In Mg-Ca alloys the grain refining mechanism,in particular regarding the role of nucleant substrates,remains the object of debates.Although native MgO is being recognised as a nucleating substrate accounting for grain...In Mg-Ca alloys the grain refining mechanism,in particular regarding the role of nucleant substrates,remains the object of debates.Although native MgO is being recognised as a nucleating substrate accounting for grain refinement of Mg alloys,the possible interactions of MgO with alloying elements that may alter the nucleation potency have not been elucidated yet.Herein,we design casting experiments of Mg-xCa alloys varied qualitatively in number density of native MgO,which are then comprehensively studied by advanced electron microscopy.The results show that grain refinement is enhanced as the particle number density of MgO increases.The native MgO particles are modified by interfacial layers due to the co-segregation of Ca and N solute atoms at the MgO/Mg interface.Using aberration-corrected scanning transmission electron microscopy and electron energy loss spectroscopy,we reveal the nature of these Ca/N interfacial layers at the atomic scale.Irrespective of the crystallographic termination of MgO,Ca and N co-segregate at the MgO/Mg interface and occupy Mg and O sites,respectively,forming an interfacial structure of a few atomic layers.The interfacial structure is slightly expanded,less ordered and defective compared to the MgO matrix due to compositional deviations,whereby the MgO substrate is altered as a poorer template to nucleate Mg solid.Upon solidification in a TP-1 mould,the impotent MgO particles account for the grain refining mechanism,where they are suggested to participate into nucleation and grain initiation processes in an explosive manner.This work not only reveals the atomic engineering of a substrate through interfacial segregation but also demonstrates the effectiveness of a strategy whereby native MgO particles can be harnessed for grain refinement in Mg-Ca alloys.展开更多
Additive manufacturing(AM)of Mg alloys has become a promising strategy for producing complex structures,but the corrosion performance of AM Mg components remains unexploited.In this study,wire and arc additive manufac...Additive manufacturing(AM)of Mg alloys has become a promising strategy for producing complex structures,but the corrosion performance of AM Mg components remains unexploited.In this study,wire and arc additive manufacturing(WAAM)was employed to produce single AZ31 layer.The results revealed that the WAAM AZ31 was characterized by significant grain refinement with non-textured crystallographic orientation,similar phase composition and stabilized corrosion performance comparing to the cast AZ31.These varied corrosion behaviors were principally ascribed to the size of grain,where cast AZ31 and WAAM AZ31 were featured by micro galvanic corrosion and intergranular corrosion,respectively.展开更多
An alloy of A1-8wt% Si-0.8wt% Fe was cast in a metallic die, and its microstrucmral changes due to Ti-B refiner and Sr modifier additions were studied. Apart from usual refinement and modification of the microstructur...An alloy of A1-8wt% Si-0.8wt% Fe was cast in a metallic die, and its microstrucmral changes due to Ti-B refiner and Sr modifier additions were studied. Apart from usual refinement and modification of the microstructure, some mutual influences of the additives took place, and no mutual poisoning effects by these additives, in combined form, were observed. It was noticed that the dimensions of the iron-rich intermetallics were influenced by the additives causing them to become larger. The needle-shaped intermetallics that were obtained from refiner addition became thicker and longer when adding the modifier. It was also found that a-Al and eutectic silicon phases preferentially nucleate on different types of intermetallic compounds. The more iron content of the intermetallic compounds and the more changes in their dimensions occurred. Formation of the shrinkage porosities was also observed.展开更多
Al-Ti-C grain refiner was prepared by SHS (self-propagating high-temperature synthesis )-melting technique. The effect of La on the microstructures of grain refiner was studied by OM, TEM, SEM, XRD, and EDS. The exp...Al-Ti-C grain refiner was prepared by SHS (self-propagating high-temperature synthesis )-melting technique. The effect of La on the microstructures of grain refiner was studied by OM, TEM, SEM, XRD, and EDS. The experimental results indicate that La can improve the wettability between liquid aluminum and graphite ; the addition of La results in dispersive distribution of TiAl3 and TiC particles in the matrix. An excellent grain refining performance of Al-Ti-C grain refiner on commercially pure Al was obtained.展开更多
Erratum to:International Journal of Minerals, Metallurgy and MaterialsVolume 28, Number 7, July 2021, Page 1112 The original version of this article unfortunately contained mistakes. Symbols in Table 2 are used incorr...Erratum to:International Journal of Minerals, Metallurgy and MaterialsVolume 28, Number 7, July 2021, Page 1112 The original version of this article unfortunately contained mistakes. Symbols in Table 2 are used incorrectly.展开更多
The effects of different complex shear stress conditions on grain refinement and texture evolution of Mg-13Gd-4Y-2Zn-0.5Zr alloy were investigated.With increasing strain rate,the average grain size of compression-shea...The effects of different complex shear stress conditions on grain refinement and texture evolution of Mg-13Gd-4Y-2Zn-0.5Zr alloy were investigated.With increasing strain rate,the average grain size of compression-shear(CS)and compression-torsion(CT)samples are decreased,and the grain size of dynamic recrystallization(DRX)grains is also decreased.This is because that the precipitation number ofβphases is increased,and the hindering effect on grain growth can be significantly enhanced.The DRX fractions of CS and CT samples are decreased with increased strain rate.The low DRX fraction at high strain rate is related to the insufficient time for grains to nucleate.The DRX process can be promoted by the PSN mechanism of second phases,and the grain growth can be restricted by the pinning effect.At the same time,the texture strength is enhanced as the strain rate increased.Besides,the kinking degree of lamellar long-period stacking ordered(LPSO)phases is increased.Under complex shear stress conditions,non-basal slip,especially pyramidal slip,is easily activated and the texture is deflected greatly.Compared with the CS samples,CT samples have smaller average grain size,higher DRX fraction,and lower texture strength for a certain strain rate.This is because that the equivalent stress of the CT sample is larger,the stress triaxiality is smaller,so more serious dislocations are piled up near grain boundaries and second phases.At the same time,since CT sample was sheared with torsion,the dislocation movement path can be called“rotational dislocation accumulation”,and the longer distribution path of the CT sample is generated,so more sub-grains and low-angle grain boundaries(LAGBs)are formed.Compared with the CS sample,more huge-angle grain boundaries(HAGBs)and DRX grains are formed from grain boundary to grain interior,so better grain refinement effect is achieved.展开更多
High-performance cast magnesium rare-earth(Mg-RE) alloys are one of the most important materials among all developed Mg alloy families, and have shown great potential in military and weapons, aerospace and aviation, o...High-performance cast magnesium rare-earth(Mg-RE) alloys are one of the most important materials among all developed Mg alloy families, and have shown great potential in military and weapons, aerospace and aviation, orthopedic implants, etc. Controlling grain size and distribution of it is key to the promising mechanical performance of Mg-RE alloy casting components. During the casting of a real component, nearly every procedure in the fabrication process will influence the grain refinement effect. The procedure may include and may not be limited to the chemical inoculations, possibly applied physical fields, the interfere between grain refiner and purifications, and the casting techniques with different processing parameters. This paper reviews the recent advances and proposed future developments in these categories on grain refinement of cast Mg-RE alloys. The review will provide insights for the future design of grain refinement techniques,the choosing of processing parameters, and coping strategies for the failure of coarsening for cast Mg-RE components with high quality and good performance.展开更多
Low absolute strength becomes one major obstacle for the wider applications of low/no rare-earth(RE) containing Mg alloys. This review firstly demonstrates the importance of grain refinement in improving strength of M...Low absolute strength becomes one major obstacle for the wider applications of low/no rare-earth(RE) containing Mg alloys. This review firstly demonstrates the importance of grain refinement in improving strength of Mg alloys by comprehensively comparing with other strategy, e.g., precipitation strengthening. Dynamic recrystallization(DRX) plays a crucial role in refining grain size of Mg wrought alloys.Therefore, secondly, the DRX models, grain nucleation mechanisms and the related grain refinement abilities in Mg alloys are summarized,including phase boundary, twin boundary and general boundary induced recrystallization. Thirdly, the newly developed low-RE containing Mg alloy, e.g., Mg-Ce, Mg-Nd and Mg-Sm based alloys, and the RE-free Mg alloys, e.g., Mg-Al, Mg-Zn, Mg-Sn and Mg-Ca based alloy,are reviewed, with the focus on enhancing the mechanical properties mainly via the grain refinement strategy. At the last section, the perspectives and outstanding issues concerning high-performance Mg wrought alloys are also proposed. This review is meant to promote the deep understanding on the critical role of grain refinement in Mg alloys and provide reference for the development of other high strength and low-cost Mg alloys which are fabricated by the conventional extrusion/rolling processing.展开更多
A wide-spectrum pulsed magnetic field(WSPMF)was obtained by adjusting the number of current pulses and the pulse interval between adjacent pulses.The effect of WSPMF on the grain refinement of pure aluminium was studi...A wide-spectrum pulsed magnetic field(WSPMF)was obtained by adjusting the number of current pulses and the pulse interval between adjacent pulses.The effect of WSPMF on the grain refinement of pure aluminium was studied.The distribution of electromagnetic force and flow field in the melt under the WSPMF was simulated to reveal the grain refining mechanism.Results show that the grain refinement is attributed to the combined effect of the melt flow and oscillation under a WSPMF.When the pulse interval is 5 ms,the extreme value of electromagnetic force is the highest,and the size of the crystal nucleus is 0.35 mm.In the case of similar flow rates,the grain size gradually decreases as the pulse interval increases.The range of the harmonic frequency of the magnetic field gradually expands with the increase of the pulse interval,which can provide more energy for nucleation at the solid-liquid interface and promote nucleation.展开更多
Numerical simulation is one of the important auxiliary methods for studying materials-related problems. In this study, phase field simulation was employed to investigate the refinement behavior of BAg55CuZn-x B brazin...Numerical simulation is one of the important auxiliary methods for studying materials-related problems. In this study, phase field simulation was employed to investigate the refinement behavior of BAg55CuZn-x B brazing alloys. Simulation and experimental studies were conducted for B contents ranging from 0 wt.% to 0.2 wt.%. The results demonstrated that the addition of 0.05 wt.% B in the brazing alloy leads to a significant refinement effect. As the B content increases, the grain size further reduces, and a refinement stagnation phenomenon occurs after exceeding 0.15 wt.%. The solidification process of brazing alloys with different B content was predicted by simulation, and the simulation results showed that with the increase of B content, the initial number of nucleation increased, and the radius of the dendrite tip decreased. The simulation results are in good agreement with the experimental findings, providing further evidence of the refining effect of the B element and the reliable predictive capability of the phase field model.展开更多
This work aims to present a perspective for porosity formation in three different alloys:A356,A413 and A380.1 by taking into account the addition of Al-B grain refiners:AlTi5B1 and Al3B.The directional solidification ...This work aims to present a perspective for porosity formation in three different alloys:A356,A413 and A380.1 by taking into account the addition of Al-B grain refiners:AlTi5B1 and Al3B.The directional solidification method was used,and microstructural changes of the alloys and its correlation with porosity formation were investigated.Pore size,number of pores,average pore length and distribution of pores were statistically analyzed.Also,external shrinkage was examined,and the volume of external shrinkage was calculated.It was found that there was a relationship between external shrinkage and the size and number of pores.As the size and number of pores internally decrease,external shrinkage increases.Additionally,porosity is decreased in all the three Al-Si alloys when Al-B grain refiners are used.The distribution of pore diameters is low when AlTi5B1 is used.Grain refiners have a different effect on porosity formation of Al-Si alloys with regard to their solidification morphology.展开更多
The effects of vibration and grain refiner on the microstructure of semisolid slurry of hypoeutectic Al-Si alloy were studied. The impact of vibration on the convection of liquid was conducted by using a system of wat...The effects of vibration and grain refiner on the microstructure of semisolid slurry of hypoeutectic Al-Si alloy were studied. The impact of vibration on the convection of liquid was conducted by using a system of water-particle tracer. The 356 melt at temperature of 630-660 ℃ with or without grain refiner Al-5%Ti-1%B was poured into a metal cup as the vibrating vessel, then it was cooled to 590-610 ℃ in the semisolid zone and kept for some time, subsequently vibration with different frequencies was applied. The results show that the primary α(Al) particles become finer and rounder with the increase of vibration frequency. The slurry with primary α(Al) equivalent particle diameter(EPD) of about 90 μm and average shape coefficient(ASC) of about 0.5 can be prepared under vibration of 20 Hz. With the combined action of vibration and grain refiner Al-5Ti-B, even smaller and rounder spheroids with EPD of about 85 μm and ASC of about 0.6 are obtained.展开更多
Grain refinement of superalloy K4169 was achieved by adding refiners into the alloy melt and their effects on the mechanical properties were investigated. The tensile properties at room temperature and 700 ℃ and low ...Grain refinement of superalloy K4169 was achieved by adding refiners into the alloy melt and their effects on the mechanical properties were investigated. The tensile properties at room temperature and 700 ℃ and low cycle fatigue properties at room temperature were compared for both conventional and fine grained test bars. The results indicate that the rupture strength, yield strength, elongation and reduction of area for refined grains are all much superior to those for coarse ones. Whereas the elongation and reduction of area of fine grained samples decrease at 700 ℃. Low cycle fatigue properties of samples with refined grains at room temperature are improved significantly. In addition, the degree of dispersion of low cycle fatigue data of samples with refined grains is diminished.展开更多
The hereditary effect of Al Ti, Al Ti B, Al Sr master alloys on the structure and properties of A356.2 alloys was investigated, and comparison analysis between the master alloys used in the foundry industry and the fi...The hereditary effect of Al Ti, Al Ti B, Al Sr master alloys on the structure and properties of A356.2 alloys was investigated, and comparison analysis between the master alloys used in the foundry industry and the fine crystalline grain refiners produced by technologies of Samara State Technical University was conducted. The results show that less than 0.5% additions of FCR master alloys can promote 8%~20% in the elongation of as cast A356.2 alloys. FCR additives are more efficient in comparison with conventional grain refiners and modifiers. Their effectiveness depends on their genetic effect of their finer structures.展开更多
Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure o...Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.展开更多
An Al-3Ti-0.2C-1RE grain refiner was prepared by in-situ reaction method.The microstructure was investigated by optical microscopy(OM),scanning electron microscopy(SEM) equipped with energy-dispersive spectrometry(EDS...An Al-3Ti-0.2C-1RE grain refiner was prepared by in-situ reaction method.The microstructure was investigated by optical microscopy(OM),scanning electron microscopy(SEM) equipped with energy-dispersive spectrometry(EDS) and X-ray diffraction(XRD).The results show that the Al-3Ti-0.2C-1RE grain refiner is composed of α-Al,TiAl3,TiC and Ti2 Al20 Ce phases.Compared with Al-3Ti-0.2C refiner,the morphology of TiAl3 phase is changed and Ti2 Al20 Ce phases form with the addition of RE.Accordingly,the refining performance is improved.The phase forming process of the refiner is as follows: Blocky Ti2 Al20 Ce and fine blocky TiAl3 form in the melt at the initial stage of reaction,then the fine blocky TiAl3 gradually disappears,and the blocky Ti2 Al20 Ce grows bigger with the increase of holding time.The predominant mechanism to synthesize TiC particles is the reaction between high concentration of solute Ti atoms and graphite particles.展开更多
The effects of grain refining parameters on grain size of AM60B magnesium alloy have been investigated using an Al-5Ti-1B master alloy as refiner; and an appropriate refining technique has been developed. The results ...The effects of grain refining parameters on grain size of AM60B magnesium alloy have been investigated using an Al-5Ti-1B master alloy as refiner; and an appropriate refining technique has been developed. The results indicate that the Al-Ti-B master alloy is an effective grain refiner for AM60B alloy and the grain size can be decreased from 348 μm to 76 μm. Raising the addition temperature or the pouring temperature is beneficial for grain refinement; while for the addition amount and holding time, there is an optimal value. The appropriate grain refining technique is that 0.3% Al-Ti-B master alloy is added at 780oC and then the melt is held for 30 min before pouring. The above phenomena can be explained by the refining mechanisms that have been proposed from the related studies on Al and Mg alloys and theoretical analysis.展开更多
Through the use of purification and recirculation superheating techniques on molten glass,the Ni65Cu33Co2 alloy was successfully undercooled to a maximum temperature of 292 K.High-speed photography was employed to cap...Through the use of purification and recirculation superheating techniques on molten glass,the Ni65Cu33Co2 alloy was successfully undercooled to a maximum temperature of 292 K.High-speed photography was employed to capture the process of interface migration of the alloy liquid,allowing for an analysis of the relationship between the morphological characteristics of the alloy liquid solidification front and the degree of undercooling.Additionally,the microstructure of the alloy was examined using metallographic microscopy,leading to a systematic study of the microscopic morphological characteristics and evolution laws of the refined structure during rapid solidification.The research reveals that the grain refining mechanism of the Ni-Cu-Co ternary alloy is consistent with that of the binary alloy(Ni-Cu).Specifically,under low undercooling conditions,intense dendritic remelting was found to cause grain refinement,while under high undercooling conditions,recrystallization driven by accumulated stress and plastic strain resulting from the interaction between the liquid flow and the primary dendrites caused by rapid solidification was identified as the main factor contributing to grain refinement.Furthermore,the study highlights the significant role of the Co element in influencing the solidification rate and reheat effect of the alloy.The addition of Co was also found to facilitate the formation of non-segregated solidification structure,indicating its importance in the overall solidification process.展开更多
In order to obtain Mg alloys with fine microstructures and high mechanical performances,a novel friction-based processing method,name as“constrained friction processing(CFP)”,was investigated.Via CFP,defect-free Mg-...In order to obtain Mg alloys with fine microstructures and high mechanical performances,a novel friction-based processing method,name as“constrained friction processing(CFP)”,was investigated.Via CFP,defect-free Mg-Zn-Ca rods with greatly refined grains and high mechanical properties were produced.Compared to the previous as-cast microstructure,the grain size was reduced from more than 1 mm to around 4μm within 3 s by a single process cycle.The compressive yield strength was increased by 350%while the ultimate compressive strength by 53%.According to the established material flow behaviors by“tracer material”,the plastic material was transported by shear deformation.From the base material to the rod,the material experienced three stages,i.e.deformation by the tool,upward flow with additional tilt,followed by upward transportation.The microstructural evolution was revealed by“stop-action”technique.The microstructural development at regions adjacent to the rod is mainly controlled by twinning,dynamic recrystallization(DRX)as well as particle stimulated nucleation,while that within the rod is related to DRX combined with grain growth.展开更多
An electrostrictive uniaxial ultrasonic levitation reaction system was designed to perform TiC synthesis reaction by suspending graphite powder in Al-3Ti melt and an Al-3Ti-0.15C grain refiner alloy was obtained. The ...An electrostrictive uniaxial ultrasonic levitation reaction system was designed to perform TiC synthesis reaction by suspending graphite powder in Al-3Ti melt and an Al-3Ti-0.15C grain refiner alloy was obtained. The results show that sound pressure node in which graphite suspends is formed in the melt between radiation block and reflecting board by ultrasonic and TiAl3 particles congregate around C powder. Meanwhile, due to ultrasonic cavitation, dissolved TiAl3 provides better surface condition for the synthesis reaction of TiC. The reaction route is that C and dissolved Ti react to form TiC. Ultrasonic cavitation has a thermal activation effect on TiC particles and Al-3Ti-0.15C refiner has excellent microstructural refining effect on α-Al.展开更多
基金financial support under grant number EP/N007638/1supported by EPSRC under grant number EP/W021080/1
文摘In Mg-Ca alloys the grain refining mechanism,in particular regarding the role of nucleant substrates,remains the object of debates.Although native MgO is being recognised as a nucleating substrate accounting for grain refinement of Mg alloys,the possible interactions of MgO with alloying elements that may alter the nucleation potency have not been elucidated yet.Herein,we design casting experiments of Mg-xCa alloys varied qualitatively in number density of native MgO,which are then comprehensively studied by advanced electron microscopy.The results show that grain refinement is enhanced as the particle number density of MgO increases.The native MgO particles are modified by interfacial layers due to the co-segregation of Ca and N solute atoms at the MgO/Mg interface.Using aberration-corrected scanning transmission electron microscopy and electron energy loss spectroscopy,we reveal the nature of these Ca/N interfacial layers at the atomic scale.Irrespective of the crystallographic termination of MgO,Ca and N co-segregate at the MgO/Mg interface and occupy Mg and O sites,respectively,forming an interfacial structure of a few atomic layers.The interfacial structure is slightly expanded,less ordered and defective compared to the MgO matrix due to compositional deviations,whereby the MgO substrate is altered as a poorer template to nucleate Mg solid.Upon solidification in a TP-1 mould,the impotent MgO particles account for the grain refining mechanism,where they are suggested to participate into nucleation and grain initiation processes in an explosive manner.This work not only reveals the atomic engineering of a substrate through interfacial segregation but also demonstrates the effectiveness of a strategy whereby native MgO particles can be harnessed for grain refinement in Mg-Ca alloys.
基金the financial support by National Key Research and Development Project(Grand No.2020YFC1107202)Guangdong Basic and Applied Basic Research Foundation(Grand No.2020A1515110754)+3 种基金MOE Key Lab of Disaster Forest and Control in Engineering,Jinan University(Grand No.20200904008)Educational Commission of Guangdong Province(Grand No.2020KTSCX012)the Fundamental Research Funds for Central Universities(Grand No.21620342)the support from National Natural Science Foundation of China,NSFC(Grand No.51775556)。
文摘Additive manufacturing(AM)of Mg alloys has become a promising strategy for producing complex structures,but the corrosion performance of AM Mg components remains unexploited.In this study,wire and arc additive manufacturing(WAAM)was employed to produce single AZ31 layer.The results revealed that the WAAM AZ31 was characterized by significant grain refinement with non-textured crystallographic orientation,similar phase composition and stabilized corrosion performance comparing to the cast AZ31.These varied corrosion behaviors were principally ascribed to the size of grain,where cast AZ31 and WAAM AZ31 were featured by micro galvanic corrosion and intergranular corrosion,respectively.
文摘An alloy of A1-8wt% Si-0.8wt% Fe was cast in a metallic die, and its microstrucmral changes due to Ti-B refiner and Sr modifier additions were studied. Apart from usual refinement and modification of the microstructure, some mutual influences of the additives took place, and no mutual poisoning effects by these additives, in combined form, were observed. It was noticed that the dimensions of the iron-rich intermetallics were influenced by the additives causing them to become larger. The needle-shaped intermetallics that were obtained from refiner addition became thicker and longer when adding the modifier. It was also found that a-Al and eutectic silicon phases preferentially nucleate on different types of intermetallic compounds. The more iron content of the intermetallic compounds and the more changes in their dimensions occurred. Formation of the shrinkage porosities was also observed.
基金Project supported by the Natural Science Foundation of Shanxi Province (20011047)Patent Generalization Project ofShanxi Province (051025)
文摘Al-Ti-C grain refiner was prepared by SHS (self-propagating high-temperature synthesis )-melting technique. The effect of La on the microstructures of grain refiner was studied by OM, TEM, SEM, XRD, and EDS. The experimental results indicate that La can improve the wettability between liquid aluminum and graphite ; the addition of La results in dispersive distribution of TiAl3 and TiC particles in the matrix. An excellent grain refining performance of Al-Ti-C grain refiner on commercially pure Al was obtained.
文摘Erratum to:International Journal of Minerals, Metallurgy and MaterialsVolume 28, Number 7, July 2021, Page 1112 The original version of this article unfortunately contained mistakes. Symbols in Table 2 are used incorrectly.
基金supported by Project supported by the Joint Funds of the National Natural Science Foundation of China(Grant No.U20A20230)Natural Science Foundation of Shanxi Province(No.201901D111176)+2 种基金Project supported by the Key R&D program of Shanxi Province(No.2020XXX015)Research Project Supported by Shanxi Scholarship Council of China(2021-127)Graduate Education Innovation Program of Shanxi Province(2022Y579).
文摘The effects of different complex shear stress conditions on grain refinement and texture evolution of Mg-13Gd-4Y-2Zn-0.5Zr alloy were investigated.With increasing strain rate,the average grain size of compression-shear(CS)and compression-torsion(CT)samples are decreased,and the grain size of dynamic recrystallization(DRX)grains is also decreased.This is because that the precipitation number ofβphases is increased,and the hindering effect on grain growth can be significantly enhanced.The DRX fractions of CS and CT samples are decreased with increased strain rate.The low DRX fraction at high strain rate is related to the insufficient time for grains to nucleate.The DRX process can be promoted by the PSN mechanism of second phases,and the grain growth can be restricted by the pinning effect.At the same time,the texture strength is enhanced as the strain rate increased.Besides,the kinking degree of lamellar long-period stacking ordered(LPSO)phases is increased.Under complex shear stress conditions,non-basal slip,especially pyramidal slip,is easily activated and the texture is deflected greatly.Compared with the CS samples,CT samples have smaller average grain size,higher DRX fraction,and lower texture strength for a certain strain rate.This is because that the equivalent stress of the CT sample is larger,the stress triaxiality is smaller,so more serious dislocations are piled up near grain boundaries and second phases.At the same time,since CT sample was sheared with torsion,the dislocation movement path can be called“rotational dislocation accumulation”,and the longer distribution path of the CT sample is generated,so more sub-grains and low-angle grain boundaries(LAGBs)are formed.Compared with the CS sample,more huge-angle grain boundaries(HAGBs)and DRX grains are formed from grain boundary to grain interior,so better grain refinement effect is achieved.
基金supported by the National Natural Science Foundation of China (Grant Nos.U2037601,51821001,and 52105348)the Natural Science Foundation for Young of Jiangsu Province (Grant No.BK20190863)the Research Program of Joint Research Center of Advanced Spaceflight Technologies (No.USCAST2020-31)。
文摘High-performance cast magnesium rare-earth(Mg-RE) alloys are one of the most important materials among all developed Mg alloy families, and have shown great potential in military and weapons, aerospace and aviation, orthopedic implants, etc. Controlling grain size and distribution of it is key to the promising mechanical performance of Mg-RE alloy casting components. During the casting of a real component, nearly every procedure in the fabrication process will influence the grain refinement effect. The procedure may include and may not be limited to the chemical inoculations, possibly applied physical fields, the interfere between grain refiner and purifications, and the casting techniques with different processing parameters. This paper reviews the recent advances and proposed future developments in these categories on grain refinement of cast Mg-RE alloys. The review will provide insights for the future design of grain refinement techniques,the choosing of processing parameters, and coping strategies for the failure of coarsening for cast Mg-RE components with high quality and good performance.
基金supported by National Key Research and Development Program of China (No.2023YFB3710900)National Natural Science Foundation of China (Nos.U2241235,U2167213,51971053)+2 种基金funded by the Project of Promoting Talents in Liaoning province (No.XLYC2203202)the financial assistance from Young Elite Scientists Sponsorship Program by CAST (2019-2021QNRC001,2019-2021QNRC002,2019-2021QNRC003)the fund from the Fundamental Research Funds for the Central Universities (N2202020)。
文摘Low absolute strength becomes one major obstacle for the wider applications of low/no rare-earth(RE) containing Mg alloys. This review firstly demonstrates the importance of grain refinement in improving strength of Mg alloys by comprehensively comparing with other strategy, e.g., precipitation strengthening. Dynamic recrystallization(DRX) plays a crucial role in refining grain size of Mg wrought alloys.Therefore, secondly, the DRX models, grain nucleation mechanisms and the related grain refinement abilities in Mg alloys are summarized,including phase boundary, twin boundary and general boundary induced recrystallization. Thirdly, the newly developed low-RE containing Mg alloy, e.g., Mg-Ce, Mg-Nd and Mg-Sm based alloys, and the RE-free Mg alloys, e.g., Mg-Al, Mg-Zn, Mg-Sn and Mg-Ca based alloy,are reviewed, with the focus on enhancing the mechanical properties mainly via the grain refinement strategy. At the last section, the perspectives and outstanding issues concerning high-performance Mg wrought alloys are also proposed. This review is meant to promote the deep understanding on the critical role of grain refinement in Mg alloys and provide reference for the development of other high strength and low-cost Mg alloys which are fabricated by the conventional extrusion/rolling processing.
基金financially supported by the National Natural Science Foundation of China(Grant Nos.52071194,U1760204)the National Key Research Program of China(Grant Nos.2020YFB2008401 and 2017YFB0701800)。
文摘A wide-spectrum pulsed magnetic field(WSPMF)was obtained by adjusting the number of current pulses and the pulse interval between adjacent pulses.The effect of WSPMF on the grain refinement of pure aluminium was studied.The distribution of electromagnetic force and flow field in the melt under the WSPMF was simulated to reveal the grain refining mechanism.Results show that the grain refinement is attributed to the combined effect of the melt flow and oscillation under a WSPMF.When the pulse interval is 5 ms,the extreme value of electromagnetic force is the highest,and the size of the crystal nucleus is 0.35 mm.In the case of similar flow rates,the grain size gradually decreases as the pulse interval increases.The range of the harmonic frequency of the magnetic field gradually expands with the increase of the pulse interval,which can provide more energy for nucleation at the solid-liquid interface and promote nucleation.
基金the Major Science and Technology Project of Henan Province.(No.221100230300).
文摘Numerical simulation is one of the important auxiliary methods for studying materials-related problems. In this study, phase field simulation was employed to investigate the refinement behavior of BAg55CuZn-x B brazing alloys. Simulation and experimental studies were conducted for B contents ranging from 0 wt.% to 0.2 wt.%. The results demonstrated that the addition of 0.05 wt.% B in the brazing alloy leads to a significant refinement effect. As the B content increases, the grain size further reduces, and a refinement stagnation phenomenon occurs after exceeding 0.15 wt.%. The solidification process of brazing alloys with different B content was predicted by simulation, and the simulation results showed that with the increase of B content, the initial number of nucleation increased, and the radius of the dendrite tip decreased. The simulation results are in good agreement with the experimental findings, providing further evidence of the refining effect of the B element and the reliable predictive capability of the phase field model.
文摘This work aims to present a perspective for porosity formation in three different alloys:A356,A413 and A380.1 by taking into account the addition of Al-B grain refiners:AlTi5B1 and Al3B.The directional solidification method was used,and microstructural changes of the alloys and its correlation with porosity formation were investigated.Pore size,number of pores,average pore length and distribution of pores were statistically analyzed.Also,external shrinkage was examined,and the volume of external shrinkage was calculated.It was found that there was a relationship between external shrinkage and the size and number of pores.As the size and number of pores internally decrease,external shrinkage increases.Additionally,porosity is decreased in all the three Al-Si alloys when Al-B grain refiners are used.The distribution of pore diameters is low when AlTi5B1 is used.Grain refiners have a different effect on porosity formation of Al-Si alloys with regard to their solidification morphology.
基金Project(50775086) supported by the National Natural Science Foundation of ChinaProject (2007AA03Z557) supported by the Hi-tech Research and Development Program of China
文摘The effects of vibration and grain refiner on the microstructure of semisolid slurry of hypoeutectic Al-Si alloy were studied. The impact of vibration on the convection of liquid was conducted by using a system of water-particle tracer. The 356 melt at temperature of 630-660 ℃ with or without grain refiner Al-5%Ti-1%B was poured into a metal cup as the vibrating vessel, then it was cooled to 590-610 ℃ in the semisolid zone and kept for some time, subsequently vibration with different frequencies was applied. The results show that the primary α(Al) particles become finer and rounder with the increase of vibration frequency. The slurry with primary α(Al) equivalent particle diameter(EPD) of about 90 μm and average shape coefficient(ASC) of about 0.5 can be prepared under vibration of 20 Hz. With the combined action of vibration and grain refiner Al-5Ti-B, even smaller and rounder spheroids with EPD of about 85 μm and ASC of about 0.6 are obtained.
基金Project(G2000067202) supported by the National Basic Research Program of China
文摘Grain refinement of superalloy K4169 was achieved by adding refiners into the alloy melt and their effects on the mechanical properties were investigated. The tensile properties at room temperature and 700 ℃ and low cycle fatigue properties at room temperature were compared for both conventional and fine grained test bars. The results indicate that the rupture strength, yield strength, elongation and reduction of area for refined grains are all much superior to those for coarse ones. Whereas the elongation and reduction of area of fine grained samples decrease at 700 ℃. Low cycle fatigue properties of samples with refined grains at room temperature are improved significantly. In addition, the degree of dispersion of low cycle fatigue data of samples with refined grains is diminished.
文摘The hereditary effect of Al Ti, Al Ti B, Al Sr master alloys on the structure and properties of A356.2 alloys was investigated, and comparison analysis between the master alloys used in the foundry industry and the fine crystalline grain refiners produced by technologies of Samara State Technical University was conducted. The results show that less than 0.5% additions of FCR master alloys can promote 8%~20% in the elongation of as cast A356.2 alloys. FCR additives are more efficient in comparison with conventional grain refiners and modifiers. Their effectiveness depends on their genetic effect of their finer structures.
文摘Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.
基金Project(51174177)supported by the National Natural Science Foundation of China
文摘An Al-3Ti-0.2C-1RE grain refiner was prepared by in-situ reaction method.The microstructure was investigated by optical microscopy(OM),scanning electron microscopy(SEM) equipped with energy-dispersive spectrometry(EDS) and X-ray diffraction(XRD).The results show that the Al-3Ti-0.2C-1RE grain refiner is composed of α-Al,TiAl3,TiC and Ti2 Al20 Ce phases.Compared with Al-3Ti-0.2C refiner,the morphology of TiAl3 phase is changed and Ti2 Al20 Ce phases form with the addition of RE.Accordingly,the refining performance is improved.The phase forming process of the refiner is as follows: Blocky Ti2 Al20 Ce and fine blocky TiAl3 form in the melt at the initial stage of reaction,then the fine blocky TiAl3 gradually disappears,and the blocky Ti2 Al20 Ce grows bigger with the increase of holding time.The predominant mechanism to synthesize TiC particles is the reaction between high concentration of solute Ti atoms and graphite particles.
基金financially supported by the National Basic Research Program of China (grant No.G2007CB613706)the Program for New Century Excellent Talents in University of China (grant No. NCET-10-0023)
文摘The effects of grain refining parameters on grain size of AM60B magnesium alloy have been investigated using an Al-5Ti-1B master alloy as refiner; and an appropriate refining technique has been developed. The results indicate that the Al-Ti-B master alloy is an effective grain refiner for AM60B alloy and the grain size can be decreased from 348 μm to 76 μm. Raising the addition temperature or the pouring temperature is beneficial for grain refinement; while for the addition amount and holding time, there is an optimal value. The appropriate grain refining technique is that 0.3% Al-Ti-B master alloy is added at 780oC and then the melt is held for 30 min before pouring. The above phenomena can be explained by the refining mechanisms that have been proposed from the related studies on Al and Mg alloys and theoretical analysis.
基金Funded by the Basic Research Project in Shanxi Province(No.202103021224183)。
文摘Through the use of purification and recirculation superheating techniques on molten glass,the Ni65Cu33Co2 alloy was successfully undercooled to a maximum temperature of 292 K.High-speed photography was employed to capture the process of interface migration of the alloy liquid,allowing for an analysis of the relationship between the morphological characteristics of the alloy liquid solidification front and the degree of undercooling.Additionally,the microstructure of the alloy was examined using metallographic microscopy,leading to a systematic study of the microscopic morphological characteristics and evolution laws of the refined structure during rapid solidification.The research reveals that the grain refining mechanism of the Ni-Cu-Co ternary alloy is consistent with that of the binary alloy(Ni-Cu).Specifically,under low undercooling conditions,intense dendritic remelting was found to cause grain refinement,while under high undercooling conditions,recrystallization driven by accumulated stress and plastic strain resulting from the interaction between the liquid flow and the primary dendrites caused by rapid solidification was identified as the main factor contributing to grain refinement.Furthermore,the study highlights the significant role of the Co element in influencing the solidification rate and reheat effect of the alloy.The addition of Co was also found to facilitate the formation of non-segregated solidification structure,indicating its importance in the overall solidification process.
基金the China Scholarship Council for the award of fellowship and funding(No.202006230137)。
文摘In order to obtain Mg alloys with fine microstructures and high mechanical performances,a novel friction-based processing method,name as“constrained friction processing(CFP)”,was investigated.Via CFP,defect-free Mg-Zn-Ca rods with greatly refined grains and high mechanical properties were produced.Compared to the previous as-cast microstructure,the grain size was reduced from more than 1 mm to around 4μm within 3 s by a single process cycle.The compressive yield strength was increased by 350%while the ultimate compressive strength by 53%.According to the established material flow behaviors by“tracer material”,the plastic material was transported by shear deformation.From the base material to the rod,the material experienced three stages,i.e.deformation by the tool,upward flow with additional tilt,followed by upward transportation.The microstructural evolution was revealed by“stop-action”technique.The microstructural development at regions adjacent to the rod is mainly controlled by twinning,dynamic recrystallization(DRX)as well as particle stimulated nucleation,while that within the rod is related to DRX combined with grain growth.
基金Funded by National Natural Science Foundation of China(No.50774023)
文摘An electrostrictive uniaxial ultrasonic levitation reaction system was designed to perform TiC synthesis reaction by suspending graphite powder in Al-3Ti melt and an Al-3Ti-0.15C grain refiner alloy was obtained. The results show that sound pressure node in which graphite suspends is formed in the melt between radiation block and reflecting board by ultrasonic and TiAl3 particles congregate around C powder. Meanwhile, due to ultrasonic cavitation, dissolved TiAl3 provides better surface condition for the synthesis reaction of TiC. The reaction route is that C and dissolved Ti react to form TiC. Ultrasonic cavitation has a thermal activation effect on TiC particles and Al-3Ti-0.15C refiner has excellent microstructural refining effect on α-Al.