Nanostructured materials, characterized by an ultrafine grain size, have stimulated much research interest by virtue of their unusual mechanical, electrical, optical, and magnetic properties. In this paper, the sinter...Nanostructured materials, characterized by an ultrafine grain size, have stimulated much research interest by virtue of their unusual mechanical, electrical, optical, and magnetic properties. In this paper, the sintering process of nano-powders were reviewed, to which sintering of the traditional materials compared. The microstructural development, i.e., grain growth and densification during sintering as well as the mechanism of crystal surface diffusion and boundary migration were analyzed, and the dynamic models on sintering process were summarized by the relationship of grain growth and pores size, interface diffusion, densification rate, and sintering temperature. Finally, the research tendency of this major on the basis of above models was discussed.展开更多
By using microwave-assisted co-precipitation in aqueous phase, adding surface activation agent PEG-6000 into the mixture of InCl3 solution and SnCl4 solution, and dropping the ammonia solution with the density (volume...By using microwave-assisted co-precipitation in aqueous phase, adding surface activation agent PEG-6000 into the mixture of InCl3 solution and SnCl4 solution, and dropping the ammonia solution with the density (volume ratio) of 1-0 to 1-4, ITO precursor was prepared at different reaction system temperatures of 35 ℃-85 ℃, then ITO nano-powder was obtained after it was calcinated at 800 ℃ for 1 h. The morphology of ITO nano-powder was characterized by SEM and its electrical conductivity was determined by conductivity meter. The effects of different temperatures and ammonia concentration in microwave-assisted reaction system on its morphology and electric conductivity were discussed. The experimental results indicate that with the dilution of the ammonia solution or the rise of reacting system temperature, the morphology of ITO particles is transformed from spherical to rod-like one with the decline of its electric conductivity. And the electric conductivity of ITO nano-powders with spherical morphology is higher than that of ITO nano-powders with rod-like morphology.展开更多
Yb 3+-doped TiO_2 composite nano-particles were prepared by the acid-catalyzed sol-gel method using Ti(OC_4H_9)_4 and Yb(NO_3)_3 as precursors. The effects of the amount of Yb 3+ doping and calcination temperature on ...Yb 3+-doped TiO_2 composite nano-particles were prepared by the acid-catalyzed sol-gel method using Ti(OC_4H_9)_4 and Yb(NO_3)_3 as precursors. The effects of the amount of Yb 3+ doping and calcination temperature on the phase transformation, crystallite size, surface texture of the nanopowders were investigated by XRD and BET specific surface area. Their photocatalytic activities were evaluated using the photocatalytic degradation of methylene blue in aqueous solution as a probe reaction. At the interface, titanium ions substitute for ytterbium ions in the lattice of Yb_2O_3 to form Ti-O-Yb bonds, which cause distortion and inhibit the anatase to rutile phase transformation in TiO_2. The results indicate that Yb 3+-doping can enhance the photocatalytic activity of TiO_2 nano-powders as compared with pure TiO_2. 0.125%(mass fraction) Yb 3+ doped TiO_2 nano-powders calcined at 600 ℃ for 2 h show the highest photocatalytic activity. The increase in photoactivity is due to the effects of the factors such as crystal phase, crystallite size, surface chemical property, surface density of OH groups, and surface texture properties of the TiO_2 nano-powders.展开更多
Wire electrical explosion may result in the existence of micro-sized large particles in powders while current injection ways may influence the size and content of micro-sized large particles. Therefore, two kinds of e...Wire electrical explosion may result in the existence of micro-sized large particles in powders while current injection ways may influence the size and content of micro-sized large particles. Therefore, two kinds of electrical explosion devices with different electrodes by gas discharge were designed in this paper. The pole-board electrodes and the cone electrodes were used respectively for studying copper wire electrical explosion process. The current and voltage data were measured with the Rogowski coil and high voltage probe. The results show that the pulverizing process of electrical explosion is more efficient when the wire electrode current density injected into the cone electrodes is approximately twice as much as the pole-board electrodes. The content of micro-sized large particles is the least among the products of the electrical explosion, when the total deposition energy of the wire prior to vaporization stage is 2. 5 times larger than that of the theoretical value of the completed vaporization.展开更多
High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of...High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of Y_2O_3 particles were controlled by such processingparameters as concentration of YCl_3 and oxalic acid and complex non-ionic surfactant etc. TEMphotomicrographs show that Y_2O_3 particles are spherical in shape, with an average diameter of lessthan 30 nm. Test results certify that the purity and particle diameter as well as the dispersion ofY_2O_3 nano-powder depend on the concentrations of YCl_3, oxalic acid and complex non-ionicsurfactant. The optimum ranges of the concentrations for YCl_3 and complex non-ionic surfactant whenthe diameter of Y_2O_3 particles is smaller than 100 nm are 0.43 ～1.4 mol ? L^(-1) and0.031～0.112 mol·L^(-1) respectively, while the mass fraction range of oxalic acid is 10% ～18% .The purity of Y_2O_3 nano-powder tested by ICP-AES analysis is 99.99% .展开更多
At present, there are two ways to produce 99Mo in a reactor: 1) fission process—from U fission product by reaction 235U (n, f) 99Mo and 2) activation process—by radiation capture reaction 98Mo (n, γ) 99Mo. This pap...At present, there are two ways to produce 99Mo in a reactor: 1) fission process—from U fission product by reaction 235U (n, f) 99Mo and 2) activation process—by radiation capture reaction 98Mo (n, γ) 99Mo. This paper presents the results of experiments performed with molybdenum carbide nano-powder to produce 99Mo. These results show the implementation of the above idea in practice.展开更多
Using A1(NO3)3·9H2O, NH4Al(SO4)2·12H2O, Y(NO3)3as mother salts, and urea as precipitant, YAG nano-powders were synthesized by microwave homogeneous precipitation. The composition, morphology, and phase trans...Using A1(NO3)3·9H2O, NH4Al(SO4)2·12H2O, Y(NO3)3as mother salts, and urea as precipitant, YAG nano-powders were synthesized by microwave homogeneous precipitation. The composition, morphology, and phase transformation of precursor were analyzed by IR, XRD and TEM. The size distribution of YAG powders was characterized using laser diffraction method. The results show that sulfate ions influence the dispersion, composition and morphology of the YAG precursors. The addition of moderate sulfate ions can produce YAG powders with nano size and excellent dispersion at 1100℃.展开更多
High quality nano-sized zirconium carbide （ZrC） powders were successfully fabricated via a developed chemical active dilution self-propagating high-temperature synthesis （SHS） method assisted by ball milling pretr...High quality nano-sized zirconium carbide （ZrC） powders were successfully fabricated via a developed chemical active dilution self-propagating high-temperature synthesis （SHS） method assisted by ball milling pretreatment process using traditional cheap zirconium dioxide powder （ZrO2）, magnesium powder （Mg） and sucrose （C12H22Oll） as raw materials. FSEM, TEM, HRTEM, SAED, XRD, FTIR and Raman, ICP- AES, laser particle size analyzer, oxygen and nitrogen analyzer, carbon/sulfur determinator and TG-DSC were employed for the characterization of the morphology, structure, chemical composition and thermal stability of the as-synthesized ZrC samples. The as-synthesized samples demonstrated high purity, low oxygen content and evenly distributed ZrC nano-powders with an average particle size of 50nm. In addition, the effects of endothermic rate and the possible chemical reaction mechanism were also discussed.展开更多
CeB6 powders were prepared by high-temperature self-propagating synthesis （SHS） in which CeO2, B203 and Mg were taken as reactants. The adiabatic temperature and dynamics of SHS reactions were investigated. The SHS ...CeB6 powders were prepared by high-temperature self-propagating synthesis （SHS） in which CeO2, B203 and Mg were taken as reactants. The adiabatic temperature and dynamics of SHS reactions were investigated. The SHS reaction products and leached products were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results indicated that the adiabatic temperature of Mg-B2Oa-CeO2 reaction system was rather higher than 1800 K to make the reaction propagate by itself, and the apparent activation energy （Ea） and reaction order （n） of exothermic peak on Mg-BzO3-CeO2 differential scanning calorimetry （DSC） curve were 23.03 kJ/mol and 1.31, respectively. The apparent activation energy was lower, so the reaction occurred easily. The SHS products consisted of MgO, CeB6 and little MgaB2O6. The leached products consisted of single CeB6 phase and its purity was higher than 99.0%, and the average particle sizes of CeB6 were smaller than 150 nm.展开更多
The Yb:Lu_(2)O_(3)precursor made up of spherical particles was synthesized through the co-precipitation method in the water/ethanol solvent.The 5 at% Yb:Lu_(2)O_(3)powder is in the cubic phase after calcination at 110...The Yb:Lu_(2)O_(3)precursor made up of spherical particles was synthesized through the co-precipitation method in the water/ethanol solvent.The 5 at% Yb:Lu_(2)O_(3)powder is in the cubic phase after calcination at 1100℃ for 4 h.The powder also consists of spherical nanoparticles with the average particle and grain sizes of 96 and 49 nm,respectively.The average grain size of the pre-sintered ceramic sample is 526 nm and that of the sample by hot isostatic pressing grows to 612 nm.The 1.0 mm-thick sample has an in-line transmittance of 81.6%(theoretical value of 82.2%)at 1100 nm.The largest absorption cross-section at 976 nm is 0.96×1^(0-20)cm^(2) with the emission cross-section at 1033 nm of 0.92×10^(-20)cm^(2) and the gain cross sections are calculated with the smallest population inversion parameter β of 0.059.The highest slope efficiency of 68.7% with the optical efficiency of 65.1% is obtained at 1033.3 nm in quasi-continuous wave(QCW)pumping.In the case of continuous wave(CW)pumping,the highest slope efficiency is 61.0% with the optical efficiency of 54.1%.The obtained laser performance indicates that Yb:Lu_(2)O_(3)ceramics have excellent resistance to thermal load stresses,which shows great potential in high-power solid-state laser applications.展开更多
Sol-gel-derived nano-powders of lead magnesium niobate and lead titanate solid solutions （PMN-PT or PMNT） were prepared from lead acetate trihydrate （Pb（CH3COO）2·3H2O）, magnesium acetate trihydrate （Mg（CH...Sol-gel-derived nano-powders of lead magnesium niobate and lead titanate solid solutions （PMN-PT or PMNT） were prepared from lead acetate trihydrate （Pb（CH3COO）2·3H2O）, magnesium acetate trihydrate （Mg（CH3COO）2·3H2O）, niobium ethoxide （Nb（OC2H5）5） and titanium isopropoxide （Ti（OCH（CH3）2）4）. The key steps in the preparation process were discussed, The crystalline phases in the powders were investigated using X-ray diffraction （XRD） analysis and the size of grains was observed by field-emission scanning electron microscopy （SEM）. These powders, with good dispersion characteristics and narrow grain size distribution （ranging from 50 nm to 200 nm）, may be used to prepare PMNT thick films and ceramics.展开更多
基金This project was financially supported by the Natural Science Foundation of Hebei Province (No.E2005000027) and Natural Science Foundation of Tianjin (No.06YFJMJC02400).
文摘Nanostructured materials, characterized by an ultrafine grain size, have stimulated much research interest by virtue of their unusual mechanical, electrical, optical, and magnetic properties. In this paper, the sintering process of nano-powders were reviewed, to which sintering of the traditional materials compared. The microstructural development, i.e., grain growth and densification during sintering as well as the mechanism of crystal surface diffusion and boundary migration were analyzed, and the dynamic models on sintering process were summarized by the relationship of grain growth and pores size, interface diffusion, densification rate, and sintering temperature. Finally, the research tendency of this major on the basis of above models was discussed.
基金Project (50725416) supported by the National Science Fund for Distinguished Young Scholars of ChinaProject(2008RS4037) supported by the Postdoctoral Science and Research Special Foundation of Hunan Province, ChinaProject supported by the Postdoctoral Science Foundation of Central South University, China
文摘By using microwave-assisted co-precipitation in aqueous phase, adding surface activation agent PEG-6000 into the mixture of InCl3 solution and SnCl4 solution, and dropping the ammonia solution with the density (volume ratio) of 1-0 to 1-4, ITO precursor was prepared at different reaction system temperatures of 35 ℃-85 ℃, then ITO nano-powder was obtained after it was calcinated at 800 ℃ for 1 h. The morphology of ITO nano-powder was characterized by SEM and its electrical conductivity was determined by conductivity meter. The effects of different temperatures and ammonia concentration in microwave-assisted reaction system on its morphology and electric conductivity were discussed. The experimental results indicate that with the dilution of the ammonia solution or the rise of reacting system temperature, the morphology of ITO particles is transformed from spherical to rod-like one with the decline of its electric conductivity. And the electric conductivity of ITO nano-powders with spherical morphology is higher than that of ITO nano-powders with rod-like morphology.
文摘Yb 3+-doped TiO_2 composite nano-particles were prepared by the acid-catalyzed sol-gel method using Ti(OC_4H_9)_4 and Yb(NO_3)_3 as precursors. The effects of the amount of Yb 3+ doping and calcination temperature on the phase transformation, crystallite size, surface texture of the nanopowders were investigated by XRD and BET specific surface area. Their photocatalytic activities were evaluated using the photocatalytic degradation of methylene blue in aqueous solution as a probe reaction. At the interface, titanium ions substitute for ytterbium ions in the lattice of Yb_2O_3 to form Ti-O-Yb bonds, which cause distortion and inhibit the anatase to rutile phase transformation in TiO_2. The results indicate that Yb 3+-doping can enhance the photocatalytic activity of TiO_2 nano-powders as compared with pure TiO_2. 0.125%(mass fraction) Yb 3+ doped TiO_2 nano-powders calcined at 600 ℃ for 2 h show the highest photocatalytic activity. The increase in photoactivity is due to the effects of the factors such as crystal phase, crystallite size, surface chemical property, surface density of OH groups, and surface texture properties of the TiO_2 nano-powders.
基金This research was supported by National Natural Science Foundation of China （No. 51061011 ）.
文摘Wire electrical explosion may result in the existence of micro-sized large particles in powders while current injection ways may influence the size and content of micro-sized large particles. Therefore, two kinds of electrical explosion devices with different electrodes by gas discharge were designed in this paper. The pole-board electrodes and the cone electrodes were used respectively for studying copper wire electrical explosion process. The current and voltage data were measured with the Rogowski coil and high voltage probe. The results show that the pulverizing process of electrical explosion is more efficient when the wire electrode current density injected into the cone electrodes is approximately twice as much as the pole-board electrodes. The content of micro-sized large particles is the least among the products of the electrical explosion, when the total deposition energy of the wire prior to vaporization stage is 2. 5 times larger than that of the theoretical value of the completed vaporization.
文摘High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of Y_2O_3 particles were controlled by such processingparameters as concentration of YCl_3 and oxalic acid and complex non-ionic surfactant etc. TEMphotomicrographs show that Y_2O_3 particles are spherical in shape, with an average diameter of lessthan 30 nm. Test results certify that the purity and particle diameter as well as the dispersion ofY_2O_3 nano-powder depend on the concentrations of YCl_3, oxalic acid and complex non-ionicsurfactant. The optimum ranges of the concentrations for YCl_3 and complex non-ionic surfactant whenthe diameter of Y_2O_3 particles is smaller than 100 nm are 0.43 ～1.4 mol ? L^(-1) and0.031～0.112 mol·L^(-1) respectively, while the mass fraction range of oxalic acid is 10% ～18% .The purity of Y_2O_3 nano-powder tested by ICP-AES analysis is 99.99% .
文摘At present, there are two ways to produce 99Mo in a reactor: 1) fission process—from U fission product by reaction 235U (n, f) 99Mo and 2) activation process—by radiation capture reaction 98Mo (n, γ) 99Mo. This paper presents the results of experiments performed with molybdenum carbide nano-powder to produce 99Mo. These results show the implementation of the above idea in practice.
基金Project supported by the Excellent Middle-aged or Young Scientists from Shandong Province (02BS049)
文摘Using A1(NO3)3·9H2O, NH4Al(SO4)2·12H2O, Y(NO3)3as mother salts, and urea as precipitant, YAG nano-powders were synthesized by microwave homogeneous precipitation. The composition, morphology, and phase transformation of precursor were analyzed by IR, XRD and TEM. The size distribution of YAG powders was characterized using laser diffraction method. The results show that sulfate ions influence the dispersion, composition and morphology of the YAG precursors. The addition of moderate sulfate ions can produce YAG powders with nano size and excellent dispersion at 1100℃.
基金Funded by the Program for New Century Excellent Talents in University(No.NCET-12-0655)the Guangxi Natural Science Foundation(No.2014GXNSFFA118004)the Self-determined and Innovative Research Funds of WUT(Nos.136643002 and No.2013IV058)
文摘High quality nano-sized zirconium carbide （ZrC） powders were successfully fabricated via a developed chemical active dilution self-propagating high-temperature synthesis （SHS） method assisted by ball milling pretreatment process using traditional cheap zirconium dioxide powder （ZrO2）, magnesium powder （Mg） and sucrose （C12H22Oll） as raw materials. FSEM, TEM, HRTEM, SAED, XRD, FTIR and Raman, ICP- AES, laser particle size analyzer, oxygen and nitrogen analyzer, carbon/sulfur determinator and TG-DSC were employed for the characterization of the morphology, structure, chemical composition and thermal stability of the as-synthesized ZrC samples. The as-synthesized samples demonstrated high purity, low oxygen content and evenly distributed ZrC nano-powders with an average particle size of 50nm. In addition, the effects of endothermic rate and the possible chemical reaction mechanism were also discussed.
基金supported by National Natural Science Foundation of China(51002025,50644016,50874027)
文摘CeB6 powders were prepared by high-temperature self-propagating synthesis （SHS） in which CeO2, B203 and Mg were taken as reactants. The adiabatic temperature and dynamics of SHS reactions were investigated. The SHS reaction products and leached products were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results indicated that the adiabatic temperature of Mg-B2Oa-CeO2 reaction system was rather higher than 1800 K to make the reaction propagate by itself, and the apparent activation energy （Ea） and reaction order （n） of exothermic peak on Mg-BzO3-CeO2 differential scanning calorimetry （DSC） curve were 23.03 kJ/mol and 1.31, respectively. The apparent activation energy was lower, so the reaction occurred easily. The SHS products consisted of MgO, CeB6 and little MgaB2O6. The leached products consisted of single CeB6 phase and its purity was higher than 99.0%, and the average particle sizes of CeB6 were smaller than 150 nm.
基金supported by the National Key R&D Program of China(Grant No.2017YFB0310500)the National Natural Science Foundation of China(Grant No.61575212)the Key Research Project of the Frontier Science of the Chinese Academy of Sciences(No.QYZDB-SSW-JSC022).
文摘The Yb:Lu_(2)O_(3)precursor made up of spherical particles was synthesized through the co-precipitation method in the water/ethanol solvent.The 5 at% Yb:Lu_(2)O_(3)powder is in the cubic phase after calcination at 1100℃ for 4 h.The powder also consists of spherical nanoparticles with the average particle and grain sizes of 96 and 49 nm,respectively.The average grain size of the pre-sintered ceramic sample is 526 nm and that of the sample by hot isostatic pressing grows to 612 nm.The 1.0 mm-thick sample has an in-line transmittance of 81.6%(theoretical value of 82.2%)at 1100 nm.The largest absorption cross-section at 976 nm is 0.96×1^(0-20)cm^(2) with the emission cross-section at 1033 nm of 0.92×10^(-20)cm^(2) and the gain cross sections are calculated with the smallest population inversion parameter β of 0.059.The highest slope efficiency of 68.7% with the optical efficiency of 65.1% is obtained at 1033.3 nm in quasi-continuous wave(QCW)pumping.In the case of continuous wave(CW)pumping,the highest slope efficiency is 61.0% with the optical efficiency of 54.1%.The obtained laser performance indicates that Yb:Lu_(2)O_(3)ceramics have excellent resistance to thermal load stresses,which shows great potential in high-power solid-state laser applications.
文摘Sol-gel-derived nano-powders of lead magnesium niobate and lead titanate solid solutions （PMN-PT or PMNT） were prepared from lead acetate trihydrate （Pb（CH3COO）2·3H2O）, magnesium acetate trihydrate （Mg（CH3COO）2·3H2O）, niobium ethoxide （Nb（OC2H5）5） and titanium isopropoxide （Ti（OCH（CH3）2）4）. The key steps in the preparation process were discussed, The crystalline phases in the powders were investigated using X-ray diffraction （XRD） analysis and the size of grains was observed by field-emission scanning electron microscopy （SEM）. These powders, with good dispersion characteristics and narrow grain size distribution （ranging from 50 nm to 200 nm）, may be used to prepare PMNT thick films and ceramics.