采用共沉淀-高温固相法合成正极材料LiNi0．7 Mn0．3 O 2,利用 X 射线衍射分析（XRD）表征其结构、扫描电子显微镜（SEM）表征其形貌、X 射线光电子能谱（XPS）表征其价态,最终确定了该材料最佳烧成温度为820℃.研究表明,该温度下合成的...采用共沉淀-高温固相法合成正极材料LiNi0．7 Mn0．3 O 2,利用 X 射线衍射分析（XRD）表征其结构、扫描电子显微镜（SEM）表征其形貌、X 射线光电子能谱（XPS）表征其价态,最终确定了该材料最佳烧成温度为820℃.研究表明,该温度下合成的 LiNi0．7 Mn0．3 O 2具有典型的α-NaFeO 2型层状结构,颗粒形貌呈类球形且分布均匀；XPS 数据表明,LiNi0．7 Mn0．3 O 2中的 Ni 主要以＋3价形态存在,Mn 主要以＋4价形态存在.室温条件下以0．2 C 倍率在2．75~4．35 V 的电压范围内充放电,首次放电比容量高达188．9 mAh/g,70次循环后容量保持率为95．2％.展开更多
NiO-La0.3Ce0.7O2-δ(LDC30) novel anode was investigated for IT-SOFCs(Intermediate Temperature-Solid Oxide Fuel Cells) with LaGaO3-based electrolyte. The results showed that LDC30 has a suitable chemical compatibility ...NiO-La0.3Ce0.7O2-δ(LDC30) novel anode was investigated for IT-SOFCs(Intermediate Temperature-Solid Oxide Fuel Cells) with LaGaO3-based electrolyte. The results showed that LDC30 has a suitable chemical compatibility with NiO and NiO-LDC30 has a good thermal expansion matching with LDC30 interlayer and LSGM(La0.8Sr0.2Ga0.8Mg0.2O3-δ) electrolyte, so NiO-LDC30/LDC30 was considered as a feasible and novel anode system. It was also shown that NiO content plays a key role on polarization performance and morphology of the anode. When the content of NiO was 60%(mass fraction), the polarization loss of anode was the lowest. Next we will optimize the porosity and sintering procedure to modify the microstructure and performance of the anode.展开更多
文摘采用共沉淀-高温固相法合成正极材料LiNi0．7 Mn0．3 O 2,利用 X 射线衍射分析（XRD）表征其结构、扫描电子显微镜（SEM）表征其形貌、X 射线光电子能谱（XPS）表征其价态,最终确定了该材料最佳烧成温度为820℃.研究表明,该温度下合成的 LiNi0．7 Mn0．3 O 2具有典型的α-NaFeO 2型层状结构,颗粒形貌呈类球形且分布均匀；XPS 数据表明,LiNi0．7 Mn0．3 O 2中的 Ni 主要以＋3价形态存在,Mn 主要以＋4价形态存在.室温条件下以0．2 C 倍率在2．75~4．35 V 的电压范围内充放电,首次放电比容量高达188．9 mAh/g,70次循环后容量保持率为95．2％.
文摘NiO-La0.3Ce0.7O2-δ(LDC30) novel anode was investigated for IT-SOFCs(Intermediate Temperature-Solid Oxide Fuel Cells) with LaGaO3-based electrolyte. The results showed that LDC30 has a suitable chemical compatibility with NiO and NiO-LDC30 has a good thermal expansion matching with LDC30 interlayer and LSGM(La0.8Sr0.2Ga0.8Mg0.2O3-δ) electrolyte, so NiO-LDC30/LDC30 was considered as a feasible and novel anode system. It was also shown that NiO content plays a key role on polarization performance and morphology of the anode. When the content of NiO was 60%(mass fraction), the polarization loss of anode was the lowest. Next we will optimize the porosity and sintering procedure to modify the microstructure and performance of the anode.