A significant temperature raise within hydrogen vehicle cylinder during the fast filling process will be observed, while the strength and fatigue life of the cylinder will dramatically decrease at high temperature. In...A significant temperature raise within hydrogen vehicle cylinder during the fast filling process will be observed, while the strength and fatigue life of the cylinder will dramatically decrease at high temperature. In order to evaluate the strength and fatigue of composite hydrogen storage vessel, a 70-MPa fatigue test system using hydrogen medium was set up. Experimental study on the fatigue of composite hydrogen storage vessels under real hydrogen environment was performed. The experimental results show that the ultimate strength and fatigue life both decreased obviously compared with the values under hydraulic fatigue test. Furthermore, fatigue property, failure behavior, and safe hydrogen charging/discharging working mode of onboard hydrogen storage vessels were obtained through the fatigue tests.展开更多
文摘A significant temperature raise within hydrogen vehicle cylinder during the fast filling process will be observed, while the strength and fatigue life of the cylinder will dramatically decrease at high temperature. In order to evaluate the strength and fatigue of composite hydrogen storage vessel, a 70-MPa fatigue test system using hydrogen medium was set up. Experimental study on the fatigue of composite hydrogen storage vessels under real hydrogen environment was performed. The experimental results show that the ultimate strength and fatigue life both decreased obviously compared with the values under hydraulic fatigue test. Furthermore, fatigue property, failure behavior, and safe hydrogen charging/discharging working mode of onboard hydrogen storage vessels were obtained through the fatigue tests.