镧系金属有机骨框架(Lanthanide metal organic frameworks,Ln-MOFs)是以镧系离子为中心,与配体有机物组合的多孔材料,具有良好的光学性质,在许多领域有广泛的应用。不同的镧系离子与相应的有机配体结合,可组成不同性能的Ln-MOFs。在众...镧系金属有机骨框架(Lanthanide metal organic frameworks,Ln-MOFs)是以镧系离子为中心,与配体有机物组合的多孔材料,具有良好的光学性质,在许多领域有广泛的应用。不同的镧系离子与相应的有机配体结合,可组成不同性能的Ln-MOFs。在众多镧系元素中,Tb^(3+)和Eu^(3+)是良好的发光中心,常被用于组建发光Ln-MOFs。由Tb^(3+)/Eu^(3+)与有机配体形成的Ln-MOFs具有独特的荧光特性、较大Stokes位移以及长发光寿命等优点,在荧光检测领域具有重要应用。综述了基于Tb^(3+)/Eu^(3+)的Ln-MOFs在离子检测、生物标志物检测以及小分子检测领域的研究进展,并对Ln-MOFs的发展前景进行了展望。展开更多
The structure of the low-temperature 4f^N→4f^N-15d excitation spectra of Eu^3+ and Tb^3+ doped in crystals LiYF4, YPO4 and CaF2 measured by van Pieterson et al. in 2002 was analyzed and assigned based on the simple...The structure of the low-temperature 4f^N→4f^N-15d excitation spectra of Eu^3+ and Tb^3+ doped in crystals LiYF4, YPO4 and CaF2 measured by van Pieterson et al. in 2002 was analyzed and assigned based on the simple model proposed by Duan and co-workers in the last few years. Some complemental discussion on effects of J-mixing on the f-d transition intensities for Eu^3+ due to the f-electron crystal-field interaction Hcf(f), which was ignored in the simple mod- el, was presented. Some previously unexplained peaks for Tb^3 + were interpreted to be spin-forbidden transitions to higher 5d crystal-field levels, or assigned to be f→d excitations with the core 4f7 excited from ^8S to ^6P, ^6I and ^6D, respectively. It is shown that the main structure of 4f-Sd excitation spectra of Eu^3+ and Tb^3+ can be well interpreted with the simple model.展开更多
Al-doped and B, Al-codoped silica xerogel was fabricated by sol-gel process. The influence of B ions and annealing temperature on luminescent properties of phosphors were studied by using fluorescence spectrum, X-ray ...Al-doped and B, Al-codoped silica xerogel was fabricated by sol-gel process. The influence of B ions and annealing temperature on luminescent properties of phosphors were studied by using fluorescence spectrum, X-ray diffraction, DSC, TG/DTG analysis and IR spectrum. The heat treatment has a large effect on the luminescent properties. Under 248 nm excitation, the emission spectrum of samples heated shows characteristic emission peaks of Eu^3+ ions are, which are due to the transitions of ^5D0→^7FJ(J = 0, 1, 2, 3, 4) of Eu^3+ , respectively. The transition of ^5D0→^7F1 is split into two peaks.展开更多
By using an improved Bridgman method,0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/y mol%Eu^(3+)(y=0,0.4,0.6,0.8)doped Na_(5)Y_(9)F_(32)single crystals were prepared.The x-ray diffraction,excitation spectra,emission spectra and flu...By using an improved Bridgman method,0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/y mol%Eu^(3+)(y=0,0.4,0.6,0.8)doped Na_(5)Y_(9)F_(32)single crystals were prepared.The x-ray diffraction,excitation spectra,emission spectra and fluorescence decay curves were used to explore the crystal structure and optical performance of the obtained samples.When excited by 362 nm light,the cool white emission was realized by Na_(5)Y_(9)F_(32)single crystal triply-doped with 0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/0.8 mol%Eu^(3+),in which the Commission Internationale de l’Eclairage(CIE)chromaticity coordinate was(0.2995,0.3298)and the correlated color temperature(CCT)was 6586 K.The integrated normalized emission intensity of the tridoped single crystal at 448 K could keep 62%of that at 298 K.The internal quantum yield(QY)was calculated to be~15.16%by integrating spheres.These results suggested that the single crystals tri-doped with Tm^(3+),Tb^(3+)and Eu^(3+)ions have a promising potential application for white light-emitting diodes(w-LEDs).展开更多
To obtain high efficiency luminescent materials, the system Al2O3-B2O3 containing Ce3+ andTb3+ ions with variation of B2O3-content, has been prepared by Al2O3, H3BO3, CeO2 and Tb4O7 underreducing atmosphere at 1250i ....To obtain high efficiency luminescent materials, the system Al2O3-B2O3 containing Ce3+ andTb3+ ions with variation of B2O3-content, has been prepared by Al2O3, H3BO3, CeO2 and Tb4O7 underreducing atmosphere at 1250i . It is notable that the brightness of the sample with appropriatecomposition is similar to that of commercial phosphorous containing Ce3+ and Tb3+, indicating that a newhigh efficency green luminescent material was obtained with appropriate B2O3-content.展开更多
文摘镧系金属有机骨框架(Lanthanide metal organic frameworks,Ln-MOFs)是以镧系离子为中心,与配体有机物组合的多孔材料,具有良好的光学性质,在许多领域有广泛的应用。不同的镧系离子与相应的有机配体结合,可组成不同性能的Ln-MOFs。在众多镧系元素中,Tb^(3+)和Eu^(3+)是良好的发光中心,常被用于组建发光Ln-MOFs。由Tb^(3+)/Eu^(3+)与有机配体形成的Ln-MOFs具有独特的荧光特性、较大Stokes位移以及长发光寿命等优点,在荧光检测领域具有重要应用。综述了基于Tb^(3+)/Eu^(3+)的Ln-MOFs在离子检测、生物标志物检测以及小分子检测领域的研究进展,并对Ln-MOFs的发展前景进行了展望。
文摘The structure of the low-temperature 4f^N→4f^N-15d excitation spectra of Eu^3+ and Tb^3+ doped in crystals LiYF4, YPO4 and CaF2 measured by van Pieterson et al. in 2002 was analyzed and assigned based on the simple model proposed by Duan and co-workers in the last few years. Some complemental discussion on effects of J-mixing on the f-d transition intensities for Eu^3+ due to the f-electron crystal-field interaction Hcf(f), which was ignored in the simple mod- el, was presented. Some previously unexplained peaks for Tb^3 + were interpreted to be spin-forbidden transitions to higher 5d crystal-field levels, or assigned to be f→d excitations with the core 4f7 excited from ^8S to ^6P, ^6I and ^6D, respectively. It is shown that the main structure of 4f-Sd excitation spectra of Eu^3+ and Tb^3+ can be well interpreted with the simple model.
文摘Al-doped and B, Al-codoped silica xerogel was fabricated by sol-gel process. The influence of B ions and annealing temperature on luminescent properties of phosphors were studied by using fluorescence spectrum, X-ray diffraction, DSC, TG/DTG analysis and IR spectrum. The heat treatment has a large effect on the luminescent properties. Under 248 nm excitation, the emission spectrum of samples heated shows characteristic emission peaks of Eu^3+ ions are, which are due to the transitions of ^5D0→^7FJ(J = 0, 1, 2, 3, 4) of Eu^3+ , respectively. The transition of ^5D0→^7F1 is split into two peaks.
基金Project supported by the National Natural Science Foundation of China(Grant No.62275133)the Natural Science Foundation of Zhejiang Province of China(Grant No.LY22E020002)+1 种基金the Natural Science Foundation of Ningbo(Grant Nos.2021J077 and 202003N4099)K.C.Wong Magna Fund in Ningbo University
文摘By using an improved Bridgman method,0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/y mol%Eu^(3+)(y=0,0.4,0.6,0.8)doped Na_(5)Y_(9)F_(32)single crystals were prepared.The x-ray diffraction,excitation spectra,emission spectra and fluorescence decay curves were used to explore the crystal structure and optical performance of the obtained samples.When excited by 362 nm light,the cool white emission was realized by Na_(5)Y_(9)F_(32)single crystal triply-doped with 0.3 mol%Tm^(3+)/0.6 mol%Tb^(3+)/0.8 mol%Eu^(3+),in which the Commission Internationale de l’Eclairage(CIE)chromaticity coordinate was(0.2995,0.3298)and the correlated color temperature(CCT)was 6586 K.The integrated normalized emission intensity of the tridoped single crystal at 448 K could keep 62%of that at 298 K.The internal quantum yield(QY)was calculated to be~15.16%by integrating spheres.These results suggested that the single crystals tri-doped with Tm^(3+),Tb^(3+)and Eu^(3+)ions have a promising potential application for white light-emitting diodes(w-LEDs).
文摘To obtain high efficiency luminescent materials, the system Al2O3-B2O3 containing Ce3+ andTb3+ ions with variation of B2O3-content, has been prepared by Al2O3, H3BO3, CeO2 and Tb4O7 underreducing atmosphere at 1250i . It is notable that the brightness of the sample with appropriatecomposition is similar to that of commercial phosphorous containing Ce3+ and Tb3+, indicating that a newhigh efficency green luminescent material was obtained with appropriate B2O3-content.