Chip shape is one of the important factors that affect the processing quality of the deep hole.The flow field of 17 mm standard gun-drill is simulated by taking the coolant pressure as a single factor variable,and the...Chip shape is one of the important factors that affect the processing quality of the deep hole.The flow field of 17 mm standard gun-drill is simulated by taking the coolant pressure as a single factor variable,and the influence of coolant pressure on chip forming is discussed by combining with experiments in this paper.The results show that at the initial stage of chip forming,the flow of cutting fluid will intensify the lateral crimp of chips,and then affect the crimp radius of the chip and the number of turns of the crimp screw.The lateral crimp degree increases first and then decreases with the increase of coolant pressure,and the crimp degree is the smallest at 3 MPa.In addition,during the chip removal process,the stream shrinking in the flow field is the main influencing factor that drive and force the chip to break again,and their influence on the chip removal and chip breaking is proportional to the coolant pressure.展开更多
The low cycle fatigue（LCF） tests were carried out using symmetrical cyclic loading under total strain amplitude control conditions.The present paper is devoted to investigating the cyclic deformation response of Ti...The low cycle fatigue（LCF） tests were carried out using symmetrical cyclic loading under total strain amplitude control conditions.The present paper is devoted to investigating the cyclic deformation response of Ti–6Al–4V titanium and the electron-beam-welded（EBW） joint in the following aspects,i.e.,cyclic deformation behavior,fatigue life and fatigue fracture behavior.The results show that the softening of the joint is significant at larger strain ranges,while not obvious at smaller strain ranges.The joint shows shorter fatigue life at larger strain ranges and equivalent fatigue life at smaller strain ranges compared with Ti–6Al–4V base metal.A fatigue crack of the joint not only originates at the surface or subsurface,but also at defects in the fusion zone（FZ）.The crack propagation zone of Ti–6Al–4V base metal shows ductile fracture mechanism,while the joint shows brittle fracture mechanism.In all the fatigue fracture zones many dimples appear,showing the typical ductile fracture.展开更多
基金supported in part by the National Natural Science Foundation of China (No. 51505409)the Six Talent Peak Project in Jiangsu Province (No. GDZB-080)the Natural Science Research in Jiangsu Province(No.17KJB460008)。
文摘Chip shape is one of the important factors that affect the processing quality of the deep hole.The flow field of 17 mm standard gun-drill is simulated by taking the coolant pressure as a single factor variable,and the influence of coolant pressure on chip forming is discussed by combining with experiments in this paper.The results show that at the initial stage of chip forming,the flow of cutting fluid will intensify the lateral crimp of chips,and then affect the crimp radius of the chip and the number of turns of the crimp screw.The lateral crimp degree increases first and then decreases with the increase of coolant pressure,and the crimp degree is the smallest at 3 MPa.In addition,during the chip removal process,the stream shrinking in the flow field is the main influencing factor that drive and force the chip to break again,and their influence on the chip removal and chip breaking is proportional to the coolant pressure.
基金financially supported by the HiTech Research and Development Program of China(No.2012AA052102)the Program of International Science Technology Cooperation of China(No.2013DFA61590)
文摘The low cycle fatigue（LCF） tests were carried out using symmetrical cyclic loading under total strain amplitude control conditions.The present paper is devoted to investigating the cyclic deformation response of Ti–6Al–4V titanium and the electron-beam-welded（EBW） joint in the following aspects,i.e.,cyclic deformation behavior,fatigue life and fatigue fracture behavior.The results show that the softening of the joint is significant at larger strain ranges,while not obvious at smaller strain ranges.The joint shows shorter fatigue life at larger strain ranges and equivalent fatigue life at smaller strain ranges compared with Ti–6Al–4V base metal.A fatigue crack of the joint not only originates at the surface or subsurface,but also at defects in the fusion zone（FZ）.The crack propagation zone of Ti–6Al–4V base metal shows ductile fracture mechanism,while the joint shows brittle fracture mechanism.In all the fatigue fracture zones many dimples appear,showing the typical ductile fracture.