Microstructure,interfacial reaction behavior,and mechanical properties of Ti_(3)AlC_(2)reinforced Al6061 composites

The interfacial reaction behavior of Al and Ti_(3)AlC_(2)at different pouring temperatures and its effect on the microstructure and mechanical properties of the composites were investigated.The results show that the addition of3.0 wt.%Ti_(3)AlC_(2)refines the average grain size ofα(Al)in the composite by 50.1%compared to Al6061 alloy.Morphological analyses indicate that an in-situ Al_(3Ti)transition layer of-180 nm in thickness is generated around the edge of Ti_(3)AlC_(2)at 720℃,forming a well-bonded Al-Al_(3Ti)interface.At this processing temperature,the ultimate tensile strength of A16061-3.0 wt.%Ti_(3)AlC_(2)composite is 199.2 MPa,an improvement of 41.5%over the Al6061 matrix.Mechanism analyses further elucidate that 720℃is favourable for forming the nano-sized transition layer at the Ti_(3)AlC_(2)edges.And,the thermal mismatch strengthening plays a dominant role in this state,with a strengthening contribution of about 74.8%.

Morphology and Frictional Characteristics Under Electrical Currents of Al_2O_3/Cu Composites Prepared by Internal Oxidation

Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.

Microstructure and evolution of(TiB_2+Al_2O_3)/NiAl composites prepared by self-propagation high-temperature synthesis

（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.

Friction and wear properties of in-situ synthesized Al_2O_3 reinforced aluminum composites

Al-5%Si-AI2O3 composites were prepared by powder metallurgy and in-situ reactive synthesis technology. Friction and wear properties of Al-5%Si-Al2O3 composites were studied using an M-2000 wear tester. The effects of load, sliding speed and long time continuous friction on friction and wear properties of Al-5%Si-Al2O3 composites were investigated, respectively. Wear surface and wear mechanism of Al-5%Si-Al2O3 composites were studied by Quanta 200 FE-SEM. Results showed that with load increasing, wear loss and coefficient of friction increased. With sliding speed going up, the surface temperature of sample made the rate of the producing of oxidation layer increase, while wear loss and coefficient of friction decreased. With the sliding distance increasing, coefficient of friction increased because the adhesive wear mechanism occurred in the initial stage, then formation and destruction of the oxide layer on the surface of the sample tended to a dynamic equilibrium, the surface state of the sample was relatively stable and so did the coefficient of friction. The experiment shows that the main wear mechanism of Al-5%Si-Al2O3 composites includes abrasive wear, adhesive wear and oxidation wear.

Hot deformation and processing maps of Al_2O_3/Al composites fabricated by flake powder metallurgy

The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.

Effect of CuO particle size on synthesis temperature and microstructure of Al_2O_(3p)-Al composites from Al-CuO system

Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.

Modification of Nano-α-Al2O3 and Its Influence on the Surface Properties of Waterborne Polyurethane Resin Composite Passivation Films

Silane coupling agent KH560 was used to modify the surface of nano-α-Al2O3 in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al2O3 was determined by nano-particle size analyzer, and the effects of nano-α-Al2O3 content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al2O3 were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al2O3 dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al2O3 increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al2O3.

Synthesis of Y_2O_3 particle enhanced Ni/TiC composite on TC4 Ti alloy by laser cladding

A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.

IN SITU PROCESSING OF Al_(2)O_(3) WHISKERS REINFORCED Ti-Al INTERMETALLIC COMPOSITES

In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.

Preparation of Z-scheme WO_3(H_2O)_(0.333)/Ag_3PO_4 composites with enhanced photocatalytic activity and durability

Ag3PO4 is widely used in the field of photocatalysis because of its unique activity. However, photocorrosion limits its practical application. Therefore, it is very urgent to find a solution to improve the light corrosion resistance of Ag3PO4. Herein, the Z-scheme WO3(H2O)0.333/Ag3PO4 composites are successfully prepared through microwave hydrothermal and simple stirring. The WO3(H2O)0.333/Ag3PO4 composites are characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy and UV-Vis spectroscopy. In the degradation of organic pollutants, WO3(H2O)0.333/Ag3PO4 composites exhibit excellent performance under visible light. This is mainly attributed to the synergy of WO3(H2O)0.333 and Ag3PO4. Especially, the photocatalytic activity of 15%WO3(H2O)0.333/Ag3PO4 is the highest, and the methylene blue can be completely degraded in 4 min. In addition, the stability of the composites is also greatly enhanced. After five cycles of testing, the photocatalytic activity of 15%WO3(H2O)0.333/Ag3PO4 is not obviously decreased. However, the degradation efficiency of Ag3PO4 was only 20.2%. This indicates that adding WO3(H2O)0.333 can significantly improve the photoetching resistance of Ag3PO4. Finally, Z-scheme photocatalytic mechanism is investigated.

Reaction thermodynamics and kinetics on in situ Al_2O_3/Cu composites

The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.

Aluminum matrix composites reinforced by in situ Al_2O_3 and Al_3Zr particles fabricated via magnetochemistry reaction

Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.

Properties of Hot-Pressed Al_2O_3-Fe Composites

Alumina-(0 similar to 20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed-alumina and iron powders at 1400 degreesC and 30 MPa for 30 min. Hot-pressed bodies with nearly theoretical density were obtained for addition up to 10 vol. pct Fe, but relative density decreased gradually with further increase in Fe addition. The materials exhibit a homogeneous dispersion of Fe. Fracture strength of the composites exhibits a maximum value of 604 MPa at 15 vol. pct Fe, which is 1.5 times that of alumina alone. Fracture toughness increases with the increase in Fe content, reaching 7.5 MPa.m(1/2) at 20 vol. pct Fe. The theoretical values of fracture toughness was calculated and compared with the experimental one. Toughening mechanisms of the composites are also discussed.

Influence of Adding Ti Powder in Preform on Microstructure and Mechanical Properties of Al_2O_3p/Steel Composites by Squeeze Casting

To improve the mechanical properties of alumina particulates reinforced steel matrix composite, Ti powder was added into the alumina preform, a 5140 steel matrix composite was fabricated by squeeze casting, and the influences of Ti powder on the microstructure, hardness and bending strength of the composite were investigated, compared with the composite without adding Ti powder. Applied Ti powder and alumina particulates were 10-25 μm and 100-180 μm in size, respectively. Both composites were successfully fabricated, however Ti powder addition increased the infiltration thickness of the composite. In the Ti contained composite, a TiC film in micron scale is formed on the surface of alumina particles, many TiC aggregates are dispersed in the steel matrix without obvious remaining Ti powder. The hardness and the three-point bending strength of the composite reach 49.5 HRC and 1 018 MPa, respectively, which are 17.9% and 52.4% higher than those of the composite in the absence of Ti addition. Fracture morphology shows that the debonding of alumina particulates is eliminated for the composite in the presence of Ti addition. Sessile drop test shows the average wetting angle between 5140 steel and that of Ti coated Al2O3 is about 82.15°, much lower than the wetting angle 150° between steel and pure Al2O3. Therefore, the increase in the mechanical properties of the composite is attributed to the improvement of Al2O3 p/steel interface wetting and bonding by adding Ti powder in the preform.

Crystallization and dielectric properties of lead-free glass-ceramic composites with Gd_2O_3 addition

Lead-free glass-ceramic composites in barium sodium niobate silica system with Gd2O3 addition were synthesized through melt-casting fol-lowed by controlled crystallization technique. Crystallization and dielectric properties of the Gd2O3 adding glass-ceramic composites were investigated. With the increase in the concentration of Gd2O3, the glass transition temperature and the crystallization temperature of the pre-cursor glass shift towards the higher temperature. The crystallization behavior that occurred during the heat treatment procedure leads to the enhancement of dielectric constant. All the three compositions of glass-ceramic composites exhibit ferroelectricity when tested at room tem-perature. Both the values of the remanent polarization and coercive field are enhanced regularly with the gradual increase in the concentration of Gd2O3 additive under the same testing field.

MICROSTRUCTURES AND MECHANICAL PROPERTIES OF IN-SITU Al_2O_3/TiAl COMPOSITES BY EXOTHERMIC DISPERSION METHOD

In-situ Al2O3/TiAl composites were fabricated by pressure-assisted exothermic dispersion （PAXD） method from elemental powder mixtures of Ti, Al, TiO2, and Nb2O5. The microstructures and mechanical properties of the as-sintered composites are investigated. The results show that the as-sintered products consist of γ-TiAl, α2-Ti3Al, Al2O3, and NbAl3 phases. Microstructure analysis indicates that Al2O3 particles tend to disperse on the grain boundaries. Application of a moderate pressure of 35 MPa at 1200℃ yields Al2O3/TiAl composites with fine Al2O3 reinforcement and a discontinuous network linking by Al2O3 particles. The aluminide component has a fine submicron γ ＋α2 lamellar microstructure. With increasing Nb2O5 content, Al2O3 particles are dispersed uniformly in the matrix. The hardness of the composites increases gradually, and the bending strength and fracture toughness of the composites reach to the maximum value, respectively.

Effect of Al2O3np on the Properties and Microstructure of B4Cp/Al Composites

Aluminum-matrix boron carbide (B4Cp/Al) is a kind of neutron absorbing material widely used in nuclear spent fuel storage. In order to improve the tensile property of B4Cp/Al composites, a new type of nano-Al2O3 particle (Al2O3np) reinforced B4Cp/Al + Al2O3np composites were prepared by powder metallurgy method. The Monte Carlo particle transport program (MCNP) was used to determine the influence of Al2O3np on the thermal neutron absorptivity of composites. The universal material testing machine and scanning electron microscope (SEM) were used to study the mechanical properties, microstructure and fracture morphology of B4Cp/Al composites. The results indicated that the neutron absorption properties of B4Cp/Al composites were not affected by the addition of nano-Al2O3 particles in the range of 1 wt%-15 wt%. The addition of Al2O3np can obviously reduce the grain size of B4Cp/Al matrix metals thus improve the tensile strength of the composites. The addition threshold of Al2O3np is about 2.5 wt%. Both B4Cp and Al2O3np change the fracture characteristics of the composites from toughness to brittleness, and the latter is more important.

Effects of Y_2O_3 on Thermal Shock of Al_2O_3/TiCN Composites

Thermal shock resistance of Al2O3-TiCN(30%)-Y2O3(0.2%) composite was studied by hot pressing(HP) method at different temperatures. The study shows that thermal shock resistance of the material is determined by its microstructure and reinforced mechanism. According to SEM and calculation of thermal shock, the fractured surface of Al2O3-30%TiCN-0.2%Y2O3 composite is undulate. The residual strength of Al2O3-30%TiCN-0.2%Y2O3 is higher than Al2O3-30%TiCN at 200～800 ℃ after thermal shock. Cracks initiation resistance (R′)and cracks propagation resistance (R″″)of Al2O3-30%TiCN-0.2%Y2O3 composite increases 12% and 5% respectively compared with that of Al2O3-30%TiCN. It matches with experimental results. The addition of Y2O3 forms YAG that inhibits crystal growth, and increases fracture stress, fracture toughness, cracks initiation resistance and cracks propagation resistance. Therefore, thermal shock resistance increases. The fracture work of Al2O3-30%TiCN and Al2O3-30%TiCN-0.2%Y2O3 composites are 132 and 148 J·m-2 respectively.

Effects of Cerium on the Mechanical Properties of the ZA22／Al_2O_3 Composites

ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that both the UTS and the hardness are improved and the impact toughness is decreased with the increase of the volume fraction of fibers (Vf). After Ce is added ,UTS (Vf>15%) and the hardness are improved at room temperature because of the modification of Ce, but the impact toughness and UTS at elevated temperature are lowered.The filtered action of the fiber preform results in that the influence of the amount of Ce added from 0. 1 wt% to 0. 5 wt% on the mechanical properties of the composites can be ignored.

Microstructure and Tribological Behavior of Al2O3 Particle Reinforced Al Matrix Composites Fabricated by Spark Plasma Sintering

Nanoparticles and microparticles reinforced Al matrix composites were fabricated by spark plasma sintering, and the microstructure and tribological properties were investigated systemically. The nano-Al2O3 particle and micro-Al2O3 particle uniformly dispersed in Al matrix composites. The introduction of nanoparticles is beneficial to the decrease of friction coefficient and wear rate, while microparticles are responsible to the high friction coefficient, resulting in the abrasive wear. With the introduction of both nanoparticles and microparticles, their synergic effect will lead to the variation of tribological behavior.