Synthesis of Y_2O_3 particle enhanced Ni/TiC composite on TC4 Ti alloy by laser cladding

A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.

Arrhenius-type constitutive model and dynamic recrystallization behavior of V-5Cr-5Ti alloy during hot compression

To clarify the high temperature flow stress behavior and microstructures evolution of a V-5Cr-5Ti （mass fraction, %） alloy, the isothermal hot compression tests were conducted in the temperature range of 1423-1573 K with strain rates of 0.01, 0.1, and 1 s-1. The results show that the measured flow stress should be revised by friction and the calculated values of friction coefficient m are in the range of 0.45-0.56. Arrhenius-type constitutive equation was developed by regression analysis. The comparison between the experimental and predicted flow stress shows that the R~ and the average absolute relative error （AARE） are 0.948 and 5.44%, respectively. The measured apparent activation energy Qa is in the range of 540-890 kJ/mol. Both dis-continuous dynamic recrystallization （DDRX） and continuous dynamic recrystallization （CDRX） mechanisms are observed in the deformed alloy, but dynamic recovery （DRV） is the dominant softening mechanism up to a true strain of 1.5.

Hot deformation behavior of Al-9.0Mg-0.5Mn-0.1Ti alloy based on processing maps

Hot deformation behavior of extrusion preform of the spray-formed Al-9.0Mg-0.5Mn-0.1Ti alloy was studied using hot compression tests over deformation temperature range of 300-450 ℃ and strain rate range of 0.01-10 s-1. On the basis of experiments and dynamic material model, 2D processing maps and 3D power dissipation maps were developed for identification of exact instability regions and optimization of hot processing parameters. The experimental results indicated that the efficiency factor of energy dissipate （η） lowered to the minimum value when the deformation conditions located at the strain of 0.4, temperature of 300 ° C and strain rate of 1 s-1. The softening mechanism was dynamic recovery, the grain shape was mainly flat, and the portion of high angle grain boundary （〉15°） was 34%. While increasing the deformation temperature to 400 ° C and decreasing the strain rate to 0.1 s-1, a maximum value of η was obtained. It can be found that the main softening mechanism was dynamic recrystallization, the structures were completely recrystallized, and the portion of high angle grain boundary accounted for 86.5%. According to 2D processing maps and 3D power dissipation maps, the optimum processing conditions for the extrusion preform of the spray-formed Al？9.0Mg？0.5Mn？0.1Ti alloy were in the deformation temperature range of 340-450 ° C and the strain rate range of 0.01-0.1 s-1 with the power dissipation efficiency range of 38%？43%.

Effects of heat treatment on microstructure and microhardness of linear friction welded dissimilar Ti alloys

A detailed investigation for the influence of post weld heat treatment （PWHT） on the microstructure of TC4 and TC17 dissimilar joints was analyzed. The fully transformed microstructure in the as-welded zone indicated that the peak temperature exceeded theβ-transus temperature at the weld interface during linear friction welding. TC4 side was mainly composed of martensiteα′phase with random distribution and it was singleβfor that of TC17. In the thermomechanically affected zones of TC4 and TC17, the structure undergoes severe plastic deformation and re-orientation, yet without altering the phase fractions. After PWHT, in the weld zone of TC4 alloy, the phase transformationα′→α＋βoccurred and the acicularαwas coarsened, which resulted in a decrease in hardness. In the weld zone of TC17 alloy, fineαphase precipitated at the grain boundary and withinβgrains, which resulted in a sharp increase in hardness.

Effects of stabilizing heat treatment on microstructures and creep behavior of Zn-10Al-2Cu-0.02Ti alloy

The microstructures of as-extruded and stabilizing heat-treated Zn-10Al-2Cu-0.02Ti alloys were observed by scanning electron microscopy,transmission electron microscopy,electron probe microanalysis and X-ray diffraction analysis techniques.The change in structure after heat treatment and its effects on room temperature creep behavior were investigated by creep experiments at constant stress and slow strain rate tensile tests.The results show that after stabilizing heat treatment（（350℃,30 min,water-cooling）＋（100℃,12 h,air-cooling））,the amount of α＋η lamellar structure decreases,while the amount of cellular and granular structure increases.The heat-treated Zn-10Al-2Cu-0.02Ti alloy exhibits better creep resistance than the as-extruded alloy,and the rate of steady state creep decreases by 96.9% after stabilizing heat treatment.

MILLER WEAR IN MILLING Ti ALLOY WITH NITROGEN GAS MEDIA

Milling Ti alloy is a very difficult technology. The primary problem is that the miller wear is very rapid and makes the miller break or rapture. Although cutting fluid is mainly used to reduce friction and temperature in cutting area to enhance tool life, it is the largest source of environmental pollution. To develop a technology for the clean and efficient milling Ti alloys, nitrogen gas is used as a cutting media in this paper. Based on lots of experiments and researches, the tool life and wear mechanism of high speed steel miller is analyzed. A conclusion is drawn that, milling with nitrogen gas media yields much longer tool life than dry milling. Tool life equations (Taylor′s equations) are derived for both milling types.

Thermal activation parameters of V-5Cr-5Ti alloy under hot compression

In order to well understand the elementary mechanisms that govern the hot working process of a V？5Cr？5Ti alloy （mass fraction, %）, thermal activation parameters under compression were measured in a temperature range of 1373？1673 K by a Gleeble？3800 system. The results show that the stress exponentn is 4.87 and the activation energyQis 375.89 kJ/mol for the power law equation. The activation energy is determined as 288.34 kJ/mol, which is close to the self-diffusion energy of alloy （270？300 kJ/mol） by introducing a threshold stress（σ0） variable. The typical values of physical activation volume （Vp） and strain rate sensitivity （m） are measured as （120？700）b3 and 0.075？0.122, respectively, by the repeated stress relaxation tests. These activation parameters indicate that the rate controlling mechanism for V？5Cr？5Ti alloy compressed in ranges of 1373？1673 K and 0.001？1.0 s？1 is the dislocation climb by overcoming of forest dislocations.

Surface modification of TC4 Ti alloy by laser cladding with TiC+Ti powders

Laser surface cladding was applied on a TC4 Ti alloy to improve its surface properties. Mixed TiC and Ti powders with a TiC-to-Ti mass ratio of 1：3 were put onto the TC4 Ti alloy and subsequently treated by laser beam. The microstructure and composition modifications in the surfaee layer were carefully investigated by using SEM, EDX and XRD. Due to melting, liquid state mixing followed by rapid solidification and cooling, a layer with graded microstructures and compositions formed. The TiC powders were completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The inter-dendritic areas were filled with fine a＇ phase lamellae enrich in A1. Mainly due to the reduced TiC volume fraction with increasing depth, the hardness decreases with increasing depth in the laser clad layer with a maximum value of HV1400, about 4.5 times of the initial one.

Effect of surface preparation on corrosion properties and nickel release of a NiTi alloy

Surface preparation is potentially important to the corrosion and biomedical properties of NiTi shape memory alloys. The effect of surface preparation on corrosion properties and nickel release of a Ti-56 wt.%Ni alloy has been studied. Surface of the NiTi coupons were prepared by four methods, namely, chemical etching, electropolishing, mechanical polishing and oxidizing, and then examined by corrosion test system. Furthermore, the Ni ion releases from NiTi samples with different surface preparations dipped in 1% HCl solution were analysed. Compared with the surface after chemical treatment, mechanical polishing and thermal oxidation, electropolished surface has better corrosion resistance and less nickel release for not only its lower surface roughness, but also the composition and property of its surface film.

Cellular automaton simulation of dynamic recrystallization behavior in V-10Cr-5Ti alloy under hot deformation conditions

The deformation behavior of V-10Cr-5Ti alloy was studied on the Gleeble-1500 thermomechanical simulator at the temperatures of 950-1350℃, and the strain rates of 0.01-10 s^-1. Based on the Arrhenius model, dislocation density model, nucleation model and grain growth model, a numerical cellular automaton (CA) model coupling simulation of hot deformation is established to simulate and characterize the microstructural evolution during DRX. The results show that the flow stress is fairly sensitive to the strain rate and deformation temperature. The error between the predicted stress by the Arrhenius model and the actual measured value is less than 8%. The initial average grain size calculated by the CA model is 86.25 μm, which is close to the experimental result (85.63 μm). The simulations show that the effect of initial grain size on the dynamic recrystallization microstructure evolution is not significant, while increasing the strain rate or reducing the temperature can refine the recrystallized grains.

Preparation of Diamond-like Carbon Films on the Surface of Ti Alloy by Electro-deposition

In this paper, diamond-like carbon (DLC) films were deposited on Ti alloy by electro-deposition. DLC films were brown andcomposed of the compact grains whose diameter was about 400 nm. Examined by XPS, the main composition of the filmswas carbon. In the Raman spectrum, there were a broad peak at 1350 cm^(-1) and a broad peak at 1600 cm^(-1), which indicatedthat the films were DLC films.

Salt spray corrosion test of micro-plasma oxidation ceramic coatings on Ti alloy

Ceramic coatings were prepared on Ti-6Al-4V alloy in NaAlO2 solution by micro-plasma oxidation （MPO）. The salt spray tests of the coated samples and the substrates were carded out in a salt spray test machine. The phase composition and surface morphology of the coatings were investigated by XRD and SEAM. Severe corrosion occurred on the substrate surface, while there were no obvious corrosion phenomena on the coated samples. The coatings were composed of Al2TiO5 and a little α-Al2O3 and mille TiO2, and the salt spray test did not change the composition of the coatings. The weight loss rate of the coatings decreased with increasing MPO time because of the increase in density and thickness of the coatings. The surface morphology of the coatings was influenced by salt spray corrosion test. Among the coated samples, the coating prepared for 2 h has the best corrosion resistance under salt spray test.

Homogeneity of microstructure and Vickers hardness in cold closed-die forged spur-bevel gear of 20Cr Mn Ti alloy

Cold closed-die forging is a suitable process to produce spur-bevel gears due to its advantages, such as saving materials and time, reducing costs, increasing die life and improving the quality of the product. The homogeneity of microstructure of cold closed-die forged gears can highly affect their service performance. The homogeneity of microstructure and Vickers hardness in cold closed-die forged gear of 20 Cr Mn Ti alloy is comprehensively studied by using optical microscopy and Vickers hardness tester. The results show that the distribution homogeneity of the aspect ratio of grain and Vickers hardness is the same. In the circumferential direction of the gear tooth, the distribution of the aspect ratio of grain and Vickers hardness is inhomogeneous and they gradually decrease from the surface to the center of the tooth. In the radial direction, the distribution of the aspect ratio of grain and Vickers hardness is inhomogeneous on the surface of the gear tooth; while it is relatively homogeneous in the center of the gear tooth. In the axial direction of the gear tooth, the distribution of the aspect ratio of grain and Vickers hardness is relatively homogeneous from the small-end to the large-end of the gear tooth.

Theoretical and experimental investigation of Ti alloy powder production using low-power plasma torches

This study was carried out to investigate the possibility of titanium alloy metal powder production using low-power plasma torches.An argon DC non-transferred arc plasma torch was designed,and numerical analysis was conducted to determine the plasma jet properties and wire temperature.The highest velocities inside the nozzle attachment were between 838 and 1178 m/s.The velocities of the jets at the apex were between 494 and 645 m/s for different gas flow rates.The studied plasma gas flow rates had no significant effect on the effective plasma jet length.It was shown that the plasma jet length can be estimated by numerical analysis using the temperature and velocity changes of the plasma jet over distance.It was observed that the powders produced were spherical without any satellites.As a result of this study,a plasma torch was developed and powder production was performed successfully by using relatively low torch power.

Sinterability of Zirconia Top Coat of Investment Mold for Ti Alloy

In this paper. zirconia is used as top mold material for Ti investment casting. Top mold samples are made by proper mold building technology. The effect of different sintering temperature on chemical composition, microstructure and residual bending strength of the top mold sample is Studied. The volume and homogeneity of the air holes in the top mold are determined by sintering temperature. and finally determined the residual bending strength of the mold sample was determined.

Thermodynamic Analysis on Interaction between Molten Ti Alloys and Oxide Molding Materials

A thermodynamic model has been built up for the interactions between molten Ti alloys and oxide molding materials in the way of decomposition and solution of molding materials, then the influences on the reaction free energy changes have been calculated and discussed.

Effect of Cold Deformation and Annealing on Microstructure of Al-Ti Alloy Target for Sputter Deposition

The microstructure of the Al Ti alloy was studied.It was found that Al x Ti( x <5.0wt%) alloy consists of two phases,the solid solution of titanium in aluminum and the intermetallic compound Al 3Ti.The alloy was deformed by rolling and heat treated.The results show that the second phase precipitates are broken and refined in the matrix by large amount of cold work and crystalline grains are refined by annealing after the cold work.Deformation and heat treatment can improve the distribution of second phase of precipitates in the matrix to certain extent.

CLEAVAGE RUPTURE OF Ti ALLOY TC11 UNDER FATIGUE-CREEP INTERACTION

The cleavage rupture behaviour of the Ti alloy TC11 with various microstructures,i.e., equiaxed,duplex and interweaving,has been studied under fatigue-creep interaction at 520℃.It was found to be not only related to the rate of creep void initiating,but also control- led by the creep strain accumulation on holding under tension test and stress state at crack-tip.This seem to be combinably offected by both value of critic void initiating strain and parameter,V_(GC),of critic void growth.

Mechanical Behaviour and Structure Instability of Al_3Ti Alloy

Trialuminide alloys of elements such as Ti. Nb or Zr are of particular interest as materials for high temperature usage because their density is very low and specific strength and elastic rnoduli are then very high. This report concentrates on recent work on Al3Ti alloys which have been alloyed with ternary elements such that the higher symmetry ordered cubic structure is obtained, leading to somewhat easier operation of deformation mechan isms and hence improved ductility and toughness.Fine details of the crystal structure of cubic trialuminides are considered here and it is shown that the materials generally possess some remnant tetragonal chemical ordering which can affect their me chanical behaviour. In addition the compositional range over which a stable single phase is retained is shown to be extremely small, such that in most cases the materials examined show some form of microstructural instability. These instabilities affect the mechanical behaviour of the materials, for exarnple producing general strengthening. leading to precipitation hardening du ring hig h temperature testing, and causing age hardening instabilities during high temperature static or dynamic testing.Such structural instabifity feads to significant modifications at superdislocations, affecting both the dislocation cores and their associated APB's. Failure for these cubic materials still occurs at very small plastic strains and seems to be determined by difficulties of superdislocation creation near a propagating crack rather than by problems of suitable dislocation configuration and mobility. Possible ways to enhance ductility and toughness by alloying and microstructural modification will be discussed.

Mechanical Properties of Interface between U-0.75Ti Alloy and TiC

The microhardness and modulus changes of the interface between U-0.75Ti alloy and TiC before andafter heat treatment were studied by SEM and Nano Indenter II, and the results show that the hardness and modulusof the interface are greatly increased after 820℃, 2 h water quenching and 450℃, 6 h aging. This result probablycomes from much more U2Ti and U6Ni precipitates along the interface.