Mg-3Al-1Zn(AZ31)sheets were produced by transverse gradient extrusion(TGE)process.The flow behavior and dynamic recrystallization during extrusion were systematically analyzed.The microstructures,textures,and mechanic...Mg-3Al-1Zn(AZ31)sheets were produced by transverse gradient extrusion(TGE)process.The flow behavior and dynamic recrystallization during extrusion were systematically analyzed.The microstructures,textures,and mechanical behavior of extruded AZ31 sheet were also analyzed and compared with conventional extruded(CE)sheet.The results showed that fine grain structure and multi-type unique textures were formed in TGE sheet because of the generation of extra flow velocity along transverse direction(TD)and flow velocity gradient along extrusion direction(ED)during extrusion.The basal poles gradually deviated away normal direction(ND)from edge to center of the TGE sheet along TD,and the largest inclination angle at center region reached around 65°.Furthermore,the basal poles inclined from ED to TD 40°-63°,except for the center region of TGE sheet.The TGE sheet presented higher ductility and strain hardening exponent(n-value),but lower yield strength and Lankford value(r-value)in comparison with the CE sheet.Both the basal<a>slip and tensile twins were easy to be activated during deformation,and the largest elongation of 41%and the lowest yield strength of 86.5 MPa were obtained for the ED-center sample in the TGE sheet.展开更多
Mueller matrix imaging is emerging for the quantitative characterization of pathological microstructures and is especially sensitive to fibrous structures.Liver fibrosis is a characteristic of many types of chronic li...Mueller matrix imaging is emerging for the quantitative characterization of pathological microstructures and is especially sensitive to fibrous structures.Liver fibrosis is a characteristic of many types of chronic liver diseases.The clinical diagnosis of liver fibrosis requires time-consuming multiple staining processes that specifically target on fibrous structures.The staining proficiency of technicians and the subjective visualization of pathologists may bring inconsistency to clinical diagnosis.Mueller matrix imaging can reduce the multiple staining processes and provide quantitative diagnostic indicators to characterize liver fibrosis tissues.In this study,a fibersensitive polarization feature parameter(PFP)was derived through the forward sequential feature selection(SFS)and linear discriminant analysis(LDA)to target on the identification of fibrous structures.Then,the Pearson correlation coeffcients and the statistical T-tests between the fiber-sensitive PFP image textures and the liver fibrosis tissues were calculated.The results show the gray level run length matrix(GLRLM)-based run entropy that measures the heterogeneity of the PFP image was most correlated to the changes of liver fibrosis tissues at four stages with a Pearson correlation of 0.6919.The results also indicate the highest Pearson correlation of 0.9996 was achieved through the linear regression predictions of the combination of the PFP image textures.This study demonstrates the potential of deriving a fiber-sensitive PFP to reduce the multiple staining process and provide textures-based quantitative diagnostic indicators for the staging of liver fibrosis.展开更多
In the production of compression springs,high forming velocities and grades of deformation during winding and setting may induce cracks that can lead to failure causing risks of an accident and damage.The AE(acoustic ...In the production of compression springs,high forming velocities and grades of deformation during winding and setting may induce cracks that can lead to failure causing risks of an accident and damage.The AE(acoustic emission)technology,a non-destructive monitoring method,can detect acoustic signals reflected from cracks.To establish this method in the production of technical springs,it was necessary,to find out whether the AE signal is influenced by material properties,phase fractions distribution from tempered martensite,retained austenite,and microstructure including crystallographic texture.In addition,it was investigated to what extent the detected AE signal can be useful to separate between an actual crack and other material responses.Within an in-situ three-point bending test with the AE technology,macro-and micro-crack-typical AE signals were detected for five different spring steel wires(SH,VDSiCr,and FDSiCr according to EN-10270-1 and EN-10270-2).The relative energy related to the initiation,propagation,and growth of cracks caused by mechanical stress was measured using a piezoelectric sensor.If a crack AE signal appeared for the first time,the bending tests were stopped immediately.The results show that the frequency spectrum combined with the intensity of the acoustic signals generated during crack growth depends on the material properties and the crystallographic texture.Furthermore,it could be shown that it is possible to differentiate between micro-crack-typical AE signals and other signals that result from different material responses.展开更多
By selecting flexible polycrystalline Ag as the metallic substrates, highly c axis (001) textured YBCO thin films were fabricated by using a modified magnetron sputtering equipment which can accomplish dynamic de...By selecting flexible polycrystalline Ag as the metallic substrates, highly c axis (001) textured YBCO thin films were fabricated by using a modified magnetron sputtering equipment which can accomplish dynamic deposition and in-situ anneal treatment. The textures of Ag substrates have important effects on forming YBCO films with high critical current densities. Research on the textures of cold rolling Ag at different deformation degrees and recrystallization textures of Ag at different temperatures shows that in plane alignment of YBCO films is difficult to be obtained directly on cold rolling Ag substrates, because of the texture change of Ag during deposition heating of substrates and the strong dependence of J c of YBCO films on grain boundary misorientation angle of substrates. The recrystallization textures with cube (001) and rotated cube (001) in Ag were obtained. Experiments offer a possible prospect for the further research of fabricating sharp biaxially texture in Ag and the following deposition of high J c YBCO films directly on it.展开更多
The evolution of recrystallization textures in high voltage aluminum capacitor foils which are produced with a high level of cold reduction was tracked by analysis of microstructure and crystallographic texture. The r...The evolution of recrystallization textures in high voltage aluminum capacitor foils which are produced with a high level of cold reduction was tracked by analysis of microstructure and crystallographic texture. The results show that the deformation textures are mainly composed of S orientation, Cu orientation and a little B s orientation. During the low temperature stages of final annealing, the iron precipitates first along the sub grain boundaries, and the Fe concentration in the matrix becomes low. Then, the cube grains nucleate preferably into the sub grains. At high temperature stages, the cube nuclei can grow preferably because of their 40°<111> orientation relationship to the S orientation, the main component of the rolling texture. Finally, the cube texture is sharply strong and the R orientation is very weak in the foils.展开更多
Study of dolomite texture can contribute to understanding the process of dolomitization.This research reports textures and homogenization temperatures of dolomites from the Permian-Triassic strata in the Sichuan Basin...Study of dolomite texture can contribute to understanding the process of dolomitization.This research reports textures and homogenization temperatures of dolomites from the Permian-Triassic strata in the Sichuan Basin and the Lower Paleozoic strata in the Tarim Basin,which provided insights into relationships between dolomite textures and their formation temperatures.Our results are summarized as follows:1) dolomites with well-preserved texture indicate low dolomitization temperature.However,in certain diagenetic environments,the hydrothermal dolomitization may completely or partially preserve the original texture of dolomites.2) The formation temperatures of non-planar dolomites are always higher than those of planar dolomites.3) The formation temperatures of dolomite cements are generally higher than those of replacive dolomites.4) Although the formation temperatures of saddle dolomite cements have a wide range,they show higher values than those of the planar subhedral to euhedral dolomite cements.Thus,saddle dolomites could generally be an indicator of high precipitation temperature.5) The fluid Mg/Ca ratio is another element controlling dolomite morphology.Micritic dolomites,which precipitate from hypersaline fluids with a high Mg/Ca ratio in a subaerial environment could also have features of non-planar anhedral crystal shape because of rapid nucleation and crystallization during dolomitization.展开更多
Rotary swaging processing on commercial as-cast pure Mg has been carried out. Bulk texture variation with the processing passes was investigated using large gauge volume by neutron diffraction, of which results showed...Rotary swaging processing on commercial as-cast pure Mg has been carried out. Bulk texture variation with the processing passes was investigated using large gauge volume by neutron diffraction, of which results showed a combination of different components such as {00.2} basal fibre and two weak {10.0} and {11.0} fibres. Asymmetric distribution of the basal fibre around swaging direction was observed and being related to the processing parameters. Texture gradient analysis by synchrotron radiation demonstrates a non-uniform deformation of the RS processed pure Mg from surface to the centre.展开更多
Most of the massive sulfide deposits (VMS) occurring from Precambrian to Cenozoic throughout the world has been subsequently metamorphosed at various grades. Thus, all the original textures have been either completely...Most of the massive sulfide deposits (VMS) occurring from Precambrian to Cenozoic throughout the world has been subsequently metamorphosed at various grades. Thus, all the original textures have been either completely destroyed or strongly modified. However, there are a very few examples, rather younger deposits such as late Cretaceous Turkish VMS deposits and Miocene Kuroko deposits of Japan in which representative and original ore textures are preserved. The Turkish massive sulfide deposits are mainly Cu-Zn-Pb-type and entirely hosted by Late Cretaceous felsic volcanic rocks within a paleoarc geotectonic setting.展开更多
In this paper, shapes and surface textures of quartz grains in 13 layers of a core (NP95 1) collected from a continental slope at the Antarctic Prydz Bay were quantitatively and statistically analyzed. The quartz gr...In this paper, shapes and surface textures of quartz grains in 13 layers of a core (NP95 1) collected from a continental slope at the Antarctic Prydz Bay were quantitatively and statistically analyzed. The quartz grain surfaces exhibit the characteristics caused by intense glaciation and a weaker chemical solution precipitation, indicating the sediments are mainly morainic debris under a low energy marine environment. The obtained quantitatively statistical results of the assemblages of surface textures caused by the chemical solution precipitation are well correlated to the analytical results of micropaleontologic analysis and can be used to better explain the changes of sedimentary environment and paleoclimate occurred in the marine zone concerned.展开更多
In the gneisses from the drillhole ZK2304 of the Donghai area, there have been preserved high- and ultrahigh-pressure metamorphic mineral assemblages, a series of complicated retrogressive textures and relevant metamo...In the gneisses from the drillhole ZK2304 of the Donghai area, there have been preserved high- and ultrahigh-pressure metamorphic mineral assemblages, a series of complicated retrogressive textures and relevant metamorphic reactions. In addition to garnet, jadeititic-clinopyroxene and rutile, other peak stage (M2) minerals in some gneisses include phengite, aragonite and coesite or quartz pseudomorphs after coesite. The typical peak-stage mineral assemblages in gneisses are characterized by garnet + jadeitic-clinopyroxene + rutile + coesite, garnet + jadeitic-clinopyroxene + phengite + rutile ± coesite and garnet + jadeitic-clinopyroxene + aragonite + rutile ± coesite. The grossular content (Gro) in garnet is high and may reach 50. 1 mol%. The SiO2 content of phengite ranges from 54.37% to 54.84% with 3.54-3.57 p.f.u. Quartz pseudomorphs after coesite occur as inclusions in garnet.The gneisses of the Donghai area have been subjected to multistage recrystallization and exhibit a closewise P-T evolutional path characterized by the near-isothermal decompression. The inclusion assemblage (Hb+Ep+Bi+Pl+Qz) within garnet and other minerals has recorded a pre-peak stage (Mi) epidote amphibole fades metamorphic event. High- and ultrahigh-pressure peak metamorphism (M2) took place at T=750-860℃ and P>2.7 GPa. The symplectitic assemblages after garnet, jadeitic-clinopyroxene and rutile imply a near-isothermal decompression metamorphism (M3, M4) during the rapid exhumation. Several lines of evidence of petrography and metamorphic reactions indicate that both gneisses and eclogites have experienced ultrahigh-pressure metamorphism in the Donghai area. This research may be of great significance for an in-depth study of the metamorphism and tectonic evolution in the Su-Lu ultrahigh-pressure metamorphic belt.展开更多
Channel die compression and initial textures are used to activate different deformation mechanisms in a fine-grained magnesium alloy AZ31. The σ-ε curves, microstructures and, particularly, textures are analyzed to ...Channel die compression and initial textures are used to activate different deformation mechanisms in a fine-grained magnesium alloy AZ31. The σ-ε curves, microstructures and, particularly, textures are analyzed to reveal different deformation mechanisms and to compare with those of coarse grained samples. Dominant double-prismatic slip, {1012} twinning and basal slip are detected in three types of samples, respectively, which is similar to those of coarse grained samples. The detrimental effect of shear band formation or {1011} twinning is limited in fine grained microstructure. In addition to the higher flow stress at low temperature an early decrease in flow stress at higher temperature is also found in fine-grained samples in comparison with their coarse-grained counterparts. This softening is ascribed to the early dynamic recrystallization or grain boundary glide.展开更多
Ingot metallurgy (IM) aluminum has long been the subject and attracted the attention of many metallurgists and textural researchers of materials. Due to the introduction of large amounts of ex situ interfaces, however...Ingot metallurgy (IM) aluminum has long been the subject and attracted the attention of many metallurgists and textural researchers of materials. Due to the introduction of large amounts of ex situ interfaces, however, the textures in powder metallurgy (PM) processed aluminum has been rarely reported. In this article, a pure aluminum plate was prepared via PM route. The starting billet was first produced with uni-axially cold compaction and flat hot-extrusion and then followed by cold rolling processes. The hot-extruded and cold rolling deformation textures of the pure PM aluminum at 50%, 80% and 90% cold rolling reductions were studied by orientation distribution functions (ODFs) analysis. The finite element polycrystal model (FEPM) was finally utilized to simulate the cold rolling textural evolution at various stages of cold rolling. In FEPM simulation, the initial hot-extruded textures were taken into account as inputs. The results showed that typical β-fiber texture formed in pure PM aluminum with the cold rolling reduction increased till 80%, and there was not much change after excessive cold rolling deformation. Homogeneous slip is not the only deformation mode in PM processed pure aluminum plate at over 80% cold rolling reduction. The experimental results were qualitatively in good agreement with the simulated ones.展开更多
Textures of high-strength and low-expansion Fe-Ni alloy wires during cold-drawing processes were investigated using X-ray diffraction (XRD) and electron back scatter diffraction (EBSD) techniques. The experimental...Textures of high-strength and low-expansion Fe-Ni alloy wires during cold-drawing processes were investigated using X-ray diffraction (XRD) and electron back scatter diffraction (EBSD) techniques. The experimental results show that the 〈111〉 and 〈100〉 fibre textures are the main texture components, and crystalline grains in the surface are more fine and uniform than those in the center of Fe-Ni alloy wires during cold-drawing processes. It is found that the volume fraction of the 〈111〉 fibre texture component determined by quantitative regression calculation of the Gaussian distribution function reaches more than 60% and the strong 〈111〉 fibre texture component favors the torsional property of Fe-Ni alloy wires.展开更多
A unidirectional carbon/carbon composite (1D-C/C) of low bulk density with textures of poruns granular and isotropic carbons sharply manifests brittle fracture and does not display high pseudoplasticity as expected. ...A unidirectional carbon/carbon composite (1D-C/C) of low bulk density with textures of poruns granular and isotropic carbons sharply manifests brittle fracture and does not display high pseudoplasticity as expected. The results of transmisson electron microscopy (TEM) studies show that the strong interface of fiber-matrix should determine its fracture mode.展开更多
The finite element polycrystal model (FEPM) was extended and applied to simulate the development of the cold rolling textures of matrix aluminum in deformation processed two-phase 10% and 20%Nb/Al(in volume fraction) ...The finite element polycrystal model (FEPM) was extended and applied to simulate the development of the cold rolling textures of matrix aluminum in deformation processed two-phase 10% and 20%Nb/Al(in volume fraction) metal-metal composites on the basis of slip deformation of individual grains. This simulation method can assure the continuity of stress and displacement at the boundary during heterogeneous deformation and take arbitrary boundary conditions into consideration. The starting hot-extruded textures, as initial input condition, were taken into account in the FEPM simulation. The simulation results show that the main texture components and their evolution after various cold rolling reductions in 10% and 20%Nb/Al metal-metal composites are well qualitatively in agreement with the experimental ones. The initially extruded textures are rather weak, so they have no much influence on the simulated final cold rolling textures of the matrix aluminum for Nb/Al composites.展开更多
The feasibility of using B-mode ultrasound image textures and pattern recognition technique to characterize the thermal coagulation in vitro during radiofrequency ablation was investigated. The changes of ultrasonic t...The feasibility of using B-mode ultrasound image textures and pattern recognition technique to characterize the thermal coagulation in vitro during radiofrequency ablation was investigated. The changes of ultrasonic textures in the different regions of samples varied with the heating time in the in-vitro experiments, which would result in that the coagulated and noncoagulated regions of tissue had different ultrasonic textures. Using support vector machine to extract the ultrasonic texture features and characterize the state of tissue, the size and boundaries of thermal lesions could be detected and measured more exactly than only using the gray scale information of B-mode ultrasound image. The proposed method would be applied to the image-guided radiofrequency ablation (IGRA) procedure for monitoring the thermal coagulation.展开更多
基金financially supported by the Guangdong Academy of Science Fund(No.2020GDASYL-20200101001)the Guangdong Major Project of Basic and Applied Basic Research(No.2020B0301030006)+4 种基金the China Postdoctoral Science Foundation(No.2022M720858)the Scientific Research Fund of Hunan Provincial Education Department(No.21B0726)the National Natural Science Foundation of China(Nos.U1764253,51971044,U1910213,52001037,and U207601)the Qinghai Scientific&Technological Program(No.2018-GX-A1)the Natural Science Foundation of Chongqing,China(No.cstc2019jcyjmsxmX0234).
文摘Mg-3Al-1Zn(AZ31)sheets were produced by transverse gradient extrusion(TGE)process.The flow behavior and dynamic recrystallization during extrusion were systematically analyzed.The microstructures,textures,and mechanical behavior of extruded AZ31 sheet were also analyzed and compared with conventional extruded(CE)sheet.The results showed that fine grain structure and multi-type unique textures were formed in TGE sheet because of the generation of extra flow velocity along transverse direction(TD)and flow velocity gradient along extrusion direction(ED)during extrusion.The basal poles gradually deviated away normal direction(ND)from edge to center of the TGE sheet along TD,and the largest inclination angle at center region reached around 65°.Furthermore,the basal poles inclined from ED to TD 40°-63°,except for the center region of TGE sheet.The TGE sheet presented higher ductility and strain hardening exponent(n-value),but lower yield strength and Lankford value(r-value)in comparison with the CE sheet.Both the basal<a>slip and tensile twins were easy to be activated during deformation,and the largest elongation of 41%and the lowest yield strength of 86.5 MPa were obtained for the ED-center sample in the TGE sheet.
基金supported by the National Natural Science Foundation of China(NSFC)(Nos.11974206 and 61527826).
文摘Mueller matrix imaging is emerging for the quantitative characterization of pathological microstructures and is especially sensitive to fibrous structures.Liver fibrosis is a characteristic of many types of chronic liver diseases.The clinical diagnosis of liver fibrosis requires time-consuming multiple staining processes that specifically target on fibrous structures.The staining proficiency of technicians and the subjective visualization of pathologists may bring inconsistency to clinical diagnosis.Mueller matrix imaging can reduce the multiple staining processes and provide quantitative diagnostic indicators to characterize liver fibrosis tissues.In this study,a fibersensitive polarization feature parameter(PFP)was derived through the forward sequential feature selection(SFS)and linear discriminant analysis(LDA)to target on the identification of fibrous structures.Then,the Pearson correlation coeffcients and the statistical T-tests between the fiber-sensitive PFP image textures and the liver fibrosis tissues were calculated.The results show the gray level run length matrix(GLRLM)-based run entropy that measures the heterogeneity of the PFP image was most correlated to the changes of liver fibrosis tissues at four stages with a Pearson correlation of 0.6919.The results also indicate the highest Pearson correlation of 0.9996 was achieved through the linear regression predictions of the combination of the PFP image textures.This study demonstrates the potential of deriving a fiber-sensitive PFP to reduce the multiple staining process and provide textures-based quantitative diagnostic indicators for the staging of liver fibrosis.
文摘In the production of compression springs,high forming velocities and grades of deformation during winding and setting may induce cracks that can lead to failure causing risks of an accident and damage.The AE(acoustic emission)technology,a non-destructive monitoring method,can detect acoustic signals reflected from cracks.To establish this method in the production of technical springs,it was necessary,to find out whether the AE signal is influenced by material properties,phase fractions distribution from tempered martensite,retained austenite,and microstructure including crystallographic texture.In addition,it was investigated to what extent the detected AE signal can be useful to separate between an actual crack and other material responses.Within an in-situ three-point bending test with the AE technology,macro-and micro-crack-typical AE signals were detected for five different spring steel wires(SH,VDSiCr,and FDSiCr according to EN-10270-1 and EN-10270-2).The relative energy related to the initiation,propagation,and growth of cracks caused by mechanical stress was measured using a piezoelectric sensor.If a crack AE signal appeared for the first time,the bending tests were stopped immediately.The results show that the frequency spectrum combined with the intensity of the acoustic signals generated during crack growth depends on the material properties and the crystallographic texture.Furthermore,it could be shown that it is possible to differentiate between micro-crack-typical AE signals and other signals that result from different material responses.
文摘By selecting flexible polycrystalline Ag as the metallic substrates, highly c axis (001) textured YBCO thin films were fabricated by using a modified magnetron sputtering equipment which can accomplish dynamic deposition and in-situ anneal treatment. The textures of Ag substrates have important effects on forming YBCO films with high critical current densities. Research on the textures of cold rolling Ag at different deformation degrees and recrystallization textures of Ag at different temperatures shows that in plane alignment of YBCO films is difficult to be obtained directly on cold rolling Ag substrates, because of the texture change of Ag during deposition heating of substrates and the strong dependence of J c of YBCO films on grain boundary misorientation angle of substrates. The recrystallization textures with cube (001) and rotated cube (001) in Ag were obtained. Experiments offer a possible prospect for the further research of fabricating sharp biaxially texture in Ag and the following deposition of high J c YBCO films directly on it.
文摘The evolution of recrystallization textures in high voltage aluminum capacitor foils which are produced with a high level of cold reduction was tracked by analysis of microstructure and crystallographic texture. The results show that the deformation textures are mainly composed of S orientation, Cu orientation and a little B s orientation. During the low temperature stages of final annealing, the iron precipitates first along the sub grain boundaries, and the Fe concentration in the matrix becomes low. Then, the cube grains nucleate preferably into the sub grains. At high temperature stages, the cube nuclei can grow preferably because of their 40°<111> orientation relationship to the S orientation, the main component of the rolling texture. Finally, the cube texture is sharply strong and the R orientation is very weak in the foils.
基金supported by the National Natural Science Foundation(Nos.41172099,41272130)
文摘Study of dolomite texture can contribute to understanding the process of dolomitization.This research reports textures and homogenization temperatures of dolomites from the Permian-Triassic strata in the Sichuan Basin and the Lower Paleozoic strata in the Tarim Basin,which provided insights into relationships between dolomite textures and their formation temperatures.Our results are summarized as follows:1) dolomites with well-preserved texture indicate low dolomitization temperature.However,in certain diagenetic environments,the hydrothermal dolomitization may completely or partially preserve the original texture of dolomites.2) The formation temperatures of non-planar dolomites are always higher than those of planar dolomites.3) The formation temperatures of dolomite cements are generally higher than those of replacive dolomites.4) Although the formation temperatures of saddle dolomite cements have a wide range,they show higher values than those of the planar subhedral to euhedral dolomite cements.Thus,saddle dolomites could generally be an indicator of high precipitation temperature.5) The fluid Mg/Ca ratio is another element controlling dolomite morphology.Micritic dolomites,which precipitate from hypersaline fluids with a high Mg/Ca ratio in a subaerial environment could also have features of non-planar anhedral crystal shape because of rapid nucleation and crystallization during dolomitization.
文摘Rotary swaging processing on commercial as-cast pure Mg has been carried out. Bulk texture variation with the processing passes was investigated using large gauge volume by neutron diffraction, of which results showed a combination of different components such as {00.2} basal fibre and two weak {10.0} and {11.0} fibres. Asymmetric distribution of the basal fibre around swaging direction was observed and being related to the processing parameters. Texture gradient analysis by synchrotron radiation demonstrates a non-uniform deformation of the RS processed pure Mg from surface to the centre.
文摘Most of the massive sulfide deposits (VMS) occurring from Precambrian to Cenozoic throughout the world has been subsequently metamorphosed at various grades. Thus, all the original textures have been either completely destroyed or strongly modified. However, there are a very few examples, rather younger deposits such as late Cretaceous Turkish VMS deposits and Miocene Kuroko deposits of Japan in which representative and original ore textures are preserved. The Turkish massive sulfide deposits are mainly Cu-Zn-Pb-type and entirely hosted by Late Cretaceous felsic volcanic rocks within a paleoarc geotectonic setting.
文摘In this paper, shapes and surface textures of quartz grains in 13 layers of a core (NP95 1) collected from a continental slope at the Antarctic Prydz Bay were quantitatively and statistically analyzed. The quartz grain surfaces exhibit the characteristics caused by intense glaciation and a weaker chemical solution precipitation, indicating the sediments are mainly morainic debris under a low energy marine environment. The obtained quantitatively statistical results of the assemblages of surface textures caused by the chemical solution precipitation are well correlated to the analytical results of micropaleontologic analysis and can be used to better explain the changes of sedimentary environment and paleoclimate occurred in the marine zone concerned.
基金This work is supported by key project of the National Nat-ural Science Foundation of China(Grant No.50231030)the National High Technology Research and Development Pro-gram of China(Grant No.2003AA331030)the Teaching and Research Award Program for Outstanding Young Teach-ers in Higher Education Institutions.
文摘In the gneisses from the drillhole ZK2304 of the Donghai area, there have been preserved high- and ultrahigh-pressure metamorphic mineral assemblages, a series of complicated retrogressive textures and relevant metamorphic reactions. In addition to garnet, jadeititic-clinopyroxene and rutile, other peak stage (M2) minerals in some gneisses include phengite, aragonite and coesite or quartz pseudomorphs after coesite. The typical peak-stage mineral assemblages in gneisses are characterized by garnet + jadeitic-clinopyroxene + rutile + coesite, garnet + jadeitic-clinopyroxene + phengite + rutile ± coesite and garnet + jadeitic-clinopyroxene + aragonite + rutile ± coesite. The grossular content (Gro) in garnet is high and may reach 50. 1 mol%. The SiO2 content of phengite ranges from 54.37% to 54.84% with 3.54-3.57 p.f.u. Quartz pseudomorphs after coesite occur as inclusions in garnet.The gneisses of the Donghai area have been subjected to multistage recrystallization and exhibit a closewise P-T evolutional path characterized by the near-isothermal decompression. The inclusion assemblage (Hb+Ep+Bi+Pl+Qz) within garnet and other minerals has recorded a pre-peak stage (Mi) epidote amphibole fades metamorphic event. High- and ultrahigh-pressure peak metamorphism (M2) took place at T=750-860℃ and P>2.7 GPa. The symplectitic assemblages after garnet, jadeitic-clinopyroxene and rutile imply a near-isothermal decompression metamorphism (M3, M4) during the rapid exhumation. Several lines of evidence of petrography and metamorphic reactions indicate that both gneisses and eclogites have experienced ultrahigh-pressure metamorphism in the Donghai area. This research may be of great significance for an in-depth study of the metamorphism and tectonic evolution in the Su-Lu ultrahigh-pressure metamorphic belt.
基金This work was supported by the National Natural Sci-ence Foundation of China under grant No.50171009the National 863 Program of China(No.2002A A305501)Part work was performed at IMM RWTH A achen,Germany.
文摘Channel die compression and initial textures are used to activate different deformation mechanisms in a fine-grained magnesium alloy AZ31. The σ-ε curves, microstructures and, particularly, textures are analyzed to reveal different deformation mechanisms and to compare with those of coarse grained samples. Dominant double-prismatic slip, {1012} twinning and basal slip are detected in three types of samples, respectively, which is similar to those of coarse grained samples. The detrimental effect of shear band formation or {1011} twinning is limited in fine grained microstructure. In addition to the higher flow stress at low temperature an early decrease in flow stress at higher temperature is also found in fine-grained samples in comparison with their coarse-grained counterparts. This softening is ascribed to the early dynamic recrystallization or grain boundary glide.
文摘Ingot metallurgy (IM) aluminum has long been the subject and attracted the attention of many metallurgists and textural researchers of materials. Due to the introduction of large amounts of ex situ interfaces, however, the textures in powder metallurgy (PM) processed aluminum has been rarely reported. In this article, a pure aluminum plate was prepared via PM route. The starting billet was first produced with uni-axially cold compaction and flat hot-extrusion and then followed by cold rolling processes. The hot-extruded and cold rolling deformation textures of the pure PM aluminum at 50%, 80% and 90% cold rolling reductions were studied by orientation distribution functions (ODFs) analysis. The finite element polycrystal model (FEPM) was finally utilized to simulate the cold rolling textural evolution at various stages of cold rolling. In FEPM simulation, the initial hot-extruded textures were taken into account as inputs. The results showed that typical β-fiber texture formed in pure PM aluminum with the cold rolling reduction increased till 80%, and there was not much change after excessive cold rolling deformation. Homogeneous slip is not the only deformation mode in PM processed pure aluminum plate at over 80% cold rolling reduction. The experimental results were qualitatively in good agreement with the simulated ones.
文摘Textures of high-strength and low-expansion Fe-Ni alloy wires during cold-drawing processes were investigated using X-ray diffraction (XRD) and electron back scatter diffraction (EBSD) techniques. The experimental results show that the 〈111〉 and 〈100〉 fibre textures are the main texture components, and crystalline grains in the surface are more fine and uniform than those in the center of Fe-Ni alloy wires during cold-drawing processes. It is found that the volume fraction of the 〈111〉 fibre texture component determined by quantitative regression calculation of the Gaussian distribution function reaches more than 60% and the strong 〈111〉 fibre texture component favors the torsional property of Fe-Ni alloy wires.
文摘A unidirectional carbon/carbon composite (1D-C/C) of low bulk density with textures of poruns granular and isotropic carbons sharply manifests brittle fracture and does not display high pseudoplasticity as expected. The results of transmisson electron microscopy (TEM) studies show that the strong interface of fiber-matrix should determine its fracture mode.
文摘The finite element polycrystal model (FEPM) was extended and applied to simulate the development of the cold rolling textures of matrix aluminum in deformation processed two-phase 10% and 20%Nb/Al(in volume fraction) metal-metal composites on the basis of slip deformation of individual grains. This simulation method can assure the continuity of stress and displacement at the boundary during heterogeneous deformation and take arbitrary boundary conditions into consideration. The starting hot-extruded textures, as initial input condition, were taken into account in the FEPM simulation. The simulation results show that the main texture components and their evolution after various cold rolling reductions in 10% and 20%Nb/Al metal-metal composites are well qualitatively in agreement with the experimental ones. The initially extruded textures are rather weak, so they have no much influence on the simulated final cold rolling textures of the matrix aluminum for Nb/Al composites.
基金The National Basic Research Program ofChina (973 Program) (No2003CB716103)Key Project of Shanghai Science and Tech-nology Committee (No05DZ19509)
文摘The feasibility of using B-mode ultrasound image textures and pattern recognition technique to characterize the thermal coagulation in vitro during radiofrequency ablation was investigated. The changes of ultrasonic textures in the different regions of samples varied with the heating time in the in-vitro experiments, which would result in that the coagulated and noncoagulated regions of tissue had different ultrasonic textures. Using support vector machine to extract the ultrasonic texture features and characterize the state of tissue, the size and boundaries of thermal lesions could be detected and measured more exactly than only using the gray scale information of B-mode ultrasound image. The proposed method would be applied to the image-guided radiofrequency ablation (IGRA) procedure for monitoring the thermal coagulation.