Performance of High Thermal Conductivity Dense Silica Bricks and Their High Thermal Conductivity Mechanism

High thermal conductivity dense silica bricks have the higher thermal conductivity than ordinary silica bricks,which is conducive to the realization of energy saving and emission reduction in the iron and steel industry.The performance of ordinary silica bricks and high thermal conductivity dense silica bricks was compared,and the high thermal conductivity mechanism was analyzed.The results show that(1)compared with ordinary silica bricks,high thermal conductivity dense silica bricks have the characteristics of higher thermal conductivity,lower apparent porosity,higher tridymite content,higher compressive strength,and higher thermal expansion;(2)by increasing the tridymite content and reducing the porosity,the close packing of honeycombα-tridymite improves the density and continuity of the SiO_(2)frame structure of the silica bricks,and the larger area perpendicular to the heat transfer direction improves the thermal conductivity of the bricks;(3)the densification of the silica bricks also increases the thermal expansion of the bricks,but they still meet the standard requirements.

Breaking Through Bottlenecks for Thermally Conductive Polymer Composites:A Perspective for Intrinsic Thermal Conductivity,Interfacial Thermal Resistance and Theoretics

Rapid development of energy,electrical and electronic technologies has put forward higher requirements for the thermal conductivities of polymers and their composites.However,the thermal conductivity coefficient(λ)values of prepared thermally conductive polymer composites are still difficult to achieve expectations,which has become the bottleneck in the fields of thermally conductive polymer composites.Aimed at that,based on the accumulation of the previous research works by related researchers and our research group,this paper proposes three possible directions for breaking through the bottlenecks:(1)preparing and synthesizing intrinsically thermally conductive polymers,(2)reducing the interfacial thermal resistance in thermally conductive polymer composites,and(3)establishing suitable thermal conduction models and studying inner thermal conduction mechanism to guide experimental optimization.Also,the future development trends of the three above-mentioned directions are foreseen,hoping to provide certain basis and guidance for the preparation,researches and development of thermally conductive polymers and their composites.

Influence of Yb_2O_3-MgO on Mechanical Properties and Thermal Conductivity of Silicon Nitride Ceramics via Gas Pressure Sintering

In this work,Yb2O3 and Mg O were used as sintering aids in preparing silicon nitride ceramics by gas pressure sintering（ 0. 6 MPa N2atmosphere） to investigate how the amounts of Yb2O3- Mg O influence the mechanical properties and thermal conductivity of silicon nitride ceramics. The total contents of Yb2O3- Mg O added were 1 mol%,2 mol%,4 mol%,6 mol%,8 mol%,10 mol%,12 mol%,14 mol%,keeping the Yb2O3-Mg O molar ratio of 1 ∶ 1 steadily. Curves of the relative density,thermal conductivity and bending strength plotted against the aids content present a ‘mountain＇shape with a maximum at nearly 10 mol% aids. The fracture toughness increased with the amounts of additives up to10 mol% and decreased slightly thereafter. The mechanical properties and thermal conductivity were almost proportional to the amount of the additives before10 mol%. When the content of aids exceeded 10 mol%,it would weaken the mechanical properties and thermal conductivity of the ceramics. The optimum content of Yb2O3- Mg O was 10 mol% by gas pressure sintering（ 0. 6MPa） at 1 850 ℃ for 4 h,which led to a relative density of 98. 9%,a flexural strength of（ 966 ± 38）MPa as well as a fracture toughness of（ 6. 29 ± 0. 29）MPa·m1 /2and thermal conductivity of 82 W /（ m·K）.

Mechanical, electrical, and thermal expansion properties of carbon nanotube-based silver and silver–palladium alloy composites

The mechanical, electrical, and thermal expansion properties of carbon nanotube（CNT）-based silver and silver–palladium（10：1, w/w） alloy nanocomposites are reported. To tailor the properties of silver, CNTs were incorporated into a silver matrix by a modified molecular level-mixing process. CNTs interact weakly with silver because of their non-reactive nature and lack of mutual solubility. Therefore, palladium was utilized as an alloying element to improve interfacial adhesion. Comparative microstructural characterizations and property evaluations of the nanocomposites were performed. The structural characterizations revealed that decorated type-CNTs were dispersed, embedded, and anchored into the silver matrix. The experimental results indicated that the modification of the silver and silver–palladium nanocomposite with CNT resulted in increases in the hardness and Young＇s modulus along with concomitant decreases in the electrical conductivity and the coefficient of thermal expansion（CTE）. The hardness and Young＇s modulus of the nanocomposites were increased by 30%？40% whereas the CTE was decreased to 50%-60% of the CTE of silver. The significantly improved CTE and the mechanical properties of the CNT-reinforced silver and silver–palladium nanocomposites are correlated with the intriguing properties of CNTs and with good interfacial adhesion between the CNTs and silver as a result of the fabrication process and the contact action of palladium as an alloying element.

Transient thermal cracking associated with non-classical heat conduction in cylindrical coordinate system

This paper studies the fracture behavior of a thermoelastic cylinder subjected to a sudden temperature change on its outer surface within the framework of non-classical heat conduction.The heat conduction equation is solved by separation of variable technique.Closed form solution for the temperature field and the associated thermal stress are established.The critical parameter governing the level of the transient thermal stress is identified.Exact expression for the transient stress intensity factor is obtained for a crack in the cylinder.The difference between the non-classical solutions and the classical solution are discussed.It is found that the traditional classical heat conduction considerably underestimates the transient thermal stress and thermal stress intensity factor.