Dry sliding friction and wear behaviors of TiC_p/ZA- 12 composites

The TiC particle reinforced ZA 12 matrix composites was fabricated by XD TM process combined with stirring casting and its friction and wear properties under dry conditions were investigated using MM 200 wear testing apparatus. The effects of TiC particle content and applied load on the wear resistance properties of the composites were studied. The results show that the friction and wear properties can be greatly improved with an increase in the TiC particle content. The wear mass loss of the composites and the unreinforced ZA 12 matrix alloy increase with increasing applied load, but the increased extent of the former is smaller than that of the latter. Finally the morphologies of worn surface was analyzed using scanning electron microscope(SEM).

TiC_p/ZA-12复合材料磨损行为的研究

采用 XDTM与搅拌铸造技术相结合的工艺制备 Ti Cp/ZA- 12复合材料。利用 MM- 2 0 0摩擦磨损测试仪测试干摩擦条件下这种复合材料的磨损性能。研究了 Ti C颗粒含量、应用载荷和滑动距离对其磨损程度的影响。结果表明 :复合材料的磨损率低于基体合金磨损率 ,且磨损率随 Ti C颗粒含量的增加而减小 ;增大应用载荷和滑动距离 ,并且复合材料和基体 ZA- 12合金的磨损程度均增加 ,但复合材料的增幅明显偏小。同时发现 ,在磨损过程中存在瞬变载荷 ,当应用载荷低于瞬变载荷时 ,磨损表现为微磨损 ,当高于瞬变载荷时为剧烈磨损 ,复合材料的瞬变载荷比基体合金高得多。

TiC_p/ZA—12复合材料凝固时TiC_p的行为

利用XD法与搅拌铸造技术相结合的工艺制备TiCp/ZA— 12复合材料 ,采用常规凝固与定向凝固的技术研究增强粒子TiCp 在凝固界面的行为。结果表明 :常规凝固条件下 ,TiC含量较低时 ,颗粒主要分布于共晶相内 ,TiC含量较高时 ,颗粒不仅存在于共晶相内 ,也存在初生相内 ;定向凝固条件下 ,由于初生相对TiC的排斥作用使TiCp/ZA— 12复合材料凝固组织中存在TiC聚集的带状组织。TiCp 在带状组织中的聚集程度与TiC含量有关 ,随TiCp 含量增加 ,聚集程度减小。当TiCp 含量超过 6 %后 ,聚集带已不明显。

XD^(TM)法制备TiC_p/ZA—12复合材料

采用XD^(TM)法制备TiC_p/ZA—12复合材料。组织现察表明:TiC_p原位自生,在基体中均匀分布,没有颗粒的偏聚和宏观、微观偏析存在;自生的TiC_p多呈近球形,其表面光滑圆整,没有棱角和尖角;与基体合金的界面结合较为紧密,无反应产物存在。拉伸试验表明:复合材料具有较高的抗拉强度和屈服强度。