent dyeing fastness on silk.

Lignite oxidative desulphurization. Notice 2： effects of process parameters

The influence of main characteristics upon conversion directions of the lignite organic part during its oxidation desulphurization was studied. The optimum temperature values, the ratio oxidant ： raw material, and time of coal stay in the reaction zone, which provide the maximum degree of sulphur conversion and hydrogen sulphide content in desulphur- ization gases, were calculated. The process implemented under these conditions will decrease environment pollution by sulphur dioxide during further lignite burning at least to 55 %-60 % and utilize sulphur in coal in the form of desul- phurization gases with hydrogen sulphide content of 7 %. Such obtaining sulphur. The effect of the above three factors on the depth was studied. gases can be reprocessed by the known methods of and character of the coal organic matter transformation

Perspective on ultramicroporous carbon as sulphur host for Li-S batteries

Lithium-sulphur(Li-S)batteries are currently considered as next-generation battery technology.Sulphur is an attractive positive electrode for lithium metal batteries,mainly due to its high capacity(1675 m Ah g^(-1))and high specific energy(2600 Wh kg^(-1)).The electrochemical reaction of lithium with sulphur in non-aqueous electrolytes results in the formation of electrolyte soluble intermediate lithium-polysulphides.The dissolved polysulphides shuttle to the anode and get reduced at the anode resulting in Li metal corrosion.The solubility of polysulphide gradually reduces the amount of sulphur in the cathode,thereby limiting the cycle life of Li-S batteries.Several strategies have been proposed to improve the cycling stability of Li-S batteries.A unique approach to eliminate the polysulphide shuttle is to use ultramicroporous carbon(UMC)as a host for sulphur.The pore size of UMC which is below 7A,is the bottleneck for carbonate solvents to access sulphur/polysulphides confined in the pores,thereby preventing the polysulphide dissolution.This perspective article will emphasise the role of UMC host in directing the lithiation mechanism of sulphur and in inhibiting polysulphide dissolution,including the resulting parasitic reaction on the lithium anode.Further,the challenges that need to be addressed by UMC-S based Li-S batteries,and the strategies to realise high power density,high Coulombic efficiency,and resilient Li-S batteries will be discussed.

Effect of hydrodynamic desulphurisation of low parameters on the oxidative rank coal

In this paper, the desulphurisation of high sulphur low-rank coal is proposed as a raw material for pulverised coal injection technology. Therefore, the influence of oxidant linear velocity and the size of the coal grain was investigated in a fluidised bed. The hydrodynamic parameters of the fluidised bed including： porosity, Sherwood criterion （diffusion Nusselt number）, and mass transfer coefficient （external surface） were calculated. Furthermore, the study examined the effects of intensity and efficiency on the desulphurised coal properties; organic matter, ash, and volatile matter contents. The key changes during the conversion of pyritic sulphur and coal organic matter were subsequently examined. The results showed that the sulphur content （St^d 3.16 wt%） of the low-rank coal, was transformed to （St^d 〈 1.5 wt%） after desulfurization. Other enhanced properties were： V^daf ≤ 38.0 wt%; A^d 〈 10.0 wt%, now suitable for pulverised coal injection technology.

Preparation of Cs-Rb-V series sulphuric acid catalyst

Cs Rb V series low temperature sulphuric acid catalyst was prepared for the first time by using carbonized mother liquor containing alkali metal salts. The results show that the conversion of SO 2 on catalyst prepared directly with carbonized mother liquor could reach to 24.8% at 410?℃. If n (Na)/ n (V) was adjusted properly, the conversion of SO 2 could be increased to 35.6% at 410?℃. Refined carbonized mother liquor could make the catalytic activity even higher at low temperature, the conversion of SO 2 could be increased to 36.65% at 410?℃. The catalyst was examined with differential thermal analysis. It was found that both endothermic peaks and exothermic peaks of catalyst shifted forward obviously and the catalyst possessed higher activity at low temperature.

Lignite oxidative desulphurization: notice 3-process technological aspects and application of products

The study reviews the process of oxidative desulphurization of high-sulphur Ukrainian lignite, which was performed by coal treatment using an air or air-steam mixture. In the process. sulphur-free fuel and tar from the decomposition of coal organic matter was obtained. Hence, the sulphur in the coal was converted inlo hydrogen sulphide. The coal desulphurization process is critical to power generatio n. power generation and technology, and tech no logy field of application. The coal desulphurization process ensures the maximum recovery of the highest content of sulphur and hydrogen sulphide (H2S) in desulphurized gases at minimal energy costs. The process also enhances the maximum decomposition of tar and sulphur recovery (> 50%) during coal power generation. Based on smnniarized field studies, a block schematic diagram coupled with heat and material balances of the process was developed for the calculations. The application of the tech no logy at the first stage of coal combustion in thermal power plants will en able the utilizatio n of over 50% of recovered coal sulphur in the form of concentrated H2S or commercial elemental sulphur. This will, nevertheless, allow for a reduction of sulphur oxide pollution in the environment by at least 53%-56%. It has been suggested that the product of thermal decomposition of coal organic matter (tar) can be used as a componenl of fumace fuel oil or as a plasticizer of petroleum-based road bitumen.

Analysis and Producing Causes of Available Sulphur Status quo(Rich or Insufficient) in Farmlands and Countermeasures in Dengzhou City

In the research, available sulphur in 4 700 soil samples was tested and analyzed in 2006-2007 in Dengzhou, and the results showed that available sulphur was insufficient in farmlands in Dengzhou for cereal crop and about 60% farmlands with available sulphur belong to the farmlands with potential shortage of available sulphur for Cruciferae, Liliaceae and Leguminosae. Meanwhile, the producing causes were analyzed from the perspectives of fertilization structure and planting structure and the countermeasures were proposed in terms of sulphur movements in plants and characters.

The Ionization Theory of Desulphurization of the Panzhihua Blast Furnace Slag

With the proper choice of the ion species present in the Panzhihua blast furnace slag, the sulphur partition ratio was calculated based on the ionization theory of the slag. It can be concluded that TiO_2 reacts as an acidtc oxide and the Panzhihua ore or concentrate cannot be treated as a semi-self-fluxing ore.

Sulphur Status in Some Surface Horizons and Typical Profiles of Soils Derived from Xiashu Loess in China

Studies were conducted to examine factors which might influence the status and distribution of S insome surface horizons and typical profiles of soils derived from Xiashu loess on the upper.slope (US), middleslope (MS) and lower slope (LS) of Nanjing-Zhenjiang-Yangzhou hilly zone. The total S contents varied from70.30 to 350.21 mg/kg, and the average for all surface soils was 218.3 mg/kg. The average S contents inthe profiles followed the sequence: US<MS<LS. The total S was closely correlated with organic S, inorganicS, organic matter, total N, amorphous iron oxide (Fe_o) and the ratio of amorphous iron oxide to free ironoxide (Fe_o/Fe_a), but no significant relationship was found between total S and the ratio of free iron oxideto total iron (Fe_d/Fe_t). Inorganic sulphate in paddy soils (MS and LS) was nearly higher in surface soilthan in subsurface soil and subsoil, it, however, remained relatively unchanged with increasing depth for theoriginal soil profile (US). The average organic S accounted for 94% of the total S in the surface soils, butthe percentage decreased with depth in the profiles. Like the total S, the organic and inorganic S contentswere highly significantly correlated with organic matter, total N, Fe. and Fe_o/Fe_d ratio, but they wereinsignificantly related to Fe_d/Fe_t ratio. The C/S and N/S ratios in this study were somewhat lower thanthe results reported by others. The C/N/S ratios varied considerably within the same profile and amongdifferent soils but they fell within the range of values reported worldwide.

Sulfidation roasting of lead and zinc carbonate with sulphur by temperature gradient method

In order to enhance the lead and zinc recovery from the refractory Pb-Zn oxide ore, a new technology was developed based on sulfidation roasting with sulphur by temperature gradient method. The solid-liquid reaction system was established and the sulfidation thermodynamics of lead and zinc carbonate was calculated with the software HSC 5.0. The effects of roasting temperature,molar ratio of sulphur to lead and zinc carbonate and reaction time in the first step roasting, and holding temperature and time in the second roasting on the sulfidation extent were studied at a laboratory-scale. The experimental results show that the sulfidation extents of lead and zinc are 96.50% and 97.29% under the optimal conditions, respectively, and the artificial galena, sphalerite and wurtzite were formed. By the novel sulfidizing process, it is expected that the sulphides can be recovered by conventional flotation technology.

Leaching Mechanism of the Spodumene Sulphuric Acid Process

Leaching mechanism of acid roasted ore in the spodumene sulphuric acid process was investigated. Experimental results of leaching rates along with variations of leaching temperature in the acidized and neutral leaching processes were reported. Applying ion exchange mechanism in acidized roasting and absorption entrainment mechanism at high temperature, leaching mechanism was discussed. A better explanation of experimental results was given.

Role of dissolved oxygen reduction in improvement inhibition performance of ascorbic acid during copper corrosion in 0.50 mol/L sulphuric acid

The kinetics of dissolved O_2 reduction and hydrogen evolution reactions on copper surface was studied in naturally aerated and air and O_2-saturated 0.50 mol/L H_2SO_4 solutions using polarization measurements combined with the rotating disc electrode (RDE).The Koutecky-Levich plot indicated that the dissolved O_2 reduction at the copper electrode was an apparent four-electron process.A correlation between the presence of dissolved O_2 and the formation of Cu_2O,confirmed from XRD,was discussed. Ascorbic a...

Tribology properties of composite layer of CrMoCu alloy cast iron by combined treatment of ion nitrocarburizing and sulphurizing

Composite layer with nitrocarbonide and sulfide was made on the surface of CrMoCu alloy cast iron by combined treatment of ion nitrocarburizing and sulphurizing. The composite layer is composed of sulfide layer, nitrocarbonide hypo-surface layer and its diffusing layer, the size of sulfide globular grains distributing equably on the surface is in nano-micron-scale, and the phase structure of the composite layer is composed of FeS, FeS1-x, Fe2C and Fe3N. Under oil lubrication, sulphurized surface shows good scuffing-resistance only under low velocity, and nitrocarburized and sulphurized surface greatly improves the scuffing-resistance and wear-resistance of CrMoCu alloy cast iron, its integrated friction and wear properties are better than those of the plain and sulphurized surfaces under all the velocities.

Post-sulphuration enhances the performance of a lactone polymer donor

Remarkable progress has been made in conjugated copoly-mer donors due to the development of novel fused-ring ac-ceptor(FRA)building units[1−15].The copolymers based on FRA units have delivered excellent power conversion efficien-cies(PCEs)up to 18.69%in organic solar cells(OSCs)[16].Fused-ring aromatic lactones are promising FRA units[17−19].

Effect of Sulphur in Rainfall, Irrigation Waterand Perco colating Water on Soil Sulphur in Jiangxi Province

Ten rainfall and irrigation water-collecting posts were set up in different ecotype districts of JiangxiProvince, China, to quarterly measure S content in rainfall and irrigation water. A rainwater chemicalcomposition- collecting device was used to collect the sulphur in rainfall land the amount of sulphur adsorbedon the resin column in the device was determined. The soil percolating water was gathered using 6 lysimeters,built up according to the profile sequence of the red soil derived from red sandstone and the red soil derivedfrom Quaternary red clay, separately. On the lysimeters peanuts, soybean and radish were grown in rotation.Two treatments were designed: without S addition and with S addition at a rate of 14 kg S ha-1. The SO24contents in rainfall, irrigation water and soil percolating water were determined by the turbidimetry.The results in 1997 showed that the average annual S content in rainwater was 28.13 kg S ha-1, theaverage S content in irrigation water was 1.7 mg S L-1 , and the average content of in soil percolationwater was 2.30 kg S ha-1 year-1 and 4.70 kg S ha-l year-1 in treatments without and with sulphurapplication, respectively. In Jiangxi Province, apart from the losses by runoff and leaching, the sulphur inrainfall available to crops is 7.3 kg S ha-1 year-1 and additional S application is required. When rice isgrown , however, irrigation water can supply 6.9 kg S ha-1, which, along with the sulphur in rainfall, canalmost meet the S requirement of one cropping of rice.