Poly N-isopropyl acrylamide (abbreviated as PNIPA) as a kind of thermally sensitive hydrogel is utilized to concentrate Bovin Serum Albumin (BSA) solution. In order to decrease its surface adsorption to BSA in aqueous...Poly N-isopropyl acrylamide (abbreviated as PNIPA) as a kind of thermally sensitive hydrogel is utilized to concentrate Bovin Serum Albumin (BSA) solution. In order to decrease its surface adsorption to BSA in aqueous solution, surface layer grafting of the gels by radiation technology was carried out. The results showed that hydroxyl propyl methacrylate (HPMA) grained gel exhibited a low level of BSA adsorption and still kept the original thermally sensitive properties of PNIPA hydrogels.展开更多
Low density polyethylene film surface-grafted phenolic resole was prepared by a sequential processes. Firstly, acrylic acid was grafted to the surface of low density polyethylene by photo-grafting. Secondly, the carbo...Low density polyethylene film surface-grafted phenolic resole was prepared by a sequential processes. Firstly, acrylic acid was grafted to the surface of low density polyethylene by photo-grafting. Secondly, the carboxylic groups in poly(acrylic acid) chains were transferred to sulfonic groups by the reaction of carboxylic groups with sulfanilic acid. Finally, a thin layer of phenolic resole was cured onto the surface of low density polyethylene. The grafting process was characterized by FTIR-ATR and gravimetric analysis. A possible model was proposed to interpret the experimental results.展开更多
In order to control the surface pore sizes of polyvinylidene fluoride membranes and their distribution, low temperature plasma-induced grafting modifications of PVDF were studied to prepare hydrophobe membranes. By ar...In order to control the surface pore sizes of polyvinylidene fluoride membranes and their distribution, low temperature plasma-induced grafting modifications of PVDF were studied to prepare hydrophobe membranes. By argon (Ar) treating and subsequent grafting reaction, a hydrophobe monomer, styrene, was introduced into the PVDF membrane. Fourier transform infrared attenuated total reflection (FTIR-ATR) was utilized to characterize the chemical and physical changes in the Ar plasma modified membrane. The surface modifications of PVDF membranes were investigated by using scanning electron microscopy (SEM), atomic force microscopy (AFM) and differential scanning calorimeter (DSC). The water permeability and the solute rejection were measured by PVDF membrane modified in different graft conditions. Results demonstrated that the pores in the modified membranes get smaller and the distribution of pores gets narrowed with the increase in grafting reaction duration. Longer graft time caused the water flux of PVDF membrane to decrease from 578 kg/(m^2· h) to 23 kg/(m^2· h) and the solute rejection to increase from 73% to 92%.展开更多
A new process for lamination of polymer films by 'bulk surface photografting' has been developed. The chemical component of the invention is that the curing of reactive solution between two substrates is initi...A new process for lamination of polymer films by 'bulk surface photografting' has been developed. The chemical component of the invention is that the curing of reactive solution between two substrates is initiated by the surface free radicals produced by aromatic ketones and surface-hydrogen of substrates. Using the new approach, two or more polymer films are bonded together by a grafted polymer network which is grafted to adjacent substrate surfaces. The technique has been applied to film substrates of different polymers such as polyolefins, polyesters, and polyamides which have abstractable hydrogens at the surface. The photolaminated film composites containing carrier films and an intermediate functional film of low permeability give strong laminates with high barrier properties, e.g, for oxygen and air.展开更多
Photoinduced grafting of acrylic and allyl monomers on polyethylene surface was generally studied by using benzophenone (BP) as a photoinitiator. The grafting process was carried out either in vapor-phase or in soluti...Photoinduced grafting of acrylic and allyl monomers on polyethylene surface was generally studied by using benzophenone (BP) as a photoinitiator. The grafting process was carried out either in vapor-phase or in solution of the monomers. In the vapor-phase reaction with a filter used to cut off the short wavelength UV light, allyl amine is the most reactive of the four monomers used and acrylic amide is comparatively more reactive than acrylic acid and allyl alcohol. Acetone, as a solvent and carrier for initiator and monomers, however, shows its reactivity to participate the reaction. The solution grafting with a filter is much faster than the corresponding vapor-phase reaction, and a fully covered surface by the grafted polymer can be achieved in this way.展开更多
This work aimed at investigating the feasibility of surface modification of cellulose nanocrystals (CNCs) using <em>in situ</em> ring opening polymerization of <em>ε</em>-caprolactone (<em&...This work aimed at investigating the feasibility of surface modification of cellulose nanocrystals (CNCs) using <em>in situ</em> ring opening polymerization of <em>ε</em>-caprolactone (<em>ε</em>-CL) at room temperature. Residues of flax and milkweed (<em>Asclepias syriaca</em>) stem fibers were used as a source of cellulose to obtain and isolate CNCs. The cationic ring opening polymerization (CROP) of the monomer <em>ε</em>-CL was used to covalently graft polycaprolactone (PCL) chains at the CNCs surface. Silver hexafluoroantimonate (AgSbF<sub>6</sub>) was used in combination with the extracted CNCs to initiate, at room temperature, the polymerization and the grafting reactions with no other stimulus. Fourier-Transform InfraRed (FTIR), X-ray Photoelectron Spectrometry (XPS), UV/visible absorption and Gel Permeation Chromatography (GPC) analyses evidenced the presence of PCL chains covalently grafted at CNCs surface, the formation of Ag(0) particles as well as low or moderate molecular weight free PCL chains.展开更多
Two grafting methods, i.e. solution grafting and pre-adsorbing, are introduced to covalently immobilizehydrophilic polymers on segmented polyurethane (SPU) to modify its hydrophilicity and to improve its cell compatib...Two grafting methods, i.e. solution grafting and pre-adsorbing, are introduced to covalently immobilizehydrophilic polymers on segmented polyurethane (SPU) to modify its hydrophilicity and to improve its cell compatibility.Solution grafting results in higher degree of grafting and rougher surface morphology. Cell culture evaluation demonstratesthat the modified membranes thus obtained are disadvantageous to the endothelial cell (ECs) growth probably because thehydrophilic groups on the surface are over-crowded. However, pre-absorbing grafting generates lower degree of grafting,which is detected and confirmed by ATR-FTIR spectra and water conted angle. Scanning electron microscopic (SEM)measurement shows that the latter method produces a plane and smooth morphology, which is similar to the SPU controlsample controlled. When grafting with lower monomer concentration, ECs could grow on SPU-g-PHEA [poly(2-hydroxyethyl acrylate)], SPU-g-PAAm (polyacrylamide), SPU-g-PDMA [poly(2-(dimethylamino)ethyl methacrylate)] orquatemized SPU-g-PDMA surface with elongated cell shapes. Hence, the cell compatibility of SPU is improved and a usefulmethod to construct a cell compatible layer on the polymer surface has been developed.展开更多
Three new hybrid organic/inorganic polymeric ligand-exchange chiral stationary phases were developed by radical chain transfer reaction and surface grafting on silica gel, and successfully used for the enantioseparati...Three new hybrid organic/inorganic polymeric ligand-exchange chiral stationary phases were developed by radical chain transfer reaction and surface grafting on silica gel, and successfully used for the enantioseparations of DL-amino acids and DL-hydroxyl adds. The resolutions were achieved by using water containing 2.0 × 10^-4 mol/L of CuAc2 as a mobile phase, column temperature of 40 ℃, flow rate of 1.0 mL/min and detection at UV 254 nm. The elution order of D-isomer before L-isomer was observed for all DL-amino acids resolved except DL-Pro.展开更多
In addition to electrical insulation properties,the thermal properties of nanodielectrics,such as glass transition temperature,thermal expansion coefficients,thermal conductivity,and mechanical properties,including Yo...In addition to electrical insulation properties,the thermal properties of nanodielectrics,such as glass transition temperature,thermal expansion coefficients,thermal conductivity,and mechanical properties,including Young's modulus,bulk modulus,and shear modulus,are also very important.This paper describes the molecular dynamics simulations of epoxy resin doped with SiO_(2)nanoparticles and with SiO_(2)nanoparticles that have been surface grafted with hexamethyldisilazane(HMDS)at 10%and 20%grafting rates.The results show that surface grafting can improve certain thermal and mechanical properties of the system.Our analysis indicates that the improved thermal performance occurs because the formation of thermal chains becomes easier after the surface grafting treatment.The improved mechanical properties originate from two causes.First,doping with SiO_(2)nanoparticles inhibits the degree of movement of molecular chains in the system.Second,the surface grafting treatment weakens the molecular repulsion between SiO_(2)and epoxy resin,and the van der Waals excluded region becomes thinner.Thus,the compatibility between SiO_(2)nanoparticles and polymers is improved by the grafting treatment.The analysis method and conclusions in this paper provide guidance and reference for the future studies of the thermal and mechanical properties of nanodielectrics.展开更多
Linear low-density polyethylene(LLDPE)was melt and blended with styrene-maleic anhydride copolymer(SMA).The blending films were then immersed in poly(ethylene glycol)400(PEG400)at room temperature.The surface composit...Linear low-density polyethylene(LLDPE)was melt and blended with styrene-maleic anhydride copolymer(SMA).The blending films were then immersed in poly(ethylene glycol)400(PEG400)at room temperature.The surface composition of the blend films was determined by Fourier transform infra-red spectroscopy coupled with a variable incidence angle attenuated total reflection accessory(ATR-FTIR).Results show that PEG400 can be grafted onto the surface of the films via esterification with SMA.The immersion of PEG promotes the enrichment of SMA onto the surface of the films.The water contact angle data show that grafting of PEG400 onto PE can greatly improve the hydro-philicity of the PE surface.These experiments show that sur-face functionalization of polyethylene films by blending SMA and then surface grafting of PEG is feasible,which suggest an effective and simple route for PE surface modification via blending and grafting.展开更多
The surface of polypropylene (iPP) is modified with glow discharge plasma of Ar, so that the modified surfaces of iPP films are obtained. The studies of scanning electron microscopy (SEM) show the surface etching ...The surface of polypropylene (iPP) is modified with glow discharge plasma of Ar, so that the modified surfaces of iPP films are obtained. The studies of scanning electron microscopy (SEM) show the surface etching pattern of iPP films. The chemical structures of iPP films are confirmed by X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared (FTIR) spectroscopy. The wetting properties of modified surfaces of iPP films are characterized by contact angle, and the free energy of surfaces is calculated. The free radical of modification surfaces of iPP is measured by chemical method. The surfaces of iPP are achieved with Ar plasma treatment followed by grafting copolymerization with styrene (St) in St. The grafting polymer of St onto iPP is characterized by FTIR. The grafting rate is dependent on plasma exposure time and discharge voltage. The studies show that homopolymerization of St is undergone at the sane time during the graftingcopolymerization of St onto/PP.展开更多
12%acrylamide(AM) was grafted onto the surface of nanocellulose whiskers(NCW),which was self-assembled to be the chiral nematic suspension at 3%content.The acrylamide grafted NCW(AM-g-NCW) was characterized with...12%acrylamide(AM) was grafted onto the surface of nanocellulose whiskers(NCW),which was self-assembled to be the chiral nematic suspension at 3%content.The acrylamide grafted NCW(AM-g-NCW) was characterized with Fourier Transform Infrared Spectroscopy(FTIR).The grafting ratio was measured by elemental analysis.The degrees of crystallinity of the AM-g-NCW were measured by X-ray diffraction(XRD).The liquid crystalline properties of the AM-g-NCW were investigated by the polarizing optical microscopy(POM).The AM-g-NCW was found to self-assembly to be a lyotropic state.展开更多
Engineered scaffolds for bone tissue regeneration are designed to promote cell adhesion,growth,proliferation and differentiation.Recently,covalent and selective functionalization of glass and titanium surfaces with an...Engineered scaffolds for bone tissue regeneration are designed to promote cell adhesion,growth,proliferation and differentiation.Recently,covalent and selective functionalization of glass and titanium surfaces with an adhesive peptide(HVP)mapped on[351e359]sequence of human Vitronectin allowed to selectively increase osteoblast attachment and adhesion strength in in vitro assays,and to promote osseointegration in in vivo studies.For the first time to our knowledge,in this study we investigated the resistance of adhesion sequences to proteolytic digestion:HVP was completely cleaved after 5 h.In order to overcome the enzymatic degradation of the native peptide under physiological conditions we synthetized three analogues of HVP sequence.A retro-inverted peptide D-2HVP,composed of D amino acids,was completely stable in serum-containing medium.In addition,glass surfaces functionalized with D-2HVP increased human osteoblast adhesion as compared to the native peptide and maintained deposition of calcium.Interestingly,D-2HVP increased expression of IBSP,VTN and SPP1 genes as compared to HVP functionalized surfaces.Total internal reflection fluorescence microscope analysis showed cells with numerous filopodia spread on D-2HVP-functionalized surfaces.Therefore,the D-2HVP sequence is proposed as new osteoblast adhesive peptide with increased bioactivity and high proteolytic resistance.展开更多
Firstly,we synthesized N-methacryloyl-histidine monomer and N-methacryloyl-histidine-Cu^2+ complex(MAH-Cu^2+).Then the molecular imprinting polymers(MIP) has been prepared by surface grafting on uniform polystyr...Firstly,we synthesized N-methacryloyl-histidine monomer and N-methacryloyl-histidine-Cu^2+ complex(MAH-Cu^2+).Then the molecular imprinting polymers(MIP) has been prepared by surface grafting on uniform polystyrene(PS) core using reversible addition-fragmentation transfer polymerization(RAFT) with MAH-Cu^2+ as the functional monomer,methyl paraoxon as the template to simulate phosphodiesterase(PTE).Finally,we have investigated the catalytic hydrolytic activities of MIP and non-imprinting polymers(NIP) to the template methyl paraoxon and the template analogue ethyl paraoxon respectively by UV spectrophotometry.The results showed that the catalytic hydrolytic activity of MIP to the template methyl paraoxon was highest and the value of k is 8.67×10^-5 mmol L^-1 min^-1,3.89-fold higher than MIP to the template analogue ethyl paraoxon,2.79-fold higher than NIP to the template methyl paraoxon.The KM,rm of MSP are also determined,and KM = 3.95×10^-4)mol/L,rm = 2.12μmol/ min.The MIP can be reused with only lose 7%of catalytic activity for four cycles.展开更多
Thermal and salt dual stimuli-responsive filter-paper-based membranes were prepared by UV-induced grafting of NIPAM-based polymers on paper surface. The grafting ratio could be controlled by monomer concentration duri...Thermal and salt dual stimuli-responsive filter-paper-based membranes were prepared by UV-induced grafting of NIPAM-based polymers on paper surface. The grafting ratio could be controlled by monomer concentration during grafting polymerization. The results from pressure drop measurement of the mobile phase flowed cross the membrane demonstrate that an appropriate grafting ratio would be 8%-10%. Protein adsorption on the membrane through hydrophobic interaction could be promoted by increasing temperature and lyotropic salt concentration. The effect of grafted polymer structure on protein binding performance was studied. Filter paper grafted with NIPAM-based branched copolymer consisting of hydrophobic monomer moieties shows ten times higher protein binding capacity than that of the original filter paper. The separation of plasma proteins using the dual stimuli-responsive membrane was examined to demonstrate feasible application for hydrophobic interaction chromatographic separation of proteins.展开更多
Novel thermo-responsive cellulose papers were prepared via grafting poly(di(ethylene glycol)methyl ether methacrylate)(PDEGMA)by activators regenerating electron transfer(ARGET)and atom transfer radical polymerization...Novel thermo-responsive cellulose papers were prepared via grafting poly(di(ethylene glycol)methyl ether methacrylate)(PDEGMA)by activators regenerating electron transfer(ARGET)and atom transfer radical polymerization(ATRP).Attenuated total refraction Fourier-transform infrared spectroscopy(ATR-FTIR)and scanning electron microscopy(SEM)measurements of the modified paper showed that PDEGMA brushes were successfully grafted on the paper surface.The thermal stability of the papers before and after grafting was evaluated by thermogravimetric analysis(TGA).The PDEGMA-grafted paper exhibited a two-step thermal degradation process,and presented thermo-responsive characteristics.It was hydrophilic at room temperature but changed rapidly to highly hydrophobic when the temperature rose above 50℃.展开更多
Multi-walled carbon nanotubes(CNTs) were modified by an amination treatment with hexamethylenediamine(HMD), and then bismaleimide(BMI)/epoxy(E-44)/CNTs ternary composites were prepared using modified CNTs as t...Multi-walled carbon nanotubes(CNTs) were modified by an amination treatment with hexamethylenediamine(HMD), and then bismaleimide(BMI)/epoxy(E-44)/CNTs ternary composites were prepared using modified CNTs as the reinforcement via a simple mixing and curing molding method. The results show that the surfaces of CNTs are grafted polymer with the thickness of 3 nm and the dispersity of surface grafted carbon nanotubes(SG-CNTs) in the resin composites can be improved. The prepared composites contain C-C, C-N, C=O and-COOH groups and can keep a smooth surface. In addition, the composites have the flexural strength of 152 MPa, the tensile strength of 73 MPa and the impact strength of 87 k J m^(-2),respectively, when the weight ratio of BMI to E-44 is 1:8 and the content of SG-CNTs is 2 wt%. However,the thermal stability of the composites with SG-CNTs is a little lower than that of the composites without SG-CNTs.展开更多
基金This project is sponsored by the National Natural Science Foundation of China.
文摘Poly N-isopropyl acrylamide (abbreviated as PNIPA) as a kind of thermally sensitive hydrogel is utilized to concentrate Bovin Serum Albumin (BSA) solution. In order to decrease its surface adsorption to BSA in aqueous solution, surface layer grafting of the gels by radiation technology was carried out. The results showed that hydroxyl propyl methacrylate (HPMA) grained gel exhibited a low level of BSA adsorption and still kept the original thermally sensitive properties of PNIPA hydrogels.
文摘Low density polyethylene film surface-grafted phenolic resole was prepared by a sequential processes. Firstly, acrylic acid was grafted to the surface of low density polyethylene by photo-grafting. Secondly, the carboxylic groups in poly(acrylic acid) chains were transferred to sulfonic groups by the reaction of carboxylic groups with sulfanilic acid. Finally, a thin layer of phenolic resole was cured onto the surface of low density polyethylene. The grafting process was characterized by FTIR-ATR and gravimetric analysis. A possible model was proposed to interpret the experimental results.
基金supported by the Major State Basic Research Program of China (No. 2009CB623404) National Natural Science Foundation of China (Nos. 20736003, 20676067)+2 种基金 National High Technology Research and Development Program of China (No. 2007AA06Z317)Foundation of Ministry of Education of China (No. 20070003130)Foundation of the State Key Laboratory of Chemical Engineering (No. SKL-ChE-08A01)
文摘In order to control the surface pore sizes of polyvinylidene fluoride membranes and their distribution, low temperature plasma-induced grafting modifications of PVDF were studied to prepare hydrophobe membranes. By argon (Ar) treating and subsequent grafting reaction, a hydrophobe monomer, styrene, was introduced into the PVDF membrane. Fourier transform infrared attenuated total reflection (FTIR-ATR) was utilized to characterize the chemical and physical changes in the Ar plasma modified membrane. The surface modifications of PVDF membranes were investigated by using scanning electron microscopy (SEM), atomic force microscopy (AFM) and differential scanning calorimeter (DSC). The water permeability and the solute rejection were measured by PVDF membrane modified in different graft conditions. Results demonstrated that the pores in the modified membranes get smaller and the distribution of pores gets narrowed with the increase in grafting reaction duration. Longer graft time caused the water flux of PVDF membrane to decrease from 578 kg/(m^2· h) to 23 kg/(m^2· h) and the solute rejection to increase from 73% to 92%.
文摘A new process for lamination of polymer films by 'bulk surface photografting' has been developed. The chemical component of the invention is that the curing of reactive solution between two substrates is initiated by the surface free radicals produced by aromatic ketones and surface-hydrogen of substrates. Using the new approach, two or more polymer films are bonded together by a grafted polymer network which is grafted to adjacent substrate surfaces. The technique has been applied to film substrates of different polymers such as polyolefins, polyesters, and polyamides which have abstractable hydrogens at the surface. The photolaminated film composites containing carrier films and an intermediate functional film of low permeability give strong laminates with high barrier properties, e.g, for oxygen and air.
基金This work was supported by the Fund for Young Scientist from the National Advanced Materials Committee of China
文摘Photoinduced grafting of acrylic and allyl monomers on polyethylene surface was generally studied by using benzophenone (BP) as a photoinitiator. The grafting process was carried out either in vapor-phase or in solution of the monomers. In the vapor-phase reaction with a filter used to cut off the short wavelength UV light, allyl amine is the most reactive of the four monomers used and acrylic amide is comparatively more reactive than acrylic acid and allyl alcohol. Acetone, as a solvent and carrier for initiator and monomers, however, shows its reactivity to participate the reaction. The solution grafting with a filter is much faster than the corresponding vapor-phase reaction, and a fully covered surface by the grafted polymer can be achieved in this way.
文摘This work aimed at investigating the feasibility of surface modification of cellulose nanocrystals (CNCs) using <em>in situ</em> ring opening polymerization of <em>ε</em>-caprolactone (<em>ε</em>-CL) at room temperature. Residues of flax and milkweed (<em>Asclepias syriaca</em>) stem fibers were used as a source of cellulose to obtain and isolate CNCs. The cationic ring opening polymerization (CROP) of the monomer <em>ε</em>-CL was used to covalently graft polycaprolactone (PCL) chains at the CNCs surface. Silver hexafluoroantimonate (AgSbF<sub>6</sub>) was used in combination with the extracted CNCs to initiate, at room temperature, the polymerization and the grafting reactions with no other stimulus. Fourier-Transform InfraRed (FTIR), X-ray Photoelectron Spectrometry (XPS), UV/visible absorption and Gel Permeation Chromatography (GPC) analyses evidenced the presence of PCL chains covalently grafted at CNCs surface, the formation of Ag(0) particles as well as low or moderate molecular weight free PCL chains.
基金This project was supported by the National Natural Science Foundation of China (No. 59803006), the Major State Basic Research Program of China (G1999054305) and the Natural Science Foundation of Zhejiang Province.
文摘Two grafting methods, i.e. solution grafting and pre-adsorbing, are introduced to covalently immobilizehydrophilic polymers on segmented polyurethane (SPU) to modify its hydrophilicity and to improve its cell compatibility.Solution grafting results in higher degree of grafting and rougher surface morphology. Cell culture evaluation demonstratesthat the modified membranes thus obtained are disadvantageous to the endothelial cell (ECs) growth probably because thehydrophilic groups on the surface are over-crowded. However, pre-absorbing grafting generates lower degree of grafting,which is detected and confirmed by ATR-FTIR spectra and water conted angle. Scanning electron microscopic (SEM)measurement shows that the latter method produces a plane and smooth morphology, which is similar to the SPU controlsample controlled. When grafting with lower monomer concentration, ECs could grow on SPU-g-PHEA [poly(2-hydroxyethyl acrylate)], SPU-g-PAAm (polyacrylamide), SPU-g-PDMA [poly(2-(dimethylamino)ethyl methacrylate)] orquatemized SPU-g-PDMA surface with elongated cell shapes. Hence, the cell compatibility of SPU is improved and a usefulmethod to construct a cell compatible layer on the polymer surface has been developed.
文摘Three new hybrid organic/inorganic polymeric ligand-exchange chiral stationary phases were developed by radical chain transfer reaction and surface grafting on silica gel, and successfully used for the enantioseparations of DL-amino acids and DL-hydroxyl adds. The resolutions were achieved by using water containing 2.0 × 10^-4 mol/L of CuAc2 as a mobile phase, column temperature of 40 ℃, flow rate of 1.0 mL/min and detection at UV 254 nm. The elution order of D-isomer before L-isomer was observed for all DL-amino acids resolved except DL-Pro.
基金Project supported by the National Key Research and Development Program of China(Grant.Nos.2017YFB0902503 and 2016YFB0900802)。
文摘In addition to electrical insulation properties,the thermal properties of nanodielectrics,such as glass transition temperature,thermal expansion coefficients,thermal conductivity,and mechanical properties,including Young's modulus,bulk modulus,and shear modulus,are also very important.This paper describes the molecular dynamics simulations of epoxy resin doped with SiO_(2)nanoparticles and with SiO_(2)nanoparticles that have been surface grafted with hexamethyldisilazane(HMDS)at 10%and 20%grafting rates.The results show that surface grafting can improve certain thermal and mechanical properties of the system.Our analysis indicates that the improved thermal performance occurs because the formation of thermal chains becomes easier after the surface grafting treatment.The improved mechanical properties originate from two causes.First,doping with SiO_(2)nanoparticles inhibits the degree of movement of molecular chains in the system.Second,the surface grafting treatment weakens the molecular repulsion between SiO_(2)and epoxy resin,and the van der Waals excluded region becomes thinner.Thus,the compatibility between SiO_(2)nanoparticles and polymers is improved by the grafting treatment.The analysis method and conclusions in this paper provide guidance and reference for the future studies of the thermal and mechanical properties of nanodielectrics.
基金supported by the National Natural Science Foundation of China(Grant No.50273048)Ministry of Education of China(Grant No.20050558001).
文摘Linear low-density polyethylene(LLDPE)was melt and blended with styrene-maleic anhydride copolymer(SMA).The blending films were then immersed in poly(ethylene glycol)400(PEG400)at room temperature.The surface composition of the blend films was determined by Fourier transform infra-red spectroscopy coupled with a variable incidence angle attenuated total reflection accessory(ATR-FTIR).Results show that PEG400 can be grafted onto the surface of the films via esterification with SMA.The immersion of PEG promotes the enrichment of SMA onto the surface of the films.The water contact angle data show that grafting of PEG400 onto PE can greatly improve the hydro-philicity of the PE surface.These experiments show that sur-face functionalization of polyethylene films by blending SMA and then surface grafting of PEG is feasible,which suggest an effective and simple route for PE surface modification via blending and grafting.
基金financially supported by the National Natural Science Foundation of China(No.50673073)the Doctoral Foundation of Ministry of Education of China(No.20060056043)
文摘The surface of polypropylene (iPP) is modified with glow discharge plasma of Ar, so that the modified surfaces of iPP films are obtained. The studies of scanning electron microscopy (SEM) show the surface etching pattern of iPP films. The chemical structures of iPP films are confirmed by X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared (FTIR) spectroscopy. The wetting properties of modified surfaces of iPP films are characterized by contact angle, and the free energy of surfaces is calculated. The free radical of modification surfaces of iPP is measured by chemical method. The surfaces of iPP are achieved with Ar plasma treatment followed by grafting copolymerization with styrene (St) in St. The grafting polymer of St onto iPP is characterized by FTIR. The grafting rate is dependent on plasma exposure time and discharge voltage. The studies show that homopolymerization of St is undergone at the sane time during the graftingcopolymerization of St onto/PP.
基金support received from the National Natural Science Foundation of China(No20646003)Guangdong Province Natural Science Foundation(No07300767)the Fundamental Research Funds for the Central Universities of South China University of Technology(No2009ZM0239)
文摘12%acrylamide(AM) was grafted onto the surface of nanocellulose whiskers(NCW),which was self-assembled to be the chiral nematic suspension at 3%content.The acrylamide grafted NCW(AM-g-NCW) was characterized with Fourier Transform Infrared Spectroscopy(FTIR).The grafting ratio was measured by elemental analysis.The degrees of crystallinity of the AM-g-NCW were measured by X-ray diffraction(XRD).The liquid crystalline properties of the AM-g-NCW were investigated by the polarizing optical microscopy(POM).The AM-g-NCW was found to self-assembly to be a lyotropic state.
文摘Engineered scaffolds for bone tissue regeneration are designed to promote cell adhesion,growth,proliferation and differentiation.Recently,covalent and selective functionalization of glass and titanium surfaces with an adhesive peptide(HVP)mapped on[351e359]sequence of human Vitronectin allowed to selectively increase osteoblast attachment and adhesion strength in in vitro assays,and to promote osseointegration in in vivo studies.For the first time to our knowledge,in this study we investigated the resistance of adhesion sequences to proteolytic digestion:HVP was completely cleaved after 5 h.In order to overcome the enzymatic degradation of the native peptide under physiological conditions we synthetized three analogues of HVP sequence.A retro-inverted peptide D-2HVP,composed of D amino acids,was completely stable in serum-containing medium.In addition,glass surfaces functionalized with D-2HVP increased human osteoblast adhesion as compared to the native peptide and maintained deposition of calcium.Interestingly,D-2HVP increased expression of IBSP,VTN and SPP1 genes as compared to HVP functionalized surfaces.Total internal reflection fluorescence microscope analysis showed cells with numerous filopodia spread on D-2HVP-functionalized surfaces.Therefore,the D-2HVP sequence is proposed as new osteoblast adhesive peptide with increased bioactivity and high proteolytic resistance.
基金the support of the National Natural Science Foundation of China(No.50978138)
文摘Firstly,we synthesized N-methacryloyl-histidine monomer and N-methacryloyl-histidine-Cu^2+ complex(MAH-Cu^2+).Then the molecular imprinting polymers(MIP) has been prepared by surface grafting on uniform polystyrene(PS) core using reversible addition-fragmentation transfer polymerization(RAFT) with MAH-Cu^2+ as the functional monomer,methyl paraoxon as the template to simulate phosphodiesterase(PTE).Finally,we have investigated the catalytic hydrolytic activities of MIP and non-imprinting polymers(NIP) to the template methyl paraoxon and the template analogue ethyl paraoxon respectively by UV spectrophotometry.The results showed that the catalytic hydrolytic activity of MIP to the template methyl paraoxon was highest and the value of k is 8.67×10^-5 mmol L^-1 min^-1,3.89-fold higher than MIP to the template analogue ethyl paraoxon,2.79-fold higher than NIP to the template methyl paraoxon.The KM,rm of MSP are also determined,and KM = 3.95×10^-4)mol/L,rm = 2.12μmol/ min.The MIP can be reused with only lose 7%of catalytic activity for four cycles.
基金financially supported by the China Scholarship Council and the National Natural Science Foundation of China(No.20874004)
文摘Thermal and salt dual stimuli-responsive filter-paper-based membranes were prepared by UV-induced grafting of NIPAM-based polymers on paper surface. The grafting ratio could be controlled by monomer concentration during grafting polymerization. The results from pressure drop measurement of the mobile phase flowed cross the membrane demonstrate that an appropriate grafting ratio would be 8%-10%. Protein adsorption on the membrane through hydrophobic interaction could be promoted by increasing temperature and lyotropic salt concentration. The effect of grafted polymer structure on protein binding performance was studied. Filter paper grafted with NIPAM-based branched copolymer consisting of hydrophobic monomer moieties shows ten times higher protein binding capacity than that of the original filter paper. The separation of plasma proteins using the dual stimuli-responsive membrane was examined to demonstrate feasible application for hydrophobic interaction chromatographic separation of proteins.
基金supported by the National Natural Science Foundation of China (No.31200453,31200454)the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD).
文摘Novel thermo-responsive cellulose papers were prepared via grafting poly(di(ethylene glycol)methyl ether methacrylate)(PDEGMA)by activators regenerating electron transfer(ARGET)and atom transfer radical polymerization(ATRP).Attenuated total refraction Fourier-transform infrared spectroscopy(ATR-FTIR)and scanning electron microscopy(SEM)measurements of the modified paper showed that PDEGMA brushes were successfully grafted on the paper surface.The thermal stability of the papers before and after grafting was evaluated by thermogravimetric analysis(TGA).The PDEGMA-grafted paper exhibited a two-step thermal degradation process,and presented thermo-responsive characteristics.It was hydrophilic at room temperature but changed rapidly to highly hydrophobic when the temperature rose above 50℃.
基金supported by the National Natural Science Foundation of China (Grant Nos. 51172180 and 51372200)the Scientific Research Plan Project of Shaanxi Education Department (Grant No. 16JK1551)+1 种基金the Science and Technology Plan of Xi’an (Grant No. CXY1430(9))the China Postdoctoral Science Foundation Funded Project (Grant No. 2016M592824)
文摘Multi-walled carbon nanotubes(CNTs) were modified by an amination treatment with hexamethylenediamine(HMD), and then bismaleimide(BMI)/epoxy(E-44)/CNTs ternary composites were prepared using modified CNTs as the reinforcement via a simple mixing and curing molding method. The results show that the surfaces of CNTs are grafted polymer with the thickness of 3 nm and the dispersity of surface grafted carbon nanotubes(SG-CNTs) in the resin composites can be improved. The prepared composites contain C-C, C-N, C=O and-COOH groups and can keep a smooth surface. In addition, the composites have the flexural strength of 152 MPa, the tensile strength of 73 MPa and the impact strength of 87 k J m^(-2),respectively, when the weight ratio of BMI to E-44 is 1:8 and the content of SG-CNTs is 2 wt%. However,the thermal stability of the composites with SG-CNTs is a little lower than that of the composites without SG-CNTs.