Al2O3 thermal barrier coatings with different TiO2 contents were deposited on 6061 aluminum alloy by plasma spraying. The corrosion resistance, thermal insulation property and phase composition of these coatings were ...Al2O3 thermal barrier coatings with different TiO2 contents were deposited on 6061 aluminum alloy by plasma spraying. The corrosion resistance, thermal insulation property and phase composition of these coatings were investigated. The results indicate that all the feedstock powders exhibit phase transformation during the spray process. With the increase of the TiO2 content in the powder, the corrosion resistance of the coating is enhanced but the thermal insulation property is decreased. This can be attributed to the higher thermal conductivity but lower melting point and brittleness of TiO2 than those of Al2O3, so it is easy for TiO2 to disperse in the brittle Al2O3 substrate during spraying, in which these dispersively distributed TiO2 play the role of hole sealing, releasing stress and reducing cracks.展开更多
Al_(2)O_(3)–SiO_(2)sols were synthesized by using aluminum chloride hex hydrate and tetraethoxysilane(TEOS)as precursors,deionized water and ethanol mixture as the solvent,and propylene oxide as the coagulant aids.Al...Al_(2)O_(3)–SiO_(2)sols were synthesized by using aluminum chloride hex hydrate and tetraethoxysilane(TEOS)as precursors,deionized water and ethanol mixture as the solvent,and propylene oxide as the coagulant aids.Alumina coatings were prepared on the surfaces of hollow quartz filament fiber,then a new lightweight and thermal insulating material were successfully prepared by impregnatingAl_(2)O_(3)–SiO_(2)sol into a needle fabric made by coated hollow quartz filament fiber.The coated quartz fiber,aerogels and composites were characterized by Fourier transform infrared spectroscopy(FTIR),X-ray diffraction(XRD),energy dispersive spectroscopy(EDS),nitrogen adsorption-desorption(BET),scanning electron microscopy(SEM),transmission electron microscopy(TEM),and tensile tests.The effects of different fiber and calcination temperatures on the microstructures and properties ofAl_(2)O_(3)–SiO_(2)composite aerogels were investigated.The test results indicate that the mechanical properties of the aerogels are improved by introducing quartz filament fabrics and the introduction of alumina coating improves the thermal stability of the material.Compared to other fibers,Al_(2)O_(3)-coated hollow quartz fiber has significant advantages as reinforcement for composite,and their tensile strength is well retained after high temperature heat treatment.展开更多
基金Project(51271099)supported by the National Natural Science Foundation of China
文摘Al2O3 thermal barrier coatings with different TiO2 contents were deposited on 6061 aluminum alloy by plasma spraying. The corrosion resistance, thermal insulation property and phase composition of these coatings were investigated. The results indicate that all the feedstock powders exhibit phase transformation during the spray process. With the increase of the TiO2 content in the powder, the corrosion resistance of the coating is enhanced but the thermal insulation property is decreased. This can be attributed to the higher thermal conductivity but lower melting point and brittleness of TiO2 than those of Al2O3, so it is easy for TiO2 to disperse in the brittle Al2O3 substrate during spraying, in which these dispersively distributed TiO2 play the role of hole sealing, releasing stress and reducing cracks.
文摘Al_(2)O_(3)–SiO_(2)sols were synthesized by using aluminum chloride hex hydrate and tetraethoxysilane(TEOS)as precursors,deionized water and ethanol mixture as the solvent,and propylene oxide as the coagulant aids.Alumina coatings were prepared on the surfaces of hollow quartz filament fiber,then a new lightweight and thermal insulating material were successfully prepared by impregnatingAl_(2)O_(3)–SiO_(2)sol into a needle fabric made by coated hollow quartz filament fiber.The coated quartz fiber,aerogels and composites were characterized by Fourier transform infrared spectroscopy(FTIR),X-ray diffraction(XRD),energy dispersive spectroscopy(EDS),nitrogen adsorption-desorption(BET),scanning electron microscopy(SEM),transmission electron microscopy(TEM),and tensile tests.The effects of different fiber and calcination temperatures on the microstructures and properties ofAl_(2)O_(3)–SiO_(2)composite aerogels were investigated.The test results indicate that the mechanical properties of the aerogels are improved by introducing quartz filament fabrics and the introduction of alumina coating improves the thermal stability of the material.Compared to other fibers,Al_(2)O_(3)-coated hollow quartz fiber has significant advantages as reinforcement for composite,and their tensile strength is well retained after high temperature heat treatment.